CN104514088A - A preparing method of a formaldehyde adsorption rope - Google Patents
A preparing method of a formaldehyde adsorption rope Download PDFInfo
- Publication number
- CN104514088A CN104514088A CN201310448950.6A CN201310448950A CN104514088A CN 104514088 A CN104514088 A CN 104514088A CN 201310448950 A CN201310448950 A CN 201310448950A CN 104514088 A CN104514088 A CN 104514088A
- Authority
- CN
- China
- Prior art keywords
- rope
- formaldehyde absorbing
- carbon fiber
- formaldehyde
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparing method of a formaldehyde adsorption rope. An active carbon fiber rope core is braided into a braided rope sheath through a braiding device to form the rope body of the formaldehyde adsorption rope. The rope body is dipped with an aqueous aminobenzoic acid solution having a mass concentration of 10-40%. The prepared formaldehyde adsorption rope can effectively adsorb formaldehyde and other harmful gases, and is high in adsorbability and low in cost.
Description
Technical field
The present invention relates to field of rope, particularly a kind of preparation method of formaldehyde absorbing rope.
Background technology
In recent years, formaldehyde pollution becomes the key factor that household is polluted.Formaldehyde can produce obvious spread effect to eye, nose, larynx, skin etc.Absorption method has that removal efficiency is high, enrichment function is strong, can not cause the advantages such as secondary pollution, becomes the effective ways administering low concentration unwanted gas in recent years.Activated carbon fiber has that form of diverse, very thin, the micro-pore distribution concentration of diameter, quick adsorption and adsorption capacity are large, specific area high, is applicable to adsorbing gas phase or liquid phase low molecular weight.In addition, formaldehydes material contains hydroxyl, can generate the derivative of ammonia with some ammoniac compounds addition.Existing rope does not have formaldehyde absorbing effect.
Summary of the invention
The object of the invention is: the preparation method of the formaldehyde absorbing rope providing a kind of high adsorption capacity, cost low.
For achieving the above object, the present invention by the following technical solutions: a kind of preparation method of formaldehyde absorbing rope, comprises the following steps:
A, activated carbon fiber wire rope core is woven into kernmantle intracutaneous by braiding apparatus, forms formaldehyde absorbing rope rope body;
B, aminobenzoic acid is mixed with the aqueous solution that mass concentration is 10%-40%, as sizing agent;
C, by formaldehyde absorbing rope rope body dry after, be immersed in sizing agent, infiltrate 10-60min, then through pressure rolling, dry after obtain formaldehyde absorbing rope.
Kernmantle skin raw materials comprises chemical fibre class, natural fabric class, special fibre class long filament or yarn, and weaving manner comprises plain weave, twill.
Activated carbon fiber wire rope core comprise in activated carbon fiber, cloth felt one or both.
The advantage that the present invention has or good effect are: formaldehyde absorbing rope prepared by the present invention is made up of kernmantle skin and activated carbon fiber wire rope core, then use aminobenzoic acid solution to carry out infiltration process to rope body.This formaldehyde absorbing rope relies on physics and chemistry suction type can the effective pernicious gas such as formaldehyde adsorption, and having that high adsorption capacity, cost are low, applied range, the feature such as can to reuse, is effective product that in life staying idle at home, removal has formaldehyde pernicious gas.
Accompanying drawing explanation
Fig. 1 is the structural representation of formaldehyde absorbing rope prepared by the present invention.
Detailed description of the invention
Below in conjunction with specific embodiment, further elaboration the present invention, shown in the structural representation of formaldehyde absorbing rope prepared by Fig. 1 the present invention, this formaldehyde absorbing rope is made up of kernmantle skin 1 and activated carbon fiber wire rope core 2, then uses aminobenzoic acid solution to carry out infiltration process to rope body.
The preparation method of formaldehyde absorbing rope, comprises the following steps:
A, activated carbon fiber wire rope core 2 is woven in kernmantle skin 1 by braiding apparatus, forms formaldehyde absorbing rope rope body; Kernmantle skin 1 raw materials comprises chemical fibre class, natural fabric class, special fibre class long filament or yarn, and weaving manner comprises plain weave, twill; Activated carbon fiber wire rope core 2 comprise in activated carbon fiber, cloth felt one or both;
B, aminobenzoic acid is mixed with the aqueous solution that mass concentration is 10%-40%, as sizing agent;
C, by formaldehyde absorbing rope rope body dry after, be immersed in sizing agent, infiltrate 10-60min, then through pressure rolling, dry after obtain formaldehyde absorbing rope.
Embodiment 1:
The preparation method of formaldehyde absorbing rope, comprises the following steps:
First, activated carbon fiber wire rope core is woven into kernmantle intracutaneous and forms formaldehyde absorbing rope rope body.Rope skin material therefor is polypropylene filament yarn, and weaving manner is plain weave; Wire rope core material therefor is active carbon fiber fabrics felt.Secondly, be that the aminobenzoic aqueous acid of 10% is as sizing agent using mass concentration.Finally, after formaldehyde absorbing rope rope body is dried, be immersed in sizing agent, infiltrate 60min, then after pressure rolling, oven dry, obtain formaldehyde absorbing rope.
Embodiment 2:
The preparation method of formaldehyde absorbing rope, comprises the following steps:
First, activated carbon fiber wire rope core is woven into kernmantle intracutaneous and forms formaldehyde absorbing rope rope body.Rope skin material therefor is cotton yarn, and weaving manner is plain weave; Wire rope core material therefor is activated carbon fiber.Secondly, be that the aminobenzoic aqueous acid of 30% is as sizing agent using mass concentration.Finally, after formaldehyde absorbing rope rope body is dried, be immersed in sizing agent, infiltrate 20min, then after pressure rolling, oven dry, obtain formaldehyde absorbing rope.
Embodiment 3:
The preparation method of formaldehyde absorbing rope, comprises the following steps:
First, activated carbon fiber wire rope core is woven into kernmantle intracutaneous and forms formaldehyde absorbing rope rope body.Rope skin material therefor is polyester filament, and weaving manner is plain weave; Wire rope core material therefor is active carbon fiber fabrics felt.Secondly, be that the aminobenzoic aqueous acid of 40% is as sizing agent using mass concentration.Finally, after formaldehyde absorbing rope rope body is dried, be immersed in sizing agent, infiltrate 10min, then after pressure rolling, oven dry, obtain formaldehyde absorbing rope.
Formaldehyde absorbing rope prepared by the present invention has that high adsorption capacity, cost are low, applied range, the feature such as can to reuse, and is remove the effective product having formaldehyde pernicious gas in life staying idle at home.
Claims (3)
1. a preparation method for formaldehyde absorbing rope, is characterized in that, comprises the following steps:
A, activated carbon fiber wire rope core (2) is woven in kernmantle skin (1) by braiding apparatus, forms formaldehyde absorbing rope rope body;
B, aminobenzoic acid is mixed with the aqueous solution that mass concentration is 10%-40%, as sizing agent;
C, by formaldehyde absorbing rope rope body dry after, be immersed in sizing agent, infiltrate 10-60min, then through pressure rolling, dry after obtain formaldehyde absorbing rope.
2. the preparation method of formaldehyde absorbing rope according to claim 1, is characterized in that: kernmantle skin (1) raw materials comprises chemical fibre class, natural fabric class, special fibre class long filament or yarn, and weaving manner comprises plain weave, twill.
3. the preparation method of formaldehyde absorbing rope according to claim 1, is characterized in that: activated carbon fiber wire rope core (2) comprise in activated carbon fiber, cloth felt one or both.