CN104562099A - Novel chloride zinc-plating brightener and preparation method thereof - Google Patents
Novel chloride zinc-plating brightener and preparation method thereof Download PDFInfo
- Publication number
- CN104562099A CN104562099A CN201310486817.XA CN201310486817A CN104562099A CN 104562099 A CN104562099 A CN 104562099A CN 201310486817 A CN201310486817 A CN 201310486817A CN 104562099 A CN104562099 A CN 104562099A
- Authority
- CN
- China
- Prior art keywords
- parts
- brightener
- benzylideneacetone
- alcohol
- auxiliary brightener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the chemical field, in particular to a novel chloride zinc-plating brightener. The brightener comprises ingredients in parts by mass as follows: 20-40 parts of benzylideneacetone, 240-280 parts of a ZY-1 high-temperature carrier, 50-70 parts of an OP-21 emulsifier, 60-80 parts of sodium benzoate, 55-65 parts of a dispersing agent NNO, 6-8 parts of an auxiliary brightener A, 1.3-1.6 parts of an auxiliary brightener B and 50-100 parts of alcohol. The brightener is high in brightening speed, high in brightness and good in decoration performance; on one hand, the cost can be reduced, and the dosage of the high-temperature carrier can be decreased; on the other hand, the using effect of the brightener at the low temperature can be guaranteed.
Description
Technical field
The present invention relates to chemical field, be specifically related to a kind of novel chloride galvanizing brightening agent.
Background technology
Electroplating Operations has the history of more than 100 year from being developed so far, proposed with Russian scientist by a British scientist, afterwards their Kai Liaoyijia Electroplate Factory in partnership, and slowly expand subsequently, from then on electroplating technology starts to propagate into all over the world.Again afterwards electroplating technology also slowly be applied to decoration industry.At present, integrating with of the advanced brightening agent in domestic brightening agent production technology and the world, the development of the brightening agent having driven China emerging and application, also rise in a new aspect gradually.Because domestic brightening agent is wide in variety and assorted, level differs.So bring very large puzzlement for the selection of product to the human consumer of a lot of plating aspect.In recent years, due to the impact of Asia financial disturbance, the weakness of domestic market, staterun enterprise's bad economic results is also that depressed state appears in Electroplating Operations, and not only task amount is not enough, and technician requires high, and processing charges reduces.For helping Electroplate Factory to improve the competitiveness, significantly reducing costs, thus obtaining maximum benefit, need to produce a kind of novel product.
Summary of the invention
The object of the invention is to invent a kind of novel chloride galvanizing brightening agent, under prerequisite of improving the quality of products, can significantly reduce sound field cost again, thus obtain income to greatest extent.
The solution of the present invention is:
Novel chloride galvanizing brightening agent batching comprises: a benzylideneacetone, ZY-1 higher temperature carrier, OP-21 emulsifying agent, Sodium Benzoate, dispersing agent NNO, auxiliary brightener A, auxiliary brightener B, alcohol.The massfraction of each component is: benzylideneacetone 20 ~ 40 parts, ZY-1 higher temperature carrier 240 ~ 280 parts, OP-21 emulsifying agent 50 ~ 70 parts, Sodium Benzoate 60 ~ 80 parts, dispersing agent NNO 55 ~ 65 parts, auxiliary brightener A 6 ~ 8 parts, auxiliary brightener B 1.3 ~ 1.6 parts, alcohol 50 ~ 100 parts.The step of preparation is:
(1) in stainless steel cask fire crane porcelain enamel barrel, add water and be heated to boiling;
(2) in bucket, add dispersing agent NNO, boil 5 minutes ~ 10 minutes, be dissolved to transparent, solution is without fine particle;
(3) auxiliary brightener A, B are added, stirring and dissolving;
(4) benzylideneacetone is added again, ZY-1 higher temperature carrier, OP-21 emulsifying agent, alcohol.
In the winter time, temperature is lower.Bath temperature is low, and current density is little, to consume benzylideneacetone few, the benzylideneacetone content in brightening agent suitably can be reduced; The add-on of alcohol can optionally be determined, and can add even not good, should add in the winter time before summer, is that benzylideneacetone in brightening agent is not till precipitation.
Beneficial effect of the present invention:
Go out ray velocity fast, brightness is high, and decorate properties is good, can reduce costs on the one hand, reduces the consumption of higher temperature carrier, on the other hand, and can the result of use of precious permanent brightening agent under low-temperature condition.
Embodiment
Embodiment 1
Batching comprises: benzylideneacetone, ZY-1 higher temperature carrier, OP-21 emulsifying agent, Sodium Benzoate, dispersing agent NNO, auxiliary brightener A, auxiliary brightener B, alcohol.The massfraction of each component is: benzylideneacetone 40g/L, ZY-1 higher temperature carrier 280g/L, OP-21 emulsifying agent 50g/L, Sodium Benzoate 80g/L, dispersing agent NNO 60g/L, auxiliary brightener A 6g/L, auxiliary brightener B 1.5g/L, alcohol 100g/L.The step of preparation is: in stainless steel cask fire crane porcelain enamel barrel, add water be heated to boiling; In bucket, add dispersing agent NNO, boil 5 minutes ~ 10 minutes, be dissolved to transparent, solution is without fine particle; Auxiliary brightener A, B are added, stirring and dissolving; Add benzylideneacetone again, ZY-1 higher temperature carrier, OP-21 emulsifying agent, alcohol.
Claims (3)
1. novel chloride galvanizing brightening agent and a distributing style thereof, it is characterized in that, batching comprises: benzylideneacetone, higher temperature carrier, emulsifying agent, Sodium Benzoate, diffusant, auxiliary brightener, alcohol.
2. chloride galvanizing brightening agent according to claim 1, it is characterized in that, the massfraction of each component is: benzylideneacetone 20 ~ 40 parts, higher temperature carrier 240 ~ 280 parts, OP-21 emulsifying agent 50 ~ 70 parts, Sodium Benzoate 60 ~ 80 parts, diffusant 55 ~ 65 parts, auxiliary brightener A 6 ~ 8 parts, auxiliary brightener B 1.3 ~ 1.6 parts, alcohol 50 ~ 100 parts.
3. chloride galvanizing brightening agent according to claim 1, is characterized in that, step is: (1) adds water and is heated to boiling in stainless steel cask fire crane porcelain enamel barrel; (2) in bucket, add dispersing agent NNO, boil 5 minutes, be dissolved to transparent, solution is without fine particle; (3) auxiliary brightener A, B are added, stirring and dissolving; (4) benzylideneacetone is added again, ZY-1 higher temperature carrier, OP-21 emulsifying agent, alcohol.