CN104478336A - 一种强固型硅藻泥 - Google Patents
一种强固型硅藻泥 Download PDFInfo
- Publication number
- CN104478336A CN104478336A CN201410778922.5A CN201410778922A CN104478336A CN 104478336 A CN104478336 A CN 104478336A CN 201410778922 A CN201410778922 A CN 201410778922A CN 104478336 A CN104478336 A CN 104478336A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- strong
- dispersion machine
- bubble
- attapulgite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种强固型硅藻泥,由下述成分按重量比构成:精细硅土35-55KG,凹凸棒土0.5-1.5KG,海泡土2.5-3.5KG,负氧离子0.2-2KG,纤维素1.2-2KG,木制纤维0.5-0.7KG,滑泡0.2-0.6KG,重质碳酸钙40-60KG,雪花粉15-25KG,灰钙粉4-6KG,纳米二氧化钛1.5-2.5 KG,将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到,本发明相较与普通建筑装饰材料,不含有任何有毒物质,附着力强,能与墙体基层强有利粘合,确保不空鼓、不脱落、不粉化,而且更耐水、防潮透气。
Description
技术领域
本发明属于一种墙面涂料,特别涉及一种强固型硅藻泥。
背景技术
硅藻泥作为室内涂料,由于其施工、涂抹和制作图案均优于现有的装饰涂料,由于其超强的吸附能力,还能吸收空气中的有害气体,因此受到人们的青睐,应用越来越广。
发明内容
本发明的目的在于提供一种强固型硅藻泥,加强硅藻泥上墙后的附着力和表面强度,绿色环保。
为了实现上述目的,本发明解决方案如下:
一种强固型硅藻泥,由下述成分按重量比构成:精细硅土35-55KG,凹凸棒土0.5-1.5KG,海泡土2.5-3.5KG,负氧离子0.2-2KG, 纤维素1.2-2KG,木制纤维0.5-0.7KG,滑泡0.2-0.6KG,重质碳酸钙40-60KG,雪花粉15-25KG,灰钙粉4-6KG,纳米二氧化钛1.5-2.5 KG。
本发明的最佳原料重量比为:精细硅土40KG,凹凸棒土1KG,海泡土3KG,负氧离子1KG, 纤维素1.6KG,木制纤维0.6KG,滑泡0.4KG,重质碳酸钙50KG,雪花粉20KG,灰钙粉5KG,纳米二氧化钛2 KG。
为了进一步保证混合得到优质成品,所述滑泡为粉状。
强固型硅藻泥的制备方法为:将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到。
本发明的有益效果在于:本发明相较与普通建筑装饰材料,不含有任何有毒物质,附着力强,加强硅藻泥上墙后的附着力和表面强度,能抵抗一定强度的外力作用,施工后“干后不掉粉,湿后不掉泥”,施工工艺上增加了更多可塑性,增强了工艺表现力。
具体实施方式
为了能够更清楚地理解本发明的技术内容,特举以下实施例详细说明。
实施例一:
一种强固型硅藻泥,由下述成分按重量比构成:精细硅土35KG,凹凸棒土0.5KG,海泡土2.5KG,负氧离子0.2KG, 纤维素1.2KG,木制纤维0.5KG,粉状滑泡0.2KG,重质碳酸钙40KG,雪花粉15KG,灰钙粉4KG,纳米二氧化钛1.5 KG,将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到。
实施例二:
一种强固型硅藻泥,由下述成分按重量比构成:精细硅土40KG,凹凸棒土1KG,海泡土3KG,负氧离子1KG, 纤维素1.6KG,木制纤维0.6KG,滑泡0.4KG,重质碳酸钙50KG,雪花粉20KG,灰钙粉5KG,纳米二氧化钛2 KG,将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到。
实施例三:
一种强固型硅藻泥,由下述成分按重量比构成:精细硅土55KG,凹凸棒土1.5KG,海泡土3.5KG,负氧离子2KG, 纤维素2KG,木制纤维0.7KG,滑泡0.6KG,重质碳酸钙60KG,雪花粉25KG,灰钙粉6KG,纳米二氧化钛2.5 KG,将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到。
Claims (4)
1.一种强固型硅藻泥,其特征在于,由下述成分按重量比构成:精细硅土35-55KG,凹凸棒土0.5-1.5KG,海泡土2.5-3.5KG,负氧离子0.2-2KG, 纤维素1.2-2KG,木制纤维0.5-0.7KG,滑泡0.2-0.6KG,重质碳酸钙40-60KG,雪花粉15-25KG,灰钙粉4-6KG,纳米二氧化钛1.5-2.5 KG。
2.根据权利要求1所述强固型硅藻泥,其特征在于,由下列重量比的原料构成:精细硅土40KG,凹凸棒土1KG,海泡土3KG,负氧离子1KG, 纤维素1.6KG,木制纤维0.6KG,滑泡0.4KG,重质碳酸钙50KG,雪花粉20KG,灰钙粉5KG,纳米二氧化钛2 KG。
3. 根据权利要求1或2所述强固型硅藻泥,其特征在于,所述滑泡为粉状。
4. 如权利要求1或2所述强固型硅藻泥的制备方法,其特征在于,将上述按重量比组分的原料混合并加入分散机,在分散机内分散15分钟,过滤得到。