CN104513508A - 一种墙面耐磨固化涂料 - Google Patents
一种墙面耐磨固化涂料 Download PDFInfo
- Publication number
- CN104513508A CN104513508A CN201310457907.6A CN201310457907A CN104513508A CN 104513508 A CN104513508 A CN 104513508A CN 201310457907 A CN201310457907 A CN 201310457907A CN 104513508 A CN104513508 A CN 104513508A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- coating
- curable coating
- resistant curable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种墙面耐磨固化涂料，其由以下重量份数的原料制成：聚乙烯醇缩定醛2.5-4.3份，六偏磷酸钠2.1-3.4份，丙烯酸多元醇0.8-1.5份，12-羟基硬脂酸5.6-7.2份，四甲基氯化铵4.5-6.6份，亚甲基丁二酸1.2-1.5份，填料0.3-0.7份，分散剂0.3-0.5份；防霉剂0.1-0.2份。本发明的防紫外线的耐磨固化涂料具有高生产效率、低耗能与低成本等优点，获得的漆膜具有外观好、耐刮划佳、耐磨性和耐溶剂性佳之特点；另外水性有色涂料组合物具有不含挥发性有机化合物或其含量较低的优点，对环境污染性低，可作为环保材料。
Description
技术领域
本发明涉及一种涂料，尤其是涉及一种墙面耐磨固化涂料，属于涂料领域。
背景技术
过去用于基材的涂料大多为溶剂型涂料，然而溶剂型涂料所排放到大气中的挥发性有机溶剂，却会对环境造成恶劣影响。近年来，由于人类对环保及能源的重视，世界各国相继对涂料中VOC 的含量严格控制，促使涂料的研究由习用的溶剂型涂料渐渐转移至水性涂料。与溶剂型涂料相比，水性涂料具有不含VOC 或VOC 含量较低的优点，对环境污染性低。传统的在塑料件表面的涂布，一般需要经过二涂二烤或三涂三烤的程序。以二涂二烤为例，先喷涂底漆，底漆除提供塑料件表面上所需的颜色之外，尚可封固基底并增强之后喷涂的面漆与基底的附着力等。底漆在经过烘烤后，接着，再喷涂面漆，面漆与底漆搭配使整体涂层显出光泽及色彩感，并使涂层具有高耐磨等特性。多道工序的操作，不只涂料的用量大，也非常的耗工时，进而增加了成本。因此，业界均致力于开发通过一次涂装即可达到美观与性能兼具的涂层的耐磨固化涂料。
发明内容
针对现有技术的不足，本发明所要解决的技术问题是，提供一种墙面耐磨固化涂料，提高了涂料的防紫外线性能和稳定性，无毒环保，提高了生产效率，降低了生产成本。
为解决上述技术问题，本发明采取的技术方案是，一种墙面耐磨固化涂料，其由以下重量份数的原料制成：
聚乙烯醇缩定醛2.5-4.3份，六偏磷酸钠2.1-3.4份，丙烯酸多元醇0.8-1.5 份，12-羟基硬脂酸5.6-7.2份，四甲基氯化铵4.5-6.6份，亚甲基丁二酸1.2-1.5份，填料0.3-0.7份，分散剂0.3-0.5份；防霉剂0.1-0.2份。
优化的，上述墙面耐磨固化涂料，其由以下重量份数的原料制成：
聚乙烯醇缩定醛2.5份，六偏磷酸钠2.1份，丙烯酸多元醇0.8份，12-羟基硬脂酸5.6份，四甲基氯化铵4.5份，亚甲基丁二酸1.2份，填料0.3份，分散剂0.3份；防霉剂0.1份。
优化的，上述墙面耐磨固化涂料，其填料为沉淀硫酸钡。
本发明的防紫外线的耐磨固化涂料当以一次喷涂施工即可获得美观与高性能兼具的涂膜，相较于传统二次或三次的涂装方式；本发明具有高生产效率、低耗能与低成本等优点，获得的漆膜具有外观好、耐刮划佳、耐磨性和耐溶剂性佳之特点；另外水性有色涂料组合物具有不含挥发性有机化合物或其含量较低的优点，对环境污染性低，可作为环保材料。
具体实施方式
下面结合其实施例对发明进一步详细说明。
实施例1
本发明为一种墙面耐磨固化涂料，其由以下重量份数的原料制成：
聚乙烯醇缩定醛2.5份，六偏磷酸钠2.1份，丙烯酸多元醇0.8份，12-羟基硬脂酸5.6份，四甲基氯化铵4.5份，亚甲基丁二酸1.2份，填料0.3份，分散剂0.3份；防霉剂0.1份。
填料为沉淀硫酸钡。
实施例2
本发明为一种墙面耐磨固化涂料，其由以下重量份数的原料制成：
聚乙烯醇缩定醛4.3份，六偏磷酸钠3.4份，丙烯酸多元醇1.5 份，12-羟基硬脂酸7.2份，四甲基氯化铵6.6份，亚甲基丁二酸1.5份，填料0.7份，分散剂0.5份；防霉剂0.2份。
填料为沉淀硫酸钡。本发明的防紫外线的耐磨固化涂料当以一次喷涂施工即可获得美观与高性能兼具的涂膜，相较于传统二次或三次的涂装方式；本发明具有高生产效率、低耗能与低成本等优点，获得的漆膜具有外观好、耐刮划佳、耐磨性和耐溶剂性佳之特点；另外水性有色涂料组合物具有不含挥发性有机化合物或其含量较低的优点，对环境污染性低，可作为环保材料。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明的保护范围。
Claims (3)
1.一种墙面耐磨固化涂料，其特征在于：由以下重量份数的原料制成：
聚乙烯醇缩定醛2.5-4.3份，六偏磷酸钠2.1-3.4份，丙烯酸多元醇0.8-1.5 份，12-羟基硬脂酸5.6-7.2份，四甲基氯化铵4.5-6.6份，亚甲基丁二酸1.2-1.5份，填料0.3-0.7份，分散剂0.3-0.5份；防霉剂0.1-0.2份。
2.根据权利要求1所述的墙面耐磨固化涂料，其特征在于：
由以下重量份数的原料制成：聚乙烯醇缩定醛2.5份，六偏磷酸钠2.1份，丙烯酸多元醇0.8份，12-羟基硬脂酸5.6份，四甲基氯化铵4.5份，亚甲基丁二酸1.2份，填料0.3份，分散剂0.3份；防霉剂0.1份。
3.根据权利要求1所述的墙面耐磨固化涂料，其特征在于：所述填料为沉淀硫酸钡。