CN104559494A - Sound absorbing and noise reducing seaweed mud indoor coating and production technology thereof - Google Patents

Sound absorbing and noise reducing seaweed mud indoor coating and production technology thereof Download PDF

Info

Publication number
CN104559494A
CN104559494A CN201310470433.9A CN201310470433A CN104559494A CN 104559494 A CN104559494 A CN 104559494A CN 201310470433 A CN201310470433 A CN 201310470433A CN 104559494 A CN104559494 A CN 104559494A
Authority
CN
China
Prior art keywords
parts
algae clay
resin emulsion
water
sound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310470433.9A
Other languages
Chinese (zh)
Inventor
王和山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Kailin Chemical Co Ltd
Original Assignee
Tianchang Kailin Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Kailin Chemical Co Ltd filed Critical Tianchang Kailin Chemical Co Ltd
Priority to CN201310470433.9A priority Critical patent/CN104559494A/en
Publication of CN104559494A publication Critical patent/CN104559494A/en
Pending legal-status Critical Current

Abstract

The invention discloses a sound absorbing and noise reducing seaweed mud indoor coating and a production technology thereof. The coating comprises, by weight, 500-800 parts of a synthetic resin emulsion, 50-80 parts of cellulose, 100-200 parts of seaweed mud, 3-5 parts of a diluent, 20-30 parts of a film forming aid, 0.1-5 parts of an antifoaming agent, 0.1-1 part of an antiseptic, 0.5-2 parts of a leveling agent, 1-2 parts of a pH adjusting agent, and 600-800 parts of water. After the coating containing seaweed mud is finished on an indoor metope, sound waves are transmitted to the metope coated with the coating containing the seaweed mud and discontinuously extend in porous molecules, and weaken with the extension, so the influences of indoor noises on the environment are reduced, thereby the coating has an obvious sound absorbing effect.

Description

Dry algae clay indoor paint and production technique fall in a kind of sound-absorbing
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of sound-absorbing and fall dry algae clay indoor paint and production technique.
Background technology
In house decoration, being of wide application of wall paint is almost cover entire building room.Wall paint has waterproof, resistant, the characteristic of weather change, these characteristics house can be made to keep Nian Jiuru is new, metope can not turn to be yellow because of the passage in years.Along with the raising of people's living standard, requirements at the higher level are proposed to interior wall wall paint, not only wish attractive in appearance, also wish to have other additional function.Such as, comparatively large in generation noise ratio, and the place that may have an impact to external world spaces such as () such as singing-halls, need to take soundproof measures; And coating of the prior art can not have this function, can only be realized by the extra pugging that increases, operational procedure is complicated, and cost is high.
Summary of the invention
In order to solve the technical problem existed in background technology, the present invention proposes a kind of sound-absorbing and falling dry algae clay indoor paint and production technique, reduce room noise impact to external world.
Dry algae clay indoor paint falls in a kind of sound-absorbing that the present invention proposes, and comprises following composition according to parts by weight:
Synthetic resin emulsion: 500-800 part; Mierocrystalline cellulose: 50-80 part; Algae clay: 100-200 part; Thinner: 3-5 part; Film coalescence aid: 20-30 part; Defoamer: 0.1-5 part; Sanitas: 0.1-1 part; Flow agent: 0.5-2 part; PH conditioning agent: 1-2 part; Water: 600-800 part;
Wherein, described synthetic resin emulsion is stupid third resin emulsion or organosilicon acrylic resin emulsion; Described algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter; Described thinner is methylcyclohexane; Described film coalescence aid is one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol; Described PH conditioning agent is ammoniacal liquor and trolamine; Described flow agent is polydimethylsiloxane or PSI.
Preferably, described sound-absorbing falls dry algae clay indoor paint and comprises following composition according to parts by weight:
Synthetic resin emulsion: 550-750 part; Mierocrystalline cellulose: 55-75 part; Algae clay: 120-180 part; Thinner: 3.5-5 part; Film coalescence aid: 22-30 part; Defoamer: 1-5 part; Sanitas: 0.2-1 part; Flow agent: 0.8-2 part; PH conditioning agent: 1-2 part; Water: 600-800 part.
Preferably, described sound-absorbing falls dry algae clay indoor paint and comprises following composition according to parts by weight:
Synthetic resin emulsion: 600-700 part; Mierocrystalline cellulose: 50-70 part; Algae clay: 150-160 part; Thinner: 3.4-4.5 part; Film coalescence aid: 22-27 part; Defoamer: 1-4 part; Sanitas: 0.2-0.9 part; Flow agent: 0.8-1.5 part; PH conditioning agent: 1-2 part; Water: 600-800 part.
Fall dry algae clay indoor paint according to above-mentioned sound-absorbing, the present invention proposes the production technique that dry algae clay indoor paint falls in a kind of sound-absorbing, comprise the following steps:
The Mierocrystalline cellulose of said ratio is placed in 95 DEG C of water, uniform stirring 30 minutes;
The synthetic resin emulsion of said ratio is placed in above-mentioned solution, uniform stirring 30 minutes, keeps 70 DEG C of water temperatures;
Add the PH conditioning agent of said ratio, thinner and sanitas, uniform stirring 30 minutes, keep 70 DEG C of water temperatures;
Evenly add the algae clay of said ratio, stir and keep 70 DEG C of water temperatures in 60 minutes;
Add the membrane-forming agent of said ratio, defoamer and flow agent, after keeping 50 DEG C of water temperatures to stir 20 minutes, be naturally down to room temperature.
In the present invention, the paint finishing containing algae clay on indoor wall after, sound wave, when being delivered to the wall of coated algae clay, constantly extending, and weakens thereupon in vesicular molecule, and reducing indoor dry sound affects to external world, and sound-absorbing effect is obvious.And this coating can be whitewashed to increase coat-thickness by multilayer, make soundproof effect more obvious.
Embodiment
The embodiment of the present invention 1 provides a kind of sound-absorbing and falls dry algae clay indoor paint, comprises following composition according to parts by weight:
Synthetic resin emulsion: 500-800 part;
Mierocrystalline cellulose: 50-80 part;
Algae clay: 100-200 part;
Thinner: 3-5 part;
Film coalescence aid: 20-30 part;
Defoamer: 0.1-5 part;
Sanitas: 0.1-1 part;
Flow agent: 0.5-2 part;
PH conditioning agent: 1-2 part;
Water: 600-800 part.
The embodiment of the present invention 2 provides a kind of sound-absorbing and falls dry algae clay indoor paint, comprises following composition according to parts by weight:
Synthetic resin emulsion: 550-750 part;
Mierocrystalline cellulose: 55-75 part;
Algae clay: 120-180 part;
Thinner: 3.5-5 part;
Film coalescence aid: 22-30 part;
Defoamer: 1-5 part;
Sanitas: 0.2-1 part;
Flow agent: 0.8-2 part;
PH conditioning agent: 1-2 part;
Water: 600-800 part.
The embodiment of the present invention 3 provides a kind of sound-absorbing and falls dry algae clay indoor paint, comprises following composition according to parts by weight:
Synthetic resin emulsion: 600-700 part;
Mierocrystalline cellulose: 50-70 part;
Algae clay: 150-160 part;
Thinner: 3.4-4.5 part;
Film coalescence aid: 22-27 part;
Defoamer: 1-4 part;
Sanitas: 0.2-0.9 part;
Flow agent: 0.8-1.5 part;
PH conditioning agent: 1-2 part;
Water: 600-800 part.
In above-described embodiment 1 to 3, synthetic resin emulsion can use stupid third resin emulsion, organosilicon acrylic resin emulsion.Mierocrystalline cellulose is Vltra tears or Natvosol.Algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter, comprises multiple inorganics, such as calcium sulfate, calcium phosphate, calcium carbonate, trimagnesium phosphate, iron carbonate.Described thinner is: methylcyclohexane.Film coalescence aid can be one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol.Sanitas is Sodium Benzoate, nitrate or nitrite.Flow agent, impels coating in drying and forming-film process, to form smooth, smooth, a uniform film, such as polydimethylsiloxane or PSI.PH conditioning agent is for regulating the auxiliary agent of pH value, and PH adjusting coating conditioning agent such as uses ammoniacal liquor and trolamine.
The embodiment of the present invention 4 provides a kind of sound-absorbing and falls the dry algae clay indoor paint technological process of production, comprises the following steps:
Step 101, is placed in 95 DEG C of water, uniform stirring 30 minutes by the Mierocrystalline cellulose of said ratio;
Step 102, is placed in the solution of step 101 by the synthetic resin emulsion of said ratio, uniform stirring 30 minutes, keeps 70 DEG C of water temperatures;
Step 103, adds the PH conditioning agent of said ratio, thinner and sanitas, uniform stirring 30 minutes, keeps 70 DEG C of water temperatures;
Step 104, evenly adds the algae clay of said ratio, stirs and keeps 70 DEG C of water temperatures in 60 minutes;
Step 105, adds the membrane-forming agent of said ratio, defoamer and flow agent, after keeping 50 DEG C of water temperatures to stir 20 minutes, is naturally down to room temperature.
Coating soundproof effect of the present invention has good result through verification experimental verification, and concrete data are as shown in the table:
In the present invention, the paint finishing containing algae clay on indoor wall after, sound wave, when being delivered to the wall of coated algae clay, constantly extending, and weakens thereupon in vesicular molecule, and reducing indoor dry sound affects to external world, and sound-absorbing effect is obvious.And this coating can be whitewashed to increase coat-thickness by multilayer, make soundproof effect more obvious.
Embodiments provide the above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.

Claims (4)

1. a dry algae clay indoor paint falls in sound-absorbing, it is characterized in that, comprises following composition according to parts by weight:
Synthetic resin emulsion: 500-800 part; Mierocrystalline cellulose: 50-80 part; Algae clay: 100-200 part; Thinner: 3-5 part; Film coalescence aid: 20-30 part; Defoamer: 0.1-5 part; Sanitas: 0.1-1 part; Flow agent: 0.5-2 part; PH conditioning agent: 1-2 part; Water: 600-800 part;
Wherein, described synthetic resin emulsion is stupid third resin emulsion or organosilicon acrylic resin emulsion; Described algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter; Described thinner is methylcyclohexane; Described film coalescence aid is one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol; Described PH conditioning agent is ammoniacal liquor and trolamine; Described flow agent is polydimethylsiloxane or PSI.
2. dry algae clay indoor paint falls in sound-absorbing according to claim 1, it is characterized in that, comprises following composition according to parts by weight:
Synthetic resin emulsion: 550-750 part; Mierocrystalline cellulose: 55-75 part; Algae clay: 120-180 part; Thinner: 3.5-5 part; Film coalescence aid: 22-30 part; Defoamer: 1-5 part; Sanitas: 0.2-1 part; Flow agent: 0.8-2 part; PH conditioning agent: 1-2 part; Water: 600-800 part.
3. dry algae clay indoor paint falls in sound-absorbing according to claim 2, it is characterized in that, comprises following composition according to parts by weight:
Synthetic resin emulsion: 600-700 part; Mierocrystalline cellulose: 50-70 part; Algae clay: 150-160 part; Thinner: 3.4-4.5 part; Film coalescence aid: 22-27 part; Defoamer: 1-4 part; Sanitas: 0.2-0.9 part; Flow agent: 0.8-1.5 part; PH conditioning agent: 1-2 part; Water: 600-800 part.
4. a production technique for dry algae clay indoor paint falls in the sound-absorbing according to any one of claim 1-3, it is characterized in that, comprises the following steps:
The Mierocrystalline cellulose of said ratio is placed in 95 DEG C of water, uniform stirring 30 minutes;
The synthetic resin emulsion of said ratio is placed in above-mentioned solution, uniform stirring 30 minutes, keeps 70 DEG C of water temperatures;
Add the PH conditioning agent of said ratio, thinner and sanitas, uniform stirring 30 minutes, keep 70 DEG C of water temperatures;
Evenly add the algae clay of said ratio, stir and keep 70 DEG C of water temperatures in 60 minutes;
Add the membrane-forming agent of said ratio, defoamer and flow agent, after keeping 50 DEG C of water temperatures to stir 20 minutes, be naturally down to room temperature.
CN201310470433.9A 2013-10-10 2013-10-10 Sound absorbing and noise reducing seaweed mud indoor coating and production technology thereof Pending CN104559494A (en)