CN105948686A - Glass magnesium board - Google Patents
Glass magnesium board Download PDFInfo
- Publication number
- CN105948686A CN105948686A CN201610338343.8A CN201610338343A CN105948686A CN 105948686 A CN105948686 A CN 105948686A CN 201610338343 A CN201610338343 A CN 201610338343A CN 105948686 A CN105948686 A CN 105948686A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- magnesium
- magnesium board
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of decoration materials, in particular to a glass magnesium board. The glass magnesium board is prepared by, by weight, 30-40 parts of magnesium oxide, 20-30 parts of magnesium chloride, 10-15 parts of sodium bentonite, 2-4 parts of glass fibers and 20-40 parts of purified water. The glass magnesium board is durable and high in strength.
Description
Technical field
The present invention relates to decoration material field, particularly relate to a kind of glass magnesium board.
Background technology
Chinese architecture ornament materials industry is developed rapidly along with the development of real estate, building decorating industry.At present, in
State has become as ornament materials big producing country, consumption big country and big export country in the world.Material leading products are not only in total amount
Occupy the first in the world for years, and pre-capita consumption index is near and above advanced international standard.
Along with Chinese people's growth in the living standard and the reinforcement of overall national strength, architectural decoration is not only in building industry
Proportion constantly rise, act on and becoming increasingly conspicuous, simultaneously in economic growth and social progress, the effect of performance also becomes more and more important.
Accelerate the development of architectural decoration, improve industry overall operation quality, be the important content built a well-off society in an all-round way,
Make full use of computer technology and network technology, improve business administration and design, the level of IT application of construction, will be to realize building
The important channel of decoration industry great-leap-forward development.
At present, at some special environments, needing the glass magnesium board that intensity is big, some presently commercially available glass magnesium board intensity are low, real
Border using effect is the most bad.
Summary of the invention
For overcoming the deficiencies in the prior art, the invention provides a kind of durable and that intensity is big glass magnesium board.
For solving above-mentioned technical problem, the present invention is by following technical scheme:
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 30-40 part, and magnesium chloride 20-30 part, sodio is swollen
Profit soil 10-15 part, glass fibre 2-4 part, pure water 20-40 part.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 10-15 part, magnesium oxide 30-40 part, the mixing of magnesium chloride 20-30 part, it is subsequently adding 10-20 part water,
Pour ball mill after sizing mixing into be ground, after drying, obtain powder, cross 200 mesh；
2) powder arrived of step 1) is mixed with glass fibre 2-4 part, be subsequently adding 10-20 part water, put in blender, stir
Mix 60min, form pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
The present invention compared with the existing technology has the beneficial effect that the glass magnesium board of the present invention, can be effectively improved glass magnesium
The intensity of plate, improves service life.
Detailed description of the invention
The invention discloses a kind of glass magnesium board, those skilled in the art can use for reference present disclosure, is suitably modified technique ginseng
Number realizes.Special needs to be pointed out is, all similar replacements and change apparent to those skilled in the art,
They are considered as being included in the present invention.Product of the present invention is described by preferred embodiment, related personnel
Substantially in without departing from present invention, spirit and scope, compositions as herein described and application can be modified or suitably become
More with combination, realize and apply the technology of the present invention.
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 30 parts, 20 parts of magnesium chloride, sodium bentonite 10
Part, glass fibre 2 parts, pure water 40 parts.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 10 parts, magnesium oxide 30 parts, the mixing of 20 parts of magnesium chloride, it is subsequently adding 20 parts of water, after sizing mixing, pours ball into
Grinding machine is ground, and obtains powder after drying, crosses 200 mesh；
2) powder arrived of step 1) and glass fibre 2 parts is mixed, be subsequently adding 20 parts of water, put in blender, stirring
60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
Embodiment 2
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 40 parts, 20 parts of magnesium chloride, sodium bentonite 10
Part, glass fibre 2 parts, pure water 40 parts.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 10 parts, magnesium oxide 40 parts, the mixing of 20 parts of magnesium chloride, it is subsequently adding 20 parts of water, after sizing mixing, pours ball into
Grinding machine is ground, and obtains powder after drying, crosses 200 mesh；
2) powder arrived of step 1) and glass fibre 2 parts is mixed, be subsequently adding 20 parts of water, put in blender, stirring
60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
Embodiment 3
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 35 parts, 20 parts of magnesium chloride, sodium bentonite 10
Part, glass fibre 4 parts, pure water 40 parts.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 10 parts, magnesium oxide 35 parts, the mixing of 20 parts of magnesium chloride, it is subsequently adding 20 parts of water, after sizing mixing, pours ball into
Grinding machine is ground, and obtains powder after drying, crosses 200 mesh；
2) powder arrived of step 1) and glass fibre 4 parts is mixed, be subsequently adding 20 parts of water, put in blender, stirring
60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
Embodiment 4
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 35 parts, 20 parts of magnesium chloride, sodium bentonite 15
Part, glass fibre 4 parts, pure water 40 parts.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 15 parts, magnesium oxide 35 parts, the mixing of 20 parts of magnesium chloride, it is subsequently adding 20 parts of water, after sizing mixing, pours ball into
Grinding machine is ground, and obtains powder after drying, crosses 200 mesh；
2) powder arrived of step 1) and glass fibre 4 parts is mixed, be subsequently adding 20 parts of water, put in blender, stirring
60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
Embodiment 5
A kind of glass magnesium board, is prepared from by the raw material of following weight portion: magnesium oxide 35 parts, 20 parts of magnesium chloride, sodium bentonite 15
Part, glass fibre 4 parts, pure water 20 parts.
A kind of glass magnesium board, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 15 parts, magnesium oxide 35 parts, the mixing of 20 parts of magnesium chloride, it is subsequently adding 10 parts of water, after sizing mixing, pours ball into
Grinding machine is ground, and obtains powder after drying, crosses 200 mesh；
2) powder arrived of step 1) and glass fibre 4 parts is mixed, be subsequently adding 10 parts of water, put in blender, stirring
60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.
Contrast test: glass magnesium board glass magnesium board commercially and the present invention made contrasts, and carries out it
Strength test, result shows: the intensity of the glass magnesium board that the present invention makes is more than 35MPa, and the intensity of commercially available glass magnesium board is
Between 20-30MPa.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (2)
1. a glass magnesium board, it is characterised in that be prepared from by the raw material of following weight portion: magnesium oxide 30-40 part, magnesium chloride
20-30 part, sodium bentonite 10-15 part, glass fibre 2-4 part, pure water 20-40 part.
A kind of glass magnesium board the most according to claim 1, it is characterised in that be made up of step in detail below:
1) by sodium bentonite 10-15 part, magnesium oxide 30-40 part, the mixing of magnesium chloride 20-30 part, it is subsequently adding 10-20 part water,
Pour ball mill after sizing mixing into be ground, after drying, obtain powder, cross 200 mesh；
2) powder arrived of step 1) is mixed with glass fibre 2-4 part, is subsequently adding 10-20 part water, puts in blender,
Stirring 60min, forms pastel；
3) by step 2) pastel that obtains is poured in the template of forming machine, is provided with low alkali glass fiber, roller in forming machine
Molded, last trimming shaping.