CN104480284A - 一种链轮的热处理方法 - Google Patents

一种链轮的热处理方法 Download PDF

Info

Publication number
CN104480284A
CN104480284A CN201410648910.0A CN201410648910A CN104480284A CN 104480284 A CN104480284 A CN 104480284A CN 201410648910 A CN201410648910 A CN 201410648910A CN 104480284 A CN104480284 A CN 104480284A
Authority
CN
China
Prior art keywords
sprocket wheel
foundry goods
cooling
insulation
heat treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410648910.0A
Other languages
English (en)
Inventor
李大志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU JINLONG MOLD FORGING CO Ltd
Original Assignee
WUHU JINLONG MOLD FORGING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU JINLONG MOLD FORGING CO Ltd filed Critical WUHU JINLONG MOLD FORGING CO Ltd
Priority to CN201410648910.0A priority Critical patent/CN104480284A/zh
Publication of CN104480284A publication Critical patent/CN104480284A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种链轮的热处理方法，属于机械制造技术领域。其加工步骤为：（1）人工时效处理；（2）消除铸件白口退火；（3）正火。本发明解决了现有链轮在铸造过程中，因冷却速度过快出现白口组织，使得铸件的硬度和脆性增加，进而造成切屑加工困难的问题，具有方法简单，成本低，加工容易的优点。

Description

一种链轮的热处理方法
技术领域
本发明属于机械制造技术领域，更具体地说，涉及一种链轮加工前的热处理方法。
背景技术
灰铸铁是一种断口呈暗灰色的铸铁，因其碳全部或者大部分以片状石墨的形式存在，而造成断口成暗灰色，灰铸铁具有以下特点：（1）可获得比铸钢更薄而复杂的铸件，铸件中残余内应力及翘曲变形较铸钢小；（2）表面光洁，加工余量比铸钢小，表面的加工质量对疲劳极限影响小；（3）消振性高；（4）不同截面上性能较均匀。因此灰铸铁的应用广泛，但灰铸铁对冷却速度敏感性大，因此薄截面容易形成白口和裂纹，而厚截面又易形成琉松，故灰铸铁件当壁厚超过其临界值时，随着壁厚的增加其力学性能反而显著降低。
链轮是一种带嵌齿式扣链齿的轮子，用以与节链环或缆索上节距准确的块体相啮合一种实心或带辐条的齿轮，通过与链啮合以传递运动。一般链轮是利用HT200灰铸铁制造，但由于灰铸铁常容易出现白口，增加了对于链轮的加工难度。
发明内容
针对现有链轮在铸造过程中，因冷却速度过快出现白口组织，使得铸件的硬度和脆性增加，进而造成切屑加工困难的问题，本发明提供一种链轮的热处理方法，通过对铸件进行相关热处理，消除铸件的白口组织，从而达到降低其切屑加工难度的目的。
为解决上述问题，本发明采用如下的技术方案。
一种链轮的热处理方法，包括以下步骤：
（1）人工时效处理：
将链轮铸件缓慢加热到500-600℃，保温一段时间，随炉冷却至200℃后出炉空冷；
（2）消除铸件白口退火：
将链轮铸件加热到850-950℃，保温2-4h，随炉冷却至400-500℃后出炉空冷；
（3）正火：
将链轮铸件加热到860-920℃，保温后风冷。
优选的，所述的步骤（1）中，将链轮铸件缓慢加热到550℃。
优选的，所述的步骤（2）中，将链轮铸件加热到900℃，保温3h，随炉冷却至450℃后出炉空冷。
相比于现有技术，本发明的有益效果为：
（1）本发明通过对链轮铸件进行相关热处理，消除了铸件的白口组织，从而降低其切屑加工的难度。
（2）本发明方法简单，成本低，加工容易。
具体实施方式
下面结合实施例对本发明进行详细描述。
实施例1
一种链轮的热处理方法，包括以下步骤：
（1）人工时效处理：
将链轮铸件缓慢加热到500℃，保温一段时间，随炉冷却至200℃后出炉空冷；
（2）消除铸件白口退火：
将链轮铸件加热到850℃，保温2h，随炉冷却至400℃后出炉空冷；
（3）正火：
将链轮铸件加热到860℃，保温后风冷。
实施例2
一种链轮的热处理方法，包括以下步骤：
（1）人工时效处理：
将链轮铸件缓慢加热到600℃，保温一段时间，随炉冷却至200℃后出炉空冷；
（2）消除铸件白口退火：
将链轮铸件加热到950℃，保温4h，随炉冷却至500℃后出炉空冷；
（3）正火：
将链轮铸件加热到920℃，保温后风冷。

Claims (3)

1.一种链轮的热处理方法，其特征在于以下步骤：
（1）人工时效处理：
将链轮铸件缓慢加热到500-600℃，保温一段时间，随炉冷却至200℃后出炉空冷；
（2）消除铸件白口退火：
将链轮铸件加热到850-950℃，保温2-4h，随炉冷却至400-500℃后出炉空冷；
（3）正火：
将链轮铸件加热到860-920℃，保温后风冷。
2.根据权利要求1所述的一种链轮的热处理方法，其特征在于，所述的步骤（1）中，将链轮铸件缓慢加热到550℃。
3.根据权利要求1所述的一种链轮的热处理方法，其特征在于，所述的步骤（2）中，将链轮铸件加热到900℃，保温3h，随炉冷却至450℃后出炉空冷。
CN201410648910.0A 2014-11-17 2014-11-17 一种链轮的热处理方法 Pending CN104480284A (zh)