CN107379202A - A kind of manufacture craft of luminous bamboo blind - Google Patents

A kind of manufacture craft of luminous bamboo blind Download PDF

Info

Publication number
CN107379202A
CN107379202A CN201710819234.2A CN201710819234A CN107379202A CN 107379202 A CN107379202 A CN 107379202A CN 201710819234 A CN201710819234 A CN 201710819234A CN 107379202 A CN107379202 A CN 107379202A
Authority
CN
China
Prior art keywords
bamboo
bamboo chip
fluorescent material
strontium aluminate
cladding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710819234.2A
Other languages
Chinese (zh)
Inventor
蒋红卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710819234.2A priority Critical patent/CN107379202A/en
Publication of CN107379202A publication Critical patent/CN107379202A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of manufacture craft of luminous bamboo blind, comprise the following steps：1st, bamboo chip is prepared：Hacking, a slicing, sterilization carbonization, dry, secondary slicing 2, prepare blade：Subdivision, dipping, microwave explosion, the processing of strontium aluminate fluorescent material cladding, bamboo chip and strontium aluminate fluorescent material is compound, sanding 3, prepares upper and lower shrouding：Applying glue, assembly, cold pressing, fixed length, fixed width, sanding 4, the luminous bamboo blind of preparation：Sorting, dotting punch, covering with paint, installation and inspection.

Description

A kind of manufacture craft of luminous bamboo blind
Technical field
The present invention relates to a kind of manufacture craft of blind, more particularly to a kind of manufacture craft of luminous bamboo blind.
Background technology
Bamboo blind is proposed in the case where modern house arranges the theory of new opinion " refitting decorations, with light packs to repair ", traditional family The window decorations such as the tulle gently waved in ornaments, thick and heavy curtain are occupied just gradually to be taken by rich in color, sharp-featured bamboo blind Generation.Bamboo blind because with light controllability, ventilation, it is easy to clean, protection private space many advantages, such as and it is wide It is general to be used for the places such as Urban House, country villa, coffee-house.
In the market there is not yet the relevant report about the bamboo blind that lights, in addition, for manufacture craft, city Problems be present in the fluorescent paint sold：1st, service life is shorter；2nd, fluorescent paint is inevitably present various organic solvents, meeting There is potential potential safety hazard to environment and the mankind.For strontium aluminate fluorescent material as a kind of important light-light conversion material, it is luminous The performance such as brightness and persistence all reaches actual operation requirements, and persistence is up to 8 hours as long as, has good energy storage Effect.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides for providing a kind of manufacture craft of luminous bamboo blind.
Present invention employs following technical scheme：A kind of manufacture craft of luminous bamboo blind, comprises the following steps：
1st, bamboo chip is prepared
1.1st, hacking：Mao bamboon carries out hacking by slicer；
1.2nd, a slicing：Slicing is carried out to bamboo chip with four side moulder, removes bamboo green grass or young crops and tabasheer；
1.3rd, sterilization carbonization：Bamboo chip is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C, 2-4 hours heat times, it is carbonized in bamboo chip table, carbonizing degree is 5%-30%；
1.4th, dry：The bamboo chip of sterilization paralysis is removed by loop wheel machine, and is inserted by slide rail in drying box in 65 ± 5 DEG C Dry 24~30 hours, it is 35 ± 2% to control bamboo chip moisture content；
1.5th, secondary slicing：Slicing is carried out to bamboo chip with four side moulder, the defects of removing warpage and ftracture；
1.6th, sort：Bamboo chip is sorted, classified by aberration；
2nd, blade is prepared
2.1st, subdivision：Subdivision is carried out to bamboo chip prepared by step 1 with multiple blade saw, obtains thin bamboo plate；
2.2nd, impregnate：Thin bamboo plate is impregnated into 6-10 hours in normal temperature boiling pond；
2.3rd, microwave explosion：Carry out microwave explosion treatment to thin bamboo plate, the power output of microwave is 8~11kW, during processing Between be 120~210s, obtain pre-process bamboo chip；
2.4th, strontium aluminate fluorescent material cladding is handled：Handled using inorganic oxide cladding process cladding, the aluminic acid coated Strontium fluorescent material product；
2.5th, bamboo chip and strontium aluminate fluorescent material are compound
2.5.1, mix：It is 10-30 to take mass ratio:1:60-140 pretreatment bamboo chip, cladding strontium aluminate fluorescent material and Ethanol solution, the strontium aluminate fluorescent material of cladding is dispersed in ethanol solution by above-mentioned mass ratio, the ultrasonic 5-10 in ultrasonic wave Minute makes the strontium aluminate fluorescent material of cladding be uniformly dispersed, and adds the pretreatment bamboo chip of above-mentioned mass ratio, obtains mixture；
2.5.2, react：Gained mixture in step 2.5.1 is moved into initial action 30-90 minutes in magnetic stirring apparatus, then Put into stainless steel pressurized canister, after air compressor regulation pressure to 0.6MPa, room temperature constant pressure reacts 85-100 points again Clock；
2.5.3, dry：The uniform compound bamboo chip of strontium aluminate fluorescent material in step 2.5.2 with cladding is taken out to do in high frequency 8-15 hours are dried in dry case, drying process is divided into two stages, and the first stage uses the quick method of high temperature, heating-up temperature For 80 ± 2 DEG C, the time is 4 hours；Second stage uses the method for low temperature at a slow speed, and heating-up temperature is 60 ± 2 DEG C, the time 4 ~11 hours, the compound low-light source material plate of bamboo chip/strontium aluminate fluorescent material is obtained, it is 10-15% to control moisture content；
2.6th, sanding：Sanding processing is carried out to bamboo chip/strontium aluminate fluorescent material composite panel with sander, obtains thickness For the semi-finished product of 2-5mm blind blades；
3rd, upper and lower shrouding is prepared
3.1st, applying glue, assembly：Bamboo chip prepared by step 1 is glued, assembly；
3.2nd, it is cold-pressed：Applying glue, the bamboo chip of assembly prepare 2 layers of bamboo cord wood through cold pressing；
3.3rd, fixed length：Bamboo cord wood carries out fixed length by briar；
3.4th, fixed width：The bamboo cord wood of fixed length carries out fixed width by four sides；
3.5th, sanding：The bamboo cord wood of fixed width is subjected to sanding processing by sander, obtains length-adjustable envelope up and down The semi-finished product of plate；
4th, luminous bamboo blind is prepared
4.1st, sort：The semi-finished product of shrouding sort above and below semi-finished product and step 3 to step 2 blind blades；
4.2nd, dotting punch：Dotting punch processing is carried out to the semi-finished product of sorting；
4.3rd, cover with paint, lacquer, colour wash, etc.：Covering with paint processing is carried out using polyurethane lacquer to the semi-finished product of dotting punch processing；
4.4th, install and examine：Semi-finished product after covering with paint is handled are installed with accessories such as blade threading, unlatching ropes, And test to obtain luminous bamboo blind finished product.
Further, in 1.1 hackings of step 1, for the mao bamboon of different-diameter, by adjusting blade density to obtain The equal bamboo chip of width.
Further, the inorganic oxide cladding process employed in the 2.4 of step 2 is that coated with silica is modified method, institute State coated with silica and be modified concretely comprising the following steps for method：
A, hydrolyze：It is 1 to take mass ratio:28-32:28-32 tetraethyl orthosilicate, water, ethanol, by above-mentioned mass ratio by second Alcohol and water mixes, and obtains ethanol water, takes the tetraethyl orthosilicate of above-mentioned mass ratio to be dissolved in ethanol water, then drip Add nitre acid for adjusting pH value that ammoniacal liquor is then added dropwise and adjusts pH value to neutrality, obtains mixed liquor A to 1~2；
B, coat：It is 1-2 by mass ratio is added in mixed liquor A:1:13 strontium aluminate fluorescent material, urea and water, is mixed Liquid B is closed, mixed liquid B is placed under 95 ± 2 DEG C of isoperibols and stirred 1 hour, is cooled to room temperature afterwards；
C, separation is filtered：Mixed liquid B is washed 10-15 times respectively with distilled water and ethanol solution, obtains mixed liquor C；
D, drying：Mixed liquor C is dried into 10-15 hours at 80 ± 2 DEG C, finally gives the strontium aluminate fluorescent material of cladding Product.
Further, bamboo chip, the strontium aluminate fluorescent material of cladding, the matter of ethanol solution are pre-processed in the 1.10 of the step 1 It is 12-20 to measure ratio:1:80-120.
Further, the blank thickness that step 3 obtains length-adjustable shrouding up and down is 15-25mm, width 25- 35mm。
Beneficial effect using above technical scheme is：First, this kind of manufacture craft of luminous bamboo blind, institute Make luminous bamboo blind product realize good low-light source material of the bamboo wood as light source carrier, by luminous energy conversion and Reach the decorative effect of similar neon light at night, part electric energy can be saved, potential safety hazard will not be caused to environment and the mankind, And service life is longer, energy-conserving and environment-protective, there is preferable actual application value and promotional value；
Secondly, the strontium aluminate fluorescent material of cladding is dispersed in ethanol solution, is ultrasonically treated the strontium aluminate fluorescence for making cladding Powder is uniformly dispersed, and adds pretreatment bamboo chip, is easy to obtain uniform mixture, glimmering so as to finally give the strontium aluminate of cladding The equally distributed bamboo chip of light powder/strontium aluminate fluorescence powder composite material；
Initial reaction is carried out in magnetic stirring apparatus in addition, mixture is moved to, mixture carries out uniform in magnetic stirring apparatus Stirring, make the strontium aluminate fluorescent material distribution on bamboo chip surface more uniform；Make the strontium aluminate on bamboo chip surface using air pressurized method Fluorescent material distribution uniform again；
In addition, when the above-mentioned mass ratio of the present invention and the technological parameter in reaction time can increase strontium aluminate fluorescent material sunset glow It is long；Finally, cause bamboo chip heated than more uniform using the method for dielectric drying, and moisture is spread by bamboo chip interior, is matched somebody with somebody The high temperature fast method of first stage is closed, most moisture can be removed within the regular hour, so as to efficiently reduce moisture To the hydrolysis of strontium aluminate fluorescent material, and the low temperature slow method of second stage be in order to avoid bamboo chip in the drying process The major defect such as generation cracking and warpage.
The method of the luminous bamboo blind of production of the present invention, by the way that the bamboo cane feeding dry machine of dried disinfecting carbon is disappeared Poison carbonization, the thermal efficiency is high, and penetrates inside bamboo cane, more helps the decomposition of sugar, protein inside bamboo cane, avoids bamboo cane from sending out Go mouldy color.
Embodiment
With reference to embodiment, the present invention will be further described：
Embodiment 1：
A kind of manufacture craft of luminous bamboo blind, comprises the following steps：
1st, bamboo chip is prepared
1.1st, hacking：Mao bamboon carries out hacking by slicer, for the mao bamboon of different-diameter, by adjusting blade density To obtain the equal bamboo chip of width；
1.2nd, a slicing：Slicing is carried out to bamboo chip with four side moulder, removes bamboo green grass or young crops and tabasheer；
1.3rd, sterilization carbonization：Bamboo chip is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C, 2-4 hours heat times, it is carbonized in bamboo chip table, carbonizing degree is 5%-30%；
1.4th, dry：The bamboo chip of sterilization paralysis is removed by loop wheel machine, and is inserted by slide rail in drying box in 65 ± 5 DEG C Dry 24~30 hours, it is 35 ± 2% to control bamboo chip moisture content；
1.5th, secondary slicing：Slicing is carried out to bamboo chip with four side moulder, the defects of removing warpage and ftracture；
1.6th, sort：Bamboo chip is sorted, classified by aberration；
2nd, blade is prepared
2.1st, subdivision：Subdivision is carried out to bamboo chip prepared by step 1 with multiple blade saw, obtains thin bamboo plate；
2.2nd, impregnate：Thin bamboo plate is impregnated into 6-10 hours in normal temperature boiling pond；
2.3rd, microwave explosion：Carry out microwave explosion treatment to thin bamboo plate, the power output of microwave is 8~11kW, during processing Between be 120~210s, obtain pre-process bamboo chip；
2.4th, strontium aluminate fluorescent material cladding is handled：Handled using inorganic oxide cladding process cladding, the aluminic acid coated Strontium fluorescent material product；
Used inorganic oxide cladding process is that coated with silica is modified method, and the coated with silica is modified method Concretely comprise the following steps：
A, hydrolyze：It is 1 to take mass ratio:28-32:28-32 tetraethyl orthosilicate, water, ethanol, by above-mentioned mass ratio by second Alcohol and water mixes, and obtains ethanol water, takes the tetraethyl orthosilicate of above-mentioned mass ratio to be dissolved in ethanol water, then drip Add nitre acid for adjusting pH value that ammoniacal liquor is then added dropwise and adjusts pH value to neutrality, obtains mixed liquor A to 1~2；
B, coat：It is 1-2 by mass ratio is added in mixed liquor A:1:13 strontium aluminate fluorescent material, urea and water, is mixed Liquid B is closed, mixed liquid B is placed under 95 ± 2 DEG C of isoperibols and stirred 1 hour, is cooled to room temperature afterwards；
C, separation is filtered：Mixed liquid B is washed 10-15 times respectively with distilled water and ethanol solution, obtains mixed liquor C；
D, drying：Mixed liquor C is dried into 10-15 hours at 80 ± 2 DEG C, finally gives the strontium aluminate fluorescent material of cladding Product.
2.5th, bamboo chip and strontium aluminate fluorescent material are compound
2.5.1, mix：It is 10-30 to take mass ratio:1:60-140 pretreatment bamboo chip, cladding strontium aluminate fluorescent material and Ethanol solution, the strontium aluminate fluorescent material of cladding is dispersed in ethanol solution by above-mentioned mass ratio, the ultrasonic 5-10 in ultrasonic wave Minute makes the strontium aluminate fluorescent material of cladding be uniformly dispersed, and adds the pretreatment bamboo chip of above-mentioned mass ratio, obtains mixture；
2.5.2, react：Gained mixture in step 2.5.1 is moved into initial action 30-90 minutes in magnetic stirring apparatus, then Put into stainless steel pressurized canister, after air compressor regulation pressure to 0.6MPa, room temperature constant pressure reacts 85-100 points again Clock；
2.5.3, dry：The uniform compound bamboo chip of strontium aluminate fluorescent material in step 2.5.2 with cladding is taken out to do in high frequency 8-15 hours are dried in dry case, drying process is divided into two stages, and the first stage uses the quick method of high temperature, heating-up temperature For 80 ± 2 DEG C, the time is 4 hours；Second stage uses the method for low temperature at a slow speed, and heating-up temperature is 60 ± 2 DEG C, the time 4 ~11 hours, the compound low-light source material plate of bamboo chip/strontium aluminate fluorescent material is obtained, it is 10-15% to control moisture content；
2.6th, sanding：Sanding processing is carried out to bamboo chip/strontium aluminate fluorescent material composite panel with sander, obtains thickness For the semi-finished product of 2-5mm blind blades；
3rd, upper and lower shrouding is prepared
3.1st, applying glue, assembly：Bamboo chip prepared by step 1 is glued, assembly；
3.2nd, it is cold-pressed：Applying glue, the bamboo chip of assembly prepare 2 layers of bamboo cord wood through cold pressing；
3.3rd, fixed length：Bamboo cord wood carries out fixed length by briar；
3.4th, fixed width：The bamboo cord wood of fixed length carries out fixed width by four sides；
3.5th, sanding：The bamboo cord wood of fixed width is subjected to sanding processing by sander, obtains length-adjustable envelope up and down The semi-finished product of plate, blank thickness 15-25mm, width 25-35mm；
4th, luminous bamboo blind is prepared
4.1st, sort：The semi-finished product of shrouding sort above and below semi-finished product and step 3 to step 2 blind blades；
4.2nd, dotting punch：Dotting punch processing is carried out to the semi-finished product of sorting；
4.3rd, cover with paint, lacquer, colour wash, etc.：Covering with paint processing is carried out using polyurethane lacquer to the semi-finished product of dotting punch processing；
4.4th, install and examine：Semi-finished product after covering with paint is handled are installed with accessories such as blade threading, unlatching ropes, And test to obtain luminous bamboo blind finished product.

Claims (5)

1. a kind of manufacture craft of luminous bamboo blind, comprises the following steps：
1st, bamboo chip is prepared
1.1st, hacking：Mao bamboon carries out hacking by slicer；
1.2nd, a slicing：Slicing is carried out to bamboo chip with four side moulder, removes bamboo green grass or young crops and tabasheer；
1.3rd, sterilization carbonization：Bamboo chip is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C, 2-4 hours heat times, it is carbonized in bamboo chip table, carbonizing degree is 5%-30%；
1.4th, dry：The bamboo chip of sterilization paralysis is removed by loop wheel machine, and is inserted by slide rail in drying box and dried 24 in 65 ± 5 DEG C ~30 hours, it was 35 ± 2% to control bamboo chip moisture content；
1.5th, secondary slicing：Slicing is carried out to bamboo chip with four side moulder, the defects of removing warpage and ftracture；
1.6th, sort：Bamboo chip is sorted, classified by aberration；
2nd, blade is prepared
2.1st, subdivision：Subdivision is carried out to bamboo chip prepared by step 1 with multiple blade saw, obtains thin bamboo plate；
2.2nd, impregnate：Thin bamboo plate is impregnated into 6-10 hours in normal temperature boiling pond；
2.3rd, microwave explosion：Microwave explosion treatment is carried out to thin bamboo plate, the power output of microwave is 8~11kW, and processing time is 120~210s, obtain pre-processing bamboo chip；
2.4th, strontium aluminate fluorescent material cladding is handled：Handled using inorganic oxide cladding process cladding, the strontium aluminate coated is glimmering Light powder product；
2.5th, bamboo chip and strontium aluminate fluorescent material are compound
2.5.1, mix：It is 10-30 to take mass ratio:1:60-140 pretreatment bamboo chip, the strontium aluminate fluorescent material and ethanol of cladding Solution, the strontium aluminate fluorescent material of cladding is dispersed in ethanol solution by above-mentioned mass ratio, the ultrasonic 5-10 minutes in ultrasonic wave The strontium aluminate fluorescent material of cladding is uniformly dispersed, add the pretreatment bamboo chip of above-mentioned mass ratio, obtain mixture；
2.5.2, react：Gained mixture in step 2.5.1 is moved into initial action 30-90 minutes in magnetic stirring apparatus, then put into In stainless steel pressurized canister, after air compressor regulation pressure to 0.6MPa, room temperature constant pressure reacts 85-100 minutes again；
2.5.3, dry：The uniform compound bamboo chip of strontium aluminate fluorescent material in step 2.5.2 with cladding is taken out in dielectric drying case Middle dry 8-15 hours, drying process are divided into two stages, and the first stage uses the quick method of high temperature, and heating-up temperature is 80 ± 2 DEG C, the time is 4 hours；Second stage uses the method for low temperature at a slow speed, and heating-up temperature is 60 ± 2 DEG C, and the time is 4~11 hours, The compound low-light source material plate of bamboo chip/strontium aluminate fluorescent material is obtained, it is 10-15% to control moisture content；
2.6th, sanding：Sanding processing is carried out to bamboo chip/strontium aluminate fluorescent material composite panel with sander, it is 2- to obtain thickness The semi-finished product of 5mm blind blades；
3rd, upper and lower shrouding is prepared
3.1st, applying glue, assembly：Bamboo chip prepared by step 1 is glued, assembly；
3.2nd, it is cold-pressed：Applying glue, the bamboo chip of assembly prepare 2 layers of bamboo cord wood through cold pressing；
3.3rd, fixed length：Bamboo cord wood carries out fixed length by briar；
3.4th, fixed width：The bamboo cord wood of fixed length carries out fixed width by four sides；
3.5th, sanding：The bamboo cord wood of fixed width is subjected to sanding processing by sander, obtains length-adjustable shrouding up and down Semi-finished product；
4th, luminous bamboo blind is prepared
4.1st, sort：The semi-finished product of shrouding sort above and below semi-finished product and step 3 to step 2 blind blades；
4.2nd, dotting punch：Dotting punch processing is carried out to the semi-finished product of sorting；
4.3rd, cover with paint, lacquer, colour wash, etc.：Covering with paint processing is carried out using polyurethane lacquer to the semi-finished product of dotting punch processing；
4.4th, install and examine：Semi-finished product after covering with paint is handled are installed with accessories such as blade threading, unlatching ropes, and are carried out Inspection obtains luminous bamboo blind finished product.
A kind of 2. manufacture craft of luminous bamboo blind as claimed in claim 1, it is characterised in that：1.1 hackings of step 1 In, for the mao bamboon of different-diameter, the equal bamboo chip of width is obtained by adjusting blade density.
A kind of 3. manufacture craft of luminous bamboo blind as claimed in claim 1, it is characterised in that：Institute in the 2.4 of step 2 The inorganic oxide cladding process used is modified method for coated with silica, and the coated with silica is modified the specific steps of method For：
A, hydrolyze：It is 1 to take mass ratio:28-32:28-32 tetraethyl orthosilicate, water, ethanol, by above-mentioned mass ratio by second alcohol and water Mixing, obtains ethanol water, takes the tetraethyl orthosilicate of above-mentioned mass ratio to be dissolved in ethanol water, and nitric acid is then added dropwise and adjusts PH value is saved to 1~2, ammoniacal liquor is then added dropwise and adjusts pH value to neutrality, obtains mixed liquor A；
B, coat：It is 1-2 by mass ratio is added in mixed liquor A:1:13 strontium aluminate fluorescent material, urea and water, obtains mixed liquor B, mixed liquid B is placed under 95 ± 2 DEG C of isoperibols and stirred 1 hour, is cooled to room temperature afterwards；
C, separation is filtered：Mixed liquid B is washed 10-15 times respectively with distilled water and ethanol solution, obtains mixed liquor C；
D, drying：Mixed liquor C is dried into 10-15 hours at 80 ± 2 DEG C, finally gives the strontium aluminate fluorescent material product of cladding.
A kind of 4. manufacture craft of luminous bamboo blind as claimed in claim 1, it is characterised in that：The step 1 It is 12-20 that bamboo chip, the strontium aluminate fluorescent material of cladding, the mass ratio of ethanol solution are pre-processed in 1.10:1:80-120.
A kind of 5. manufacture craft of luminous bamboo blind as claimed in claim 1, it is characterised in that：Step 3 obtains length The blank thickness of adjustable shrouding up and down is 15-25mm, width 25-35mm.
CN201710819234.2A 2017-09-12 2017-09-12 A kind of manufacture craft of luminous bamboo blind Pending CN107379202A (en)