CN104497958B - Adhesive for corrosion prevention of 3PP pipeline - Google Patents
Adhesive for corrosion prevention of 3PP pipeline Download PDFInfo
- Publication number
- CN104497958B CN104497958B CN201410745402.4A CN201410745402A CN104497958B CN 104497958 B CN104497958 B CN 104497958B CN 201410745402 A CN201410745402 A CN 201410745402A CN 104497958 B CN104497958 B CN 104497958B
- Authority
- CN
- China
- Prior art keywords
- compatilizer
- resin
- adhesive
- mah
- corrosion protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an adhesive for corrosion prevention of a 3PP pipeline, which comprises the following raw materials in percentage by weight: 20-40% of nylon 1010, 10-20% of polycarbonate, 3-8% of a compatilizer A, 20-30% of a compatilizer B, 10-20% of bonding resin and 10-20% of toughening resin. The melt index of the nylon 1010 is 3.0-20.0g/10min; the melt index of polycarbonate is 3.0-20.0g/10min; the compatilizer A is styrene-maleic anhydride copolymer; the bonding resin is ethylene-acrylic acid copolymer; and the toughening resin is one of POE-g-MAH and SEBS-g-MAH or a mixture of the two. In the invention, the bonding resin in the 3PP system still can keep relatively high bonding strength at a temperature over 100 DEG C, the using effect of a 3PP coating at high temperature can be guaranteed, and the bonding resin plays an important role on the stability of the whole 3PP corrosion prevention system.
Description
Technical field
The present invention relates to industrial coating technical field, specifically, apply to one kind of steel pipe external layer preservation
3pp pipeline corrosion protection adhesive.
Background technology
It has been the common approach of industrial employing at this stage, e.g., stone using the long-distance conveying that metallic conduit carries out resource
Oily conveying, natural gas transportation, for heated conveying, supplying water conveys etc..In the long-distance conveying of pipeline, the protection to metallic conduit is
Particularly important.Because there being longer metallic conduit to be life settlement, some locations or even the environment being embedded in away from people
Situation very severe.Therefore, people can carry out protection in power to metallic conduit, and wherein, anti-corrosion is an important ring.Mesh
Before, China mainly adopts 3pe(3 Rotating fields polyethylene coating to the anti-corrosion of long-distance transport pipes) or the painting of 3pp(3 Rotating fields polypropylene
Layer) corrosion-inhibiting coating technology.In general, not higher than 70 DEG C of the use temperature of 3pe corrosion-inhibiting coating, and the making of 3pp corrosion-inhibiting coating
Can be higher than 70 DEG C with temperature, but be usually no more than 90 DEG C.Too high can make the 3 of epoxy powder/adhesive/jacket material using temperature
Declining occurs in the adhesion of coating systems, and makes corrosion-inhibiting coating (system) premature failure.Thus it is guaranteed that the adhesive in 3pp is in high temperature
In using effect, have highly important effect to stablizing of whole 3pp protective system.
Chinese patent literature cn1317529 a discloses a kind of " adhesive for coating on steel pipe ";Chinese patent literature
Cn1754932a discloses a kind of " polymer bonding resin for steel pipe corrosion-proof and preparation method thereof ";Chinese patent literature
Cn102533162a describes " a kind of preparation method of 3pe anti-corrosion pipeline pe PUR powder ".But, above-mentioned patent literary composition
Offer PUR prepared by the resin being all to be equipped with more low melting point with pe or pp for base material, be not directed to be changed with high-melting-point polymer
The high temperature stripping performance of kind product, is also not directed to increase the compatible of product with SMA (sma)
Property.
Content of the invention
It is an object of the invention to solving the above problems, provide a kind of 3pp pipeline corrosion protection adhesive, its mainly as
Binding resin in 3pp system, to use, can remain to keep higher adhesion strength at a temperature of more than 100 DEG C.
For achieving the above object, this invention takes technical scheme below.
A kind of 3pp pipeline corrosion protection adhesive is it is characterised in that the percentage by weight of its each raw material components is:
Nylon 1010 20~40%;
Merlon 10~20%;
Compatilizer a 3~8%;
Compatilizer b 20~30%;
Binding resin 10~20%;
Toughened resin 10~20%;
The melt index of described nylon 1010 is 3.0~20.0g/10min(230 DEG C);
Described compatilizer a is SMA, and wherein, the content of described maleic anhydride is
20%~30%.
Optionally, described polycarbonate melt index is 3.0~20.0g/10min(300 DEG C).
Optionally, described binding resin is ethylene-acrylic acid copolymer, and wherein, acrylic acid content is 7%~15%.
Optionally, described toughened resin is one or two the mixing of poe-g-mah and/or sebs-g-mah, mah's
Content > 0.5%.
A kind of good effect of present invention 3pp pipeline corrosion protection adhesive is:
As the binding resin in 3pp system, at a temperature of more than 100 DEG C, remain to keep higher adhesion strength, because
This can guarantee that using effect in high temperature for the 3pp coating, and whole stablizing of 3pp protective system can be played an important role.
Specific embodiment
A kind of specific embodiment of 3pp pipeline corrosion protection adhesive of the present invention given below, provides 3 embodiments.But
It is it should be pointed out that the enforcement of the present invention is not limited to following embodiment.
Embodiment 1
(1) a kind of 3pp pipeline corrosion protection adhesive, the percentage by weight of its each raw material components is:
Nylon 1010 20%;The nylon that the melt temperature being produced using company of Xingda of Du Pont is 205 DEG C, the trade mark is 12
1010.
Merlon 10%;Produced using Merlon company limited of sinopec Mitsubishi Chemical, the trade mark is 7022ir's
Merlon.
Compatilizer a 3%;Using the SMA of polyscope company production, the trade mark is
The product of sz26080, the content of maleic anhydride is 26%.
Compatilizer b 30%;The mz 203d product being produced using E.I.Du Pont Company.
Binding resin 20%;Using Dow Chemical produce primacor3002, acrylic acid content be 8% ethylene-
Acrylic copolymer product.
Toughened resin 17%, the poe-g-mah being produced using Mitsui company, the trade mark is the product of pf508.
(2) preparation method of described 3pp pipeline corrosion protection adhesive, comprises the following steps:
(1) percentage by weight pressing each raw material components configures raw material;
(2) raw material after configuration is placed in mixing in high speed dispersor;
(3) mixed raw material is added double screw extruder extruding pelletization, the design temperature of extruder is 220 DEG C, turns
Speed is 350 turns, and draw ratio is 38:1;Obtain hot-melt adhesive granules.
Embodiment 2
(1) a kind of 3pp pipeline corrosion protection adhesive, the percentage by weight of its each raw material components is:
Nylon 1010 30%;It is 205 DEG C using the melt temperature that company of Xingda of Du Pont produces, the trade mark is 12 nylon
1010.
Merlon 20%;Produced using Merlon company limited of sinopec Mitsubishi Chemical, the trade mark is 7022ir's
Merlon.
Compatilizer a 5%;Using the SMA of polyscope company production, the trade mark is
The product of sz25010, the content of maleic anhydride is 25%.
Compatilizer b 20%;The mz 203d product being produced using E.I.Du Pont Company.
Binding resin 15%;The primacor 3460 being produced using Dow Chemical, acrylic acid content is 9.7% second
Alkene-acrylic copolymer product.
Toughened resin 10%, the sebs-g-mah being produced using Ke Teng company, the trade mark is the product of fg1901gt.
(2) preparation method (with embodiment 1) of described 3pp pipeline corrosion protection adhesive.
Embodiment 3
(1) a kind of 3pp pipeline corrosion protection adhesive, the percentage by weight of its each raw material components is:
Nylon 1010 40%, (raw material of employing is with embodiment 1).
Merlon 15%, (raw material of employing is with embodiment 1).
Compatilizer a 8%, (raw material of employing is with embodiment 1).
Compatilizer b 7%, (raw material of employing is with embodiment 1).
Binding resin 10%, (raw material of employing is with embodiment 1).
Toughened resin 20%, (raw material of employing is with embodiment 1).
(2) preparation (with embodiment 1) of described 3pp pipeline corrosion protection adhesive.
The test of 3pp pipeline corrosion protection adhesive a kind of to the present invention:
By gb/t-1633;gb/t-1040.2;Gb/t -531 standard and din-30678 are to embodiment of the present invention 1-3 system
Standby 3pp pipeline corrosion protection is tested with adhesive: using the hot-melt adhesive granules of embodiment of the present invention 1-3 preparation, by extrusion
Coating is prepared into the tack coat of 3 layers of pp anticorrosive coat, and its performance is shown in Table 1.
The 3pp pipeline corrosion protection of the table 1. embodiment 1-3 preparation test result of adhesive (hot-melt adhesive granules)
.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
Member, on the premise of without departing from weight percentages scope of the present invention, can also make some improvements and modifications, these improvement
Also should be regarded as protection scope of the present invention with retouching.
Claims (4)
1. a kind of 3pp pipeline corrosion protection adhesive is it is characterised in that the percentage by weight of its each raw material components is:
Nylon 1010 20~40%;
Merlon 10~20%;
Compatilizer a 3~8%;
Compatilizer b 20~30%;
Binding resin 10~20%;
Toughened resin 10~20%.
The melt index of described nylon 1010 is 3.0~20.0g/10min;
Described compatilizer a is SMA, wherein, the content of described maleic anhydride is 20%~
30%.
2. a kind of 3pp pipeline corrosion protection adhesive according to claim 1 is it is characterised in that described polycarbonate melt
Index is 3.0~20.0g/10min.
3. a kind of 3pp pipeline corrosion protection adhesive according to claim 1 is it is characterised in that described binding resin is second
Alkene-acrylic copolymer, wherein acrylic acid content are 7%~15%.
4. a kind of 3pp pipeline corrosion protection adhesive according to claim 1 is it is characterised in that described toughened resin is
One or two the mixing of poe-g-mah and/or sebs-g-mah, content > 0.5% of mah.