CN104609775A - Method for preparation of porous non-fired product from waste ceramic and waste glass - Google Patents
Method for preparation of porous non-fired product from waste ceramic and waste glass Download PDFInfo
- Publication number
- CN104609775A CN104609775A CN201410783487.5A CN201410783487A CN104609775A CN 104609775 A CN104609775 A CN 104609775A CN 201410783487 A CN201410783487 A CN 201410783487A CN 104609775 A CN104609775 A CN 104609775A
- Authority
- CN
- China
- Prior art keywords
- waste
- glass
- waste ceramic
- ceramic
- fired product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a method for preparation of a porous non-fired product from waste ceramic and waste glass, the process is simple, solid waste utilization rate is high, the non-fired product is light in weight, better in strength, good in durability, and smaller in energy consumption, and has no pollution to the environment, used raw materials comprise cement, waste ceramic, waste glass and gypsum and the like, and after even mixing and stirring, mold molding and steam curing, the finished product can be obtained by placing outdoor at room temperature for 10-15 days.
Description
Technical field
The present invention relates to the preparation method of unburned goods, be specifically related to utilize waste ceramic and glass to prepare the method for unburned goods.
Background technology
China has a large amount of waste ceramics and glass every year, is mainly derived from industry and life, and waste ceramic and glass are stablized due to its physicochemical property, can as building material, but utilizes it in reality and not goodly cause great destruction to environment.And utilize waste ceramic and glass compound to be prepared into burden that unburned goods not only can alleviate environment, also turn waste into wealth simultaneously, save natural resources, while the excellent insulation of unburned product properties, heat insulation of being made up of it.
Summary of the invention
The object of this invention is to provide a kind of method utilizing waste ceramic and scrap glass to prepare the unburned goods of porous, technique is simple, high to utilization rate of solid waste, described unburned goods are lightweight, intensity better, good endurance, to the less environmentally safe of energy consumption.
Technical solution of the present invention is: raw material adopts cement, waste ceramic and scrap glass, gypsum, quartz sand, stalk, water glass, water, polypropylene fibre, whipping agent, water reducer, above-mentioned raw materials counts 6-12 part, 32-70 part, 9-15 part, 20-30 part, 5-10 part, 6-8 part, 5-8 part, 2-3 part, 0.1-0.5 part, 0.05-0.2 part by weight, the length of described stalk is 2-5mm, through mixing and stirring, adobe is made through vibration, extrusion molding again in mould, vapor cure is after 48 hours, and by it, outdoor placement 10-15 days must finished product at normal temperatures.
Advantageous Effects:
Present invention process is simple, high to utilization rate of solid waste, described unburned goods are lightweight, intensity better, good endurance, to the less environmentally safe of energy consumption, lightweight and pollution-free, use organic and inorganic fibre to greatly strengthen the resistance to cleavage of unburned goods in the feed simultaneously.
Embodiment
Embodiment 1
A kind of method utilizing waste ceramic and scrap glass to prepare the unburned goods of porous, it is characterized in that: raw material adopts cement, waste ceramic and scrap glass, gypsum, quartz sand, stalk, water glass, water, polypropylene fibre, whipping agent, water reducer, above-mentioned raw materials counts 8 parts by weight, 65 parts, 15 parts, 25 parts, 5 parts, 8 parts, 8 parts, 2 parts, 0.1 part, 0.05 part, the length of described stalk is 2-5mm, through mixing and stirring, again in mould through vibration, adobe is made in extrusion molding, vapor cure is after 48 hours, its outdoor placement is at normal temperatures obtained finished product in 10 days.
Embodiment 2
A kind of method utilizing waste ceramic and scrap glass to prepare the unburned goods of porous, it is characterized in that: raw material adopts cement, waste ceramic and scrap glass, gypsum, quartz sand, stalk, water glass, water, polypropylene fibre, whipping agent, water reducer, above-mentioned raw materials counts 10 parts by weight, 50 parts, 10 parts, 20 parts, 8 parts, 6 parts, 7 parts, 2 parts, 0.1 part, 0.05 part, the length of described stalk is 2-5mm, through mixing and stirring, again in mould through vibration, adobe is made in extrusion molding, vapor cure is after 48 hours, its outdoor placement is at normal temperatures obtained finished product in 10 days.
Claims (1)
1. the method utilizing waste ceramic and scrap glass to prepare the unburned goods of porous, it is characterized in that: raw material adopts cement, waste ceramic and scrap glass, gypsum, quartz sand, stalk, water glass, water, polypropylene fibre, whipping agent, water reducer, above-mentioned raw materials counts 6-12 part by weight, 32-70 part, 9-15 part, 20-30 part, 5-10 part, 6-8 part, 5-8 part, 2-3 part, 0.1-0.5 part, 0.05-0.2 part, the length of described stalk is 2-5mm, through mixing and stirring, again in mould through vibration, adobe is made in extrusion molding, vapor cure is after 48 hours, by it, outdoor placement 10-15 days must finished product at normal temperatures.