CN104439200A - 铸钢用发热保温覆盖剂 - Google Patents

铸钢用发热保温覆盖剂 Download PDF

Info

Publication number
CN104439200A
CN104439200A CN201410682146.9A CN201410682146A CN104439200A CN 104439200 A CN104439200 A CN 104439200A CN 201410682146 A CN201410682146 A CN 201410682146A CN 104439200 A CN104439200 A CN 104439200A
Authority
CN
China
Prior art keywords
powder
agent
mixture
exothermic
vermiculite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410682146.9A
Other languages
English (en)
Inventor
刘洪林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI ZONGHUA INDUSTRIAL Co Ltd
Original Assignee
SHANGHAI ZONGHUA INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI ZONGHUA INDUSTRIAL Co Ltd filed Critical SHANGHAI ZONGHUA INDUSTRIAL Co Ltd
Priority to CN201410682146.9A priority Critical patent/CN104439200A/zh
Publication of CN104439200A publication Critical patent/CN104439200A/zh
Pending legal-status Critical Current

Abstract

本发明涉及铸造辅助材料技术领域，具体地说是一种铸钢用发热保温覆盖剂，按重量百分比，由以下组分组成：发热剂8-28％、保温剂50-70％、触发剂5-22％，其中，发热剂为铝粉和AD-20粉的混合物，铝粉中Al含量≥95.0％、Zn含量≤1.0％，AD-20粉中Al含量为18-20％，铝粉与AD-20粉的混合比为1：3-1：5；保温剂为珍珠岩、石川除渣剂F4、蛭石、漂珠组成的混合物，珍珠岩、石川除渣剂F4、蛭石、漂珠的混合比为2：1：1：1，珍珠岩、石川除渣剂F4、蛭石、漂珠中SiO2的含量均大于40％；触发剂为萤石粉、氟硅酸钠和白油的混合物；本发明同现有技术相比，不仅能够同时起到发热和保温效果，而且还提升了传统无碳发热剂的发热、保温效果。

Description

铸钢用发热保温覆盖剂
[技术领域]
本发明涉及铸造辅助材料技术领域，具体地说是一种铸钢用发热保温覆盖剂。
[背景技术]
在现有技术中，往往是将发热剂与保温剂分开使用，从而在生产时起到发热及保温的效果。另外，在研制合适配比的发热覆盖剂的同时，针对覆盖剂容易增碳的缺点，尝试研制无碳的发热覆盖剂，然而无碳覆盖剂的最大缺点是在保证不增碳的同时，却减低了覆盖剂的保温性能。
[发明内容]
本发明的目的就是要解决上述的不足而提供一种铸钢用发热保温覆盖剂，不仅能够同时起到发热和保温效果，而且通过对无碳保温材料的研究并应用到发热覆盖剂中，还提升了传统无碳发热剂的发热、保温效果。
为实现上述目的设计一种铸钢用发热保温覆盖剂，按重量百分比，由以下组分组成：发热剂8-28％、保温剂50-70％、触发剂5-22％。
所述发热剂为铝粉和AD-20粉的混合物，所述铝粉中Al含量≥95.0％、Zn含量≤1.0％，所述AD-20粉中Al含量为18-20％，所述铝粉与AD-20粉的混合比为1：3-1：5。
所述保温剂为珍珠岩、石川除渣剂F4、蛭石、漂珠组成的混合物，所述珍珠岩、石川除渣剂F4、蛭石、漂珠的混合比为2：1：1：1，所述珍珠岩、石川除渣剂F4、蛭石、漂珠中SiO2的含量均大于40％。
所述触发剂为萤石粉、氟硅酸钠和白油的混合物。
作为优选，本发明按重量百分比，由以下组分组成：
本发明同现有技术相比，具有如下优点：
(1)相对于传统覆盖剂，具有更好的保温效果，并在保温同时具备一定的发热效果；传统发热剂在发热过程中容易影响到保温剂的保温性，本发明在试验中也考虑到了这一因素，从而完善了覆盖剂中各组分配比，使得发热剂的发热效果不会影响到覆盖剂自身保温性能，并进一步防止了铸件的缩孔缩松现象。
(2)本发明在覆盖剂的基础上加入了发热材料，从而在保证保温效果的同时，还提升了生产过程中钢水温度；且在发热覆盖剂中加入了含氟的触发剂作为强氧化剂，提升发热效果。较好的发热剂和保温剂配比，使得该发热覆盖剂具有更好的保温效果，更一步延长了冒口中钢液的凝固速度，提升了铸件的紧实度和质量。
(3)本发明通过实验室和现场实践大量试验测试，研究发热保温覆盖剂中发热剂和保温剂种类和配比，使得发热和保温效果得到提升；并针对常规覆盖剂容易增碳的问题，研制新型无碳发热保温覆盖剂，提升了传统无碳发热剂的发热、保温效果。
[附图说明]
图1是本发明的制备方法流程示意图；
[具体实施方式]
下面结合具体实施例对本发明作以下进一步说明：
本发明按重量百分比，由以下组分组成：(1)发热剂8％、保温剂70％、触发剂22％；(2)发热剂28％、保温剂50％、触发剂22％；(3)发热剂26％、保温剂69％、触发剂5％；(4)发热剂22％、保温剂60％、触发剂18％；(5)发热剂16％、保温剂70％、触发剂14％。
其中，发热剂为铝粉和AD-20粉的混合物，铝粉中Al含量≥95.0％、Zn含量≤1.0％，AD-20粉中Al含量为18-20％，铝粉与AD-20粉的混合比为1：3-1：5；保温剂为珍珠岩、石川除渣剂F4、蛭石、漂珠组成的混合物，珍珠岩、石川除渣剂F4、蛭石、漂珠的混合比为2：1：1：1，珍珠岩、石川除渣剂F4、蛭石、漂珠中SiO2的含量均大于40％；触发剂为萤石粉、氟硅酸钠和白油的混合物。
本发明按重量百分比，可由以下组分组成：80目铝粉(Al≥95.0％Zn≤1.0％)、100目铝粉(Al≥95.0％Zn≤1.0％)或120目铝粉(Al≥95.0％Zn≤1.0％)为4％，AD-20粉为20％，珍珠岩为24％，日本石川除渣剂F4为12％，蛭石为12％，漂珠为12％，工业萤石粉为8％，工业级氟硅酸钠为4％，有机可燃物白油为4％。
本发明在制备时，按照附图1所示的制备方法流程图，利用混合机将上述各组分充分搅拌均匀即可。该发热保温覆盖剂避免了特大型铸钢件生产时的缩孔和缩松现象，且保温性能良好，同时热值＞12500J/g。另外，通过试验，本发明能有效保证了冒口的补缩效率，提高了钢水的使用效率。
本发明并不受上述实施方式的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。

Claims (5)

1.一种铸钢用发热保温覆盖剂，其特征在于，按重量百分比，由以下组分组成：发热剂8-28％、保温剂50-70％、触发剂5-22％。
2.如权利要求1所述的铸钢用发热保温覆盖剂，其特征在于：所述发热剂为铝粉和AD-20粉的混合物，所述铝粉中Al含量≥95.0％、Zn含量≤1.0％，所述AD-20粉中Al含量为18-20％，所述铝粉与AD-20粉的混合比为1：3-1：5。
3.如权利要求1所述的铸钢用发热保温覆盖剂，其特征在于：所述保温剂为珍珠岩、石川除渣剂F4、蛭石、漂珠组成的混合物，所述珍珠岩、石川除渣剂F4、蛭石、漂珠的混合比为2：1：1：1，所述珍珠岩、石川除渣剂F4、蛭石、漂珠中SiO2的含量均大于40％。
4.如权利要求1所述的铸钢用发热保温覆盖剂，其特征在于：所述触发剂为萤石粉、氟硅酸钠和白油的混合物。
5.如权利要求1所述的铸钢用发热保温覆盖剂，其特征在于，按重量百分比，由以下组分组成：
CN201410682146.9A 2014-11-24 2014-11-24 铸钢用发热保温覆盖剂 Pending CN104439200A (zh)