CN104609776A - Composite porous non-fired product preparation method - Google Patents
Composite porous non-fired product preparation method Download PDFInfo
- Publication number
- CN104609776A CN104609776A CN201410783548.8A CN201410783548A CN104609776A CN 104609776 A CN104609776 A CN 104609776A CN 201410783548 A CN201410783548 A CN 201410783548A CN 104609776 A CN104609776 A CN 104609776A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- fired product
- parts
- composite porous
- slag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a composite porous non-fired product preparation method, the process is simple, solid waste utilization rate is high, the non-fired product is light in weight, better in strength, good in durability, and smaller in energy consumption, and has no pollution to the environment, used raw materials comprise cement, slag and the like, after even mixing and stirring, a green brick can be prepared by vibration and extrusion molding in a mold, after 48 hours of steam curing, the green brick is placed outdoor at room temperature for 10-15 days so as to obtain the finished product.
Description
Technical field
The present invention relates to the preparation method of unburned goods, be specifically related to utilize solid waste to prepare the method for unburned goods.
Background technology
China has a large amount of dump slags and discarded ceramic tile every year, is mainly derived from industrial production and life.Slag and discarded ceramic tile are attempted it can be used as building materials raw material owing to having certain strength and stability people, but poor performance.And slag and discarded ceramic tile are prepared into the burden that unburned goods not only can alleviate environment, also turn waste into wealth simultaneously, save natural resources, while the excellent insulation of unburned product properties, heat insulation of being made up of it.
Summary of the invention
The object of this invention is to provide a kind of unburned article fabrication methods, technique is simple, and high to utilization rate of solid waste, described unburned goods are lightweight, intensity better, good endurance, to the less environmentally safe of energy consumption.
Technical solution of the present invention is: raw material (by weight) adopts cement 15-20 part, slag and discarded ceramic tile 40-70 part, gypsum 5-10 part, sand 20-35 part, stalk 5-10 part, ether of cellulose 3-5 part and water 2-6 part, whipping agent 0.1-0.5 part, water reducer 0.05-0.2 part, the length of described stalk is 2-5mm, through mixing and stirring, adobe is made through vibration, extrusion molding again in mould, vapor cure is after 48 hours, and by it, outdoor placement 10-15 days must finished product at normal temperatures.Discarded ceramic tile goods obtain by described discarded ceramic tile after pulverization process.
Advantageous Effects of the present invention:
Present invention process is simple, high to utilization rate of solid waste, described unburned goods are lightweight, intensity better, good endurance, to the less environmentally safe of energy consumption, lightweight and pollution-free.
Embodiment
Embodiment 1
A kind of preparation method of unburned goods, raw material adopts cement, slag and discarded ceramic tile, gypsum, sand, stalk, ether of cellulose and water, whipping agent, water reducer, above-mentioned raw materials counts 15 parts, 65 parts, 10 parts, 35 parts, 10 parts, 5 parts, 6 parts, 0.1 part, 0.05 part by weight, the length of described stalk is 2-5mm, through mixing and stirring, in mould, make adobe through vibration, extrusion molding again, its outdoor placement at normal temperatures, after 48 hours, is obtained finished product in 12 days by vapor cure.
Embodiment 2
A kind of preparation method of unburned goods, it is characterized in that: raw material adopts cement, slag and discarded ceramic tile, gypsum, sand, stalk, ether of cellulose and water, whipping agent, water reducer, above-mentioned raw materials counts 16 parts, 45 parts, 5 parts, 20 parts, 5 parts, 3 parts, 2 parts, 0.1 part, 0.05 part by weight, the length of described stalk is 2-5mm, through mixing and stirring, adobe is made through vibration, extrusion molding again in mould, its outdoor placement at normal temperatures, after 48 hours, is obtained finished product in 10 days by vapor cure.
Claims (1)
1. the preparation method of compound porous unburned goods, it is characterized in that: raw material (by weight) adopts cement 15-20 part, slag and discarded ceramic tile 40-70 part, gypsum 5-10 part, sand 20-35 part, stalk 5-10 part, ether of cellulose 3-5 part and water 2-6 part, whipping agent 0.1-0.5 part, water reducer 0.05-0.2 part, the length of described stalk is 2-5mm, discarded ceramic tile goods obtain by described discarded ceramic tile after pulverization process, through mixing and stirring, again in mould through vibration, adobe is made in extrusion molding, vapor cure is after 48 hours, by it, outdoor placement 10-15 days must finished product at normal temperatures.