CN104497339A - Pretreatment method of prism film base material layer - Google Patents
Pretreatment method of prism film base material layer Download PDFInfo
- Publication number
- CN104497339A CN104497339A CN201410811460.2A CN201410811460A CN104497339A CN 104497339 A CN104497339 A CN 104497339A CN 201410811460 A CN201410811460 A CN 201410811460A CN 104497339 A CN104497339 A CN 104497339A
- Authority
- CN
- China
- Prior art keywords
- ion beam
- oxygen ion
- pet
- prism film
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a pretreatment method of a prism film base material layer. The prism film base material layer is a PET layer, and treated by spraying oxygen ion beam onto the PET layer, the distance between the oxygen ion beam and the PET layer is controlled to be 50-150mm, and the flow of the oxygen ion beam is controlled at 5-30cm<3>/min, and the treatment time lasts for 5-20min. The oxygen ion beam is a plasma easily obtained at a low temperature, when the oxygen ion beam and the PET surface have mutual interaction, the chemical bonds on the PET surface are firstly destroyed, the oxygen content of the base material surface can be increased through the bonding of the oxygen ions and the chemical bonds on the PET surface, and the adhesion force of the surface of a thin film can be enhanced under the condition of unchanging the physical property.
Description
Technical field
The present invention relates to a kind of pretreatment process of prism film substrate layer.
Background technology
PET base material uses base material comparatively widely in prism film manufacturing processed, has high transmission rate, low weight, the features such as low price.In the manufacturing processed of prism, due to PET base material surface presentation inertia, the sticking power on the composition film surface of general prism coating is unsatisfactory, therefore needs people for the process of PET base material modifying surface, to improve the sticking power of prism coating composition on its surface.In the prior art not for the pretreatment process of prism film substrate layer.
Summary of the invention
In view of also there is no a kind of pretreatment process for prism film substrate layer at present, the invention provides a kind of pretreatment process for prism film substrate layer, to improve the sticking power of prism coating composition on its surface.
The technical scheme that the present invention solves its technical problem is: a kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, adopt oxygen ion beam to be sprayed onto the enterprising row relax of described pet layer, the distance controlled between oxygen ion beam and pet layer be 50 ~ 150mm, oxygen ion beam flow control at 5 ~ 30cm
3/ min, process time length 5 ~ 20min.
Beneficial effect of the present invention is: oxygen ion beam is a kind of plasma body being easier at low temperatures obtain, when oxygen ion beam and pet sheet face interact, first destroy the chemical bond in pet sheet face, at the chemical bonds in oxonium ion and pet sheet face, the oxygen level of substrate surface is increased, when not changing physical properties, add the sticking power of film surface.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment one
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 100mm, oxygen ion beam flow control at 20cm
3/ min, process time length 10min.
Embodiment two
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 50mm, oxygen ion beam flow control at 5cm
3/ min, process time length 7min.
Embodiment three
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 120mm, oxygen ion beam flow control at 10cm
3/ min, process time length 17min.
Embodiment four
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 150mm, oxygen ion beam flow control at 15cm
3/ min, process time length 5min.
Embodiment five
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 60mm, oxygen ion beam flow control at 30cm
3/ min, process time length 20min.
Embodiment six
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 70mm, oxygen ion beam flow control at 18cm
3/ min, process time length 15min.
Embodiment seven
A kind of pretreatment process of prism film substrate layer, this prism film substrate layer is pet layer, oxygen ion beam is adopted to be sprayed onto the enterprising row relax of described pet layer, oxygen ion beam is obtained by oxygen ion beam producer, the distance controlled between oxygen ion beam and pet layer be 140mm, oxygen ion beam flow control at 25cm
3/ min, process time length 12min.
Claims (2)
1. a pretreatment process for prism film substrate layer, this prism film substrate layer is pet layer, it is characterized in that: adopt oxygen ion beam to be sprayed onto the enterprising row relax of described pet layer.
2. the distance controlled between oxygen ion beam and pet layer be 50 ~ 150mm, oxygen ion beam flow control at 5 ~ 30cm
3/ min, process time length 5 ~ 20min.