CN104455125A - Improved high-temperature-resistant brake pad for automobile - Google Patents
Improved high-temperature-resistant brake pad for automobile Download PDFInfo
- Publication number
- CN104455125A CN104455125A CN201410496879.3A CN201410496879A CN104455125A CN 104455125 A CN104455125 A CN 104455125A CN 201410496879 A CN201410496879 A CN 201410496879A CN 104455125 A CN104455125 A CN 104455125A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- automobile
- brake pad
- improved high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an improved high-temperature-resistant brake pad for an automobile. The improved high-temperature-resistant brake pad for the automobile comprises, by weight, 8-15 parts of ABS, 6-10 parts of glass fibers, 2-5 parts of modifying agents, 3-6 parts of glycerol trioleate, 4-7 parts of ferric oxide, 2-9 parts of phenolic resin, 7-11 parts of ceramic fibers, 1-3 parts of red copper powder, 6-11 parts of mineral fibers, 6-14 parts of isometric system Eta-Al2O3 powder, 5-9 parts of vermiculite powder, 3-8 parts of crystalline flake graphite and 5-7 parts of petroleum coke. The improved high-temperature-resistant brake pad for the automobile has the advantages that the high-temperature resistance and strength are high, and human bodies will not be hurt in the using process.
Description
Technical field
The present invention relates to a kind of high temperature resistant vehicle brake block of improvement.
Background technique
Developing rapidly of automotive industry, more and more higher to the requirement of automobile brake perfrmance, not only want liner to have enough friction system religions, thermostability, but also require low wear rate and high impact, to ensure long service life, the characteristics such as environmentally safe.At present, automobile brake friction plate uses antimonous sulfide in a large number, for the lubrication of friction material when high temperature friction, guarantees the stable of high temperature friction coefficient.Automobile brake friction plate also exists containing heavy metal antimony, to environment, damages human body, by the disabled problem such as to use in automobile brake friction plate.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provides a kind of automobile brake sheet, and have very strong heat-resisting ability, intensity is higher, can not cause human injury in using simultaneously.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of high temperature resistant vehicle brake block of improvement, is made up of the composition of following weight portion:
ABS8-15 part, glass fibre 6-10 part, modifier 2-5 part, glycerine glycerinate 3-6 part, iron oxide 4-7 part, phenolic resin 2-9 part, ceramic fiber 7-11 part, red copper powder 1-3 part, mineral fibre 6-11 part, regular system η-Al2O3 powder 6-14 part, vermiculite power 5-9 part, crystalline flake graphite 3-8 part, petroleum coke 5-7 part.
The invention has the beneficial effects as follows, automobile brake sheet of the present invention, have very strong heat-resisting ability, intensity is higher, can not cause human injury in using simultaneously.
Embodiment
embodiment 1
A high temperature resistant vehicle brake block for improvement, is made up of the composition of following weight portion:
ABS8 part, 6 parts, glass fibre, modifier 2 parts, glycerine glycerinate 3 parts, iron oxide 4 parts, 2 parts, phenolic resin, ceramic fiber 7 parts, 1 part, red copper powder, mineral fibre 6 parts, 6 parts, regular system η-Al2O3 powder, vermiculite power 5 parts, crystalline flake graphite 3 parts, petroleum coke 5 parts.
embodiment 2
A high temperature resistant vehicle brake block for improvement, is made up of the composition of following weight portion:
ABS15 part, 10 parts, glass fibre, modifier 5 parts, glycerine glycerinate 6 parts, iron oxide 7 parts, 9 parts, phenolic resin, ceramic fiber 11 parts, 3 parts, red copper powder, mineral fibre 11 parts, 14 parts, regular system η-Al2O3 powder, vermiculite power 9 parts, crystalline flake graphite 8 parts, petroleum coke 7 parts.
Claims (1)
1. the high temperature resistant vehicle brake block improved, is characterized in that, be made up of the composition of following weight portion:
ABS8-15 part, glass fibre 6-10 part, modifier 2-5 part, glycerine glycerinate 3-6 part, iron oxide 4-7 part, phenolic resin 2-9 part, ceramic fiber 7-11 part, red copper powder 1-3 part, mineral fibre 6-11 part, regular system η-Al2O3 powder 6-14 part, vermiculite power 5-9 part, crystalline flake graphite 3-8 part, petroleum coke 5-7 part.