CN104497958A - Adhesive for corrosion prevention of 3PP pipeline - Google Patents
Adhesive for corrosion prevention of 3PP pipeline Download PDFInfo
- Publication number
- CN104497958A CN104497958A CN201410745402.4A CN201410745402A CN104497958A CN 104497958 A CN104497958 A CN 104497958A CN 201410745402 A CN201410745402 A CN 201410745402A CN 104497958 A CN104497958 A CN 104497958A
- Authority
- CN
- China
- Prior art keywords
- corrosion protection
- sticks
- compatilizer
- resin
- pipeline corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an adhesive for corrosion prevention of a 3PP pipeline, which comprises the following raw materials in percentage by weight: 20-40% of nylon 1010, 10-20% of polycarbonate, 3-8% of a compatilizer A, 20-30% of a compatilizer B, 10-20% of bonding resin and 10-20% of toughening resin. The melt index of the nylon 1010 is 3.0-20.0g/10min; the melt index of polycarbonate is 3.0-20.0g/10min; the compatilizer A is styrene-maleic anhydride copolymer; the bonding resin is ethylene-acrylic acid copolymer; and the toughening resin is one of POE-g-MAH and SEBS-g-MAH or a mixture of the two. In the invention, the bonding resin in the 3PP system still can keep relatively high bonding strength at a temperature over 100 DEG C, the using effect of a 3PP coating at high temperature can be guaranteed, and the bonding resin plays an important role on the stability of the whole 3PP corrosion prevention system.
Description
Technical field
The present invention relates to industrial coating technical field, specifically, is that a kind of 3PP pipeline corrosion protection being applicable to steel pipe external layer preservation sticks with glue agent.
Background technology
The long-distance conveying utilizing metallic conduit to carry out resource has been the common approach of present stage industrial employing, e.g., and petroleum transport, natural gas transport, heat supply conveying, conveying etc. of supplying water.In the long-distance conveying of pipeline, be particularly important to the protection of metallic conduit.Because have longer metallic conduit to be embedded in the life dwell point away from people, some locations are even environmental aspect very severe.Therefore, people can carry out protection in power to metallic conduit, and wherein, anticorrosion is an important ring.At present, China mainly adopts 3PE(3 Rotating fields polyethylene coating to the anticorrosion of long-distance transport pipes) or 3PP(3 Rotating fields polypropylene coating) technology of corrosion protection coating.In general, the use temperature of 3PE corrosion protection coating is not higher than 70 DEG C, and the use temperature of 3PP corrosion protection coating higher than 70 DEG C, but can generally be no more than 90 DEG C.Too high use temperature can make the bonding force of 3 coating systems of epoxy powder/tackiness agent/jacket material occur declining, and makes corrosion protection coating (system) premature failure.Therefore, ensure the result of use of tackiness agent in high temperature in 3PP, have very important effect to the stable of whole 3PP protective system.
Chinese patent literature CN1317529 A discloses one " adhesive for coating on steel pipe "; Chinese patent literature CN1754932A discloses one " the polymer bonding resin and preparation method thereof for steel pipe corrosion-proof "; Chinese patent literature CN102533162A describes " a kind of preparation method of 3PE anti-corrosion pipeline PE hot melt adhesive powder ".But, above-mentioned patent documentation is all the hot melt adhesive prepared for resin that base-material is equipped with more low melting point with PE or PP, do not relate to the high temperature stripping performance improving product with high-melting-point polymer, do not relate to the consistency increasing product with styrene maleic anhydride copolymer (SMA) yet.
Summary of the invention
The object of the invention is to solve the problem, provide a kind of 3PP pipeline corrosion protection to stick with glue agent, it uses mainly as the binding resin in 3PP system, still can keep higher cohesive strength at the temperature more than 100 DEG C.
For achieving the above object, this invention takes following technical scheme.
A kind of 3PP pipeline corrosion protection sticks with glue agent, and it is characterized in that, the weight percent of its each feed composition is:
Nylon 1010 20 ~ 40%;
Polycarbonate 10 ~ 20%;
Compatilizer A 3
~8%;
Compatilizer B 20
~30%;
Binding resin 10
~20%;
Toughened resin 10
~20%.
Optionally, the melting index of described nylon 1010 is 3.0
~20.0g/10min(230 DEG C).
Optionally, described polycarbonate melt index is 3.0 ~ 20.0g/10min(300 DEG C).
Optionally, described compatilizer A is styrene maleic anhydride copolymer, and wherein, the content of described MALEIC ANHYDRIDE is 20%
~30%.
Optionally, described binding resin is ethylene-acrylic acid copolymer, and wherein, acrylic acid content is 7%
~15%.
Optionally, described toughened resin is POE-g-MAH(POE grafted maleic anhydride) and/or SEBS-g-MAH(styrene block copolymer grafted maleic anhydride) one or both mixing, the content > 0.5% of MAH.
The positively effect that a kind of 3PP pipeline corrosion protection of the present invention sticks with glue agent is:
As the binding resin in 3PP system, at the temperature more than 100 DEG C, still can keep higher cohesive strength, therefore can ensure the result of use of 3PP coating in high temperature, can play an important role to whole the stable of 3PP protective system.
Embodiment
Below provide the embodiment that a kind of 3PP pipeline corrosion protection of the present invention sticks with glue agent, provide 3 embodiments.But it should be pointed out that enforcement of the present invention is not limited to following embodiment.
embodiment 1
(1) 3PP pipeline corrosion protection sticks with glue an agent, and the weight percent of its each feed composition is:
Nylon 1010 20%; The melt temperature adopting company of Xingda of Du Pont to produce is 205 DEG C, the trade mark is the nylon 1010 of 12.
Polycarbonate 10%; Adopt polycarbonate company limited of Mitsubishi Chemical of China Petrochemical Industry to produce, the trade mark is the polycarbonate of 7022IR.
Compatilizer A 3%; Adopt the styrene maleic anhydride copolymer that Polyscope company produces, the trade mark is the product of SZ26080, and the content of MALEIC ANHYDRIDE is 26%.
Compatilizer B 30%; Adopt the MZ 203D product that E.I.Du Pont Company produces.
Binding resin 20%; Adopt the Primacor3002 that Dow Chemical produces, acrylic acid content is the ethylene-acrylic acid copolymer product of 8%.
Toughened resin 17%, adopt the POE-g-MAH that Mitsui company produces, the trade mark is the product of PF508.
(2) described 3PP pipeline corrosion protection sticks with glue the preparation method of agent, comprises the following steps:
(1) by the weight percent configuration raw material of each feed composition;
(2) raw material after configuration is placed in high speed dispersor to mix;
(3) mixed raw material is added twin screw extruder extruding pelletization, the design temperature of forcing machine is 220 DEG C, and rotating speed is 350 turns, and length-to-diameter ratio is 38:1; Obtain hot-melt adhesive granules.
embodiment 2
(1) 3PP pipeline corrosion protection sticks with glue an agent, and the weight percent of its each feed composition is:
Nylon 1010 30%; The melt temperature adopting company of Xingda of Du Pont to produce is 205 DEG C, and the trade mark is the nylon 1010 of 12.
Polycarbonate 20%; Adopt polycarbonate company limited of Mitsubishi Chemical of China Petrochemical Industry to produce, the trade mark is the polycarbonate of 7022IR.
Compatilizer A 5%; Adopt the styrene maleic anhydride copolymer that Polyscope company produces, the trade mark is the product of SZ25010, and the content of MALEIC ANHYDRIDE is 25%
.
Compatilizer B 20%; Adopt the MZ 203D product that E.I.Du Pont Company produces.
Binding resin 15%; Adopt the Primacor 3460 that Dow Chemical produces, acrylic acid content is the ethylene-acrylic acid copolymer product of 9.7%.
Toughened resin 10%, adopt the SEBS-g-MAH that Ke Teng company produces, the trade mark is the product of FG1901GT.
(2) described 3PP pipeline corrosion protection sticks with glue preparation method's (with embodiment 1) of agent.
embodiment 3
(1) 3PP pipeline corrosion protection sticks with glue an agent, and the weight percent of its each feed composition is:
Nylon 1010 40%, (raw material of employing is with embodiment 1).
Polycarbonate 15%, (raw material of employing is with embodiment 1).
Compatilizer A 8%, (raw material of employing is with embodiment 1).
Compatilizer B 7%, (raw material of employing is with embodiment 1).
Binding resin 10%, (raw material of employing is with embodiment 1).
Toughened resin 20%, (raw material of employing is with embodiment 1).
(2) described 3PP pipeline corrosion protection sticks with glue the preparation (with embodiment 1) of agent.
a kind of 3PP pipeline corrosion protection of the present invention is sticked with glue to the test of agent:
By GB/T-1633; GB/T-1040.2; GB/T-531 standard and DIN-30678 stick with glue agent to 3PP pipeline corrosion protection prepared by embodiment of the present invention 1-3 and test: adopt hot-melt adhesive granules prepared by embodiment of the present invention 1-3, be prepared into the tack coat of 3 layers of PP preservative coat by Extrusion Coating, its performance is in table 1.
table 1.3PP pipeline corrosion protection prepared by embodiment 1-3 sticks with glue the test result of agent (hot-melt adhesive granules)
。
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from weight percentages scope of the present invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (6)
1. 3PP pipeline corrosion protection sticks with glue an agent, it is characterized in that, the weight percent of its each feed composition is:
nylon 1010 20 ~ 40%;
Polycarbonate 10 ~ 20%;
Compatilizer A 3
~8%;
Compatilizer B 20
~30%;
Binding resin 10
~20%;
Toughened resin 10
~20%.
2. a kind of 3PP pipeline corrosion protection according to claim 1 sticks with glue agent, it is characterized in that, the melting index of described nylon 1010 is 3.0
~20.0g/10min.
3. a kind of 3PP pipeline corrosion protection according to claim 1 sticks with glue agent, and it is characterized in that, described polycarbonate melt index is 3.0
~20.0g/10min.
4. a kind of 3PP pipeline corrosion protection according to claim 1 sticks with glue agent, and it is characterized in that, described compatilizer A is styrene maleic anhydride copolymer, and wherein, the content of described MALEIC ANHYDRIDE is 20%
~30%.
5. a kind of 3PP pipeline corrosion protection according to claim 1 sticks with glue agent, and it is characterized in that, described binding resin is ethylene-acrylic acid copolymer, and wherein acrylic acid content is 7%
~15%.
6. a kind of 3PP pipeline corrosion protection according to claim 1 sticks with glue agent, it is characterized in that, described toughened resin is POE-g-MAH(POE grafted maleic anhydride) and/or SEBS-g-MAH(styrene block copolymer grafted maleic anhydride) one or both mixing, the content > 0.5% of MAH.