CN104513611A - Air-permeable type concrete protection finishing coat - Google Patents
Air-permeable type concrete protection finishing coat Download PDFInfo
- Publication number
- CN104513611A CN104513611A CN201510032470.0A CN201510032470A CN104513611A CN 104513611 A CN104513611 A CN 104513611A CN 201510032470 A CN201510032470 A CN 201510032470A CN 104513611 A CN104513611 A CN 104513611A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- air
- finish paint
- protective finish
- permeable concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of concrete surface protection, and relates to an air-permeable type concrete protection finishing coat. The protection finishing coat consists of 60-80 parts of silicone emulsion, 10-20 parts of acrylic emulsion and/or modified acrylic emulsion, 2-6 parts of a dispersing agent, 0.5-5 parts of a preservative, 5-10 parts of a coalescing agent and an acceptable amount of water and can be steeped into concrete by 1-2mm and integrally combined with the concrete; the air permeability of the air-permeable type concrete protection finishing coat cannot be affected and is excellent in waterproofing property, weather resistance, pollution resistance and corrosion resistance. A preparation method for the air-permeable type concrete protection finishing coat comprises the steps: at room temperature, adding silicone emulsion, acrylic emulsion and/or modified acrylic emulsion and an acceptable amount of water into a container, controlling the rotating speed to 800-1,000rpm, stirring for 15-30min, keeping the rotating speed to be constant, adding the dispersing agent, the coalescing agent and the preservative into the container, stirring for 30-60min, and finally adding water to adjust to the required viscosity. The preparation method is convenient to operate and can be implemented at the room temperature.
Description
Technical field
The invention belongs to concrete surface protecting field, particularly a kind of weather resistance anti-corrosive protecting agent, be specially a kind of air-permeable concrete protective finish paint.
Background technology
Concrete material is from since appearance, and experienced by the development course of low strength, medium tenacity, high strength and even superstrength, people seem always to be happy to pursue improving constantly of intensity.But the fact of a large amount of concrete structure premature failure shows, high strength does not also mean that high-durability.Concrete structure is under arms in process, inevitably be subject to the physics of surrounding environment, chemistry and biological action, and the intrusion that the porousness of concrete self is extraneous harmful ion provides passage, make concrete material performance degradation and decline, and then the performance of harm concrete structure.Because concrete durability is not enough, cause structure premature failure so that the event destroying avalanche is seen everywhere at home and abroad, and regulation effect seems very not remarkable.Endurance issues is along with the whole military service process of concrete structure, and its consequence not only causes huge financial loss, also may cause serious social concern.Therefore, newly-built reinforced concrete structures takes necessary safeguard procedures to improving the weather resistance of concrete structure and extending its service life tool and be of great significance.Large quantity research and engineering practice show, concrete endurance quality deterioration is how relevant with water, and therefore, waterproof becomes the important means improving concrete structure durability.
Patent EP 0538555 discloses a kind of water miscible liquid including organic silicon compound for flooding inorganic materials particularly material of construction, and the tensio-active agent of anion surfactant and siliceous functional group selected by emulsifying agent.But emulsion described in this patent need be standby by high-pressure emulsification mechanism, and energy consumption is high.
Patent CN102134443A discloses a kind of Concrete Protective Agent containing resin emulsion, silicone additives and potassium methyl silicate; but in this material, there is a large amount of deionized waters; the construction effect of material in facade structures can be had a strong impact on; must repeatedly repeat to smear; and the waterproof ability of this material is limited, the long-term waterproof requirement of concrete structure can not be ensured.
Patent CN200710187907.3 discloses a kind of building surface organosilicon water-proof emulsion, at catalyst of triethylamine or pyridine or N, under the effect of N-dimethyl benzylamine, silicon (oxygen) alkane of the hydroxyl of modification or amino and silane coupling agent are obtained by emulsifier, but the hydrophobic group of this organosilicon water-proof emulsion is side chain or side chain SULPHURYL CHLORIDE structure, use under comparatively rugged environment, the poor-performing of emulsion.
Patent CN201010131848.X discloses a kind of organosilicon concrete protectant; it is prepared from primarily of alkyl silane oligopolymer, emulsifying agent, aminosilane tackifier and water; this protective material penetrating power is strong; the rapid crosslinking polymerization of the moisture absorbed with concrete becomes macromole siloxanes; do not block the kapillary in concrete structure and hole; have good ventilation property, but this protectant preparation technology of application is comparatively complicated, energy consumption is higher.
Summary of the invention
In order to solve the deficiencies in the prior art, first, the object of the present invention is to provide a kind of air-permeable concrete protective finish paint, this protective topcoat is transparent, do not hide concrete surface, ensure that the surface effect that Concrete in Natural is good, be convenient to later stage concrete structure monitoring, this protective topcoat dipping is to concrete 1-2mm, combine together with concrete, its ventilation property is unaffected, has excellent waterproof, weather-proof, resistant, anticorrosion, Tension Adjustable, thus extend concrete durable practicality; Secondly, present invention also offers the preparation method of this air-permeable concrete protective finish paint, this preparation method is easy to operate, can carry out under room temperature.
For realizing above-mentioned technical purpose, technical scheme of the present invention is:
A kind of air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion 60-80 part;
ACRYLIC EMULSION and/or modified acrylic acid emulsion 10-20 part;
Dispersion agent 2-6 part;
Sanitas 0.5-5 part;
Film coalescence aid 5-10 part;
And can the water of receiving amount.
Preferably, described a kind of air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion 70-80 part;
ACRYLIC EMULSION and/or modified acrylic acid emulsion 15-20 part;
Dispersion agent 4-6 part;
Sanitas 1-3 part;
Film coalescence aid 6-8 part;
And can the water of receiving amount.
Preferred, described a kind of air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion 78 parts;
ACRYLIC EMULSION and/or modified acrylic acid emulsion 16 parts;
Dispersion agent 5 parts;
Sanitas 2 parts;
Film coalescence aid 8 parts;
And can the water of receiving amount.
Resin emulsion of the present invention has highly cross-linked cancellated organopolysiloxane, its type mainly includes methyl phenyl silicone resin, methyl silicon resin, low phenyl methyl silicone resin, silicone resin emulsion, self-drying type silicone resin, high temperature modification silicone resin, epoxy modified silicone resin, organosilicon polyester modified resin, self-drying type environmental protection silicone resin, environment-protecting silicone resin, non-viscous paint silicone resin, high light silicone resin, phenmethyl transparent silicon resin, methyl transparent organic silicon resin, the bonding silicone resin of mica, poly-methyl silicon resin, amino silicone, fluorine silicon resin, silicon resin solution, silicone-epoxy resin, organic silicon polyester resin, solvent-resisting silicone resin, organic silicon resin adhesive, fluorine silicon resin Silicone Sealants, high-temperature resisting methyl silicone resin, self-drying type organic silicon insulating varnish, methyl MQ silicone resin, Vinyl MQ silicon resin, organosilicon acrylic resin coating etc.
ACRYLIC EMULSION of the present invention comprises pure-acrylic emulsion, organosilicon crylic acid latex, benzene emulsion, acrylate and vinyl acetate emulsion etc.
Modified acrylic acid emulsion of the present invention comprises various types of modified acrylic acid emulsion, is specifically preferably one or more in organosilicon-modified acrylic emulsion, fluorine-carbon modified ACRYLIC EMULSION and epoxy-modified acrylic acid emulsion.
Film coalescence aid of the present invention is not specifically limited, and can adopt the commercially available various film coalescence aid being applicable to acrylic coating or silicon resin coating, this is known for those skilled in the art.In the present invention, preferably, described film coalescence aid is alkoxide solvent.
Dispersion agent of the present invention is not specifically limited, and can adopt the commercially available various dispersion agents being applicable to acrylic coating or silicon resin coating, this is known for those skilled in the art.In the present invention, preferably, described dispersion agent is sodium lauryl sulphate.
Sanitas of the present invention is not specifically limited, and can adopt the commercially available various sanitass being applicable to acrylic coating or silicon resin coating, this is known for those skilled in the art.In the present invention, preferably, described sanitas is isothiazoline sanitas.
The preparation method of above-mentioned a kind of air-permeable concrete protective finish paint, comprises the step of carrying out as follows:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and/or modified acrylic acid emulsion and appropriate water add in container; controlling rotating speed is that 800-1000rpm stirs 15-30min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 30-60min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
A kind of air-permeable concrete protective finish paint of the present invention adopts above-mentioned preparation method to be prepared, and can obtain good dispersity, stability is high, the product of excellent performance.
A kind of air-permeable concrete protective finish paint of the present invention adopts resin emulsion and ACRYLIC EMULSION and/or modified acrylic acid emulsion composite; add various auxiliary agent formulated; this air-permeable concrete protective finish paint and concrete generation chemical reaction; form the hydrophobic protective layer of the 1-2mm degree of depth; make concrete surface become hydrophobic nature from wetting ability, its ventilation property is also unaffected.Its good characteristic comprise environmental protection, transparent, do not fire, flood, unidirectional breathing, not efflorescence, repeatedly construct accessible, thus improve concrete protection against corrosion, freezing-thawing resistance, can effectively keep the color and luster of base material and gloss 20 years constant, thus reach gloss and the outward appearance of permanent maintenance buildings, thus extend concrete durable practicality.
The preparation method of a kind of air-permeable concrete protective finish paint of the present invention; preparation condition is gentle; production technique is simple; possess good operability and there is not the problem of organic solvent evaporates, full scale production process produces without waste gas, waste liquid, waste residue, and product does not in use exist obvious environmental pollution yet; and without the need to heating in preparation process; energy consumption is low, carbon emission is few, reduces production cost significantly, is a kind of type material of environmental protection low-carbon type.
Embodiment
Below will be described in detail the preferred embodiments of the present invention.The experimental technique of unreceipted actual conditions in preferred embodiment, usually conveniently condition.Reagent used in following examples is all bought from business.
In following examples, water-intake rate, depth of penetration detect with reference to JTT275-2000 " concrete for marine works structural anticorrosion erosion technical regulation " and JC/T902-2002 " building surface waterproofing agent of organosilicon ".
embodiment 1
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: phenmethyl transparent silicon resin emulsion 60g;
ACRYLIC EMULSION: organosilicon crylic acid latex 12 g;
Dispersion agent: sodium lauryl sulphate 2 g;
Sanitas: BIT 1 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 6 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 2
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: epoxy modified silicone resin emulsion 78 g;
ACRYLIC EMULSION: pure-acrylic emulsion 16 g;
Dispersion agent: sodium lauryl sulphate 5 g;
Sanitas: BIT 2 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 8 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 3
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: methyl phenyl silicone resin emulsion 65 g;
ACRYLIC EMULSION: benzene emulsion 20 g;
Dispersion agent: sodium lauryl sulphate 4 g;
Sanitas: BIT 2 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 6 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 4
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: epoxy modified silicone resin emulsion 70 g;
Modified acrylic acid emulsion: fluorine-carbon modified ACRYLIC EMULSION 15 g;
Dispersion agent: sodium lauryl sulphate 4 g;
Sanitas: BIT 1 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 7 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; modified acrylic acid emulsion and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 5
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: epoxy modified silicone resin emulsion 80 g;
ACRYLIC EMULSION and modified acrylic acid emulsion: pure-acrylic emulsion 10 g, fluorine-carbon modified ACRYLIC EMULSION 5 g;
Dispersion agent: sodium lauryl sulphate 5 g;
Sanitas: BIT 3 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 6 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION, modified acrylic acid emulsion and appropriate water add in container, and controlling rotating speed is that 1000rpm stirs 20min; obtain solution I; keep rotating speed constant, in solution I, add dispersion agent, film coalescence aid, sanitas, stir 45min; finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 6
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: phenmethyl transparent silicon resin emulsion 80 g;
ACRYLIC EMULSION and modified acrylic acid emulsion: pure-acrylic emulsion 8g, organosilicon-modified acrylic emulsion 10g;
Dispersion agent: sodium lauryl sulphate 6 g;
Sanitas: BIT 2 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 6 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION, modified acrylic acid emulsion and appropriate water add in container, and controlling rotating speed is that 1000rpm stirs 20min; obtain solution I; keep rotating speed constant, in solution I, add dispersion agent, film coalescence aid, sanitas, stir 45min; finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 7
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: epoxy modified silicone resin emulsion 85 g;
ACRYLIC EMULSION: pure-acrylic emulsion 8 g;
Dispersion agent: sodium lauryl sulphate 5 g;
Sanitas: BIT 2 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 8 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
embodiment 8
Air-permeable concrete protective finish paint, mainly composed of the following components by weight:
Resin emulsion: epoxy modified silicone resin emulsion 55 g;
ACRYLIC EMULSION: pure-acrylic emulsion 30 g;
Dispersion agent: sodium lauryl sulphate 5 g;
Sanitas: BIT 2 g;
Film coalescence aid: alcohol ester 12 film coalescence aid 8 g;
And can the water of receiving amount.
Preparation method is specially:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and appropriate water add in container; controlling rotating speed is that 1000rpm stirs 20min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 45min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.
The obtained transparent uniform state of air-permeable concrete protective finish paint outward appearance, inclusion-free, without layering, without floating oil, without precipitating, being brushed and after concrete surface, being measured its water-intake rate and depth of penetration.
The water-intake rate of the air-permeable concrete protective finish paint obtained by table 1 embodiment 1-8 and depth of penetration measurement result
| Water-intake rate (mm/min 0.5） | Depth of penetration (mm) | |
| Embodiment 1 | 0.0039 | 1.6±0.2 |
| Embodiment 2 | 0.0036 | 2.0±0.2 |
| Embodiment 3 | 0.0043 | 1.8±0.2 |
| Embodiment 4 | 0.0042 | 1.6±0.2 |
| Embodiment 5 | 0.0040 | 2.0±0.2 |
| Embodiment 6 | 0.0044 | 1.6±0.2 |
| Embodiment 7 | 0.045 | 1.2±0.2 |
| Embodiment 8 | 0.036 | 1.6±0.2 |
| Blank test | 0.051 | -- |
To the air-permeable concrete protective finish paint obtained by above-described embodiment 2 according to " exterior wall coating material of synthetic resin emulsion national standard (GB) GB/T9755-2001 " test material is alkaline-resisting, sticking power, stain resistant, the performance test such as aging, test result is in table 2.
Table 2 material properties test result
| Test item | Unit | Technical requirements | Assay |
| Application property | / | Brush two roads accessible | Meet |
| Water tolerance | / | 96h is without exception | Meet |
| Alkali resistance | / | 48h is without exception | Meet |
| Abrasion resistance | Secondary | ≥2000 | By 3000 |
| Artificial ageing resistance | / | 500h is non-foaming, do not peel off, flawless | Meet |
| Efflorescence | Level | ≤1 | 0 |
| Variable color | Level | ≤2 | 0 |
| Coating temperature-change resistance | / | 5 circulations are without exception | Meet |
| Stain resistant | ％ | 15％ | 5 |
| Lipstick test for contamination | / | 100% removes | Pass through |
| Children water-based Mark pen | Blue water-color paintbrush, 100% removes | Pass through | |
| Sticking power | Level | ≤ 1 grade | 0 grade |
What finally illustrate is, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (8)
1. an air-permeable concrete protective finish paint, is characterized in that, mainly composed of the following components by weight:
Resin emulsion 60-80 part;
ACRYLIC EMULSION and/or modified acrylic acid emulsion 10-20 part;
Dispersion agent 2-6 part;
Sanitas 0.5-5 part;
Film coalescence aid 5-10 part;
And can the water of receiving amount.
2. a kind of air-permeable concrete protective finish paint according to claim 1, is characterized in that, mainly composed of the following components by weight:
Resin emulsion 70-80 part;
ACRYLIC EMULSION and/or modified acrylic acid emulsion 15-20 part;
Dispersion agent 4-6 part;
Sanitas 1-3 part;
Film coalescence aid 6-8 part;
And can the water of receiving amount.
3. a kind of air-permeable concrete protective finish paint according to claim 1, is characterized in that, described ACRYLIC EMULSION is one or more in pure-acrylic emulsion, organosilicon crylic acid latex, benzene emulsion and acrylate and vinyl acetate emulsion.
4. a kind of air-permeable concrete protective finish paint according to claim 1, is characterized in that, described modified acrylic acid emulsion is one or more in organosilicon-modified acrylic emulsion, fluorine-carbon modified ACRYLIC EMULSION and epoxy-modified acrylic acid emulsion.
5. a kind of air-permeable concrete protective finish paint according to claim 1, it is characterized in that, described film coalescence aid is alkoxide solvent.
6. a kind of air-permeable concrete protective finish paint according to claim 1, it is characterized in that, described dispersion agent is sodium lauryl sulphate.
7. a kind of air-permeable concrete protective finish paint according to claim 1, it is characterized in that, described sanitas is isothiazoline sanitas.
8. the preparation method of a kind of air-permeable concrete protective finish paint described in any one of claim 1-7, is characterized in that, comprise the step of carrying out as follows:
At room temperature; first by resin emulsion; ACRYLIC EMULSION and/or modified acrylic acid emulsion and appropriate water add in container; controlling rotating speed is that 800-1000rpm stirs 15-30min, obtains solution I, keeps rotating speed constant; dispersion agent, film coalescence aid, sanitas is added in solution I; stir 30-60min, finally add water and be adjusted to required viscosity, obtain air-permeable concrete protective finish paint.