CN104531279A - Antirust drawing oil for air-conditioner sheet metal part - Google Patents
Antirust drawing oil for air-conditioner sheet metal part Download PDFInfo
- Publication number
- CN104531279A CN104531279A CN201410845853.5A CN201410845853A CN104531279A CN 104531279 A CN104531279 A CN 104531279A CN 201410845853 A CN201410845853 A CN 201410845853A CN 104531279 A CN104531279 A CN 104531279A
- Authority
- CN
- China
- Prior art keywords
- parts
- antirust
- drawing oil
- thinner
- diethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses antirust drawing oil for an air-conditioner sheet metal part, and belongs to the technical field of air-conditioner sheet metal parts. The antirust drawing oil is composed of coating agents and antirust agents. The antirust agents are composed of benzotriazole and petroleum barium sulfonate, wherein the mass ratio of the benzotriazole to the petroleum barium sulfonate is 2 to 5. The coating agents are composed of paint materials and diluents, the mass ratio of the paint materials to the diluents is 100 to 2, and the diluents comprise, by mass, 100 parts of gasoline, 20 parts to 25 parts of X-4-amido paint diluents, 10 parts to 12 parts of zinc dialkyl dithiophosphate, 7 parts to 9 parts of diethylene glycol ethyl methyl ether, 4 parts to 7 parts of methylisobutylketone, 6 parts to 8 parts of isopropanol, 5 parts to 9 parts of polyving akohol, 11 parts to 13 parts of diethylene glycol dimethyl ether and 11 parts to 13 parts of dichloroethane. The paint materials are ester gum varnish. The antirust drawing oil can meet the requirement for lubricating during stamping and can also meet the antirust requirement.
Description
Technical field
The present invention relates to AC gold metal plate part technical field, more particularly, relate to the antirust drawing oil of a kind of AC gold metal plate part.
Background technology
AC gold metal plate goods, when punching press (as drawing, bending etc.), need to smear drawing oil on workpiece and mould, play lubrication, preventing mould and the wear of work, prevent from workpiece from producing drawing defects such as wearing.Common drawing oil does not have rust inhibition, and workpiece is easy to get rusty at damp and hot weather.AC gold metal plate goods majority will be electroplated, even if eliminate rust after getting rusty, also can leave spot at workpiece surface, both affect outward appearance, also the rustless property of the rear workpiece of impact plating.Current antirust main employing aqueous rust preventive, workpiece drawing or bending after, even if applying preventive by dipping water, also do not have rust inhibition: because profit does not dissolve each other, the drawing oil without rust inhibition sticks to workpiece surface, aqueous rust preventive is difficult to infiltration workpiece surface, and workpiece still gets rusty.
China Patent No. ZL201220367437.5, invention and created name is: prevent structure that in sheet metal component punching course, wooden dipper is out of shape partially and outdoor machine of air-conditioner top cover, this application case relates to and a kind ofly prevents structure that in sheet metal component punching course, wooden dipper is out of shape partially and outdoor machine of air-conditioner top cover, prevent the structure that in sheet metal component punching course, wooden dipper is out of shape partially from being multiple pressure-type structures that sheet metal component surface is formed, this application case forms multiple pressure-type structure at sheet metal component stamping surface, effectively shape of product can be kept in punching course, the wooden dipper not needing the position be out of shape to produce because material extending causes all directions discontinuity in punching course is prevented partially to be out of shape.Pressure-type structure can adopt straight strip structure or turning strip structure, and outdoor machine of air-conditioner stamping top cover process does not need the position be out of shape can not produce wooden dipper and be partially out of shape, and can meet production requirement.But this application case cannot solve AC gold metal plate part antirust scarce capacity and be difficult to antirust problem after punching press.
Summary of the invention
1. invent the technical problem that will solve
The object of the invention is to overcome deficiency of the prior art, provide the antirust drawing oil of a kind of AC gold metal plate part, adopt technical scheme of the present invention, the needs of lubrication time punching press (as drawing or bending etc.) can be met, antirust needs can be met again, be difficult to antirust problem with antirust scarce capacity after overcoming present workpiece punching press.
2. technical scheme
For achieving the above object, technical scheme provided by the invention is:
The antirust drawing oil of a kind of AC gold metal plate part of the present invention, this antirust drawing oil is made up of coating agent and rust-preventive agent, wherein: described coating agent and the mass ratio of rust-preventive agent are 100:8 ~ 11.
Further, described rust-preventive agent is made up of benzotriazole and barium mahogany sulfonate, wherein: the mass ratio of benzotriazole and barium mahogany sulfonate is 2:5.
Further, described coating agent is by painting material and thinner forms, the mass ratio of paint material and thinner is 100:2, wherein: described thinner is made up of following component, and each component by following mass parts composition: 100 parts, gasoline, X-4 amino paint thinner 20 ~ 25 parts, zinc dialkyl dithiophosphate 10 ~ 12 parts, diethylene glycol ethylmethyl ether 7 ~ 9 parts, mibk 4 ~ 7 parts, Virahol 6 ~ 8 parts, polyvinyl alcohol 5 ~ 9 parts, diethylene glycol dimethyl ether 11 ~ 13 parts, ethylene dichloride 11 ~ 13 parts; Described paint material is ester gum varniss.
Further, described thinner is made up of following component, and each component is by following mass parts composition:
100 parts, gasoline,
X-4 amino paint thinner 23 parts,
Zinc dialkyl dithiophosphate 11 parts,
Diethylene glycol ethylmethyl ether 8 parts,
Mibk 5 parts,
Virahol 7 parts,
Polyvinyl alcohol 7 parts,
Diethylene glycol dimethyl ether 12 parts,
Ethylene dichloride 12 parts.
Further, described thinner is made up of following component, and each component is by following mass parts composition:
100 parts, gasoline,
X-4 amino paint thinner 23 parts,
Zinc dialkyl dithiophosphate 10 parts,
Diethylene glycol ethylmethyl ether 7 parts,
Mibk 4 parts,
Virahol 6 parts,
Polyvinyl alcohol 5 parts,
Diethylene glycol dimethyl ether 11 parts,
Ethylene dichloride 11 parts.
3. beneficial effect
Adopt technical scheme provided by the invention, compared with prior art, there is following unusual effect:
The antirust drawing oil of a kind of AC gold metal plate part of the present invention; adopt benzotriazole and barium mahogany sulfonate as rust-preventive agent; and adopt the coating agent of paint material and thinner composition; diethylene glycol ethylmethyl ether in thinner, polyvinyl alcohol, ethylene dichloride not only coordinate with paint material and make coating agent lubrication in Punching Process and provide protection effect can reach the best; and can mate-assist benzotriazole and barium mahogany sulfonate, play the effect promoting rustless property.Therefore, the needs lubricated when the present invention can meet the punching press of AC gold metal plate part, can meet antirust needs again, and the workpiece rust-proof life after punching press, more than 10 days, does not need to do in addition antirust again.
Embodiment
For understanding content of the present invention further, below in conjunction with embodiment, the invention will be further described.
embodiment 1
The antirust drawing oil of a kind of AC gold metal plate part of the present embodiment, this antirust drawing oil is made up of coating agent and rust-preventive agent, wherein: described coating agent and the mass ratio of rust-preventive agent are 100:9.Rust-preventive agent in the present embodiment is made up of benzotriazole and barium mahogany sulfonate, wherein: the mass ratio of benzotriazole and barium mahogany sulfonate is 2:5.In addition, coating agent in the present embodiment is by painting material and thinner forms, the mass ratio of paint material and thinner is 100:2, wherein: described thinner is made up of following component, and each component by following mass parts composition: 100 parts, gasoline, X-4 amino paint thinner 23 parts, zinc dialkyl dithiophosphate 11 parts, diethylene glycol ethylmethyl ether 8 parts, mibk 5 parts, Virahol 7 parts, polyvinyl alcohol 7 parts, diethylene glycol dimethyl ether 12 parts, ethylene dichloride 12 parts.Paint material in the present embodiment is ester gum varniss.Gasoline in the present embodiment is mixed according to volume ratio 1:3 by No. 93 gasoline and No. 97 gasoline.
A kind of AC gold metal plate part preparation method of antirust drawing oil of the present embodiment, the steps include:
Step one, prepare rust-preventive agent; In step one, the preparation process of rust-preventive agent is as follows: prepare benzotriazole and barium mahogany sulfonate according to mass ratio, wherein: the mass ratio of benzotriazole and barium mahogany sulfonate is 2:5; Then benzotriazole and barium mahogany sulfonate are directly mixed, and be heated to 75 DEG C insulation 10 minutes after naturally cooling.
Step 2, prepare coating agent; In step 2, the preparation process of coating agent is as follows: thinner prepares according to mass fraction: 100 parts, gasoline, X-4 amino paint thinner 23 parts, zinc dialkyl dithiophosphate 11 parts, diethylene glycol ethylmethyl ether 8 parts, mibk 5 parts, Virahol 7 parts, polyvinyl alcohol 7 parts, diethylene glycol dimethyl ether 12 parts, ethylene dichloride 12 parts, be uniformly mixed to obtain thinner; Then material and mixing diluents will be painted, wherein: the mass ratio of paint material and thinner is 100:2, paint material is ester gum varniss, and mix and blend speed control is 180 rpm, churning time is 23 minutes, stirs after terminating and is warming up to 58 DEG C, react and be warming up to 79 DEG C after 50 minutes, react 23 minutes, after cooling, namely obtain coating agent.
Coating agent mixing prepared by step 3, rust-preventive agent step one prepared and step 2, obtains antirust drawing oil, wherein: the mass ratio of coating agent and rust-preventive agent is 100:9.
The antirust drawing oil of a kind of AC gold metal plate part of the present embodiment; adopt benzotriazole and barium mahogany sulfonate as rust-preventive agent; and adopt the coating agent of paint material and thinner composition; diethylene glycol ethylmethyl ether in thinner, polyvinyl alcohol, ethylene dichloride not only coordinate with paint material and make coating agent lubrication in Punching Process and provide protection effect can reach the best; and can mate-assist benzotriazole and barium mahogany sulfonate, play the effect promoting rustless property.Therefore, the needs lubricated when the present embodiment can meet the punching press of AC gold metal plate part, can meet antirust needs again, and the workpiece rust-proof life after punching press is 13 days, do not need to do in addition antirust again.
embodiment 2
A kind of AC gold metal plate part of the present embodiment is with antirust drawing oil base originally with embodiment 1, and difference is: described coating agent and the mass ratio of rust-preventive agent are 100:8.Described thinner is made up of following component, and each component is by following mass parts composition: 100 parts, gasoline, X-4 amino paint thinner 23 parts, zinc dialkyl dithiophosphate 10 parts, diethylene glycol ethylmethyl ether 7 parts, mibk 4 parts, Virahol 6 parts, polyvinyl alcohol 5 parts, diethylene glycol dimethyl ether 11 parts, ethylene dichloride 11 parts.A kind of AC gold metal plate part of the present embodiment preparation method of antirust drawing oil, its basic step is with embodiment 1.
The antirust drawing oil of a kind of AC gold metal plate part of the present embodiment; adopt benzotriazole and barium mahogany sulfonate as rust-preventive agent; and adopt the coating agent of paint material and thinner composition; diethylene glycol ethylmethyl ether in thinner, polyvinyl alcohol, ethylene dichloride not only coordinate with paint material and make coating agent lubrication in Punching Process and provide protection effect can reach the best; and can mate-assist benzotriazole and barium mahogany sulfonate, play the effect promoting rustless property.Therefore, the needs lubricated when the present embodiment can meet the punching press of AC gold metal plate part, can meet antirust needs again, and the workpiece rust-proof life after punching press is 12 days, do not need to do in addition antirust again.
embodiment 3
A kind of AC gold metal plate part of the present embodiment is with antirust drawing oil base originally with embodiment 1, and difference is: described coating agent and the mass ratio of rust-preventive agent are 100:11.100 parts, gasoline, X-4 amino paint thinner 23 parts, zinc dialkyl dithiophosphate 12 parts, diethylene glycol ethylmethyl ether 9 parts, mibk 7 parts, Virahol 8 parts, polyvinyl alcohol 9 parts, diethylene glycol dimethyl ether 13 parts, ethylene dichloride 13 parts.A kind of AC gold metal plate part of the present embodiment preparation method of antirust drawing oil, its basic step is with embodiment 1.
The antirust drawing oil of a kind of AC gold metal plate part of the present embodiment; adopt benzotriazole and barium mahogany sulfonate as rust-preventive agent; and adopt the coating agent of paint material and thinner composition; diethylene glycol ethylmethyl ether in thinner, polyvinyl alcohol, ethylene dichloride not only coordinate with paint material and make coating agent lubrication in Punching Process and provide protection effect can reach the best; and can mate-assist benzotriazole and barium mahogany sulfonate, play the effect promoting rustless property.Therefore, the needs lubricated when the present embodiment can meet the punching press of AC gold metal plate part, can meet antirust needs again, and the workpiece rust-proof life after punching press is 11 days, do not need to do in addition antirust again.
Claims (5)
1. the antirust drawing oil of AC gold metal plate part, is characterized in that, this antirust drawing oil is made up of coating agent and rust-preventive agent, wherein: described coating agent and the mass ratio of rust-preventive agent are 100:8 ~ 11.
2. the antirust drawing oil of a kind of AC gold metal plate part according to claim 1, it is characterized in that, described rust-preventive agent is made up of benzotriazole and barium mahogany sulfonate, wherein: the mass ratio of benzotriazole and barium mahogany sulfonate is 2:5.
3. a kind of AC gold metal plate part according to claim 1 antirust drawing oil, is characterized in that, described coating agent is by painting material and thinner forms, and the mass ratio of paint material and thinner is 100:2, wherein:
Described thinner is made up of following component, and each component is by following mass parts composition: 100 parts, gasoline, X-4 amino paint thinner 20 ~ 25 parts, zinc dialkyl dithiophosphate 10 ~ 12 parts, diethylene glycol ethylmethyl ether 7 ~ 9 parts, mibk 4 ~ 7 parts, Virahol 6 ~ 8 parts, polyvinyl alcohol 5 ~ 9 parts, diethylene glycol dimethyl ether 11 ~ 13 parts, ethylene dichloride 11 ~ 13 parts;
Described paint material is ester gum varniss.
4. the antirust drawing oil of a kind of AC gold metal plate part according to claim 3, it is characterized in that, described thinner is made up of following component, and each component is by following mass parts composition:
100 parts, gasoline,
X-4 amino paint thinner 23 parts,
Zinc dialkyl dithiophosphate 11 parts,
Diethylene glycol ethylmethyl ether 8 parts,
Mibk 5 parts,
Virahol 7 parts,
Polyvinyl alcohol 7 parts,
Diethylene glycol dimethyl ether 12 parts,
Ethylene dichloride 12 parts.
5. the antirust drawing oil of a kind of AC gold metal plate part according to claim 3, it is characterized in that, described thinner is made up of following component, and each component is by following mass parts composition:
100 parts, gasoline,
X-4 amino paint thinner 23 parts,
Zinc dialkyl dithiophosphate 10 parts,
Diethylene glycol ethylmethyl ether 7 parts,
Mibk 4 parts,
Virahol 6 parts,
Polyvinyl alcohol 5 parts,
Diethylene glycol dimethyl ether 11 parts,
Ethylene dichloride 11 parts.