CN104448647A - Production method of polytetrafluoroethylene anti-dripping agent - Google Patents
Production method of polytetrafluoroethylene anti-dripping agent Download PDFInfo
- Publication number
- CN104448647A CN104448647A CN201410730726.0A CN201410730726A CN104448647A CN 104448647 A CN104448647 A CN 104448647A CN 201410730726 A CN201410730726 A CN 201410730726A CN 104448647 A CN104448647 A CN 104448647A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight part
- parts
- dripping agent
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a polytetrafluoroethylene anti-dripping agent. The production method comprises the following steps of (1) adding ethylenediamine-polyoxyethylene-polyoxypropylene block polyether, 2-hexyl-1-decanol, kaolin, potassium persulfate, calcium carbonate, benzoyl peroxide, deionized water, ammonium peroxydisulfate, butyl methacrylate, maleic anhydride, tartaric acid and triethanolamine in a reaction kettle, heating to 72 DEG C, and reacting by stirring; (2) adding potassium persulfate, deionized water, benzoyl peroxide, butyl methacrylate, maleic anhydride and ammonium peroxydisulfate in the reaction kettle, heating to 80 DEG C, and reacting by stirring; (3) adding polytetrafluoroethylene dispersion liquid and deionized water into the reaction kettle, blending and compounding by heating, and adding a flocculant solution at the temperature of 55 DEG C to obtain a sediment; and (4) centrifugally separating the sediment, washing the sediment with water, centrifugally separating the sediment again, drying and smashing to obtain the anti-dripping agent. The polytetrafluoroethylene anti-dripping agent prepared by using the production method is good in stability.
Description
Technical field
The present invention relates to the production method of tetrafluoroethylene anti-dripping agent.
Background technology
Existing tetrafluoroethylene anti-dripping agent stability has much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of production method of tetrafluoroethylene anti-dripping agent, its tetrafluoroethylene anti-dripping agent good stability prepared.
For achieving the above object, technical scheme of the present invention designs a kind of production method of tetrafluoroethylene anti-dripping agent, comprises the steps:
1) 2 weight part ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 weight part hexyl decyl alcohol, 1.3 weight part pavilion soil powder, 3.4 weight part two sulphur eight oxygen acid potassium, 0.9 weight parts of calcium carbonate, 0.4 weight part benzoyl peroxide, 19.6 parts by weight of deionized water, 3.2 acid of weight part peroxo disulfate ammonium, 6.2 weight parts of methacrylic acid butyl esters, 4.8 parts by weight maleic anhydride, 2 weight part tartrate, 1 weight part trolamines are dropped in a kettle., be warming up to 72 DEG C, stirring reaction 52 minutes;
2) 0.6 weight part two sulphur eight oxygen acid potassium, 17.4 parts by weight of deionized water, 3.3 weight part benzoyl peroxides, 21.4 weight parts of methacrylic acid butyl esters, 11.2 parts by weight maleic anhydride, 3.3 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 80 DEG C, stirring reaction 70 minutes;
3) drop into 11.8 weight part polytetrafluoroethyldispersion dispersions, 26.7 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 55 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.
Advantage of the present invention and beneficial effect are: the production method providing a kind of tetrafluoroethylene anti-dripping agent, its tetrafluoroethylene anti-dripping agent good stability prepared.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
A production method for tetrafluoroethylene anti-dripping agent, comprises the steps:
1) 2 weight part ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 weight part hexyl decyl alcohol, 1.3 weight part pavilion soil powder, 3.4 weight part two sulphur eight oxygen acid potassium, 0.9 weight parts of calcium carbonate, 0.4 weight part benzoyl peroxide, 19.6 parts by weight of deionized water, 3.2 acid of weight part peroxo disulfate ammonium, 6.2 weight parts of methacrylic acid butyl esters, 4.8 parts by weight maleic anhydride, 2 weight part tartrate, 1 weight part trolamines are dropped in a kettle., be warming up to 72 DEG C, stirring reaction 52 minutes;
2) 0.6 weight part two sulphur eight oxygen acid potassium, 17.4 parts by weight of deionized water, 3.3 weight part benzoyl peroxides, 21.4 weight parts of methacrylic acid butyl esters, 11.2 parts by weight maleic anhydride, 3.3 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 80 DEG C, stirring reaction 70 minutes;
3) drop into 11.8 weight part polytetrafluoroethyldispersion dispersions, 26.7 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 55 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the production method of tetrafluoroethylene anti-dripping agent, is characterized in that, comprises the steps:
1) 2 weight part ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 weight part hexyl decyl alcohol, 1.3 weight part pavilion soil powder, 3.4 weight part two sulphur eight oxygen acid potassium, 0.9 weight parts of calcium carbonate, 0.4 weight part benzoyl peroxide, 19.6 parts by weight of deionized water, 3.2 acid of weight part peroxo disulfate ammonium, 6.2 weight parts of methacrylic acid butyl esters, 4.8 parts by weight maleic anhydride, 2 weight part tartrate, 1 weight part trolamines are dropped in a kettle., be warming up to 72 DEG C, stirring reaction 52 minutes;
2) 0.6 weight part two sulphur eight oxygen acid potassium, 17.4 parts by weight of deionized water, 3.3 weight part benzoyl peroxides, 21.4 weight parts of methacrylic acid butyl esters, 11.2 parts by weight maleic anhydride, 3.3 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 80 DEG C, stirring reaction 70 minutes;
3) drop into 11.8 weight part polytetrafluoroethyldispersion dispersions, 26.7 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 55 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.