CN104450038A - Iron processing oil - Google Patents
Iron processing oil Download PDFInfo
- Publication number
- CN104450038A CN104450038A CN201410615111.3A CN201410615111A CN104450038A CN 104450038 A CN104450038 A CN 104450038A CN 201410615111 A CN201410615111 A CN 201410615111A CN 104450038 A CN104450038 A CN 104450038A
- Authority
- CN
- China
- Prior art keywords
- oil
- parts
- ironworking
- zinc nitrate
- potassium sorbate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides iron processing oil, which is prepared from the following components in parts by mass: 55-60 parts of machine oil, 5-8 parts of palm oil, 2-3 parts of diethanolamide laurate, 1-2 parts of potassium sorbate, 0.2-0.3 part of zinc nitrate, 0.3-0.5 part of ethylenediaminetetraacetic acid, 0.1-0.2 part of potassium chloride, 0.1-0.2 part of ethyl acrylate, 0.3-0.5 part of sodium dodecyl sulfonate and 0.1-0.2 part of potassium citrate. The iron processing oil disclosed by the invention is suitable for the processing processes such as machining, grinding and stamping of iron, is good in lubricating property, cheap in raw materials, and simple in preparation method, and does not damage the surface of iron.
Description
Technical field
The present invention relates to a kind of ironworking oil.
Background technology
In the courses of processing such as machining, ground finish, punch process, usually need micro-oil feed, by these finishes, the life-span adding the instrument that man-hour uses and the precision improving machined object treated side can be extended.The treated oil formula that different metals is suitable for can be different.
Summary of the invention
The invention provides a kind of ironworking oil.
The invention provides a kind of ironworking oil, described ironworking oil is made up of each component of following mass fraction: machine oil 55-60 part, plam oil 5-8 part, lauric acid diethyl amide 2-3 part, potassium sorbate 1-2 part, zinc nitrate 0.2-0.3 part, ethylenediamine tetraacetic acid (EDTA) 0.3-0.5 part, Repone K 0.1-0.2 part, ethyl propenoate 0.1-0.2 part, sodium laurylsulfonate 0.3-0.5 part, Tripotassium Citrate 0.1-0.2 part.
Preferably, described ironworking oil is made up of each component of following mass fraction: 58 parts, machine oil, plam oil 6 parts, lauric acid diethyl amide 2.5 parts, potassium sorbate 1.5 parts, zinc nitrate 0.25 part, ethylenediamine tetraacetic acid (EDTA) 0.4 part, 0.15 part, Repone K, ethyl propenoate 0.15 part, sodium laurylsulfonate 0.4 part, Tripotassium Citrate 0.15 part.
The present invention also provides the preparation method of ironworking oil, by machine oil 55-60 part, plam oil 5-8 part, lauric acid diethyl amide 2-3 part, potassium sorbate 1-2 part, zinc nitrate 0.2-0.3 part, ethylenediamine tetraacetic acid (EDTA) 0.3-0.5 part, Repone K 0.1-0.2 part, the mixing of ethyl propenoate 0.1-0.2 part, be heated to 55-60 DEG C, stir 25-30min, add sodium laurylsulfonate 0.3-0.5 part, Tripotassium Citrate 0.1-0.2 part, stir 15-20min, be cooled to room temperature and get final product.
Ironworking oil of the present invention is applicable to the course of processing such as machining, ground finish, punch process of iron, and lubricity is good, can not damage iron surface, and raw material is cheap, and preparation method is simple.
Embodiment
Following embodiment is convenient to understand the present invention better, but does not limit the present invention.Experimental technique in following embodiment, if no special instructions, is ordinary method.
embodiment 1
The formula of ironworking oil of the present invention is as follows:
Machine oil 58kg, plam oil 6kg, lauric acid diethyl amide 2.5kg, potassium sorbate 1.5kg, zinc nitrate 0.25kg, ethylenediamine tetraacetic acid (EDTA) 0.4kg, Repone K 0.15kg, ethyl propenoate 0.15kg, sodium laurylsulfonate 0.4kg, Tripotassium Citrate 0.15kg.
The preparation method of ironworking oil of the present invention is:
Machine oil 58kg, plam oil 6kg, lauric acid diethyl amide 2.5kg, potassium sorbate 1.5kg, zinc nitrate 0.25kg, ethylenediamine tetraacetic acid (EDTA) 0.4kg, Repone K 0.15kg, ethyl propenoate 0.15kg are mixed, be heated to 58 DEG C, stir 28min, add sodium laurylsulfonate 0.4kg, Tripotassium Citrate 0.15kg, stir 18min, be cooled to room temperature and get final product.
embodiment 2
The formula of ironworking oil of the present invention is as follows:
Machine oil 55kg, plam oil 5kg, lauric acid diethyl amide 2kg, potassium sorbate 2kg, zinc nitrate 0.2kg, ethylenediamine tetraacetic acid (EDTA) 0.5kg, Repone K 0.1kg, ethyl propenoate 0.2kg, sodium laurylsulfonate 0.5kg, Tripotassium Citrate 0.1kg.
The preparation method of ironworking oil of the present invention is:
Machine oil 55kg, plam oil 5kg, lauric acid diethyl amide 2kg, potassium sorbate 2kg, zinc nitrate 0.2kg, ethylenediamine tetraacetic acid (EDTA) 0.5kg, Repone K 0.1kg, ethyl propenoate 0.2kg are mixed, be heated to 60 DEG C, stir 25min, add sodium laurylsulfonate 0.5kg, Tripotassium Citrate 0.1kg, stir 15min, be cooled to room temperature and get final product.
embodiment 3
The formula of ironworking oil of the present invention is as follows:
Machine oil 60kg, plam oil 8kg, lauric acid diethyl amide 3kg, potassium sorbate 1kg, zinc nitrate 0.3kg, ethylenediamine tetraacetic acid (EDTA) 0.3kg, Repone K 0.2kg, ethyl propenoate 0.1kg, sodium laurylsulfonate 0.3kg, Tripotassium Citrate 0.2kg.
The preparation method of ironworking oil of the present invention is:
Machine oil 60kg, plam oil 8kg, lauric acid diethyl amide 3kg, potassium sorbate 1kg, zinc nitrate 0.3kg, ethylenediamine tetraacetic acid (EDTA) 0.3kg, Repone K 0.2kg, ethyl propenoate 0.1kg are mixed, be heated to 55 DEG C, stir 30min, add sodium laurylsulfonate 0.3kg, Tripotassium Citrate 0.2kg, stir 20min, be cooled to room temperature and get final product.
embodiment 4
The formula of ironworking oil of the present invention is as follows:
Machine oil 57kg, plam oil 7kg, lauric acid diethyl amide 3kg, potassium sorbate 1kg, zinc nitrate 0.3kg, ethylenediamine tetraacetic acid (EDTA) 0.3kg, Repone K 0.12kg, ethyl propenoate 0.16kg, sodium laurylsulfonate 0.3kg, Tripotassium Citrate 0.12kg.
The preparation method of ironworking oil of the present invention is:
Machine oil 57kg, plam oil 7kg, lauric acid diethyl amide 3kg, potassium sorbate 1kg, zinc nitrate 0.3kg, ethylenediamine tetraacetic acid (EDTA) 0.3kg, Repone K 0.12kg, ethyl propenoate 0.16kg are mixed, be heated to 57 DEG C, stir 26min, add sodium laurylsulfonate 0.3kg, Tripotassium Citrate 0.12kg, stir 16min, be cooled to room temperature and get final product.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. an ironworking oil, is characterized in that: described ironworking oil is made up of each component of following mass fraction: machine oil 55-60 part, plam oil 5-8 part, lauric acid diethyl amide 2-3 part, potassium sorbate 1-2 part, zinc nitrate 0.2-0.3 part, ethylenediamine tetraacetic acid (EDTA) 0.3-0.5 part, Repone K 0.1-0.2 part, ethyl propenoate 0.1-0.2 part, sodium laurylsulfonate 0.3-0.5 part, Tripotassium Citrate 0.1-0.2 part.
2. ironworking oil according to claim 1, is characterized in that: described ironworking oil is made up of each component of following mass fraction: 58 parts, machine oil, plam oil 6 parts, lauric acid diethyl amide 2.5 parts, potassium sorbate 1.5 parts, zinc nitrate 0.25 part, ethylenediamine tetraacetic acid (EDTA) 0.4 part, 0.15 part, Repone K, ethyl propenoate 0.15 part, sodium laurylsulfonate 0.4 part, Tripotassium Citrate 0.15 part.
3. the preparation method of the ironworking oil described in claim 1 or 2, it is characterized in that: by machine oil 55-60 part, plam oil 5-8 part, lauric acid diethyl amide 2-3 part, potassium sorbate 1-2 part, zinc nitrate 0.2-0.3 part, ethylenediamine tetraacetic acid (EDTA) 0.3-0.5 part, Repone K 0.1-0.2 part, the mixing of ethyl propenoate 0.1-0.2 part, be heated to 55-60 DEG C, stir 25-30min, add sodium laurylsulfonate 0.3-0.5 part, Tripotassium Citrate 0.1-0.2 part, stir 15-20min, be cooled to room temperature and get final product.