CN104420626B - A kind of method manufacturing mosquito repellent wood floor - Google Patents
A kind of method manufacturing mosquito repellent wood floor Download PDFInfo
- Publication number
- CN104420626B CN104420626B CN201310386181.1A CN201310386181A CN104420626B CN 104420626 B CN104420626 B CN 104420626B CN 201310386181 A CN201310386181 A CN 201310386181A CN 104420626 B CN104420626 B CN 104420626B
- Authority
- CN
- China
- Prior art keywords
- anophelifuge
- microcapsule
- mosquito
- timber floor
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of method manufacturing mosquito repellent wood floor, said method comprising the steps of: (1) is by the mosquito-driving liquid injection pressure tank being dispersed with anophelifuge microcapsule；(2) timber floor it is immersed in the mosquito-driving liquid in described pressurized tank and carries out pressure impregnating；(3) timber floor after soaking step (2) is dried process and moisture equilibration；Wherein, the wall material of described anophelifuge microcapsule is formed by high molecular synthetic material, and thickness is 1 μm to 10 μm, the particle diameter of described anophelifuge microcapsule be 2 μm to 100 μm, and wherein accommodate anophelifuge.Timber floor made according to the method for the present invention can persistently play anophelifuge effect, uses this timber floor can build comfortable outdoor environment.
Description
Technical field
The present invention relates to a kind of method manufacturing mosquito repellent wood floor.
Background technology
Along with the raising of modern life level, the use of outdoor flooring gets more and more, such as garden landscape floor, villa flower
Floor, garden, wayside pavilion floor, wooden pavement floor etc. outside room, but, the mosquito in outdoor environment is more, stining of mosquito
Sting and not only make application on human skin pruritus, and also disease can be infected, there is the flooring product of repelling effect to build accordingly, it would be desirable to a kind of
Preferably outdoor environment.
Summary of the invention
In order to solve the problems referred to above, the invention provides a kind of method manufacturing mosquito repellent wood floor, described method include with
Lower step:
(1) by the mosquito-driving liquid injection pressure tank being dispersed with anophelifuge microcapsule；
(2) timber floor it is immersed in the mosquito-driving liquid in described pressurized tank and carries out pressure impregnating；
(3) timber floor after soaking step (2) is dried process and moisture equilibration；
Wherein, the wall material of described anophelifuge microcapsule is formed by high molecular synthetic material, thickness be 1 μm to 10 μm, described in drive
The particle diameter of mosquito microcapsule be 2 μm to 100 μm, and wherein accommodate anophelifuge.
In one embodiment of the invention, in the mosquito-driving liquid in described step (1) containing mass percent be 25% to
The anophelifuge microcapsule of 35%.High molecular synthetic material for described anophelifuge microcapsule is hydroxyacetic acid-hydroxyethyl cellulose, and
And preferably, in described hydroxyacetic acid-hydroxyethyl cellulose, the mass ratio of hydroxyacetic acid and hydroxyethyl cellulose is 35:65.
It is contained in the extract that the anophelifuge in described anophelifuge microcapsule can be chrysanthemum ester type compound, natural camphor and/or Folium Artemisiae Argyi, excellent
Selection of land, described chrysanthemum ester type compound is selected from Permethrin, tetramethrin, fluorine chlorine ether chrysanthemum ester, dimefluthrin and allethrin.Described
Pressure impregnating in step (2), under 6 to 10 atmospheric pressure, carries out 80 minutes to 120 minutes at 25 DEG C to 50 DEG C.Described step
(3) dried in is carried out 24 hours to 48 hours at 120 DEG C to 130 DEG C, makes the moisture content of described timber floor reach 8%
To 12%.Moisture equilibration in described step (3), at 60 DEG C to 80 DEG C, carries out 72 hours extremely under the humidity of 30% to 40%
100 hours.
In another embodiment of the present invention, the method for the present invention also includes with the paint containing described anophelifuge microcapsule
Apply the surface of the timber floor after step (3) processes.Preferably, containing mass percent in described paint is 15% to 30%
Anophelifuge microcapsule.
The term " moisture equilibration " used in the present invention refers at a certain temperature and humidity conditions, make in timber
Moisture and air in moisture no longer swap and reach the processing procedure of steady statue.
Timber floor made according to the method for the present invention is micro-due to impregnate into containing anophelifuge in its timber pore
Capsule, during floor uses, microcapsule can not only discharge anophelifuge by progressively breakage makes floor have anophelifuge
Effect, and microcapsule can also make the anophelifuge being accommodated therein slowly release, so that the timber floor of the present invention
Repelling effect can be up to 5 years as long as.The timber floor of the present invention can persistently play anophelifuge effect in its service life,
Build more comfortable outdoor environment.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, the most right below in conjunction with specific embodiment
The present invention is described in detail, it should be noted that the specific embodiment in the present invention is only used for illustrating, not to the present invention
Protection domain be construed as limiting.
Embodiment
The present embodiment provides concrete steps and the technological parameter of the mosquito repellent wood floor manufacturing the present invention.The manufacture of the present invention is driven
The method of mosquito timber floor comprises the following steps:
(1) offer accommodates the anophelifuge microcapsule of anophelifuge: according to microcapsule technology well known in the art, prepare wall material
For hydroxyacetic acid-(wherein, the mass ratio of hydroxyacetic acid and hydroxyethyl cellulose is hydroxyethyl cellulose synthesis macromolecular material
35:65), wall material thickness be 1-10 μm, particle diameter be the microcapsule of 2-100 μm, and by anophelifuge chlorine chrysanthemum commonly used in the art
Ester is wrapped in microcapsule.
(2) mosquito-driving liquid is prepared: be scattered in the concentration that mass percent is 30% by the anophelifuge microcapsule that step (1) prepares
In water, thus obtain the mosquito-driving liquid for soaking timber floor, and this mosquito-driving liquid is injected in the pressurized tank of 13 cubic metres.
(3) pressure impregnating: timber floor be immersed in the mosquito-driving liquid in pressurized tank, under 6 atmospheric pressure, at 25 DEG C to 50
Carry out pressure impregnating at DEG C and continue 100 minutes.
(4) dried: at 120 DEG C to 130 DEG C, in drying chamber, timber floor is carried out at high-temperature steam cyclic drying
Reason continues 24 hours.Specifically, in drying chamber, first inject high-temperature steam, the most progressively heat and high-temperature steam is emptied,
Emptying continues to reinject high-temperature steam in 2 to 4 hours, so carries out at least 4 high-temperature steam circulations, and each high-temperature steam circulates
No less than 2 hours, finally by steam discharging, it is dried timber floor followed by heat radiation, makes timber floor moisture content be finally reached 8%
To 12%.
(5) moisture equilibration: at 60 DEG C to 80 DEG C, under the humidity of 30% to 40%, to step in constant temperature and humidity balance room
Suddenly the timber floor after (4) dried carries out processing lasting 72 hours.
(6) after water balance completes slot this timber floor, paint process makes ground board finished product.
The mosquito repellent wood floor on normal wood floor with the present invention according to said method manufacture is contrasted, by comparatively
It is obvious that the mosquito quantity that falls on plate finds that mosquito is walked quickly and kept away effect by the timber floor of the present invention, and the rate of walking quickly and keeping away reaches 75%, and this wood ground
This repelling effect of plate can keep more than 5 years.Additionally, compared with other drying meanss of this area, the present invention uses
High-temperature steam cyclic drying method can preferably protect wood structure, reduces the loss rate of timber.
In other embodiments of the invention, other anophelifuges commonly used in the art also can be used, such as but not limited to:
Tetramethrin, fluorine chlorine ether chrysanthemum ester, dimefluthrin, allethrin, natural camphor, Folium Artemisiae Argyi extract.
In mosquito-driving liquid, the mass percent of anophelifuge microcapsule can be also 25%, 35%.
Pressurized tank used in the present invention can be the pressurized tank of any volume commonly used in the art, the volume of described pressurized tank
Such as but not limited to: 5 cubic metres, 6 cubic metres, 7 cubic metres, 8 cubic metres, 9 cubic metres, 10 cubic metres, 11 cubic metres, 12 cubes
Rice, 12.5 cubic metres, 20 cubic metres.
Pressure used in pressure impregnating step can be also 8 atmospheric pressure, 9 atmospheric pressure, 10 atmospheric pressure.
The time of pressure impregnating can be also 80 minutes, 85 minutes, 90 minutes, 95 minutes, 105 minutes, 115 minutes, 120 points
Clock.
The dried time can be also 36 hours, 48 hours.
The moisture equilibration time can be also 75 hours, 80 hours, 85 hours, 90 hours, 95 hours, 100 hours.
As a preferred embodiment of the present invention, after above-mentioned steps (5) moisture equilibration, to step (5) place
During timber floor coating paint after reason, preferably by the oil containing the anophelifuge microcapsule that mass percent is 15% to 30%
Paint is coated on the surface of timber floor, so also discharges anophelifuge on the surface of timber floor.Normal wood floor is the most real with this
The mosquito repellent wood floor executing example manufacture contrasts, by comparing the wood that the mosquito quantity that falls on floor finds that the preferred embodiment manufactures
It is obvious that mosquito is walked quickly and kept away effect by floor.
Describing the present invention above in association with detailed description of the invention, these detailed description of the invention are merely exemplary
, it is impossible to limit protection scope of the present invention with this.Those skilled in the art are permissible on the premise of without departing from essence of the present invention
Carry out various amendment, change or replace.Therefore, the various equivalent variations made according to the present invention, still fall within the present invention and contained
Scope.
Claims (9)
1. the method manufacturing mosquito repellent wood floor, said method comprising the steps of:
(1) by the mosquito-driving liquid injection pressure tank being dispersed with anophelifuge microcapsule；
(2) timber floor it is immersed in the mosquito-driving liquid in described pressurized tank and carries out pressure impregnating；
(3) timber floor after soaking step (2) is dried process and moisture equilibration；
Wherein, the wall material of described anophelifuge microcapsule is formed by high molecular synthetic material, and thickness is 1 μm to 10 μm, and described anophelifuge is micro-
The particle diameter of capsule be 2 μm to 100 μm, and wherein accommodate anophelifuge；
Described high molecular synthetic material is hydroxyacetic acid-hydroxyethyl cellulose, in described hydroxyacetic acid-hydroxyethyl cellulose,
The mass ratio of hydroxyacetic acid and hydroxyethyl cellulose is 35:65.
Containing mass percent in mosquito-driving liquid in the most described step (1) is 25%
To the anophelifuge microcapsule of 35%.
3. method as claimed in claim 1 or 2, wherein, described anophelifuge be chrysanthemum ester type compound, natural camphor and/or
The extract of Folium Artemisiae Argyi.
4. method as claimed in claim 3, wherein, described chrysanthemum ester type compound is selected from Permethrin, tetramethrin, fluorine chlorine ether chrysanthemum
Ester, dimefluthrin and allethrin.
5. method as claimed in claim 1 or 2, wherein, the pressure impregnating in described step (2) under 6 to 10 atmospheric pressure,
80 minutes to 120 minutes are carried out at 25 DEG C to 50 DEG C.
6. method as claimed in claim 1 or 2, wherein, the dried in described step (3) is entered at 120 DEG C to 130 DEG C
Row 24 hours to 48 hours, makes the moisture content of described timber floor reach 8% to 12%.
7. method as claimed in claim 1 or 2, wherein, the moisture equilibration in described step (3) is at 60 DEG C to 80 DEG C
Under, carry out 72 hours to 100 hours under the humidity of 30% to 40%.
The most described method also includes with the paint application containing described anophelifuge microcapsule
The surface of the timber floor after step (3) processes.
9. method as claimed in claim 8, wherein, micro-containing the anophelifuge that mass percent is 15% to 30% in described paint
Capsule.