CN104403609B - 高强度抗裂接缝剂 - Google Patents
高强度抗裂接缝剂 Download PDFInfo
- Publication number
- CN104403609B CN104403609B CN201410671158.1A CN201410671158A CN104403609B CN 104403609 B CN104403609 B CN 104403609B CN 201410671158 A CN201410671158 A CN 201410671158A CN 104403609 B CN104403609 B CN 104403609B
- Authority
- CN
- China
- Prior art keywords
- quartz sand
- joint mixture
- vinyl
- cracking
- white glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种粘合剂,尤其涉及高强度抗裂接缝剂,其由粗石英砂、细石英砂、重钙粉、硅酮胶和白乳胶组成,各组分的配比为(按重量百分比):粗石英砂20-40%、细石英砂10-30%、重钙粉10-30%、硅酮胶0.5-2%、白乳胶20-40%。本发明是一种粘稠状接缝剂,无需添加其他材料,即可应用于纤维水泥平板和纤维增强硅酸钙板该类材料的接缝,克服了纸面石膏板接缝腻子的缺点,具有粘结强度高、防开裂、施工方便、成本低、环保无毒等特点。
Description
技术领域
本发明涉及一种粘合剂,尤其涉及高强度抗裂接缝剂。
背景技术
目前市场上的接缝腻子大多应用于纸面石膏板,在设计、研发及生产过程中以纸面石膏板为基础,该类接缝腻子与纸面石膏板具有良好的粘结性能和抗裂性能,但纸面石膏板防水防火防霉等性能比较差,抗折强度低,应用领域受到局限。市场上的纤维水泥平板和纤维增强硅酸钙板却具有纸面石膏板所有优点,同时又具有很好的防水防火防霉等性能,抗折强度高,不易折断,应用领域广泛,室内室外都可使用。
但是由于纤维水泥平板和纤维增强硅酸钙板为硅质钙质材料,原先应用于纸面石膏板的接缝腻子用于此类材料时,会出现粘结力差,接缝处出现开裂等问题,性能达不到应用要求。
发明内容
本发明所要解决的技术问题是提供一种高强度抗裂接缝剂,具有粘结强度高、防开裂、施工方便等特点。
为解决上述问题,本发明的技术方案是:一种高强度抗裂接缝剂,所述的高强度抗裂接缝剂由粗石英砂、细石英砂、重钙粉、硅酮胶和白乳胶组成,各组分的配比为(按重量百分比):粗石英砂20-40%、细石英砂10-30%、重钙粉10-30%、硅酮胶0.5-2%、白乳胶20-40%。
所述石英砂为填充料,采用不同的粒度等级配比,可以提高接缝剂的刚性和抗裂强度。
重钙粉是用优质的方解石为原料加工而成白色粉体,它的主要成分是CaCO3,重钙白度高、纯度好、色相柔和及化学成分稳定等特点,其作为填充剂起到增加产品的体积,降低生产成本。
硅酮胶是一种类似软膏,一旦接触空气中的水分就会固化成一种坚韧的橡胶类固体的材料。主要分为脱醋酸型,脱醇型,脱氨型,脱丙型。硅酮胶因为常被用于玻璃方面的粘接和密封,所以俗称玻璃胶。
白乳胶是以水为分散介质进行乳液聚合而得,是一种水性环保胶,它具有干燥快、初粘性好、操作性佳;粘接力强、抗压强度高;耐热性强。
上述组分制成的接缝剂具有粘结强度高、防开裂、施工方便等特点,具有理想的应用效果。
优选地,所述粗石英砂细度为60目-130目。所述细石英砂细度为150目-250目。粗细石英砂通过一定比例的级配,起到填充、提高粘结强度、防止开裂的作用。
优选地,所述白乳胶主要成分为醋酸乙烯酯VAC、聚乙烯醇PVA、丙烯酸AA、丙烯酰胺AM、二甘醇二苯甲酸酯DEDB和水,上述各组分的配比为(按重量百分比):醋酸乙烯酯VAC22%-31%、聚乙烯醇PVA2.6%-2.8%、丙烯酸AA0.3%-1.2%、丙烯酰胺AM0.9%-1.8%、二甘醇二苯甲酸酯DEDB2.2%-4.9%、水55%-68%。具有常温固化、固化较快、粘接强度高、环保无毒等特点,其粘接层具有较好的韧性和耐久性且不易老化。
优选地,所述硅酮胶为中性硅酮耐候胶。能提高接缝剂的粘稠度,增强板材与接缝剂的粘结强度,提高接缝剂的耐候性能。
本发明是一种粘稠状接缝剂,无需添加其他材料,即可应用于纤维水泥平板和纤维增强硅酸钙板该类材料的接缝,接缝施工环境温度一般要求为5℃—40℃之间。
先用毛刷对需要接缝处理的部位进行粉尘清扫,避免因粉尘而造成填缝剂与板材间的粘结力减弱;再将接缝剂填入板缝,同时检查板边的高低差,将其填实刮平,待干燥后再进行后续作业;如果是不同厚度的板材应进行二次填充和干燥,避免接缝部位空洞和凹嵌。
嵌缝内的接缝剂完全干燥后,再进行接缝带的粘贴,贴完接缝带后再涂抹一层接缝剂,每道涂抹的接缝剂应比上一道涂抹的接缝剂宽50-100mm,以保证接缝部位的平整,接缝剂至少需要涂2道以上。
每次填缝处理须在上一道填缝膏完全干燥后方可施工。
本发明应用于纤维水泥平板和纤维增强硅酸钙板此类材料时,克服了纸面石膏板接缝腻子的缺点,具有粘结强度高、防开裂、施工方便、成本低、环保无毒等特点。
具体实施方式
下面结合实施例进一步详细说明本发明的技术方案。
实施例1:
本发明是由以下重量百分比的组分组成:粗石英砂30%、细石英砂20%、重钙粉18.5%、硅酮胶1.5%、白乳胶30%。其中白乳胶由以下重量百分比的组分组成:醋酸乙烯酯VAC26%、聚乙烯醇PVA2.8%、丙烯酸AA0.5%、丙烯酰胺AM1.7%、二甘醇二苯甲酸酯DEDB3%、水66%。
实施例2:
本发明是由以下重量百分比的组分组成:粗石英砂33%、细石英砂16.5%、重钙粉16.5%、硅酮胶1.0%、白乳胶33%。其中白乳胶由以下重量百分比的组分组成:醋酸乙烯酯VAC22.5%、聚乙烯醇PVA2.6%、丙烯酸AA1.2%、丙烯酰胺AM1.2%、二甘醇二苯甲酸酯DEDB4.5%、水68%。
实施例3:
本发明是由以下重量百分比的组分组成:粗石英砂28%、细石英砂15%、重钙粉20%、硅酮胶2.0%、白乳胶35%。其中白乳胶由以下重量百分比的组分组成:醋酸乙烯酯VAC31%、聚乙烯醇PVA2.7%、丙烯酸AA0.3%、丙烯酰胺AM1.1%、二甘醇二苯甲酸酯DEDB4.9%、水60%。
实施例4:
本发明是由以下重量百分比的组分组成:粗石英砂20%、细石英砂25%、重钙粉16%、硅酮胶1.0%、白乳胶38%。其中白乳胶由以下重量百分比的组分组成:醋酸乙烯酯VAC30%、聚乙烯醇PVA2.8%、丙烯酸AA1.2%、丙烯酰胺AM1.8%、二甘醇二苯甲酸酯DEDB2.2%、水62%。
实施例5:
本发明是由以下重量百分比的组分组成:粗石英砂40%、细石英砂15.5%、重钙粉23%、硅酮胶0.5%、白乳胶21%。其中白乳胶由以下重量百分比的组分组成:醋酸乙烯酯VAC31%、聚乙烯醇PVA2.7%、丙烯酸AA0.3%、丙烯酰胺AM1.1%、二甘醇二苯甲酸酯DEDB4.9%、水60%。
以上列举的仅为本发明的具体实施例,显然,本发明不限于以上实施例。本领域的普通技术人员能从本发明公开的内容直接导出或联想到的所有变形,均应属于本发明的保护范围。
Claims (4)
1.一种高强度抗裂接缝剂,其特征在于,所述的高强度抗裂接缝剂由粗石英砂、细石英砂、重钙粉、硅酮胶和白乳胶组成,各组分的重量百分比为:粗石英砂20-40%、细石英砂10-30%、重钙粉10-30%、硅酮胶0.5-2%、白乳胶20-40%,所述白乳胶主要成分为醋酸乙烯酯VAc、聚乙烯醇PVA、丙烯酸AA、丙烯酰胺AM、二甘醇二苯甲酸酯DEDB和水,且各组分的重量百分比为:醋酸乙烯酯VAc22%-31%、聚乙烯醇PVA2.6%-2.8%、丙烯酸AA0.3%-1.2%、丙烯酰胺AM0.9%-1.8%、二甘醇二苯甲酸酯DEDB2.2%-4.9%、水55%-68%。
2.根据权利要求1所述的高强度抗裂接缝剂,其特征在于,所述粗石英砂细度为60目-130目。
3.根据权利要求1所述的高强度抗裂接缝剂,其特征在于,所述细石英砂细度为150目-250目。
4.根据权利要求1或2或3所述的高强度抗裂接缝剂,其特征在于,所述硅酮胶为中性硅酮耐候胶。