CN104533265B - A kind of luminous bamboo blind - Google Patents
A kind of luminous bamboo blind Download PDFInfo
- Publication number
- CN104533265B CN104533265B CN201410831831.3A CN201410831831A CN104533265B CN 104533265 B CN104533265 B CN 104533265B CN 201410831831 A CN201410831831 A CN 201410831831A CN 104533265 B CN104533265 B CN 104533265B
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo chip
- fluorescent material
- strontium aluminate
- aluminate fluorescent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of luminous bamboo blind.This kind of luminous bamboo blind, comprises upper sealing plate, lower shrouding, to be made up of bamboo chip/strontium aluminate fluorescent material composite panel and several blades between described upper sealing plate and lower shrouding are located in arrangement from top to bottom, the blade threading be worn together by several blades described and at least one open rope.This kind of luminous bamboo blind, structure is simple, design science, easy to use, realize the good low-light source material of bamboo wood as light source carrier, changed by luminous energy and reach the decorative effect of similar neon light at night, part electric energy can be saved, can not cause potential safety hazard to environment and the mankind, and application life is longer, energy-conserving and environment-protective; There is good actual application value and promotional value.
Description
Technical field
The present invention relates to a kind of blind, particularly the luminous bamboo blind of one.
Background technology
Bamboo blind proposes under modern house arranges the theory of new opinion " refitting decorations, with light packs repair ", in traditional household decorations the window decorations such as tulle, thick and heavy curtain of light dance just gradually by rich color, sharp-featured bamboo blind replace.Bamboo blind is because having light controllability, ventilation, easy to clean, the protection plurality of advantages such as private space and being widely used in the places such as Urban House, country villa, cafe.
There is not yet the relevant report about luminous bamboo blind in the market, in addition, there is following problem in prior art: 1, complex structure; 2, application life is shorter; 3, for realizing when reaching the decorative effect of similar neon light night, also Commercial optical paint can be applied in bamboo chip surface, because fluorescent paint inevitably exists various organic solvent, potential potential safety hazard can be had to environment and the mankind.Strontium aluminate fluorescent material is as the important light-light conversion material of a class, and its luminosity and persistence etc., performance all reached actual operation requirements, reached 8 hours persistence, had good energy storage effect.
Summary of the invention
The technical problem to be solved in the present invention is the above-mentioned defect how overcoming prior art, provides a kind of luminous bamboo blind.
Technical scheme of the present invention is as follows:
This kind of luminous bamboo blind, comprises upper sealing plate, lower shrouding, to be made up of bamboo chip/strontium aluminate fluorescent material composite panel and several blades between described upper sealing plate and lower shrouding are located in arrangement from top to bottom, the blade threading be worn together by several blades described and at least one open rope.
As optimization, the processing technology of the described blade be made up of bamboo chip/strontium aluminate fluorescent material composite panel is:
1, hack: mao bamboon is hacked by slicer, for the mao bamboon of different-diameter, by adjustment blade density to obtain the equal bamboo chip of width;
2, a slicing: carry out slicing to bamboo chip with four side moulder, removes Outer part and inner part of the bamboo;
3, boiling and bleaching: by the bamboo chip stacking after slicing, adjacent layer filler strip separates, and leaves a fixed gap between bamboo chip, by loop wheel machine, bamboo chip buttress is moved into boiling pond, and apply weight, in 80 ± 5 DEG C of hot digestions, in digestion process, add the hydrogen peroxide bleaching 5 ~ 8 hours that mass percent is 5% ~ 8%;
4, dry: the bamboo chip buttress after boiling and bleaching is shifted out by loop wheel machine, and inserts in 65 ± 5 DEG C of dryings 24 ~ 30 hours in drying box by slide rail, and controlling bamboo chip moisture content is 35 ± 2%;
5, secondary slicing: carry out slicing to bamboo chip with four side moulder, removes the defect such as warpage and cracking;
6, sorting: sorting is carried out to bamboo chip, classifies by aberration;
7, subdivision: with multiple blade saw, subdivision is carried out to bamboo chip prepared by step 1, obtain thin bamboo plate;
8, flood: thin bamboo plate is flooded 6-10 hour in normal temperature boiling pond, in dipping process, moisture enters bamboo chip by conduit, pit etc., and present gradient distribution, the moisture content on bamboo chip surface is the highest, due to the polar molecule that moisture is stronger than bamboo wood, its absorb microwave energy more than bamboo chip, so the microwave energy of bamboo chip thickness direction presents decline trend from outside to inside;
9, microwave explosion: microwave explosion treatment is carried out to thin bamboo plate, the power output of microwave is 8 ~ 11kW, processing time is 120 ~ 210s, obtain pretreatment bamboo chip, during microwave explosion, under the impact of vapor pressure, the micro-assembly robot at different levels in bamboo chip produce crackle in various degree, thus increase the permeability of bamboo chip, for the compound of bamboo chip and strontium aluminate fluorescent material increases circulation path; Simultaneously, due to the gradient of microwave explosion treatment effect, make the degree of porosity on bamboo chip surface inner apparently higher than bamboo chip, thus reduce the amount that strontium aluminate fluorescent material enters bamboo chip inside, the strontium aluminate fluorescent material entering into bamboo chip inside cuts the waste, because cannot realize illumination effect by light-light conversion;
10, the coated process of strontium aluminate fluorescent material: adopt the coated process of inorganic oxide cladding process, obtain coated strontium aluminate fluorescent material product, because strontium aluminate fluorescent material is very easily hydrolyzed in aqueous, occur to be hydrolyzed in itself and bamboo chip recombination process and reduce illumination effect, adopting inorganic oxide cladding process to suppress it to be hydrolyzed;
11, bamboo chip and strontium aluminate fluorescent material compound
11.1, mix: get the pretreatment bamboo chip that mass ratio is 10-30:1:60-140, coated strontium aluminate fluorescent material and ethanolic solution, by above-mentioned mass ratio, coated strontium aluminate fluorescent material is dispersed in ethanolic solution, in ultrasonic wave, ultrasonic 5-10 minute makes coated strontium aluminate fluorescent material be uniformly dispersed, add the pretreatment bamboo chip of above-mentioned mass ratio again, obtain mixture;
11.2, react: gained mixture in step 11.1 is moved to initial action 30-90 minute in magnetic stirring apparatus, refills in stainless steel pressurized canister, after regulating pressure to 0.6MPa by air compressor, room temperature constant voltage reacts 85-100 minute again;
11.3, dry: to take out the bamboo chip dry 8-15 hour in dielectric drying case with the coated even compound of strontium aluminate fluorescent material in step 11.2, dry run is divided into two stages, first stage adopts high temperature method fast, and heating-up temperature is 80 ± 2 DEG C, and the time is 4 hours; Second stage adopts low temperature method at a slow speed, and heating-up temperature is 60 ± 2 DEG C, and the time is 4 ~ 11 hours, and obtain bamboo chip/strontium aluminate fluorescent material compound low-light source material plate, control moisture content is 10-15%;
12, sanding: with sander, sanding process is carried out to bamboo chip/strontium aluminate fluorescent material composite panel, obtain the semiproduct that thickness is the blind blades of 2-5mm.
As optimization, the inorganic oxide cladding process adopted in step 10 is coated with silica modification method, and the concrete steps of described coated with silica modification method are:
A, hydrolysis: get ethyl orthosilicate, water, ethanol that mass ratio is 1:28-32:28-32, by above-mentioned mass ratio, second alcohol and water is mixed, obtain ethanol water, the ethyl orthosilicate getting above-mentioned mass ratio is dissolved in ethanol water, then nitric acid adjust ph to 1 ~ 2 are dripped, then drip ammoniacal liquor adjust ph to neutral, obtain mixed liquor A;
B, coated: strontium aluminate fluorescent material, urea and water that mass ratio is 1-2:1:13 will to be added in mixed liquor A, and obtain mixed liquid B, stir 1 hour under mixed liquid B being placed in 95 ± 2 DEG C of isoperibols, be cooled to room temperature afterwards;
C, suction filtration are separated: mixed liquid B washed 10-15 time respectively with distilled water and ethanolic solution, obtain mixed liquor C;
D, drying: by mixed liquor C dry 10-15 hour at 80 ± 2 DEG C, finally obtain coated strontium aluminate fluorescent material product.
As optimization, described upper sealing plate, lower shrouding and blade are equipped with at least one dotting punch.
As optimization, described unlatching one end of restricting passes upper sealing plate and through the dotting punch of several blades described.
As optimization, described unlatching rope is 2.
As optimization, described vane thickness is 2.0 ~ 3.5mm, and width is 25.0 ~ 50.0mm.
As optimization, this luminous bamboo blind thickness is 8 ~ 18, and width is 20 ~ 80mm.
As optimization, described upper sealing plate and lower shrouding all adopt bamboo wood to process, and described blade threading and unlatching rope are made up of Polyester Fibers.
The beneficial effect of a kind of luminous bamboo blind of the present invention is:
1, this kind of luminous bamboo blind, structure is simple, design science, easy to use, realize the good low-light source material of bamboo wood as light source carrier, changed by luminous energy and reach the decorative effect of similar neon light at night, part electric energy can be saved, can not cause potential safety hazard to environment and the mankind, and application life is longer, energy-conserving and environment-protective; There is good actual application value and promotional value.
2, coated strontium aluminate fluorescent material is dispersed in ethanolic solution, ultrasonic process makes coated strontium aluminate fluorescent material be uniformly dispersed, add pretreatment bamboo chip again, be convenient to obtain uniform mixture, thus finally obtain the equally distributed bamboo chip of coated strontium aluminate fluorescent material/strontium aluminate fluorescent material composite material.
3, moved in magnetic stirring apparatus by mixture and carry out initial reaction, mixture carries out uniform stirring at magnetic stirring apparatus, the strontium aluminate fluorescent material on bamboo chip surface is distributed comparatively even.
4, air pressurized method is adopted to make the strontium aluminate fluorescent material distribution uniform again on bamboo chip surface.
5, the above-mentioned mass ratio of the present invention and the technological parameter in reaction time can increase strontium aluminate fluorescent material sunset glow duration.
6, adopt the method for dielectric drying that bamboo chip is heated more even, and moisture is spread by bamboo chip interior, coordinate the high temperature fast method of first stage, most moisture can be removed within the regular hour, thus the efficient moisture that reduces is to the hydrolysis of strontium aluminate fluorescent material, and the low temperature slow method of second stage is, in order to avoid bamboo chip, the major defects such as cracking and warpage occur in dry run.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, this kind of luminous bamboo blind is described further:
Fig. 1 is the structural representation of this kind of luminous bamboo blind.
In figure: 1 be upper sealing plate, 2 for lower shrouding, 3 for blade, 4 for blade threading, 5 for open rope.
Detailed description of the invention
For making object of the present invention, technical scheme and advantage clearly understand, to develop simultaneously embodiment referring to accompanying drawing, the present invention is described in more detail.
embodiment 1:
This kind of luminous bamboo blind, comprises upper sealing plate 1, lower shrouding 2, to be made up of bamboo chip/strontium aluminate fluorescent material composite panel and 64 blades 3 between described upper sealing plate 1 and lower shrouding 2 are located in arrangement from top to bottom, the blade threading 4 be worn together by described 64 blades 3 and 2 open ropes 5; Described upper sealing plate 1, lower shrouding 2 and blade 3 are equipped with a dotting punch; Described unlatching rope 5 one end passes upper sealing plate 2 and passes the dotting punch of described 64 blades 3; Described blade 3 thickness is 3mm, and width is 40.0mm; This luminous bamboo blind thickness is 10, and width is 50mm; Described upper sealing plate 1 and lower shrouding 2 all adopt bamboo wood to process, and described blade threading 4 and unlatching rope 5 are made up of Polyester Fibers.
The processing technology of the described blade 3 be made up of bamboo chip/strontium aluminate fluorescent material composite panel is:
1, hack: mao bamboon is hacked by slicer, for the mao bamboon of different-diameter, by adjustment blade density to obtain the equal bamboo chip of width;
2, a slicing: carry out slicing to bamboo chip with four side moulder, removes Outer part and inner part of the bamboo;
3, boiling and bleaching: by the bamboo chip stacking after slicing, adjacent layer filler strip separates, and leaves a fixed gap between bamboo chip, by loop wheel machine, bamboo chip buttress is moved into boiling pond, and apply weight, in 80 ± 5 DEG C of hot digestions, in digestion process, add the hydrogen peroxide bleaching 8 hours that mass percent is 8%;
4, dry: the bamboo chip buttress after boiling and bleaching is shifted out by loop wheel machine, and inserts in 65 ± 5 DEG C of dryings 30 hours in drying box by slide rail, and controlling bamboo chip moisture content is 35 ± 2%;
5, secondary slicing: carry out slicing to bamboo chip with four side moulder, removes the defect such as warpage and cracking;
6, sorting: sorting is carried out to bamboo chip, classifies by aberration;
7, subdivision: with multiple blade saw, subdivision is carried out to bamboo chip prepared by step 1, obtain thin bamboo plate;
8, flood: thin bamboo plate is flooded in normal temperature boiling pond 6 and littlely reach 35 ± 2% up to its moisture content;
9, microwave explosion: microwave explosion treatment is carried out to thin bamboo plate, the power output of microwave is 11kW, and the processing time is 210s, obtains pretreatment bamboo chip;
10, the coated process of strontium aluminate fluorescent material: adopt the coated process of inorganic oxide cladding process, obtain coated strontium aluminate fluorescent material product, the inorganic oxide cladding process adopted is coated with silica modification method, and the concrete steps of described coated with silica modification method are:
A, hydrolysis: get ethyl orthosilicate, water, ethanol that mass ratio is 1:28:28, by above-mentioned mass ratio, second alcohol and water is mixed, obtain ethanol water, the ethyl orthosilicate getting above-mentioned mass ratio is dissolved in ethanol water, then nitric acid adjust ph to 1 is dripped, then drip ammoniacal liquor adjust ph to neutral, obtain mixed liquor A;
B, coated: strontium aluminate fluorescent material, urea and water that mass ratio is 1-2:1:13 will to be added in mixed liquor A, and obtain mixed liquid B, stir 1 hour under mixed liquid B being placed in 95 ± 2 DEG C of isoperibols, be cooled to room temperature afterwards;
C, suction filtration are separated: respectively mixed liquid B is washed 10 times with distilled water and ethanolic solution, obtain mixed liquor C;
D, drying: by mixed liquor C at 80 ± 2 DEG C dry 10 hours, finally obtain coated strontium aluminate fluorescent material product;
11, bamboo chip and strontium aluminate fluorescent material compound
11.1, mix: get the pretreatment bamboo chip that mass ratio is 16:1:100, coated strontium aluminate fluorescent material and ethanolic solution, by above-mentioned mass ratio, coated strontium aluminate fluorescent material is dispersed in ethanolic solution, coated strontium aluminate fluorescent material was uniformly dispersed in ultrasonic 5 minutes in ultrasonic wave, add the pretreatment bamboo chip of above-mentioned mass ratio again, obtain mixture;
11.2, react: gained mixture in step 11.1 to be moved in magnetic stirring apparatus initial action 30 minutes, refill in stainless steel pressurized canister, after regulating pressure to 0.6MPa by air compressor, room temperature constant voltage reacts 85 minutes again;
11.3, dry: to take out in step 11.2 with the bamboo chip of the coated even compound of strontium aluminate fluorescent material in dielectric drying case dry 8 hours, dry run is divided into two stages, first stage adopts high temperature method fast, and heating-up temperature is 80 ± 2 DEG C, and the time is 4 hours; Second stage adopts low temperature method at a slow speed, and heating-up temperature is 60 ± 2 DEG C, and the time is 4 hours, obtains bamboo chip/strontium aluminate fluorescent material compound low-light source material plate, and controlling moisture content is 10 ± 2%;
12, sanding: with sander, sanding process is carried out to bamboo chip/strontium aluminate fluorescent material composite panel, obtain the semiproduct that thickness is the blind blades of 2mm.
In addition, the length of blade 3 can according to actual door and window size setting; The length of blind can according to actual door and window size setting.
This kind of luminous bamboo blind, structure is simple, design science, easy to use, realize the good low-light source material of bamboo wood as light source carrier, changed by luminous energy and reach the decorative effect of similar neon light at night, part electric energy can be saved, can not cause potential safety hazard to environment and the mankind, and application life is longer, energy-conserving and environment-protective.
Above-mentioned detailed description of the invention is only concrete case of the present invention, and be not restriction the present invention being made to other form, any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the Equivalent embodiments of equivalent variations.But every content not departing from technical solution of the present invention, any simple modification, equivalent variations and the remodeling done above embodiment according to technical spirit of the present invention, all should fall into scope of patent protection of the present invention.
Claims (7)
1. a luminous bamboo blind, is characterized in that: comprise upper sealing plate (1), lower shrouding (2), to be made up of bamboo chip/strontium aluminate fluorescent material composite panel and arrangement is from top to bottom located at several blades (3) between described upper sealing plate (1) and lower shrouding (2), the blade threading (4) described several blades (3) be worn together and at least one unlatching and is restricted (5);
The processing technology of the described blade (3) be made up of bamboo chip/strontium aluminate fluorescent material composite panel is:
1, hack: mao bamboon is hacked by slicer, for the mao bamboon of different-diameter, by adjustment blade density to obtain the equal bamboo chip of width;
2, a slicing: carry out slicing to bamboo chip with four side moulder, removes Outer part and inner part of the bamboo;
3, boiling and bleaching: by the bamboo chip stacking after slicing, adjacent layer filler strip separates, and leaves a fixed gap between bamboo chip, by loop wheel machine, bamboo chip buttress is moved into boiling pond, and apply weight, in 80 ± 5 DEG C of hot digestions, in digestion process, add the hydrogen peroxide bleaching 5 ~ 8 hours that mass percent is 5% ~ 8%;
4, dry: the bamboo chip buttress after boiling and bleaching is shifted out by loop wheel machine, and inserts in 65 ± 5 DEG C of dryings 24 ~ 30 hours in drying box by slide rail, and controlling bamboo chip moisture content is 35 ± 2%;
5, secondary slicing: carry out slicing to bamboo chip with four side moulder, removes warpage and cracking defect;
6, sorting: sorting is carried out to bamboo chip, classifies by aberration;
7, subdivision: with multiple blade saw, subdivision is carried out to bamboo chip prepared by step 1, obtain thin bamboo plate;
8, flood: thin bamboo plate is flooded 6-10 hour in normal temperature boiling pond;
9, microwave explosion: microwave explosion treatment is carried out to thin bamboo plate, the power output of microwave is 8 ~ 11kW, and the processing time is 120 ~ 210s, obtains pretreatment bamboo chip;
10, the coated process of strontium aluminate fluorescent material: adopt the coated process of inorganic oxide cladding process, obtain coated strontium aluminate fluorescent material product;
11, bamboo chip and strontium aluminate fluorescent material compound
11.1, mix: get the pretreatment bamboo chip that mass ratio is 16:1:100, coated strontium aluminate fluorescent material and ethanolic solution, by above-mentioned mass ratio, coated strontium aluminate fluorescent material is dispersed in ethanolic solution, in ultrasonic wave, ultrasonic 5-10 minute makes coated strontium aluminate fluorescent material be uniformly dispersed, add the pretreatment bamboo chip of above-mentioned mass ratio again, obtain mixture;
11.2, react: gained mixture in step 11.1 is moved to initial action 30-90 minute in magnetic stirring apparatus, refills in stainless steel pressurized canister, after regulating pressure to 0.6MPa by air compressor, room temperature constant voltage reacts 85-100 minute again;
11.3, dry: to take out the bamboo chip dry 8-15 hour in dielectric drying case with the coated even compound of strontium aluminate fluorescent material in step 11.2, dry run is divided into two stages, first stage adopts high temperature method fast, and heating-up temperature is 80 ± 2 DEG C, and the time is 4 hours; Second stage adopts low temperature method at a slow speed, and heating-up temperature is 60 ± 2 DEG C, and the time is 4 ~ 11 hours, and obtain bamboo chip/strontium aluminate fluorescent material compound low-light source material plate, control moisture content is 10-15%;
12, sanding: with sander, sanding process is carried out to bamboo chip/strontium aluminate fluorescent material composite panel, obtain the semiproduct that thickness is the blind blades of 2-5mm.
2. a kind of luminous bamboo blind as claimed in claim 1, is characterized in that: the inorganic oxide cladding process adopted in step 10 is coated with silica modification method, and the concrete steps of described coated with silica modification method are:
A, hydrolysis: get ethyl orthosilicate, water, ethanol that mass ratio is 1:28:28, by above-mentioned mass ratio, second alcohol and water is mixed, obtain ethanol water, the ethyl orthosilicate getting above-mentioned mass ratio is dissolved in ethanol water, then nitric acid adjust ph to 1 ~ 2 are dripped, then drip ammoniacal liquor adjust ph to neutral, obtain mixed liquor A;
B, coated: strontium aluminate fluorescent material, urea and water that mass ratio is 1-2:1:13 will to be added in mixed liquor A, and obtain mixed liquid B, stir 1 hour under mixed liquid B being placed in 95 ± 2 DEG C of isoperibols, be cooled to room temperature afterwards;
C, suction filtration are separated: mixed liquid B washed 10-15 time respectively with distilled water and ethanolic solution, obtain mixed liquor C;
D, drying: by mixed liquor C dry 10-15 hour at 80 ± 2 DEG C, finally obtain coated strontium aluminate fluorescent material product.
3. a kind of luminous bamboo blind as claimed in claim 1, is characterized in that: described upper sealing plate (1), lower shrouding (2) and blade (3) are equipped with at least one dotting punch.
4. a kind of luminous bamboo blind as claimed in claim 3, is characterized in that: described rope (5) one end of opening passes upper sealing plate (2) and passes the dotting punch of described several blades (3).
5. a kind of luminous bamboo blind as claimed in claim 1, is characterized in that: described unlatching rope (5) is 2.
6. a kind of luminous bamboo blind as claimed in claim 1, it is characterized in that: described blade (3) thickness is 2.0 ~ 3.5mm, width is 25.0 ~ 50.0mm.
7. a kind of luminous bamboo blind as claimed in claim 1, is characterized in that: described upper sealing plate (1) and lower shrouding (2) all adopt bamboo wood to process, and described blade threading (4) and unlatching rope (5) are made up of Polyester Fibers.