CN104382267B - Anti-radiation metal filament fabric manufacturing method and product manufactured by same - Google Patents
Anti-radiation metal filament fabric manufacturing method and product manufactured by same Download PDFInfo
- Publication number
- CN104382267B CN104382267B CN201410555427.8A CN201410555427A CN104382267B CN 104382267 B CN104382267 B CN 104382267B CN 201410555427 A CN201410555427 A CN 201410555427A CN 104382267 B CN104382267 B CN 104382267B
- Authority
- CN
- China
- Prior art keywords
- radiation
- fiber
- metal
- filament fabric
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an anti-radiation metal filament fabric manufacturing method, and also discloses a product manufactured by implementing the same. The product is formed by weaving metal core-spun yarns; each core-spun yarn comprises a metal fiber and a coating layer; the metal fiber is wound by and coated with the coating layer. The anti-radiation metal filament fabric manufacturing method has the advantages that the manufacturing process is simple and easy, and is easy to implement, the anti-radiation metal filament fabric product can be manufactured quickly, is soft and thin, has a good hand feeling, and can be next to the skin to be worn, a metal shielding net formed by the metal core-spun yarns is effectively utilized to shield radiation, and the anti-radiation and anti-static effect is remarkable; the anti-radiation metal filament fabric product can be washed or be folded for use, is washable as common clothing, is convenient and sanitary; moreover, through coloring and dyeing, the flower color of the anti-radiation metal filament fabric product is rich, the processing requirements of different sizes of clothing for different ages of people can be met, and the anti-radiation metal filament fabric product can be widely applicable to industry areas with more radiation, such as petroleum, chemical engineering, post and telecommunications, machine rooms, hospitals and electric undertaking, and facilitates wide popularization and application.
Description
Technical field
The present invention relates to the technical field of warming heating wire, particularly to a kind of long metal fiber radiation-proof fabric making side
Method and its product.
Background technology
With the development further of electrical equipment technology, radiation is seen everywhere around us, like the shadow following the person, no matter being
The mobile phone of work, computer, printer or the microwave oven of domestic, electric blanket, hair-dryer etc. all can produce a certain amount of radiation,
Threat there is is to act on the health of human body, particularly with the weaker old man of resistance and child, the damaging effect of generation is bigger, this
Outward, work in radiation environment for a long time, the symptoms such as insomnia and dreamful sleep, hypoimmunity can be caused, come particularly with pregnant woman
Say, with greater need for radiating close protection, protect fetus, be therefore badly in need of a kind of fabric of height radioprotective, conveniently comprehensively resist
Radiation.
Radiation-proof fabric on the market at present, mainly broken-staple metal fibre and two kinds of silver fiber.
Broken-staple metal fibre is to process fine stainless steel wire together with Cotton Gossypii, then unwrapping wire, woven fabric.This fabric advantage is into
This is low, but shortcoming is obvious: can only wear outward, color single it is impossible to washing, do not inhale ripple it is impossible to wear next to the skin.
Silver fiber is that metal is sprayed onto on fabric, and advantage is that radiation-proof effect is good, and shortcoming is that high cost, fabric be thin, processing
Product is single, oxidizable, can not wash nor wear next to the skin.
Content of the invention
For above-mentioned deficiency, one of the object of the invention is, provides that a kind of manufacturing process is simple, is easily achieved, can be quick
Produce flexibility, radioprotective, anti-static effect is good and can wear next to the skin, can be fine with the equally wash fast metal length of normal laundry
The long metal fiber radiation-proof fabric manufacture method of dimension radiation-proof fabric.
The present invention also aims to, provide a kind of prepared using aforesaid long metal fiber radiation-proof fabric manufacture method
Product.
For achieving the above object, the technical scheme being provided is the present invention:
A kind of long metal fiber radiation-proof fabric manufacture method is it is characterised in that it comprises the steps:
(1) cold drawn: preparation stainless steel silk, processed and be cold drawn to line footpath for 0.02~0.03mm, made stainless steel fibre
Silk;
(2) anneal: by stove, stainless steel fiber is annealed, make the metallic fiber of softness;
(3) cored: metallic fiber is wound coat with Modal fibre or cotton thread, to be formed on metallic fiber surface
Clad, makes metal composite yarn;
(4) weave: by textile machine, metal composite yarn is woven, obtain long metal fiber radiation-proof fabric system
Product.
As a modification of the present invention, model 316rl of described stainless steel silk, line footpath is 0.1mm, described rustless steel
Filametntary line footpath is 0.024~0.025mm.
As a modification of the present invention, described step (1) has specifically included following steps: line footpath is stainless for 0.1mm
Steel wire is through die hole, and spray lubrication liquid carries out being cold drawn to 0.08mm simultaneously;Then prepare corresponding mould cold drawn by 0.08mm
To 0.06mm, then prepare mould and 0.04mm is moved to by 0.06mm, then 0.025mm is moved to by 0.04mm.
As a modification of the present invention, in described step (2), stove is warming up to 950~1100 degree and is annealed.
The product that a kind of above-mentioned long metal fiber radiation-proof fabric manufacture method is made, it is woven by metal composite yarn
Form, described metal composite yarn includes the metallic fiber and voluble wrapping clad on this metallic fiber, this clad by
Modal fibre or cotton thread are entwined, and the line footpath of described metallic fiber is 0.02~0.03mm.
As a modification of the present invention, line footpath 0.025mm of described metallic fiber.Described metallic fiber is by model
316rl, line footpath is made up through cold drawn operation of the stainless steel silk of 0.1mm.
The invention has the benefit that the manufacturing process of method that the present invention provides is simple, be easily achieved, can quick Fabrication
Go out long metal fiber radiation-proof fabric product, this product softness matter is thin, good hand touch, health environment-friendly can wear next to the skin, effectively profit
Form metallic shield net with metal composite yarn come radiation-screening, radioprotective, anti-static effect are notable;Do not affect mobile phone signal,
Solve and take the contradiction that phone is interfered with each other with radiation;And washable or folding use, that is, washable as normal laundry
Wash, convenient, healthy;In addition the clothes of all ages and classes, different model can be met by coloring, printing and dyeing so as to pattern enriches
Decorations processing needs, and can be widely applied to the many industry regions of the radiation such as oil, chemical industry, post and telecommunications, machine room, hospital, electric industry, is beneficial to
Wide popularization and application.
Brief description
Fig. 1 is the cross section structure schematic diagram of metal composite yarn in the present invention.
Specific embodiment
Embodiment: referring to Fig. 1, a kind of long metal fiber radiation-proof fabric manufacture method provided in an embodiment of the present invention, its
Comprise the steps:
(1) cold drawn: preparation stainless steel silk, processed and be cold drawn to line footpath for 0.02~0.03mm, made stainless steel fibre
Silk;Preferably, model 316rl of described stainless steel silk, line footpath is 0.1mm, and the line footpath of described stainless steel fiber is
0.025mm.Specifically, by line footpath for 0.1mm stainless steel silk through die hole, and spray lubrication liquid is cold drawn to simultaneously
0.08mm;Then prepare corresponding mould and 0.06mm be cold drawn to by 0.08mma, then prepare mould and 0.04mm is moved to by 0.06mm,
Again 0.025mm is moved to by 0.04mm.
(2) anneal: be warming up to 950~1100 degree by stove and stainless steel fiber is annealed, make the gold of softness
Belong to fiber 1.
(3) cored: metallic fiber 1 is wound coat with Modal fibre or cotton thread, with metallic fiber 1 surface shape
Become clad 2, make metal composite yarn.
(4) weave: by textile machine, metal composite yarn is woven, obtain long metal fiber radiation-proof fabric system
Product.Textile machine can be the equipment such as circular weaving machine or straight-bar machines.As made looped fabric using circular weaving machine, coat straight-bar machines is weaved cotton cloth, root
Requirement according to clothing needed for oneself and client makes product.
(5) to coloring, printing and dyeing: printed and dyed according to national standard according to the requirement of oneself or client or colour.
(6) clothing: produce the product of corresponding pattern according to the requirement of oneself or client.
The manufacturing process of the method that the present invention provides is simple, be easily achieved, and quick Fabrication can go out long metal fiber radioprotective
Fabric product.
The product that a kind of above-mentioned long metal fiber radiation-proof fabric manufacture method is made, it is woven by metal composite yarn
Form, described metal composite yarn includes the metallic fiber 1 and voluble wrapping clad 2 on this metallic fiber 1, this clad
2 are entwined by Modal fibre or cotton thread, and the line footpath of described metallic fiber 1 is 0.02~0.03mm, preferably 0.025mm.
Above-described embodiment is only the preferable embodiment of the present invention, and the present invention can not enumerate out whole embodiment party
Formula, the technical scheme of all employing above-described embodiments, or the equivalent variations done according to above-described embodiment, all protect model in the present invention
In enclosing.
Long metal fiber radiation-proof fabric product softness matter of the present invention is thin, good hand touch, and health environment-friendly can wear next to the skin,
Effectively utilizes metal composite yarn forms metallic shield net and carrys out radiation-screening, and radioprotective, anti-static effect are notable.Table 1 is anti-spoke
Penetrate detection criteria parameter: (China Shanghai Text Centre)
Frequency (mhm) | p1(dbm) | p2(dbm) | sedb(db) | Se% (%) |
10 | 0.0 | -34.8 | 34.8 | 99.967 |
30 | -0.1 | -34.9 | 34.8 | 99.967 |
100 | -0.2 | -34.8 | 34.6 | 99.965 |
300 | -0.3 | -34.7 | 34.4 | 99.964 |
1000 | -0.4 | -32.76 | 32.42 | 99.940 |
3000 | -0.7 | -31.9 | 31.2 | 99.924 |
The present invention is ingenious to be processed into microfilament by 316rl rustless steel, closes with Modal fibre or cotton thread and is made into yarn, then through spinning
It is made into knitting fabric after the debugging of loom tool, so that metal composite yarn is formed netted, shielded using whole metallic shield net
Radiation, by above-mentioned table 1 it can be seen that long metal fiber radiation-proof fabric of the present invention has preferable radioprotective and static electricity resistance
Can, and good hand touch, can wear next to the skin, also washable or folding uses, i.e. wash resistant as normal laundry conveniently, is defended
Raw;In addition the duds processing need of all ages and classes, different model can be met by coloring, printing and dyeing so as to pattern enriches
Will, can be widely applied to the many industry regions of the radiation such as oil, chemical industry, post and telecommunications, machine room, hospital, electric industry.
The announcement of book and teaching according to the above description, those skilled in the art in the invention can also be to above-mentioned embodiment party
Formula is changed and is changed.Therefore, the invention is not limited in specific embodiment disclosed and described above, to the present invention's
In the scope of the claims that some modifications and changes should also be as fall into the present invention.Although additionally, using in this specification
Some specific terms, but these terms are merely for convenience of description, do not constitute any restriction to the present invention.As the present invention
Described in above-described embodiment, using fabrics other obtained from same or similar step and manufacture method, all in the present invention
In protection domain.
Claims (2)
1. a kind of long metal fiber radiation-proof fabric manufacture method is it is characterised in that it comprises the steps:
(1) cold drawn: preparation stainless steel silk, by line footpath for 0.1mm stainless steel silk through die hole, and spray lubrication liquid is carried out simultaneously
It is cold drawn to 0.08mm;Then prepare corresponding mould and 0.06mm is cold drawn to by 0.08mm, then prepare mould and moved to by 0.06mm
0.04mm, then 0.025mm is moved to by 0.04mm, make stainless steel fiber;Model 316rl of wherein said stainless steel silk;
(2) anneal: by stove, stainless steel fiber is annealed, make the metallic fiber of softness;Wherein stove is warming up to
950-1100 degree is annealed;
(3) cored: metallic fiber is wound coat with Modal fibre or cotton thread, to form cladding on metallic fiber surface
Layer, makes metal composite yarn;
(4) weave: by textile machine, metal composite yarn is woven, obtain long metal fiber radiation-proof fabric product.
2. a kind of product made using the long metal fiber radiation-proof fabric manufacture method described in claim 1, its feature exists
In it is formed by the braiding of metal composite yarn, and it is fine in this metal that described metal composite yarn includes metallic fiber and voluble wrapping
Clad in dimension, this clad is entwined by Modal fibre or cotton thread, and the line footpath of described metallic fiber is 0.025mm.