CN104404331A - 高抗拉强度镁合金的制备方法 - Google Patents

高抗拉强度镁合金的制备方法 Download PDF

Info

Publication number
CN104404331A
CN104404331A CN201410763490.0A CN201410763490A CN104404331A CN 104404331 A CN104404331 A CN 104404331A CN 201410763490 A CN201410763490 A CN 201410763490A CN 104404331 A CN104404331 A CN 104404331A
Authority
CN
China
Prior art keywords
melt
alloy
preparation
magnesium alloy
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410763490.0A
Other languages
English (en)
Inventor
单巍巍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chun Hing Seiko (changshu) Co Ltd
Original Assignee
Chun Hing Seiko (changshu) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chun Hing Seiko (changshu) Co Ltd filed Critical Chun Hing Seiko (changshu) Co Ltd
Priority to CN201410763490.0A priority Critical patent/CN104404331A/zh
Publication of CN104404331A publication Critical patent/CN104404331A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗拉强度镁合金的制备方法，该镁合金的成分按重量百分比计为：La：0.2%，Y：1.8%，B：2.3%，Sr：1.7%，Ce：3.6%，余量为Mg和不可避免的杂质；制备方法包括如下步骤：1）在保护性气氛下，将镁、La和Mg-Y合金于720℃熔融，得到第一熔体；2）在保护性气氛下，将第一熔体升温至725℃，向第一熔体中加入Mg-B合金、Mg-Sr合金和Mg-Ce合金，搅拌均匀，保温静置25min，再通入氩气，得到第二熔体；3）将第二熔体静置降温至650℃，压铸，得到镁合金。本发明制备的镁合金具有高强度和高韧性，同时具有优良的室温力学性、高温力学性能和高温蠕变性能，屈服强度和抗拉强度高。

Description

高抗拉强度镁合金的制备方法
技术领域
本发明涉及高抗拉强度镁合金的制备方法。
背景技术
现有工艺制备的镁合金，其室温力学性、高温力学性能、高温蠕变性能、屈服强度和抗拉强度都有待提高。 
发明内容
本发明的目的在于提供一种高抗拉强度镁合金的制备方法，其制备的镁合金具有高强度和高韧性，同时具有优良的室温力学性、高温力学性能和高温蠕变性能，屈服强度和抗拉强度高。
为实现上述目的，本发明的技术方案是设计一种高抗拉强度镁合金的制备方法，该镁合金的成分按重量百分比计为：
La：0.2%，
Y：1.8%，
B：2.3%，
Sr：1.7%，
Ce：3.6%，
余量为Mg和不可避免的杂质；
制备方法包括如下步骤：
1）在保护性气氛下，将镁、La和Mg-Y合金于720℃熔融，得到第一熔体；
2）在保护性气氛下，将第一熔体升温至725℃，向第一熔体中加入Mg-B合金、Mg-Sr合金和Mg-Ce合金，搅拌均匀，保温静置25min，再通入氩气，得到第二熔体；
3）将第二熔体静置降温至650℃，压铸，得到镁合金。
本发明的优点和有益效果在于：提供一种高抗拉强度镁合金的制备方法，其制备的镁合金具有高强度和高韧性，同时具有优良的室温力学性、高温力学性能和高温蠕变性能，屈服强度和抗拉强度高。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
一种高抗拉强度镁合金的制备方法，该镁合金的成分按重量百分比计为：
La：0.2%，
Y：1.8%，
B：2.3%，
Sr：1.7%，
Ce：3.6%，
余量为Mg和不可避免的杂质；
制备方法包括如下步骤：
1）在保护性气氛下，将镁、La和Mg-Y合金于720℃熔融，得到第一熔体；
2）在保护性气氛下，将第一熔体升温至725℃，向第一熔体中加入Mg-B合金、Mg-Sr合金和Mg-Ce合金，搅拌均匀，保温静置25min，再通入氩气，得到第二熔体；
3）将第二熔体静置降温至650℃，压铸，得到镁合金。
 
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.高抗拉强度镁合金的制备方法，其特征在于，该镁合金的成分按重量百分比计为：
La：0.2%，
Y：1.8%，
B：2.3%，
Sr：1.7%，
Ce：3.6%，
余量为Mg和不可避免的杂质；
制备方法包括如下步骤：
1）在保护性气氛下，将镁、La和Mg-Y合金于720℃熔融，得到第一熔体；
2）在保护性气氛下，将第一熔体升温至725℃，向第一熔体中加入Mg-B合金、Mg-Sr合金和Mg-Ce合金，搅拌均匀，保温静置25min，再通入氩气，得到第二熔体；
3）将第二熔体静置降温至650℃，压铸，得到镁合金。
CN201410763490.0A 2014-12-15 2014-12-15 高抗拉强度镁合金的制备方法 Pending CN104404331A (zh)