CN102817036B - Galvanized steel plate nick protection rust inhibitor - Google Patents
Galvanized steel plate nick protection rust inhibitor Download PDFInfo
- Publication number
- CN102817036B CN102817036B CN201210287517.4A CN201210287517A CN102817036B CN 102817036 B CN102817036 B CN 102817036B CN 201210287517 A CN201210287517 A CN 201210287517A CN 102817036 B CN102817036 B CN 102817036B
- Authority
- CN
- China
- Prior art keywords
- rust
- steel plate
- rust inhibitor
- preventive agent
- plate galvanized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a galvanized steel plate nick protection rust inhibitor. Raw materials of the rust inhibitor comprise a deep refined environmental protection base oil, a rust inhibitor, nanometer quartz powder and an aromatic amine antioxidant. The galvanized steel plate nick protection rust inhibitor of the present invention has the following advantages that: the rust inhibitor has excellent anti-rust performance and strong adhesion; the galvanized steel plate nick can be effectively protected; the rust inhibitor contains a special anti-rust component providing an extremely effective effect for the galvanized steel plate; with the thin oil film, nick rust can be effectively prevented, and stain can not be formed on the front surface and the back surface of the steel plate; the rust inhibitor does not contain formaldehyde, benzene, heavy metals and other hazardous substances so as to provide good effects for environmental protection and physical and mental health of operators; the closed film has characteristics of excellent smoothness, discoloration resistance, corrosion resistance, high adhesion and the like; the rust inhibitor has good penetration, wherein the rust inhibitor can penetrate the pore, and general anti-rust oils are difficult to reach the pore; and the galvanized steel plate nick protection rust inhibitor of the present invention is applicable for surface anti-rust treatments between processes or indoor and outdoor steel, aluminum and alloy product instruments.
Description
Technical field
The present invention relates to a kind of metal antirusting agent, particularly a kind of rust-preventive agent of superelevation sticking power steel plate galvanized incision protection rust-preventive agent for the processing of steel plate galvanized part of adding.
Background technology
For preventing steel plate corrosion, in the work-ing life of extending steel plate, be coated with layer of metal zinc at surface of steel plate, be called steel plate galvanized.Add man-hour at steel plate galvanized part, in impact briquetting, require punching oil to there is good volatility, noresidue, tend to cause steel plate galvanized otch to get rusty not because of otch antirust ability, therefore more conventional way is to smear otch from the antirust pen of external import solid, but smear that otch is taken a lot of work and time-consuming with antirust pen, tend to cause coating irregular because of the relation of operation, cause rust-proof effect low, do not reach expected effect, can not effectively protect steel plate galvanized otch, and then cause the waste of resource, the reprocessing factor of import and the factor of cost of labor, cause production cost and tooling cost greatly to improve.Simultaneously, the factor such as complicacy of the workpiece based on production scene again, the cut surface of the steel plate galvanized in punching press, moulding very easily gets rusty again, and must not have oily existence at non-cutting part, if adopt traditional dipping can cause the full surface of steel plate galvanized to cover oil, can not reach desirable effect, serious restriction is simultaneously produced.
Therefore need a kind of steel plate galvanized incision protection rust-preventive agent; there is good rust-proof effect; can effectively protect steel plate galvanized otch; needn't apply rust-proofing wax more time-consumingly; meet environmental requirement, meet the antirust demand of steel plate galvanized incision protection; and non-cutting part there will not be greasy dirt, neat and tidy, environmental protection and economy.
Summary of the invention
In view of this; the object of the present invention is to provide a kind of steel plate galvanized incision protection rust-preventive agent; there is good rust-proof effect; can effectively protect steel plate galvanized otch; needn't apply rust-proofing wax meets American-European environmental requirement, meets the antirust demand of steel plate galvanized incision protection more time-consumingly; and non-cutting part there will not be greasy dirt, neat and tidy, environmental protection and economy.
Steel plate galvanized incision protection rust-preventive agent of the present invention, rust-preventive agent raw materials by weight comprises the dark refining environmental protection base oil of following component: 80-90%, the rust-preventive agent of 3-18%, the nanometer silica powder of 1-5% and the arylamine antioxidant of 0.1-1%;
Further, rust-preventive agent raw materials by weight comprises following component: 85% dark refining environmental protection base oil, 11.5% rust-preventive agent, 3% nanometer silica powder and 0.5% arylamine antioxidant;
Further, described dark refining environmental protection base oil is the mineral oil of carbochain C6-8;
Further, described rust-preventive agent is C18 calcium mahogany sulfonate;
Further, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
Beneficial effect of the present invention: steel plate galvanized incision protection rust-preventive agent of the present invention, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus, indoor rust-proof life exceedes 3 years.
Embodiment
Embodiment mono-
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 85% dark refining environmental protection base oil, 11.5% C18 calcium mahogany sulfonate, 3% nanometer silica powder and 0.5% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C7; In this enforcement, the mineral oil of carbochain C7 is replaced with to the one in the mineral oil of carbochain C6, carbochain C8 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
In the present embodiment, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.
Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 6.4 | 112 | 3 | 76 hours | 36 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
Embodiment bis-
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 80% dark refining environmental protection base oil, 15% rust-preventive agent, 4% nanometer silica powder and 1% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C6; In this enforcement, the mineral oil of carbochain C6 is replaced with to the one in the mineral oil of carbochain C7, carbochain C8 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
In the present embodiment, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 5.8 | 113 | 3 | 70 hours | 28 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
Embodiment tri-
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 90% dark refining environmental protection base oil, 18% rust-preventive agent, 1% nanometer silica powder and 1% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C8; In this enforcement, the mineral oil of carbochain C8 is replaced with to the one in the mineral oil of carbochain C7, carbochain C6 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
In the present embodiment, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 6 | 110 | 3 | 76 hours | 36 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
Embodiment tetra-
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 90% dark refining environmental protection base oil, 8.9% rust-preventive agent, 1% nanometer silica powder and 0.1% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C6; In this enforcement, the mineral oil of carbochain C6 is replaced with to the one in the mineral oil of carbochain C7, carbochain C8 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
Nanometer silica powder in the present embodiment is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 6.1 | 112 | 3 | 66 hours | 27 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
Embodiment five
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 85% dark refining environmental protection base oil, 11% rust-preventive agent, 3% nanometer silica powder and 1% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C8; In this enforcement, the mineral oil of carbochain C8 is replaced with to the one in the mineral oil of carbochain C7, carbochain C6 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
In the present embodiment, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 6.3 | 112 | 3 | 69 hours | 31 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
Embodiment six
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, rust-preventive agent raw materials by weight comprises following component: 80% dark refining environmental protection base oil, 14.9% rust-preventive agent, 5% nanometer silica powder and 0.1% arylamine antioxidant;
In the present embodiment, described dark refining environmental protection base oil is the mineral oil of carbochain C8; In this enforcement, the mineral oil of carbochain C8 is replaced with to the one in the mineral oil of carbochain C7, carbochain C6 according to equal quality per-cent, or according to equivalent weight than the mixture of mineral oil that replaces with carbochain C6, carbochain C7, carbochain C8, all qualified steel plate galvanized incision protection rust-preventive agent, products obtained therefrom character there is no significant difference;
In the present embodiment, described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.
The steel plate galvanized incision protection rust-preventive agent of the present embodiment, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.
As can be seen here, steel plate galvanized incision protection rust-preventive agent of the present invention, there is good rustless property and extremely strong sticking power, can effectively protect steel plate galvanized otch, needn't apply rust-proofing wax more time-consumingly and meet American-European environmental requirement, meet the antirust demand of steel plate galvanized incision protection, include very effectively special antirust component of steel plate galvanized, oil film as thin as a wafer can effectively prevent that otch from getting rusty, and can not form spot at the pros and cons of steel plate, not containing formaldehyde, benzene, the objectionable impuritiess such as heavy metal, be conducive to environment protection and operator's physical and mental health, can be used as final corrosion protection coating, also can be used as rust-proofing primer uses, its sealing rete has the features such as excellent planarization, anti-discolouration, erosion resistance and high tack, and there is good seepage force, can be deep into general slushing oil be difficult to arrive hole in, be applicable to the surperficial antirust processing such as inter process or indoor outer iron and steel, aluminium and alloy product apparatus.Be below the performance comparison parameter list of steel plate galvanized incision protection rust-preventive agent of the present invention and common rust-preventive agent:
| Project | Viscosity (mm2/s) | Flash-point (DEG C) | Rust-proof life (year) | Salt-fog resistant time | The wet-heat resisting time |
| Rust-preventive agent | 5.9 | 112 | 3 | 74 hours | 33 days |
| Common rust-preventive agent | 5 | 110 | 0.5 | 12 hours | 7 days |
In above-described embodiment, the F451 that described arylamine antioxidant provides for Jinzhou is safe, is outsourcing product.
And for above technique effect, the proportioning of embodiment mono-and processing parameter, result of use is best, is obviously better than other embodiment, is the best.
Finally explanation is, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement technical scheme of the present invention, and not departing from aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (3)
1. a steel plate galvanized incision protection rust-preventive agent, is characterized in that: rust-preventive agent raw materials by weight comprises the dark refining environmental protection base oil of following component: 80-90%, the C18 calcium mahogany sulfonate of 3-18%, the nanometer silica powder of 1-5% and the arylamine antioxidant of 0.1-1%; Described dark refining environmental protection base oil is the mineral oil of carbochain C6-8.
2. steel plate galvanized incision protection rust-preventive agent according to claim 1, is characterized in that: rust-preventive agent raw materials by weight comprises following component: 85% dark refining environmental protection base oil, 11.5% C18 calcium mahogany sulfonate, 3% nanometer silica powder and 0.5% arylamine antioxidant.
3. steel plate galvanized incision protection rust-preventive agent according to claim 2, is characterized in that: described nanometer silica powder is that particle diameter is the silica powder of 3-6nm.