CN104513562A - Antibacterial intelligent clean paint and preparation method thereof - Google Patents
Antibacterial intelligent clean paint and preparation method thereof Download PDFInfo
- Publication number
- CN104513562A CN104513562A CN201510030771.XA CN201510030771A CN104513562A CN 104513562 A CN104513562 A CN 104513562A CN 201510030771 A CN201510030771 A CN 201510030771A CN 104513562 A CN104513562 A CN 104513562A
- Authority
- CN
- China
- Prior art keywords
- agent
- antibacterial
- paint
- antiseptic
- hollow glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial intelligent clean paint which comprises deionized water, hydroxyethyl cellulose, a pH value regulator, a dispersing agent, a wetting agent, titanium dioxide, talcum powder, kaolin, polyacrylate, propylene glycol, alcohol ester-12, a flatting agent, a defoaming agent, hollow glass beads, a WJ-586 antibacterial agent and a WJ-582 antibacterial agent. The invention further discloses a preparation method of the antibacterial intelligent clean paint. The antibacterial intelligent clean paint disclosed by the invention is high in antibacterial mildew resistance in damp environment; the paint film can be used for repeatedly and persistently killing the escherichia coli, staphylococcus aureus, fungi, mosses and phycomycetes and persistently resisting the reproduction and breeding of mildew and fungi; the antibacterial intelligent clean paint is relatively good in flatting property and construction property, and has superstrong adhesive force and the paint film is firm and durable.
Description
Technical field
The present invention relates to a kind of paint field, particularly one antibacterial intelligence cleaning paint and preparation method thereof.
Background technology
Toilet lacks solar radiation; the corner humidity easy breed bacteria in place and mould; that mildew appears in interior wall coating coating; not only lose its decoration and provide protection; also can send disgusting frowst, pollute indoor environment, induce an illness; the healthy of the people in serious threat, affects the quality of life of people.
Mildew-resistant common in the market, antimicrobial paint series products, lower to the restraining effect of some bacterium, need to add a large amount of mildew-resistant, antiseptic-germicide could obtain desirable effect, cause cost to increase, the pollution of environment is also increased.And traditional mildew-resistant, antibiotic emulsion paint under the plum rain season wet weather of certain areas, still there will be mildew liver moss.
Summary of the invention
For overcoming above-mentioned technological deficiency, the invention discloses a kind of antibacterial intelligence cleaning paint of environment-friendly type, can be attached to uniformly on emulsion paint and tiles in toilet.
Antibacterial intelligence cleaning paint disclosed by the invention is containing deionized water, Natvosol, pH value conditioning agent, dispersion agent, wetting agent, titanium dioxide, talcum powder, kaolin, polyacrylic ester, propylene glycol, alcohol ester-12, flow agent, defoamer, hollow glass micropearl, WJ-586 antiseptic-germicide, WJ-582 antiseptic-germicide.
Each Ni lead-free solder alloy, deionized water is 26%, Natvosol is 0.2%, PH value conditioning agent is 0.4%, dispersion agent is 0.4%, wetting agent is 0.6%, titanium dioxide is 20%, talcum powder is 4%, kaolin is 4%, polyacrylic ester 25%, propylene glycol are 2%, alcohol ester-12 is 5%, flow agent is 0.3%, defoamer is 0.3%, hollow glass micropearl is 7.5% WJ-586 antiseptic-germicide 3.6%, WJ-582 antiseptic-germicide 0.7%.
Described PH value conditioning agent is any one in the ammoniacal liquor of concentration 28%, concentration 10% potassium hydroxide, described dispersion agent
Be undersaturated polyacrylic acid sodium salt, amine amide, described lubricant is unsaturated polyester siloxanes, described inorganic antiseptic be silver,
Zinc, copper metal ion, described flow agent is Siloxane-Oxyalkylene Copolymers, and described defoamer is polysiloxane.
The invention also discloses the preparation method of above-mentioned antibacterial intelligence cleaning paint, the method is by each component of deionized water mixing except hollow glass micropearl, carry out disperseing, grinding, carry out paint after being less than 20 μm of fineness requirement, during paint, add hollow glass micropearl, make hollow glass micropearl surface adsorption inorganic antiseptic and ACRYLIC EMULSION, after making this paint film, form reticulated structure, effectively can stop infiltration and the flat smooth decorative effect of moisture.
Excellent effect of the present invention is: (1) the present invention adopts WJ-586 antiseptic-germicide, WJ-582 antiseptic-germicide, at the ring of humidity
In border, its antibacterial and mouldproof is strong, and paint film energy repeatability, permanence kill intestinal bacteria, streptococcus aureus, fungi, liver moss
Bacterium, phycomycete, can be long-term lower than mould, fungus breeding with grow; (2) the present invention adopt hollow glass micropearl make levelling property and application property better, there is superpower sticking power, paint film tight permanent; (3) the present invention adds special rhombus dihedral filling hollow glass micropearl, and have physics repellency and waterproof and breathable function, can form fine and close paint film, effectively prevent moisture penetration, more can resist the erosion of moisture and steam, paint film can not come off, get loose; (4) emulsion paint preparation method of the present invention significantly can reduce the remaining smell of product.
Embodiment
Below in conjunction with concrete embodiment, the present invention is further elaborated, but the present invention is not limited to following embodiment.
Embodiment:
Component proportion: by weight percentage, deionized water is 26%, Natvosol is 0.2%, PH value conditioning agent is 0.4%, dispersion agent is 0.4%, wetting agent is 0.6%, titanium dioxide is 20%, talcum powder is 4%, kaolin is 4%, polyacrylic ester 25%, propylene glycol are 2%, alcohol ester-12 is 5%, flow agent is 0.3%, defoamer is 0.3%, hollow glass micropearl is 7.5% WJ-586 antiseptic-germicide 3.6%, WJ-582 antiseptic-germicide 0.7%.
Preparation method: by each component of deionized water mixing except hollow glass micropearl, carry out disperseing, grinding, paint is carried out after being less than 20 μm of fineness requirement, during paint, add hollow glass micropearl, make hollow glass micropearl surface adsorption inorganic antiseptic and ACRYLIC EMULSION, after making this paint film, form reticulated structure, effectively can stop infiltration and the flat smooth decorative effect of moisture.
Claims (4)
1. an antibacterial intelligence cleaning paint, is characterized in that: containing deionized water, Natvosol, pH value conditioning agent, dispersion agent, wetting agent, titanium dioxide, talcum powder, kaolin, polyacrylic ester, propylene glycol, alcohol ester-12, flow agent, defoamer, hollow glass micropearl, WJ-586 antiseptic-germicide, WJ-582 antiseptic-germicide.
2. the antibacterial intelligence cleaning paint as described in claim 1, it is characterized in that: each Ni lead-free solder alloy, deionized water is 26%, Natvosol is 0.2%, PH value conditioning agent is 0.4%, dispersion agent is 0.4%, wetting agent is 0.6%, titanium dioxide is 20%, talcum powder is 4%, kaolin is 4%, polyacrylic ester 25%, propylene glycol be 2%, alcohol ester-12 is 5%, flow agent is 0.3%, defoamer is 0.3%, hollow glass micropearl is 7.5% WJ-586 antiseptic-germicide 3.6%, WJ-582 antiseptic-germicide 0.7%.
3. the antibacterial intelligence cleaning paint as described in claim 1, it is characterized in that: described PH value conditioning agent is any one in the ammoniacal liquor of concentration 28%, concentration 10% potassium hydroxide, described dispersion agent be in undersaturated polyacrylic acid sodium salt, amine amide any one, described lubricant is unsaturated polyester siloxanes, described inorganic antiseptic is silver, zinc, copper metal ion, described flow agent is Siloxane-Oxyalkylene Copolymers, and described defoamer is polysiloxane.
4. the preparation method of the antibacterial intelligence cleaning paint as described in claim 1, it is characterized in that: by each component of deionized water mixing except hollow glass micropearl, carry out disperseing, grinding, paint is carried out after being less than 20 μm of fineness requirement, during paint, add hollow glass micropearl, make hollow glass micropearl surface adsorption inorganic antiseptic and ACRYLIC EMULSION, after making this paint film, form reticulated structure.