CN104448654A - Preparation process of anti-dripping agent with high stability - Google Patents
Preparation process of anti-dripping agent with high stability Download PDFInfo
- Publication number
- CN104448654A CN104448654A CN201410730595.6A CN201410730595A CN104448654A CN 104448654 A CN104448654 A CN 104448654A CN 201410730595 A CN201410730595 A CN 201410730595A CN 104448654 A CN104448654 A CN 104448654A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight part
- parts
- dripping agent
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation process of an anti-dripping agent with high stability. The preparation process comprises the following steps of (1) adding polyoxyethylene monolaurate, sodium pyrophosphate, calcium carbonate, benzoyl peroxide, kaolin, deionized water, ammonium peroxydisulfate, butyl methacrylate, maleic anhydride, potassium persulfate, laurinol and methyltriethoxysilane in a reaction kettle, heating to 58 DEG C, and reacting for 65 minutes by stirring; (2) adding benzoyl peroxide, butyl methacrylate, potassium persulfate, maleic anhydride, deionized water and ammonium peroxydisulfate in the reaction kettle, heating to 75 DEG C, and reacting by stirring; (3) adding polytetrafluoroethylene dispersion liquid and deionized water into the reaction kettle, blending and compounding by heating, and adding a flocculant solution at the temperature of 48 DEG C to obtain a sediment; and (4) centrifugally separating the sediment, washing the sediment with water, centrifugally separating the sediment again, drying and smashing to obtain the anti-dripping agent. The polytetrafluoroethylene anti-dripping agent prepared by using the preparation process is good in stability.
Description
Technical field
The present invention relates to the preparation technology of high stability anti-dripping agent.
Background technology
Existing tetrafluoroethylene anti-dripping agent stability has much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of preparation technology of high stability anti-dripping agent, its tetrafluoroethylene anti-dripping agent good stability prepared.
For achieving the above object, technical scheme of the present invention designs a kind of preparation technology of high stability anti-dripping agent, comprises the steps:
1) 2 weight part lauric acid polyoxyethylene ester, 1 weight part trisodium phosphate, 1.8 weight parts of calcium carbonate, 3.4 weight part benzoyl peroxides, 4.7 weight part pavilion soil powder, 32 parts by weight of deionized water, 2.7 weight part peroxo disulfate acid ammoniums, 4.6 weight parts of methacrylic acid butyl esters, 6.5 parts by weight maleic anhydride, 2.3 acid of weight part two sulphur eight oxygen potassium, 2 weight part lauryl alcohols, 2 weight part Union carbide A-162s are dropped in a kettle., be warming up to 58 DEG C, stirring reaction 65 minutes;
2) 3.4 weight part benzoyl peroxides, 14.6 weight parts of methacrylic acid butyl esters, 2.3 weight part two sulphur eight oxygen acid potassium, 18.4 parts by weight maleic anhydride, 13.5 parts by weight of deionized water, 6.2 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 75 DEG C, stirring reaction 85 minutes;
3) drop into 19.4 weight part polytetrafluoroethyldispersion dispersions, 23.8 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 48 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.
Advantage of the present invention and beneficial effect are: the preparation technology providing a kind of high stability anti-dripping agent, its tetrafluoroethylene anti-dripping agent good stability prepared.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
A preparation technology for high stability anti-dripping agent, comprises the steps:
1) 2 weight part lauric acid polyoxyethylene ester, 1 weight part trisodium phosphate, 1.8 weight parts of calcium carbonate, 3.4 weight part benzoyl peroxides, 4.7 weight part pavilion soil powder, 32 parts by weight of deionized water, 2.7 weight part peroxo disulfate acid ammoniums, 4.6 weight parts of methacrylic acid butyl esters, 6.5 parts by weight maleic anhydride, 2.3 acid of weight part two sulphur eight oxygen potassium, 2 weight part lauryl alcohols, 2 weight part Union carbide A-162s are dropped in a kettle., be warming up to 58 DEG C, stirring reaction 65 minutes;
2) 3.4 weight part benzoyl peroxides, 14.6 weight parts of methacrylic acid butyl esters, 2.3 weight part two sulphur eight oxygen acid potassium, 18.4 parts by weight maleic anhydride, 13.5 parts by weight of deionized water, 6.2 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 75 DEG C, stirring reaction 85 minutes;
3) drop into 19.4 weight part polytetrafluoroethyldispersion dispersions, 23.8 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 48 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the preparation technology of high stability anti-dripping agent, is characterized in that, comprises the steps:
1) 2 weight part lauric acid polyoxyethylene ester, 1 weight part trisodium phosphate, 1.8 weight parts of calcium carbonate, 3.4 weight part benzoyl peroxides, 4.7 weight part pavilion soil powder, 32 parts by weight of deionized water, 2.7 weight part peroxo disulfate acid ammoniums, 4.6 weight parts of methacrylic acid butyl esters, 6.5 parts by weight maleic anhydride, 2.3 acid of weight part two sulphur eight oxygen potassium, 2 weight part lauryl alcohols, 2 weight part Union carbide A-162s are dropped in a kettle., be warming up to 58 DEG C, stirring reaction 65 minutes;
2) 3.4 weight part benzoyl peroxides, 14.6 weight parts of methacrylic acid butyl esters, 2.3 weight part two sulphur eight oxygen acid potassium, 18.4 parts by weight maleic anhydride, 13.5 parts by weight of deionized water, 6.2 weight part peroxo disulfate acid ammoniums are dropped into again in a kettle., be warming up to 75 DEG C, stirring reaction 85 minutes;
3) drop into 19.4 weight part polytetrafluoroethyldispersion dispersions, 23.8 parts by weight of deionized water more in a kettle., composite is carried out in heating, adds coagulant solution, be precipitated at 48 DEG C;
4) centrifugation is carried out to precipitation, washing, then centrifugation, dry and pulverize, obtain anti-dripping agent.