CN104448964A - 一种水性防火涂料的制备方法 - Google Patents
一种水性防火涂料的制备方法 Download PDFInfo
- Publication number
- CN104448964A CN104448964A CN201410850574.8A CN201410850574A CN104448964A CN 104448964 A CN104448964 A CN 104448964A CN 201410850574 A CN201410850574 A CN 201410850574A CN 104448964 A CN104448964 A CN 104448964A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- water
- coating
- fire retardant
- pentanone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性防火涂料的制备方法,该方法包括下列步骤:称取硅酸钠100千克、磷酸三聚氰胺30千克、季戊四醇20千克、尿素20千克、钛白粉8千克、(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮5千克和水800千克,先在涂料分散机中加入水,在转速为1500转/min的条件下加入硅酸钠、磷酸三聚氰胺、季戊四醇、尿素20千克、钛白粉和(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮,继续搅拌约30min,制得防火白浆涂料。本发明所述的水性防火涂料具有较好的防火效果,在工业应用上具有广阔的前景。
Description
技术领域
本发明涉及涂料领域,具体的说,本发明涉及一种水性防火涂料的制备方法。
背景技术
防火涂料又称阻燃涂料,它不但具有普通涂料的装饰性,而且涂料本身还具有防火保护功能。在火灾发生时,防火涂料能够阻止燃烧或者其对燃烧速度扩展有延滞作用,从而使人们有充分的时间进行火灾扑救工作,达到保护人们生命财产安全的目的。
发明内容
本发明的目的在于提供一种水性防火涂料的制备方法。
为了实现本发明的目的,本发明提供一种水性防火涂料的制备方法,其特征在于,该方法包括下列步骤:称取硅酸钠100千克、磷酸三聚氰胺30千克、季戊四醇20千克、尿素20千克、钛白粉8千克、(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮5千克和水800千克,先在涂料分散机中加入水,在转速为1500转/min的条件下加入硅酸钠、磷酸三聚氰胺、季戊四醇、尿素20千克、钛白粉和(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮,继续搅拌约30min,制得防火白浆涂料。
本发明所述的水性防火涂料具有较好的防火效果,在工业应用上具有广阔的前景。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明,但这并非是对本发明的限制,本领域技术人员根据本发明的基本思想,可以做出各种修改或改进,但是只要不脱离本发明的基本思想,均在本发明的范围之内。
实施例1
称取硅酸钠100千克、磷酸三聚氰胺30千克、季戊四醇20千克、尿素20千克、钛白粉8千克、(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮5千克和水800千克,先在涂料分散机中加入水,在转速为1500转/min的条件下加入硅酸钠、磷酸三聚氰胺、季戊四醇、尿素20千克、钛白粉和(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮,继续搅拌约30min,制得防火白浆涂料。
实施例2
按照和实施例1相同的方式制备水性防火涂料,不同之处在于不使用(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮。
实验例
根据(GB 15442.1-1995)来测试本发明的防火涂料的阻燃性。实施例1中的涂料的阻燃时间超过40分钟,而实施例2中的涂料的阻燃时间仅仅为15分钟。两者相比具有显著性差异(P<0.05)。这说明,阻燃助剂的加入大大强化了涂料的阻燃效果。
实施例1中的涂料的理化性能见下表
Claims (1)
1.一种水性防火涂料的制备方法,其特征在于,该方法可以包括下列步骤:称取硅酸钠100千克、磷酸三聚氰胺30千克、季戊四醇20千克、尿素20千克、钛白粉8千克、(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮5千克和水800千克,先在涂料分散机中加入水,在转速为1500转/min的条件下加入硅酸钠、磷酸三聚氰胺、季戊四醇、尿素20千克、钛白粉和(S)-4-(4-(二甲氨基)苯基-5-硝基-2-戊酮,继续搅拌约30min,制得防火白浆涂料。