CN104610884A - 用于显示屏的防刮保护膜 - Google Patents
用于显示屏的防刮保护膜 Download PDFInfo
- Publication number
- CN104610884A CN104610884A CN201510059212.1A CN201510059212A CN104610884A CN 104610884 A CN104610884 A CN 104610884A CN 201510059212 A CN201510059212 A CN 201510059212A CN 104610884 A CN104610884 A CN 104610884A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- resistant protective
- scratch
- display screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明一种用于显示屏的防刮保护膜,包括一薄膜基材层,此薄膜基材层上面涂覆一抗刮涂层,此薄膜基材层下表面通过压敏胶粘剂层与一离型膜粘合连接;所述压敏胶粘剂层由以下重量份组分组成:甲基丙烯酸甲酯75~78份,丙烯酸乙酯30~32份,二甲基二乙氧基硅烷16~18份,溶剂40~45份,纳米级SiO2粉体2.2~2.8份,纳米级Al2O3粉体1.2~1.8份,微米级SiO2粉体0.2~0.5份,微米级Al2O3粉体0.2~0.5份,异氰酸酯0.8~1份,松香树脂4.5~5份,萜烯树脂4~5份,偶氮化合物1.2~1.5份,N-亚硝基化合物4.5~5份,偶联剂1~1.5份。本发明在不增加颗粒直径的情况下提高了丙烯酸胶黏剂粗糙度,也避免了SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
Description
技术领域
本发明涉及一种保护膜,特别涉及一种用于显示屏的防刮保护膜。
背景技术
随着电子科技的蓬勃发展,使得例如手机、MP4、MP5、相机、数码摄影机、笔记本电脑等电子产品的推陈出新。为了避免电子产品屏幕表面受到刮伤或磨损,影响使用效果,一般会在电子产品的屏幕表面贴卜屏幕保护膜。保护膜一般由基材层和涂覆在该基材层上的胶粘剂层构成。这对粘胶带的要求也越来越高,常常需要粘着力强且厚度在较薄的粘胶带。对于电子产品或者其它产品,一旦使用粘胶带,则需要该粘胶带在温差变化大的情况下能一直维持粘性,且能容易将胶黏剂从薄膜上剥离,其次,现有技术在兼顾均匀性等其它性能下,提高雾面粗糙度存在瓶颈。
发明内容
本发明提供一种用于显示屏的防刮保护膜,该用于显示屏的防刮保护膜在不增加颗粒直径的情况下提高了丙烯酸胶黏剂粗糙度,避免了团簇,也避免了SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
为达到上述目的,本发明采用的技术方案是:一种用于显示屏的防刮保护膜,所述用于显示屏的防刮保护膜包括一薄膜基材层,此薄膜基材层上面涂覆一抗刮涂层,此薄膜基材层下表面通过压敏胶粘剂层与一离型膜粘合连接;
所述压敏胶粘剂层由以下重量份组分组成:
甲基丙烯酸甲酯 70~80份,
丙烯酸乙酯 25~38份,
二甲基二乙氧基硅烷 15~18份,
溶剂 35~45份,
纳米级SiO2粉体 2~3份,
纳米级Al2O3粉体 1.2~1.8份,
微米级SiO2粉体 0.2~0.5份,
微米级Al2O3粉体 0.2~0.5份,
异氰酸酯 0.6~1份,
松香树脂 4~6份,
萜烯树脂 3~6份,
偶氮化合物 1~1.5份,
N-亚硝基化合物 4~6份,
偶联剂 0.5~2份;
所述偶联剂化学式为: CH2=CH-Si(OC2H5)3。
上述技术方案中进一步改进的技术方案如下:
上述方案中,所述溶剂为甲苯、乙酸乙酯和丁酮中至少一种。
由于上述技术方案运用,本发明与现有技术相比具有下列优点和效果:
1. 本发明用于显示屏的防刮保护膜,其采用纳米级和微米级SiO2粉体、Al2O3粉体和甲基丙烯酸甲酯70~80份,丙烯酸乙酯25~38份,二甲基二乙氧基硅烷15~18份与硅烷偶联剂、异氰酸酯共同作用,相对单一使用纳米级或微米级SiO2粉体、Al2O3粉体,提高了丙烯酸胶黏剂粗糙度,也有利于SiO2粉体、Al2O3粉体均匀分布和在体系中的分散,避免了团簇;其次,偶氮化合物1.2~1.5份, N-亚硝基化合物4.5~5份的加入,也避免了SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
2. 本发明用于显示屏的防刮保护膜,松香树脂4~6份,萜烯树脂3~6份与甲基丙烯酸甲酯70~80份,丙烯酸乙酯25~38份,二甲基二乙氧基硅烷15~18份共同作用,避免了了由SiO2粉体、Al2O3粉体加入导致的耐高温性能的下降,提高了耐高温性能,以及在温差变化下的粘度的稳定性,从而提高了产品的可靠性。
附图说明
附图1为本发明用于显示屏的防刮保护膜结构示意图。
以上附图中:1、薄膜基材层;2、抗刮涂层;3、压敏胶粘剂层;4、离型膜。
具体实施方式
下面结合附图及实施例对本发明作进一步描述:
实施例1~5:一种用于显示屏的防刮保护膜,所述用于显示屏的防刮保护膜包括一薄膜基材层1,此薄膜基材层1上面涂覆一抗刮涂层2,此薄膜基材层1下表面通过压敏胶粘剂层3与一离型膜4粘合连接;
所述压敏胶粘剂层3由以下重量份组分组成:
甲基丙烯酸甲酯 75~78份,
丙烯酸乙酯 30~32份,
二甲基二乙氧基硅烷 16~18份,
溶剂 40~45份,
纳米级SiO2粉体 2.2~2.8份,
纳米级Al2O3粉体 1.2~1.8份,
微米级SiO2粉体 0.2~0.5份,
微米级Al2O3粉体 0.2~0.5份,
异氰酸酯 0.8~1份,
松香树脂 4.5~5份,
萜烯树脂 4~5份,
偶氮化合物 1.2~1.5份,
N-亚硝基化合物 4.5~5份,
偶联剂 1~1.5份;
所述偶联剂化学式为: CH2=CH-Si(OC2H5)3。
上述纳米SiO2粉体平均直径为12nm,所述纳米Al2O3粉体平均至今为30nm。
上述溶剂为甲苯、乙酸乙酯和丁酮中至少一种。
实施例1~5用于显示屏的防刮保护膜中压敏胶粘剂层3各组分重量份含量见表1。
表1
实施例一 | 实施例二 | 实施例三 | 实施例四 | 实施例五 | |
甲基丙烯酸甲酯 | 72 | 80 | 75 | 78 | 70 |
丙烯酸乙酯 | 32 | 35 | 28 | 30 | 26 |
二甲基二乙氧基硅烷 | 16 | 16 | 18 | 17 | 15 |
溶剂 | 38 | 41 | 44 | 42 | 40 |
纳米级SiO2粉体 | 2.6 | 3 | 2.5 | 2.3 | 2.8 |
纳米级Al2O3粉体 | 1.6 | 1.4 | 1.5 | 1.6 | 1.2 |
微米级SiO2粉体 | 0.42 | 0.25 | 0.3 | 0.4 | 0.2 |
微米级Al2O3粉体 | 0.26 | 0.3 | 0.35 | 0.45 | 0.4 |
异氰酸酯 | 0.65 | 1 | 0.9 | 0.6 | 0.8 |
松香树脂 | 4.5 | 5 | 5.5 | 6 | 4.2 |
萜烯树脂 | 5.8 | 4 | 5 | 3.2 | 4.5 |
偶氮化合物 | 1 | 1.4 | 1.2 | 1.2 | 1.5 |
N-亚硝基化合物 | 4 | 6 | 4.8 | 5.2 | 4.6 |
偶联剂 | 1.8 | 1 | 1.5 | 0.8 | 1.2 |
一种用于显示屏的防刮保护膜中压敏胶粘剂层3的制备工艺, 包括以下步骤:
步骤1. 将0.2~0.5份微米级SiO2粉体、0.2~0.5份微米级Al2O3粉体和0.5~2份硅烷偶联剂加入第一溶剂中进行超声波处理获得预分散液;
步骤2. 将2~3份纳米级SiO2粉体、1.2~1.8份纳米级Al2O3粉体和异氰酸酯0.6~1份加入预分散液中进行超声波处理获得调制后预分散液;
步骤3. 将甲基丙烯酸甲酯70~80份、丙烯酸乙酯25~38份和二甲基二乙氧基硅烷15~18份加入第二溶剂中进行机械搅拌获得聚合物溶液;
步骤4. 将步骤2的调制后预分散液、步骤3的聚合物溶液混合并依次加入松香树脂4~6份,萜烯树脂3~6份,偶氮化合物1~1.5份, N-亚硝基化合物4~6份,进行机械高速搅拌和超声波搅拌,从而获得所述压敏胶粘剂层3。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (2)
1. 一种用于显示屏的防刮保护膜,其特征在于:所述用于显示屏的防刮保护膜包括一薄膜基材层(1),此薄膜基材层(1)上面涂覆一抗刮涂层(2),此薄膜基材层(1)下表面通过压敏胶粘剂层(3)与一离型膜(4)粘合连接;
所述压敏胶粘剂层(3)由以下重量份组分组成:
甲基丙烯酸甲酯 75~78份,
丙烯酸乙酯 30~32份,
二甲基二乙氧基硅烷 16~18份,
溶剂 40~45份,
纳米级SiO2粉体 2.2~2.8份,
纳米级Al2O3粉体 1.2~1.8份,
微米级SiO2粉体 0.2~0.5份,
微米级Al2O3粉体 0.2~0.5份,
异氰酸酯 0.8~1份,
松香树脂 4.5~5份,
萜烯树脂 4~5份,
偶氮化合物 1.2~1.5份,
N-亚硝基化合物 4.5~5份,
偶联剂 1~1.5份;
所述偶联剂化学式为: CH2=CH-Si(OC2H5)3。
2. 根据权利要求1所述的用于显示屏的防刮保护膜,其特征在于:所述溶剂为甲苯、乙酸乙酯和丁酮中至少一种。