CN104315053A - Stable automotive brake pad material - Google Patents
Stable automotive brake pad material Download PDFInfo
- Publication number
- CN104315053A CN104315053A CN201410481506.9A CN201410481506A CN104315053A CN 104315053 A CN104315053 A CN 104315053A CN 201410481506 A CN201410481506 A CN 201410481506A CN 104315053 A CN104315053 A CN 104315053A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- brake pad
- pad material
- automotive brake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stable automotive brake pad material. The stable automotive brake pad material is composed of the following components in parts by weight: 6-11 parts of ABS (Acrylonitrile Butadiene Styrene) resin powder, 4-8 parts of lubricant, 3-11 parts of methyl phenyl siloxane branched chain type prepolymer, 2-6 parts of maleic anhydride, 4-10 parts of butadiene-acrylonitrile rubber powder, 3-6 parts of barite, 2-7 parts of steel cotton fiber, 5-9 parts of friction powder, 2-5 parts of graphite powder, 4-6 parts of barite powder, 1-3 parts of barium sulfate, 3-7 parts of aluminum oxide and 2-4 parts of iron powder. The stable automotive brake pad material has the benefits that the high-temperature resistance effect is good, the friction resistance is good, and a human body and an environment cannot be damaged.
Description
Technical field
The present invention relates to a kind of stable braking automobile sheet material.
Background technique
Developing rapidly of automotive industry, more and more higher to the requirement of automobile brake perfrmance, not only want liner to have enough friction system religions, thermostability, but also require low wear rate and high impact, to ensure long service life, the characteristics such as environmentally safe.At present, automobile brake friction plate uses antimonous sulfide in a large number, for the lubrication of friction material when high temperature friction, guarantees the stable of high temperature friction coefficient.Automobile brake friction plate also exists containing heavy metal antimony, to environment, damages human body, by the disabled problem such as to use in automobile brake friction plate.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provide a kind of braking automobile sheet material, high-temperature resistant result is good, has good rub resistance ability, and can not to human body and environmental pollution.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of stable braking automobile sheet material, is made up of the composition of following weight portion:
ABS resin powder 6-11 part, oiling agent 4-8 part, methyl phenyl siloxane branched chain type prepolymer 3-11 part, maleic anhydride 2-6 part, Nitrile Rubber phenol 4-10 part, barite 3-6 part, steel wool fiber 2-7 part, Frication powder 5-9 part, plumbago 2-5 part, blanc fixe 4-6 part, barium sulphate 1-3 part, aluminium oxide 3-7 part, iron powder 2-4 part.
The invention has the beneficial effects as follows, braking automobile sheet material of the present invention, high-temperature resistant result is good, has good rub resistance ability, and can not to human body and environmental pollution.
Embodiment
embodiment 1
A stable braking automobile sheet material, is made up of the composition of following weight portion:
6 parts, ABS resin powder, oiling agent 4 parts, methyl phenyl siloxane branched chain type prepolymer 3 parts, maleic anhydride 2 parts, 4 parts, Nitrile Rubber phenol, 3 parts, barite, steel wool fiber 2 parts, Frication powder 5 parts, plumbago 2 parts, blanc fixe 4 parts, 1 part, barium sulphate, 3 parts, aluminium oxide, iron powder 2 parts.
embodiment 2
A stable braking automobile sheet material, is made up of the composition of following weight portion:
11 parts, ABS resin powder, oiling agent 8 parts, methyl phenyl siloxane branched chain type prepolymer 11 parts, maleic anhydride 6 parts, 10 parts, Nitrile Rubber phenol, 6 parts, barite, steel wool fiber 7 parts, Frication powder 9 parts, plumbago 5 parts, blanc fixe 6 parts, 3 parts, barium sulphate, 7 parts, aluminium oxide, iron powder 4 parts.
Claims (1)
1. a stable braking automobile sheet material, is characterized in that, is made up of the composition of following weight portion:
ABS resin powder 6-11 part, oiling agent 4-8 part, methyl phenyl siloxane branched chain type prepolymer 3-11 part, maleic anhydride 2-6 part, Nitrile Rubber phenol 4-10 part, barite 3-6 part, steel wool fiber 2-7 part, Frication powder 5-9 part, plumbago 2-5 part, blanc fixe 4-6 part, barium sulphate 1-3 part, aluminium oxide 3-7 part, iron powder 2-4 part.