CN104559762A - Environment-friendly antistatic noise-reducing coating for machine room and preparation method thereof - Google Patents
Environment-friendly antistatic noise-reducing coating for machine room and preparation method thereof Download PDFInfo
- Publication number
- CN104559762A CN104559762A CN201510011039.8A CN201510011039A CN104559762A CN 104559762 A CN104559762 A CN 104559762A CN 201510011039 A CN201510011039 A CN 201510011039A CN 104559762 A CN104559762 A CN 104559762A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- powder
- mixture
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly antistatic noise-reducing coating for a machine room and a preparation method thereof. The environment-friendly antistatic noise-reducing coating is characterized by comprising the following raw materials in parts by weight: 2-3 parts of ammonium polyphosphate, 3-5 parts of iron powder, 1-2 parts of polyvinyl alcohol, 2-3 parts of mica powder, 1-2 parts of chlorothalonil, 2-4 parts of waterborne polyamide, 2-3 parts of methyl ethyl ketoxime, 1-2 parts of sodium alkyl naphthalene sulfonate, 0.2-0.4 part of dimethyl silicone oil, 2-3 parts of polyethylene wax emulsion, 5-7 parts of talcum powder, 2-3 parts of calcium hypophosphite, 2-3 parts of monoalkyl ether phosphate triethanolamine salt, 2-3 parts of propanediol butyl ether, 27-32 parts of organic silicone emulsion, 25-30 parts of pure acrylic emulsion, 16-20 parts of deionized water and 4-7 parts of aids. According to the coating disclosed by the invention, the preparation process is simple in flow, the reaction time is effectively shortened, the coating is stable in performance, good in economic benefits, environment-friendly, green and pollution-free, water serves as a diluent, the cured coating is high in hardness, high in wear resistance and high in glossiness, and the coating has the characteristics of water resistance, solvent resistance, noise reduction, antistatic property, rust prevention and the like and is wide in application range and simple and convenient to coat and clean.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of machine room Environmental-friendantistatic antistatic noise reducing coating and preparation method thereof.
Background technology
nowadays power equipment is if there is various problem, people are difficult to that problem is associated machine room and get on, some machine room lacks daily maintenance management, and even some months is not cleared up, and dust, paper scrap, the end of a thread are seen everywhere, and machine room door is often opened, in machine room, due malleation is destroyed, and dust, plastic foam, paper scrap fly around, and sucks power equipment, equipment is impacted, so break down.Run up in machine room many power equipments, its noise produced is very large, for the employee being in this work for a long time, body and mind brings very large injury, and the electrostatic produced in equipment running process is also harmful to the health of people, if for a long time by statics and invasion and attack, the physical and mental health of people can be affected, produce impatience, headache, uncomfortable in chest, the reactions such as insomnia of coughing; Short-term statics and invasion and attack, also can produce skin and stimulate, and causes skin pruritus, serious also can cause bronchial asthma and heart disorder.Along with the development of society, people increase for the attention of health, play simple ornamental paint, cannot meet the demand of people for machine room spraying.
Summary of the invention
The object of this invention is to provide a kind of machine room Environmental-friendantistatic antistatic noise reducing coating and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of machine room Environmental-friendantistatic antistatic noise reducing coating, is made up of the raw material of following weight part: ammonium polyphosphate 2-3, iron powder 3-5, polyvinyl alcohol 1-2, mica powder 2-3, daconil M 1-2, aqueous polyamide 2-4, methyl ethyl ketoxime 2-3, sodium alkyl naphthalene sulfonate 1-2, dimethyl silicone oil 0.2-0.4, polythene wax emulsion 2-3, talcum powder 5-7, calcium propionate 2-3, monoalky lether phosphoric acid ester triethanolamine salt 2-3, propandiol butyl ether 2-3, organic silicon emulsion 27-32, pure-acrylic emulsion 25-30, deionized water 16-20, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: tripoly phosphate sodium STPP 2-4, alkylphenol polyoxyethylene 1-2, polyvinyl alcohol 2-3, urea 6-8, nanometer silver 4-5, titanate coupling agent 1-2, methyl methacrylate 10-15, ethyl propenoate 3-5, Potassium Persulphate 1-2, water 8-11, hollow glass micropearl 6-8, fly ash micro-sphere 4-6, sepiolite powder 3-5,1.2% chitosan-acetic acid solution 3-5, ammonium molybdate 2-4, polyvinyl acetate emulsion 5-8; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
A kind of machine room Environmental-friendantistatic antistatic noise reducing coating of the present invention, be made up of following concrete steps:
(1) dimethyl silicone oil, polythene wax emulsion, sodium alkyl naphthalene sulfonate and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add ammonium polyphosphate, iron powder, mica powder, talcum powder, calcium propionate, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by organic silicon emulsion, pure-acrylic emulsion, aqueous polyamide, propandiol butyl ether, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.
Advantage of the present invention is: preparation technology's flow process of the present invention is simple, effectively shortens the reaction times, stable performance, good in economic efficiency, using water as thinner, environmentally friendly, green non-pollution, after solidification, hardness of film is high, wear resistance is good, and glossiness is good, and has water-fast, solvent resistant, noise reduction, the performance characteristics such as antistatic, antirust, use range is wide, and application is with clean simple and convenient.
specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of machine room Environmental-friendantistatic antistatic noise reducing coating, is made up of the raw material of following weight part (kilogram): ammonium polyphosphate 3, iron powder 5, polyvinyl alcohol 1, mica powder 2, daconil M 1, aqueous polyamide 3, methyl ethyl ketoxime 2, sodium alkyl naphthalene sulfonate 1, dimethyl silicone oil 0.3, polythene wax emulsion 2, talcum powder 6, calcium propionate 2, monoalky lether phosphoric acid ester triethanolamine salt 2, propandiol butyl ether 3, organic silicon emulsion 29, pure-acrylic emulsion 28, deionized water 19, auxiliary agent 5;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): tripoly phosphate sodium STPP 3, alkylphenol polyoxyethylene 1, polyvinyl alcohol 3, urea 6, nanometer silver 4, titanate coupling agent 2, methyl methacrylate 13, ethyl propenoate 4, Potassium Persulphate 2, water 8, hollow glass micropearl 6, fly ash micro-sphere 5, the chitosan-acetic acid solution 4 of sepiolite powder 3,1.2%, ammonium molybdate 3, polyvinyl acetate emulsion 7; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
A kind of machine room Environmental-friendantistatic antistatic noise reducing coating of the present invention, be made up of following concrete steps:
(1) dimethyl silicone oil, polythene wax emulsion, sodium alkyl naphthalene sulfonate and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add ammonium polyphosphate, iron powder, mica powder, talcum powder, calcium propionate, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by organic silicon emulsion, pure-acrylic emulsion, aqueous polyamide, propandiol butyl ether, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.
Paint flat appearance of the present invention is smooth, without lump, and snappiness mm≤2, hardness: 3H, shock-resistance: 50, water tolerance experiment (29 ± 1 ° of C, 36h): non-foaming, do not come off, thermotolerance experiment (100 ± 2 DEG C, 5h): non-foaming wrinkling, without cracking, resistance to artificial weathering experiment: by 500 hours, cold-hot is experiment (5 cycle) alternately: without bubbling, without cracking, without coming off, recombination loss Factor Experiment: 10 ° of C:0.159,30 ° of C:0.116.
Claims (2)
1. a machine room Environmental-friendantistatic antistatic noise reducing coating, it is characterized in that, be made up of the raw material of following weight part: ammonium polyphosphate 2-3, iron powder 3-5, polyvinyl alcohol 1-2, mica powder 2-3, daconil M 1-2, aqueous polyamide 2-4, methyl ethyl ketoxime 2-3, sodium alkyl naphthalene sulfonate 1-2, dimethyl silicone oil 0.2-0.4, polythene wax emulsion 2-3, talcum powder 5-7, calcium propionate 2-3, monoalky lether phosphoric acid ester triethanolamine salt 2-3, propandiol butyl ether 2-3, organic silicon emulsion 27-32, pure-acrylic emulsion 25-30, deionized water 16-20, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: tripoly phosphate sodium STPP 2-4, alkylphenol polyoxyethylene 1-2, polyvinyl alcohol 2-3, urea 6-8, nanometer silver 4-5, titanate coupling agent 1-2, methyl methacrylate 10-15, ethyl propenoate 3-5, Potassium Persulphate 1-2, water 8-11, hollow glass micropearl 6-8, fly ash micro-sphere 4-6, sepiolite powder 3-5,1.2% chitosan-acetic acid solution 3-5, ammonium molybdate 2-4, polyvinyl acetate emulsion 5-8; Preparation method is that methyl methacrylate, ethyl propenoate, polyvinyl acetate emulsion and water mix by (1), passes into fluidized-bed and makes its fluidisation; (2) hollow glass micropearl, fly ash micro-sphere, sepiolite powder and Potassium Persulphate are mixed, passing into fluidized-bed is boiling state; (3) mixture of step (1) is sprayed on the mixture of step (2) on the surface, under 60-80 ° of C, reacts 1-2 hour, add titanate coupling agent again and remaining surplus materials stirs after reaction terminates, then add rubber mill grinding distribution evenly.
2. a kind of machine room Environmental-friendantistatic antistatic noise reducing coating according to claim 1, is characterized in that, be made up of following concrete steps:
(1) dimethyl silicone oil, polythene wax emulsion, sodium alkyl naphthalene sulfonate and deionized water are mixed, 7-9 minute is stirred under 400-600 rev/min, add ammonium polyphosphate, iron powder, mica powder, talcum powder, calcium propionate, auxiliary agent ultrasonic disperse 15-25 minute again, obtain mixture A;
(2) be added in Scattered Kettle by organic silicon emulsion, pure-acrylic emulsion, aqueous polyamide, propandiol butyl ether, 1200-1400 rev/min of lower high-speed mixing stirs 20-40 minute, obtains mixture B;
(3) mixture A is added in mixture B, then adds all the other surplus materialss, disperse 10-20 minute under the rotating speed of 800-1000 rev/min after, forward in shredder, obtain the material of 20-40 μm, to obtain final product.