CN102181761B - 一种新型镁合金及其制备方法 - Google Patents

一种新型镁合金及其制备方法 Download PDF

Info

Publication number
CN102181761B
CN102181761B CN2011101228971A CN201110122897A CN102181761B CN 102181761 B CN102181761 B CN 102181761B CN 2011101228971 A CN2011101228971 A CN 2011101228971A CN 201110122897 A CN201110122897 A CN 201110122897A CN 102181761 B CN102181761 B CN 102181761B
Authority
CN
China
Prior art keywords
block
magnesium alloy
calcium
copper
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2011101228971A
Other languages
English (en)
Other versions
CN102181761A (zh
Inventor
方建静
王建杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011101228971A priority Critical patent/CN102181761B/zh
Publication of CN102181761A publication Critical patent/CN102181761A/zh
Application granted granted Critical
Publication of CN102181761B publication Critical patent/CN102181761B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为25％～30％，铝的质量百分含量为15％～18％，铜的质量百分含量为1％～1.5％，钙的质量百分含量为0.7％，余量为镁。上述镁合金的制备方法，首先将锌块、镁块和钙块放入坩埚中，待锌块、镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。本发明调整了镁合金中各金属的质量百分比及组分后，其着火点可大大提高，且其强度也得到了一定程度的提升。

Description

一种新型镁合金及其制备方法
(一)技术领域
本发明涉及一种镁合金以及一种镁合金的制备方法。
(二)背景技术
现有的镁合金一般包括锌、铝、镁等金属，锌的含量及铝的含量较低，镁的含量极高，锌的质量百分含量一般在1％以内，铝的质量百分含量一般在10％以内，而镁的质量百分含量在90％左右。现有的镁合金还存在的缺点在于：着火点(燃点)较低，在采用镁合金进行压铸件的生产时，由于着火点较低，因此必须在惰性气体保护氛围下进行铸造，生产铸件工艺条件复杂。另外，现有的镁合金其强度也还需加强。
(三)发明内容
为了克服现有镁合金着火点过低、强度有待提高的不足，本发明提供一种着火点更高、强度更高的新型镁合金，并提供其制备方法。
本发明解决其技术问题的技术方案是：一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为25％～30％，铝的质量百分含量为15％～18％，铜的质量百分含量为1％～1.5％，钙的质量百分含量为0.7％，余量为镁。
上述镁合金的制备方法：首先将锌块、镁块和钙块放入坩埚中，待锌块、镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。必须严格按照上述顺序向坩埚内添加金属，按照上述次序将金属放入到坩埚中，才能将各金属有机地融合在一起形成本发明的镁合金。
纯镁在高温下易挥发，但铝在镁合金中起到终脱氧作用，起到阻燃和提高镁合金着火点的作用，且有助于组织机构的加强。适当的钙和铜有助于提高镁合金的燃点。且铜和锌都组织机构的加强。
本发明的有益效果在于：调整了镁合金中各金属的质量百分比及组分后，其着火点可大大提高，且其强度也得到了一定程度的提升。
(四)具体实施方式
下面具体实施方式对本发明作进一步详细说明。
实施例一
一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为25％，铝的质量百分含量为18％，铜的质量百分含量为1.3％，钙的质量百分含量为0.7％，余量为镁。上述新型镁合金的制备方法：首先将锌块和镁块和钙块放入坩埚中，待锌块和镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
实施例二
一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为26％，铝的质量百分含量为16％，铜的质量百分含量为1.5％，钙的质量百分含量为0.7％，余量为镁。上述新型镁合金的制备方法：首先将锌块和镁块和钙块放入坩埚中，待锌块和镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
实施例三
一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为28％，铝的质量百分含量为16.5％，铜的质量百分含量为1％，钙的质量百分含量为0.7％，余量为镁。上述新型镁合金的制备方法：首先将锌块和镁块和钙块放入坩埚中，待锌块和镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
实施例四
一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为30％，铝的质量百分含量为17％，铜的质量百分含量为1.2％，钙的质量百分含量为0.7％，余量为镁。上述新型镁合金的制备方法：首先将锌块和镁块和钙块放入坩埚中，待锌块和镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
实施例五
一种新型镁合金，由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为27％，铝的质量百分含量为15％，铜的质量百分含量为1.4％，钙的质量百分含量为0.7％，余量为镁。上述新型镁合金的制备方法：首先将锌块和镁块和钙块放入坩埚中，待锌块和镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
对比例
对比例为一种普通镁合金：AZ91镁合金。
将对比例和实施例一～实施例五进行比较：
  抗拉强度(兆帕)   屈服强度(兆帕)   延伸率(％)   着火点(℃)
  实施例一   240   123   564   678
  实施例二  238   118   560   679
  实施例三  240   122   556   678
  实施例四  240   133   555   675
  实施例五  237   130   578   664
  对比例  230   112   543   500
由上表可以看出，本发明的新型镁合金，着火点显著升高，因此在采用本发明的镁合金进行铸造时，不用再营造惰性气体保护氛围；由上表也可以看出，本发明的新型镁合金强度也得到很大的提升。

Claims (1)

1.一种新型镁合金的制备方法，该新型镁合金由锌、铝、铜、钙、镁组成，该镁合金中锌的质量百分含量为25％～30％，铝的质量百分含量为15％～18％，铜的质量百分含量为1％～1.5％，钙的质量百分含量为0.7％，余量为镁，其特征在于：首先将锌块、镁块和钙块放入坩埚中，待锌块、镁块和钙块完全熔化后将铝块和铜块加入到熔液中，升温至铝块和铜块亦熔解，使得熔液混合均匀，冷却后制得镁合金。
CN2011101228971A 2011-05-09 2011-05-09 一种新型镁合金及其制备方法 Expired - Fee Related CN102181761B (zh)