CN104532274A - Novel water-based paraffin removal cleaning agent for aluminum alloy - Google Patents
Novel water-based paraffin removal cleaning agent for aluminum alloy Download PDFInfo
- Publication number
- CN104532274A CN104532274A CN201410821421.0A CN201410821421A CN104532274A CN 104532274 A CN104532274 A CN 104532274A CN 201410821421 A CN201410821421 A CN 201410821421A CN 104532274 A CN104532274 A CN 104532274A
- Authority
- CN
- China
- Prior art keywords
- parts
- paraffin removal
- sodium
- water
- aluminum alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel water-based paraffin removal cleaning agent for an aluminum alloy. The cleaning agent is prepared from the following raw materials in parts by weight: 45-55 parts of potassium pyrophosphate, 1.5-3.5 parts of borax, 20-30 parts of sodium dodecyl sulfonate, 10-15 parts of dodecyl benzene sulfonate, 3-5 parts of sodium gluconate, 20-35 parts of fatty alcohol-polyoxyethylene ether, 2-5 parts of sodium benzoate, 3-5 parts of sodium silicate, 5-10 parts of benzotriazole and the balance of pure water. Through the manner, the novel water-based paraffin removal cleaning agent for the aluminum alloy is safe and free of toxic and side effects in use, can be directly prepared by water, and is convenient and simple to operate and high in grease and paraffin removal efficiency of the aluminum alloy. The cleaning efficiency can reach up to 99.9%. The cleaning agent is free of any corrosive effects on the aluminum alloy and the cleaning quality of the aluminum alloy is improved.
Description
Technical field
The present invention relates to paraffin removal clean-out system, particularly relate to the novel water-based paraffin removal clean-out system of a kind of aluminium alloy.
Background technology
Aluminium alloy has excellent physicochemical property and surface treatment properties, applies very extensive.In order to improve its over-all properties, surface smoothness and decorative effect, surface treatment must be carried out to it, reaching result of use.Aluminum alloy surface process mainly contains three kinds of methods: mechanical polishing, chemical rightenning and electrochemical etching.Chemistry and electrochemical etching all will use strong acid and highly basic, producing a large amount of discarded, waste liquid, having a serious impact the health of operator when operating, and simultaneously also seriously pollute physical environment.So, generally mechanical polishing is adopted for aluminium alloy extrusions, but mechanical polishing can need to use aluminium alloy buffing wax, cause aluminum alloy surface can leave a large amount of residual wax, must clean it.
At present, following several method is mainly used in metal paraffin removal, degreasing, degreasing: organic solvent method, chemical method, electrochemical process and Aqueous cleaning machine method etc.Conventional organic solvent can not remove buffing wax completely, and chloride solvent not only toxicity is large, and have hydrolysis to occur, corrosion is had to workpiece, be not suitable for place's wax of aluminium alloy extrusions, and chemical method or electrochemical process can use highly basic or strong acid, also be not suitable for cleaning.
Summary of the invention
The technical problem that the present invention mainly solves is to provide the novel water-based paraffin removal clean-out system of a kind of aluminium alloy, during use, safety non-toxic is secondary, can configure by direct water, simply easy to operate, high to aluminium alloy degreasing paraffin removal efficiency, cleaning efficiency up to 99.9%, and is formed without any corrosive nature aluminium alloy, improves the cleaning quality of aluminium alloy.
For solving the problems of the technologies described above, the invention provides the novel water-based paraffin removal clean-out system of a kind of aluminium alloy, comprising following raw material component and being prepared from:
Potassium pyrophosphate: 45 ~ 55;
Borax: 1.5 ~ 3.5;
Sodium laurylsulfonate: 20 ~ 30;
Sodium dodecylbenzene sulfonate: 10 ~ 15;
Sunmorl N 60S: 3 ~ 5;
Fatty alcohol-polyoxyethylene ether: 20 ~ 35;
Sodium Benzoate: 2 ~ 5;
Water glass: 3 ~ 5;
Benzotriazole: 5 ~ 10;
All the other are pure water.
In the present invention's preferred embodiments, described each raw material component specifically comprises:
Potassium pyrophosphate: 48;
Borax: 2.5;
Sodium laurylsulfonate: 25;
Sodium dodecylbenzene sulfonate: 13;
Sunmorl N 60S: 4.5;
Fatty alcohol-polyoxyethylene ether: 25;
Sodium Benzoate: 4;
Water glass: 4.5;
Benzotriazole: 8;
All the other are pure water.
In the present invention's preferred embodiments, described each raw material component specifically comprises:
Potassium pyrophosphate: 50;
Borax: 3;
Sodium laurylsulfonate: 27.5;
Sodium dodecylbenzene sulfonate: 14.5;
Sunmorl N 60S: 5;
Fatty alcohol-polyoxyethylene ether: 28.5;
Sodium Benzoate: 3.5;
Water glass: 5;
Benzotriazole: 8.5;
All the other are pure water.
In the present invention's preferred embodiments, described Sodium Benzoate and benzotriazole are not AR level.
In the present invention's preferred embodiments, the pH value of described pure water is 6.5 ~ 7.2.
The invention has the beneficial effects as follows: the novel water-based paraffin removal clean-out system of a kind of aluminium alloy of the present invention, during use, safety non-toxic is secondary, can configure by direct water, simply easy to operate, high to aluminium alloy degreasing paraffin removal efficiency, cleaning efficiency up to 99.9%, and is formed without any corrosive nature aluminium alloy, improves the cleaning quality of aluminium alloy.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
The novel water-based paraffin removal clean-out system of a kind of aluminium alloy, comprises following raw material component and is prepared from:
Potassium pyrophosphate: 45 ~ 55;
Borax: 1.5 ~ 3.5;
Sodium laurylsulfonate: 20 ~ 30;
Sodium dodecylbenzene sulfonate: 10 ~ 15;
Sunmorl N 60S: 3 ~ 5;
Fatty alcohol-polyoxyethylene ether: 20 ~ 35;
Sodium Benzoate: 2 ~ 5;
Water glass: 3 ~ 5;
Benzotriazole: 5 ~ 10;
All the other are pure water.
The preparation method of above-mentioned clean-out system, comprise the steps: by potassium pyrophosphate: 45 ~ 55, borax: 1.5 ~ 3.5, sodium laurylsulfonate: 20 ~ 30, Sodium dodecylbenzene sulfonate: 10 ~ 15, Sunmorl N 60S: 3 ~ 5, fatty alcohol-polyoxyethylene ether: 20 ~ 35, Sodium Benzoate: 2 ~ 5, water glass: 3 ~ 5, benzotriazole: the raw material of 5 ~ 10 is configured, then add pH value be 6.7 pure water carry out stirring and obtain clean-out system finished product.
Embodiment 2
The novel water-based paraffin removal clean-out system of a kind of aluminium alloy, described each raw material component specifically comprises:
Potassium pyrophosphate: 48;
Borax: 2.5;
Sodium laurylsulfonate: 25;
Sodium dodecylbenzene sulfonate: 13;
Sunmorl N 60S: 4.5;
Fatty alcohol-polyoxyethylene ether: 25;
Sodium Benzoate: 4;
Water glass: 4.5;
Benzotriazole: 8;
All the other are pure water.
The preparation method of above-mentioned clean-out system, comprise the steps: by potassium pyrophosphate: 48, borax: 2.5, sodium laurylsulfonate: 25, Sodium dodecylbenzene sulfonate: 13, Sunmorl N 60S: 4.5, fatty alcohol-polyoxyethylene ether: 25, Sodium Benzoate: 4, water glass: 4.8, benzotriazole: the raw material of 8 is configured, then add pH value be 7 pure water carry out stirring and obtain clean-out system finished product.
Embodiment 3
The novel water-based paraffin removal clean-out system of a kind of aluminium alloy, described each raw material component specifically comprises:
Potassium pyrophosphate: 50;
Borax: 3;
Sodium laurylsulfonate: 27.5;
Sodium dodecylbenzene sulfonate: 14.5;
Sunmorl N 60S: 5;
Fatty alcohol-polyoxyethylene ether: 28.5;
Sodium Benzoate: 3.5;
Water glass: 5;
Benzotriazole: 8.5;
All the other are pure water.
The preparation method of above-mentioned clean-out system, comprises the steps: by potassium pyrophosphate: 50; Borax: 3; Sodium laurylsulfonate: 27.5, Sodium dodecylbenzene sulfonate: 14.5, Sunmorl N 60S: 5, fatty alcohol-polyoxyethylene ether: 28.5, Sodium Benzoate: 3.5, water glass: 5, benzotriazole: 8.5, water glass: 5, benzotriazole: the raw material of 8.5 is configured, then add pH value be 7.2 pure water carry out stirring and obtain clean-out system finished product.
The invention has the beneficial effects as follows: the novel water-based paraffin removal clean-out system of a kind of aluminium alloy of the present invention, during use, safety non-toxic is secondary, can configure by direct water, simply easy to operate, high to aluminium alloy degreasing paraffin removal efficiency, cleaning efficiency up to 99.9%, and is formed without any corrosive nature aluminium alloy, improves the cleaning quality of aluminium alloy.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. the novel water-based paraffin removal clean-out system of aluminium alloy, is characterized in that, comprises following raw material component and is prepared from:
Potassium pyrophosphate: 45 ~ 55;
Borax: 1.5 ~ 3.5;
Sodium laurylsulfonate: 20 ~ 30;
Sodium dodecylbenzene sulfonate: 10 ~ 15;
Sunmorl N 60S: 3 ~ 5;
Fatty alcohol-polyoxyethylene ether: 20 ~ 35;
Sodium Benzoate: 2 ~ 5;
Water glass: 3 ~ 5;
Benzotriazole: 5 ~ 10;
All the other are pure water.
2. the novel water-based paraffin removal clean-out system of aluminium alloy according to claim 1, is characterized in that, described each raw material component specifically comprises:
Potassium pyrophosphate: 48;
Borax: 2.5;
Sodium laurylsulfonate: 25;
Sodium dodecylbenzene sulfonate: 13;
Sunmorl N 60S: 4.5;
Fatty alcohol-polyoxyethylene ether: 25;
Sodium Benzoate: 4;
Water glass: 4.5;
Benzotriazole: 8;
All the other are pure water.
3. the novel water-based paraffin removal clean-out system of aluminium alloy according to claim 1, is characterized in that, described each raw material component specifically comprises:
Potassium pyrophosphate: 50;
Borax: 3;
Sodium laurylsulfonate: 27.5;
Sodium dodecylbenzene sulfonate: 14.5;
Sunmorl N 60S: 5;
Fatty alcohol-polyoxyethylene ether: 28.5;
Sodium Benzoate: 3.5;
Water glass: 5;
Benzotriazole: 8.5;
All the other are pure water.
4. the novel water-based paraffin removal clean-out system of aluminium alloy according to claim 1, is characterized in that, described Sodium Benzoate and benzotriazole are not AR level.
5. the novel water-based paraffin removal clean-out system of aluminium alloy according to claim 1, is characterized in that, the pH value of described pure water is 6.5 ~ 7.2.