CN104624664A - 一种厚度400mm连铸坯粗轧头部翘曲的控制方法 - Google Patents

一种厚度400mm连铸坯粗轧头部翘曲的控制方法 Download PDF

Info

Publication number
CN104624664A
CN104624664A CN201410787378.0A CN201410787378A CN104624664A CN 104624664 A CN104624664 A CN 104624664A CN 201410787378 A CN201410787378 A CN 201410787378A CN 104624664 A CN104624664 A CN 104624664A
Authority
CN
China
Prior art keywords
rolling
height
roughing
rolling line
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410787378.0A
Other languages
English (en)
Other versions
CN104624664B (zh
Inventor
郭伟
田士平
刘永利
董占斌
赵振甫
邱志宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Jingtang United Iron and Steel Co Ltd
Original Assignee
Qinhuangdao Shouqin Metal Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinhuangdao Shouqin Metal Materials Co Ltd filed Critical Qinhuangdao Shouqin Metal Materials Co Ltd
Priority to CN201410787378.0A priority Critical patent/CN104624664B/zh
Publication of CN104624664A publication Critical patent/CN104624664A/zh
Application granted granted Critical
Publication of CN104624664B publication Critical patent/CN104624664B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种厚度400mm连铸坯粗轧头部翘曲的控制方法，属于中厚板轧制技术领域。轧制线调整步骤如下：在四辊粗轧机二级界面中输入以下参数：最大轧制力9200吨，最大扭矩3200kNm，最大压下量40mm，咬钢速度1.0～2.5m/s，轧制速度2.0～4.5m/s；在粗轧的第1～3道次，轧制线高度为当前道次压下量的一半再减去5～10mm；在粗轧的第4～6道次，轧制线高度为当前道次压下量的一半；在粗轧第7道次及后续道次，轧制线高度为当前道次压下量的一半再加上5～10mm。优点在于：创新了轧制线及上、下工作辊咬钢速度设定方法，通过二级程序计算、一级系统自动执行，实现了特厚连铸坯在粗轧过程头部板形的良好控制。

Description

一种厚度400mm连铸坯粗轧头部翘曲的控制方法
技术领域
本发明属于中厚板轧制技术领域，特别提供了一种厚度400mm连铸坯粗轧头部翘曲的控制方法。能确保轧制过程中头部平直，避免翘钢撞击设备或扣钢撞击辊道。
背景技术
本发明针对400mm连铸坯在实际生产过程中的头部翘曲特点，发明一种400mm连铸坯轧制过程中的头部翘曲控制方法，主要是调整400mm连铸板坯每道次轧制过程的轧制线高度，同时结合上下辊咬钢速配比的调整。
发明内容
本发明的目的在于提供了一种厚度400mm连铸坯粗轧头部翘曲的控制方法，解决了翘钢撞击设备或扣钢撞击辊道的问题。
轧制线高度指下工作辊上表面与机架辊上表面之差△S。
厚度400mm连铸坯粗轧头部翘曲的控制方法，其轧制线调整步骤如下：
1、在四辊粗轧机二级界面中输入以下参数：最大轧制力9200吨，最大扭矩3200kNm，最大压下量40mm，咬钢速度1.0～2.5m/s，轧制速度2.0～4.5m/s。
2、在粗轧的第1～3道次，头部下扣，粗轧轧制线高度设置为当前道次压下量的一半再减去5～10mm，例如粗轧第3道次压下量为38mm，则轧制线高度＝0.5*38-5＝14mm。上、下工作辊咬钢线速度设置为：下辊速比上辊速快2％～8％，即SKI系数为+2～+8。
3、在粗轧的第4～6道次，头部相对较平，粗轧轧制线高度为当前道次压下量的一半，例如粗轧第5道次压下量为38mm，则轧制线高度＝0.5*38＝19mm。上、下工作辊咬钢线速度设置为相等，即SKI系数为0。
4、在粗轧第7道次及后续道次，头部上翘，粗轧轧制线高度为当前道次压下量的一半再加上5～10mm。上、下工作辊咬钢线速度设置为：上辊速比下辊速快2％～8％，即SKI系数为-2～-8。
轧制线高度的基本原则是必须大于等于10mm：按步骤2～4计算出的轧制线高度如小于10mm，则轧制线高度设置为10mm。例如计算的轧制线高度为7mm，则轧制线高度最终设置为10mm。这主要是考虑辊道的承载能力。
本发明的优点在于：本发明依照400mm连铸坯粗轧头部翘曲特点，创新了轧制线及上、下工作辊咬钢速度设定方法，通过二级程序计算、一级系统自动执行，实现了特厚连铸坯在粗轧过程头部板形的良好控制。
附图说明
图1为轧制线高度△S的示意图。其中，轴承座1，辅助设备2，阶梯垫3，底板4，液压缸5。
具体实施方式
实施例1
某块钢板粗轧由400mm轧制到130mm。每道次的轧制线高度、辊速配比如下：
轧制道次 计算厚度mm 道次压下量mm 轧制线高度mm辊速配比
1 380.4 18.6 10.0 +4
2 359.5 21.0 10.0 +4
3 335.4 23.1 10.0 +2
4 310.1 25.3 12.7 0
5 278.6 31.6 15.8 0
6 244.0 34.6 17.3 0
7 206.0 38.0 19.0 -2
8 168.0 38.0 24.0 -4
9 130.0 38.0 24.0 -4

Claims (5)

1.一种厚度400mm连铸坯粗轧头部翘曲的控制方法，其特征在于：轧制线调整步骤如下：
1)在四辊粗轧机二级界面中输入以下参数：最大轧制力9200吨，最大扭矩3200kNm，最大压下量40mm，咬钢速度1.0～2.5m/s，轧制速度2.0～4.5m/s；
2)在粗轧的第1～3道次，头部下扣，粗轧轧制线高度为当前道次压下量的一半再减去5～10mm；上、下工作辊咬钢线速度为：下辊速比上辊速快2％～8％；
3)在粗轧的第4～6道次，头部相对较平，粗轧轧制线高度为当前道次压下量的一半；上、下工作辊咬钢线速度设置为相等；即SKI系数为0。
4)在粗轧第7道次及后续道次，头部上翘，粗轧轧制线高度为当前道次压下量的一半再加上5～10mm；上、下工作辊咬钢线速度为：上辊速比下辊速快2％～8％。
2.根据权利要求1所述的方法，其特征在于：所述的步骤2)中SKI系数为+2～+8。
3.根据权利要求1所述的方法，其特征在于：所述的步骤3)中SKI系数为0。
4.根据权利要求1所述的方法，其特征在于：所述的步骤4)中SKI系数为-2～-8。
5.根据权利要求1所述的方法，其特征在于：所述的步骤2)～4)计算出的轧制线高度如小于10mm，则轧制线高度设置为10mm。
CN201410787378.0A 2014-12-17 2014-12-17 一种厚度400mm连铸坯粗轧头部翘曲的控制方法 Active CN104624664B (zh)