CN1044447A - 纯岩棉组合物及其纤维 - Google Patents

纯岩棉组合物及其纤维 Download PDF

Info

Publication number
CN1044447A
CN1044447A CN 88108546 CN88108546A CN1044447A CN 1044447 A CN1044447 A CN 1044447A CN 88108546 CN88108546 CN 88108546 CN 88108546 A CN88108546 A CN 88108546A CN 1044447 A CN1044447 A CN 1044447A
Authority
CN
China
Prior art keywords
pure
basalt
fiber
pure asbestos
asbestos composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 88108546
Other languages
English (en)
Inventor
郭珍儒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 88108546 priority Critical patent/CN1044447A/zh
Publication of CN1044447A publication Critical patent/CN1044447A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种由79-82％(重)玄武岩和18-21％(重)的石灰石在1500-1600℃温度下熔融制成的纯岩棉组合物。该纯岩棉组合物具有如下化学组成(按重量百分数计)：
SiO2 42.4～43.6
Al2O3 11.4～11.8
CaO 24.0～26.3
MgO 5.9～6.0
Fe2O3 4.9～5.0
其它 8.0～10
本发明的纯岩棉组合物可以制成各种纯岩棉制品。

Description

本发明涉及一种可纤维化的纯岩棉组合物，特别是涉及一种用石灰石改良的天然玄武岩的纯岩棉组合物，本发明的纤维可广泛地应用于建筑，热工行业作保温，隔音材料。
众所周知，“纯”玄武岩极易熔融，并易于制成玻璃，但由于玄武岩熔融物很粘常常不适宜喷吹成纤维。目前国内外生产岩棉的方法，通常是以矿渣为主要原料加部分玄武岩或辉绿岩，用这种方法制得的岩棉防腐性能差，经实验证明，这种岩棉制品在室外经风吹，日晒、雨淋不超过50天，纤维即全部破坏为粉状;而且硬度低，使用温度低，（820℃以下），耐高温性能差。
为了使玄武岩更易于纤维化，有必要改良并降低其粘度。根据文献推荐，生产矿物岩棉的最佳点是在1500℃时岩棉粘度为10泊，而纯玄武岩在此温度时的粘度很高，不适宜生产出令人满意的岩棉组合物及其纤维。
为了克服上述现有岩棉的缺点，本发明人进行了大量细致的研究工作，发现了一种改良的玄武岩的组合物，这种改良的玄武岩组合物可以制造出理想的纤维棉制品，并具有良好的产品性质。
更确切地说，本发明的岩棉组合物是由玄武岩加适量石灰石，经高温熔化后，通过离心机甩拉为无机玻璃纤维。
本发明中使用的主要原料是玄武岩，按重量百分数计占79～82%。为达到改良玄武岩粘度的目的，本发明还添加了18～21%（重）的石灰石。上述含量的玄武岩和石灰石在1500～1600℃温度下熔融，经离心甩拉成纤维制成本发明的纯岩棉。本发明的纯岩棉具有如下化学成份（按重量百分数计）：
SiO242.4～43.6%
Al2O311.4～11.8%
CaO    24.0～26.3%
MgO    5.9～6.0%
Fe2O34.9～5.0%
其它    8.0～10%
这里所说的“其它”是指微量的TiO2、MnO、K2O、P2O5、SO3F2等。
下面用实施例详细说明本发明。
实施例1，制备纯岩棉的方法。
首先将主原料玄武岩，改良剂石灰石分别破碎，并按一定的原料配比一起加入熔炉中熔融，然后，将获得的熔浆用常规方法（例如离心或喷吹法）制成纤维。
关于本发明纯岩棉的生产设备，可以使用传统的生产矿物棉的熔融炉，但最好使用与离心甩拉设备配套的冲天炉或电炉。
冲天炉中的熔浆是玄武岩和石灰石原料的混合物，为了有助于燃烧和熔融还需要添加一定量的焦炭。
熔浆可用传统的四辊离心机和高压气流离心喷吹制成纯岩棉纤维，并可用已知的工艺方法制成各种岩棉制品，如岩棉板、管、套、毡等。
实施例2、纯岩棉组合物。
用80%（重）的玄武岩，20%的石灰石，在1500～1600℃的温度下熔融，经离心甩拉成纤。
其化学成份如下（按重量百分数计）：
SiO243.00%
Al2O311.60%
CaO    25.00%
MgO    5.95%
Fe2O35.00%
其它    9.45%
本发明纯岩棉的物化性质见表1。
表1：
项目 单位 测试数
容量 kg/m2 73.7
渣球含量 ％ 0.5mm  0.25mm6.16  4.16
纤维直径 μ 小于7.85
吸湿率 ％ 0.31
烧结温度 ℃ 1100
使用温度 ℃ 1050
本发明的纯岩棉防腐性能好，置于室外风吹日晒、雨淋半年以上仍不改变其各项性能。本发明的岩棉硬度高，其它各项指标均好于目前岩棉的各项理化指标。
以上实施例只是对本发明的进一步说明，而不是对本发发的限制。

Claims (3)

1、一种纯岩棉组合物，其特征在于：
SiO242.4～43.6%
Al2O311.4～11.8%
CaO    24.0～26.3%
MgO    5.9～6.0%
Fe2O34.9～5.0%
其它   8～10%
所说百分数为重量百分数。
2、根据权利要求1所述的组合物，其特征在于所说的“其它”指微量的TiO2、MnO、K2O、P2O3、SO3、F2。
3、根据权利要求1所述的组合物，其特征在于用79～82%（重）的玄武岩和18～21%（重）的石灰石在1500～1600℃温度下熔融，然后离心甩拉制成。
CN 88108546 1988-12-19 1988-12-19 纯岩棉组合物及其纤维 Pending CN1044447A (zh)