CN104499346A - Manufacture technology for reinforced type bamboo-pulp paper - Google Patents
Manufacture technology for reinforced type bamboo-pulp paper Download PDFInfo
- Publication number
- CN104499346A CN104499346A CN201410610746.4A CN201410610746A CN104499346A CN 104499346 A CN104499346 A CN 104499346A CN 201410610746 A CN201410610746 A CN 201410610746A CN 104499346 A CN104499346 A CN 104499346A
- Authority
- CN
- China
- Prior art keywords
- fiber suspension
- bamboo
- enhancement mode
- reinforced type
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A related manufacture technology for reinforced type bamboo-pulp paper comprises the following concrete steps: a, selecting a bamboo pulp fiber suspension; b, adding plant fiber and modified fiber into the bamboo pulp fiber suspension and mixing to form a mixed fiber suspension; c, adding a reinforcing agent into the mixed fiber suspension and mixing, so as to form a reinforced type fiber suspension after stirring; and d, performing screen-applying forming, drying and press polishing on the reinforced type fiber suspension obtained in the step c, so as to finally obtain the bamboo-pulp paper. The manufacture technology for reinforced type bamboo-pulp paper employs the above design and is simple in manufacture process, and by adding the reinforcing agent during manufacture, the strength of the bamboo pulp paper is effectively improved.
Description
Technical field
The present invention relates to the field of bamboo paper, especially a kind of manufacture craft of enhancement mode bamboo paper.
Background technology
Paper is one of four inventions of Ancient Times in China science and technology, and with compass, gunpowder, the art of printing together, provides the basis of material technology to the prosperity of Ancient Times in China culture.The invention of paper finishes the complicated history of letter in ancient times wooden tablets or slips for writing, facilitates the spread and development of culture widely.Now, paper has been widely used in the every field of society, mainly comprises package paper, printing, industrial paper, paper for daily use and speciality paper etc.
In the bamboo paper field of current manufacture, most of bamboo paper intensity is lower, in use easily occurs phenomenon of rupture.
Summary of the invention
The technical problem to be solved in the present invention is: in order to overcome above-mentioned middle Problems existing, provide a kind of manufacture craft of enhancement mode bamboo paper.
The technical solution adopted for the present invention to solve the technical problems is: a kind of manufacture craft of enhancement mode bamboo paper, and concrete steps are as follows:
A. bamboo pulp fiber suspension is chosen;
B. in bamboo pulp fiber suspension, add string, modified fibre carries out being mixed to form blended fiber suspension;
C. mixing adding reinforcing agent in blended fiber suspension, after stirring, forming enhancement mode blended fiber suspension;
D. the enhancement mode blended fiber suspension drawn in c is carried out upper net forming, drying, press polish, finally obtain bamboo paper.
Mass ratio between the string added in b and modified fibre is 1:9.
In c, reinforcing agent is polyacrylamide, epoxychloropropane, polyacrylamide classification polyacrylamide Products: polyacrylamide (PAM) is high molecular weight water soluble polymer, be insoluble to most of organic solvent, there is good flocculability, the frictional resistance between liquid can be reduced, divide by ion characteristic and can be divided into nonionic, anion, CATION and amphoteric Four types; Epoxychloropropane main application is for epoxy resin processed, is also a kind of stabilizing agent and chemical intermediate of oxygen carrier, the main raw material of epoxy radicals and phenoxy resin; Manufacture glycerine; Slaking propylene-based rubber; The solvent of cellulose esters and ether; The high wet strength resin of paper industry.
The invention has the beneficial effects as follows: the manufacture craft of described a kind of enhancement mode bamboo paper, adopt the bamboo paper of this kind of design, manufacturing process is simple, adds reinforcing agent in the fabrication process, thus effectively improves the intensity of bamboo paper.
Detailed description of the invention
Be described in further detail in conjunction with the present invention now.
The manufacture craft of a kind of enhancement mode bamboo paper of the present invention, concrete steps are as follows:
A. bamboo pulp fiber suspension is chosen;
B. in bamboo pulp fiber suspension, add string, modified fibre carries out being mixed to form blended fiber suspension, the mass ratio between string and modified fibre is 1:9;
C. mix adding reinforcing agent in blended fiber suspension, reinforcing agent is polyacrylamide, epoxychloropropane, forms enhancement mode blended fiber suspension after stirring;
D. the enhancement mode blended fiber suspension drawn in c is carried out upper net forming, drying, press polish, finally obtain bamboo paper.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine its technical scope according to right.
Claims (3)
1. a manufacture craft for enhancement mode bamboo paper, is characterized in that concrete steps are as follows:
A. bamboo pulp fiber suspension is chosen;
B. in bamboo pulp fiber suspension, add string, modified fibre carries out being mixed to form blended fiber suspension;
C. mixing adding reinforcing agent in blended fiber suspension, after stirring, forming enhancement mode blended fiber suspension;
D. the enhancement mode blended fiber suspension drawn in c is carried out upper net forming, drying, press polish, finally obtain bamboo paper.
2. the manufacture craft of a kind of enhancement mode bamboo paper according to claim 1, is characterized in that: the mass ratio between the string added in b and modified fibre is 1:9.
3. the manufacture craft of a kind of enhancement mode bamboo paper according to claim 1, is characterized in that: in c, reinforcing agent is polyacrylamide, epoxychloropropane.