CN104371208B - Master batch of high-transmittance and high-masking diffusion plate, method for manufacturing master batch and method for manufacturing diffusion plate - Google Patents
Master batch of high-transmittance and high-masking diffusion plate, method for manufacturing master batch and method for manufacturing diffusion plate Download PDFInfo
- Publication number
- CN104371208B CN104371208B CN201410737722.5A CN201410737722A CN104371208B CN 104371208 B CN104371208 B CN 104371208B CN 201410737722 A CN201410737722 A CN 201410737722A CN 104371208 B CN104371208 B CN 104371208B
- Authority
- CN
- China
- Prior art keywords
- temperature
- area
- diffuser plate
- thoroughly
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses master batch of a high-transmittance and high-masking diffusion plate, a method for manufacturing the master batch and a method for manufacturing the diffusion plate. The master batch comprises, by weight, 100 parts of polystyrene, 10-11 parts of organic silicon resin, 0.3-0.4 part of titanium dioxide powder with the particle size of 2-5 micrometers, 0.15-0.2 part of fluorescent brighteners and 0.02-0.025 part of mineral oil. The polystyrene, the organic silicon resin, the titanium dioxide powder, the fluorescent brighteners and the mineral oil are blended with one another and then are squeezed to obtain the master batch, 6.1 parts of the master batch and 100 parts of polystyrene are blended with one another and then are squeezed to obtain mixtures, and the mixtures are further impressed and shaped to obtain the high-transmittance and high-masking diffusion plate. The master batch and the methods have the advantages that the purpose of plastically modifying the master batch mainly can be achieved by diffusion particles by the aid of auxiliary chemical raw materials for color increasing and toughening, accordingly, the diffusion plate has a diffusion function, high-masking effects further can be realized, the transmittance of the diffusion plate can reach 65+/-3%, the haze of the diffusion plate can reach 99%, and the diffusion of the diffusion plate can reach 88+/-5%; the cost of modules further can be reduced while requirements on light weights and thinness of the backlight modules are met.
Description
Technical field
Embodiments of the present invention are related to field of photovoltaic materials, more specifically, embodiments of the present invention are related to a kind of height
The preparation method of high shielding diffuser plate masterbatch, and this masterbatch thoroughly and the method for preparing diffuser plate using the masterbatch.
Background technology
Generally, the backlight module of display device mainly includes that light source, light guide plate, light reflecting board, diffuser plate, brightness strengthen
Film.Wherein, light diffusing sheet has the brightness uniformity made from illuminator launching light simultaneously, and covers the functions such as bright rays, and light
Diffuser plate also functions to support the effect of other optical thin films.Light source in backlight module is generally divided into full run-down type and side light type, directly
Mo(u)ld bottom half is in light sources such as bottom surface of light guide plate cold-cathode tube arranged side by side, LED;Side light type is that the light sources such as cold-cathode tube, LED are configured at leaded light
The edge of plate, light passes through from light-guide edge and lights forward.From from the viewpoint of raising backlight briliancy, based on full run-down type
Stream, but in recent years, because liquid crystal display, LED television etc. are to slimming development, making the ratio of side light type is increasing.Therefore, it is high saturating
The application of high shielding light diffusing sheet will be more extensive.
Polystyrene is because its preferable geometrical stability, heat stability, optics are through characteristic, electrical insulation characteristics and small
Moisture absorption tendency, be widely used in diffuser plate making.It is saturating due to its when non-modified polystyrene is used to make diffuser plate
Light rate is higher, the disability glare of the exposed LED of meeting.At present photodiffusion material, mainly has by the addition in transparent plastic base material
There are the inorganic or organic diffusion particle of different refractivity, including SiO2、TiO2、CaCO2、BaSO4With the inorganic particulate such as glass microballoon
Grain, and the organic polymer microparticles such as polymethyl-benzene e pioic acid methyl ester (PMMA, Polymethylmethacrylate), silicones,
Reach the purpose for improving material mist degree.
Two the key technical indexes for evaluating photodiffusion material are transmitance and mist degree, the mist degree and transmitance of usual material
It is conflicting, traditional photodiffusion material increases the light scattering ability of material and the method for increasing light diffusing agent is usually taken, and
Light diffusing agent can cause the decline of transmitance to absorption and covering of light etc..
The content of the invention
Instant invention overcomes prior art transmitance and mist degree are conflicting, mist degree improves the deficiency that then transmitance is reduced,
A kind of embodiment of the preparation method of high shielding diffuser plate masterbatch and preparation method and diffuser plate is provided, can with expectation
Reduced with solving the problems, such as that diffuser plate mist degree improves then transmitance.
To solve above-mentioned technical problem, one embodiment of the present invention is employed the following technical solutions:
A kind of high high shielding diffuser plate masterbatch thoroughly, it includes following components by weight:
100 parts of polystyrene;
10~11 parts of organic siliconresin;
0.3~0.4 part of titanium dioxide;
0.15~0.2 part of fluorescent whitening agent;
0.02~0.025 part of mineral oil;
The particle diameter of the titanium dioxide is 2~5 microns.
Preferably, the saturating high shielding diffuser plate masterbatch of described height includes following components by weight:
100 parts of polystyrene;
10.56 parts of organic siliconresin;
0.36 part of titanium dioxide;
0.18 part of fluorescent whitening agent;
0.022 part of mineral oil;
The particle diameter of the titanium dioxide is 3~4 microns.
The species and consumption of masterbatch has large effect to the light transmittance and mist degree of diffuser plate, using the former material of aforementioned proportion
Material prepares masterbatch, then the transmitance of the diffuser plate prepared with masterbatch up to 68%, and, up to 99%, diffusance is up to 93% for mist degree.
Fluorescent whitening agent can adopt Stilbene-based brightening agent.Present invention employs the titanium dioxide that particle diameter is 2~5 microns
As the titanium dioxide that inorganic light diffusing agent, particularly particle diameter are 3~4 microns.Just can make when one side titanium white powder content is relatively low
The mist degree of diffuser plate is increased substantially, but transmitance declines very little, on the other hand because the size of titanium dioxide particle diameter is more favourable
In being scattered in base material, and the fragility of polystyrene raw material itself can be overcome, therefore the toughness of diffuser plate can be improved.
Further technical scheme is that the titanium dioxide is that its surface is carried out after blending and modifying by silane coupler
Modified titanium.Silane coupler can form bonding at the interface of organic filler and inorganic particulate, promote interface fusion, strengthen
Performance, can improve dispersibility and bonding force of the titanium dioxide in resin, improve processing performance and improve filled plastics (including poly-
Styrene) the performance such as machinery, electricity and weatherability, while and not loss material mechanical property.
The silane coupler can adopt KH550 (gamma-aminopropyl-triethoxy-silane), KH560 (γ-(+)-2,3-Epoxy-1-propanol
Ether oxygen propyl trimethoxy silicane), KH570 (γ-(methacryloxypropyl) propyl trimethoxy silicane), KH792 (N- (β-ammonia
Ethyl)-γ-aminopropyltrimethoxysilane), any one in DL602, DL171.
Using silane coupler be to the method that titanium dioxide surface carries out blending and modifying by titanium dioxide and silane coupler with
100:1.5 ratio is added in high speed agitator, and high-speed stirred obtains modified titanium in 10 minutes.
Further technical scheme is that the mineral oil is silicone oil or liquid paraffin.Both mineral oil and polyphenyl second
Very well, in the masterbatch course of processing, mineral oil easily migrating between phase and phase in mixture can improve for the compatibility of alkene
Processing and lubrication, and can be distributed on boundary with more uniform.
A kind of preparation method of high shielding diffuser plate masterbatch, it is comprised the following steps:
(1) by 100 parts of polystyrene, 10~11 parts of organic siliconresin, particle diameter is 2~5 microns of titanium dioxide 0.3~0.4
Part, 0.15~0.2 part of fluorescent whitening agent, 0.02~0.025 part of mix homogeneously of mineral oil obtains feedstock blend;The titanium white
Powder is to carry out the modified titanium after blending and modifying to its surface with silane coupler, and the mineral oil is silicone oil (ring-type poly- two
Methylsiloxane) or liquid paraffin.
(2) by the raw mixture, extruding pelletization obtains high thoroughly high shielding diffuser plate mother in double screw extruder
Expect, each section of temperature of the double screw extruder is:One area's temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195
℃;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is
210℃。
Preferably, the preparation method of the saturating high shielding diffuser plate masterbatch of described height is comprised the following steps:
(1) by 100 parts of polystyrene, 10.56 parts of organic siliconresin, particle diameter is 3~4 microns of 0.36 part of titanium dioxide, glimmering
0.18 part of optical brightener, 0.022 part of mix homogeneously of mineral oil, obtains feedstock blend;
(2) by the raw mixture, extruding pelletization obtains high thoroughly high shielding diffuser plate mother in double screw extruder
Expect, each section of temperature of the double screw extruder is:One area's temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195
℃;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is
210℃。
It is a kind of using the above-mentioned high method that thoroughly high shielding diffuser plate masterbatch prepares diffuser plate, it is characterised in that it include with
Lower step:
A, the high high shielding diffuser plate masterbatch thoroughly is dried into 30~60min in drying machine with 60 DEG C of temperature;
B, according to the weight ratio 6.1 of dried high high shielding diffuser plate masterbatch and polystyrene thoroughly:100 incite somebody to action the two
Compound is obtained with double screw extruder extrusion after melt blending, each section of temperature of double screw extruder is:One area's temperature is 175
℃;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are
220℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C;
C, the compound imprinting moulding for obtaining step B, obtain high high shielding diffuser plate thoroughly.
Compared with prior art, one of beneficial effects of the present invention are:The present invention provides a kind of diffuser plate masterbatch, to spread
Based on particle, it is aided with the purpose that the industrial chemicals such as hyperchromic, toughness reinforcing reach modifying plastics, makes diffuser plate that there is the same of diffusion function
When, also with the effect of high shielding, the transmitance of diffuser plate up to 65 ± 3%, mist degree up to 99%, diffusance up to 88 ±
5%.And backlight module is lighter meeting, thinner requirement can also reduce module cost simultaneously.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that specific embodiment described herein is not used to only to explain the present invention
Limit the present invention.
Embodiment 1
By polystyrene 100Kg, organic siliconresin 10Kg, particle diameter is 2 microns of modified titanium 0.3Kg, fluorescent brightening
Agent 0.2Kg, mineral oil 0.025Kg (silicone oil) mix homogeneously, obtains feedstock blend;Then raw mixture is squeezed in twin screw
Go out extruding pelletization in machine and obtain high high shielding diffuser plate masterbatch thoroughly, each section of temperature of the double screw extruder is:One area's temperature
For 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;6th area
Temperature is 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is in drying machine
It is dried with 60 DEG C standby after 30min.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of double screw extruder is:One area's temperature is
175℃;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature
Spend for 220 DEG C;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.
Embodiment 2
By polystyrene 100Kg, organic siliconresin 11Kg, particle diameter is 5 microns of modified titanium 0.4Kg, fluorescent brightening
Agent 0.15Kg, mineral oil 0.02Kg (liquid paraffin) mix homogeneously, obtains feedstock blend;Then by raw mixture in double spiral shells
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in bar extruder, and each section of temperature of the double screw extruder is:One area
Temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;
Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is being dried
It is dried with 60 DEG C in machine standby after 60min.
Double spiral shells will be used after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Bar extruder extrusion obtains compound.Each section of temperature of double screw extruder be:One area's temperature is 175 DEG C;Two area's temperature are 185
℃;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220 DEG C;Seven area's temperature are
215℃;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.
Embodiment 3
By polystyrene 100Kg, organic siliconresin 10.56Kg, particle diameter is 3 microns of titanium dioxide 0.36Kg, fluorescent brightening
Agent 0.18Kg, mineral oil 0.022Kg (silicone oil) mix homogeneously, obtains feedstock blend;Then by raw mixture in twin screw
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in extruder, and each section of temperature of the double screw extruder is:One area's temperature
Spend for 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six
Area's temperature is 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is in drying machine
In be dried with 60 DEG C it is standby after 45min.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;Two
Area's temperature is 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.The transmission of the high high shielding diffuser plate thoroughly of test
Rate, mist degree and diffusance, testing standard such as table 1:
The diffuser plate performance test standard of table 1
Project | Testing standard | Test instrunment |
Light transmittance | JIS K7361-1 | Haze meter (CM-3600A) |
Mist degree | JIS K7136 | |
Uniformity | Luminance test instrument (BM-7) |
Using testing standard and/or instrument in table 1, the transmitance for measuring the diffuser plate of the present embodiment is 67%, mist degree
It is 99%, diffusance is 90%.
Embodiment 4
By polystyrene 100Kg, organic siliconresin 10.56Kg, particle diameter is 4 microns of modified titanium 0.36Kg, fluorescence
Brightening agent 0.18Kg, mineral oil 0.022Kg (silicone oil) mix homogeneously, obtains feedstock blend;Then by raw mixture double
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in screw extruder, and each section of temperature of the double screw extruder is:One
Area's temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210
℃;Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is dry
It is dried with 60 DEG C in dry machine standby after 45min.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;Two
Area's temperature is 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.Testing standard and instrument test using table 1 is high
The thoroughly transmitance of high shielding diffuser plate, mist degree and diffusance, the transmitance for measuring the diffuser plate of the present embodiment is 68%, mist degree
It is 99%, diffusance is 88%.
Embodiment 5
By polystyrene 100Kg, organic siliconresin 10Kg, particle diameter is 5 microns of titanium dioxide 0.4Kg, fluorescent whitening agent
0.2Kg, mineral oil 0.02Kg (liquid paraffin) mix homogeneously, obtains feedstock blend;Then by raw mixture in twin screw
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in extruder, and each section of temperature of the double screw extruder is:One area's temperature
Spend for 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six
Area's temperature is 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is in drying machine
In be dried with 60 DEG C it is standby after 45min.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound,.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;
Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.Testing standard and instrument test using table 1 is high
The thoroughly transmitance of high shielding diffuser plate, mist degree and diffusance, the transmitance for measuring the diffuser plate of the present embodiment is 62%, mist degree
It is 99%, diffusance is 83%.
Comparative example 1
By polystyrene 100Kg, organic siliconresin 10.56Kg, particle diameter is 0.5 micron of titanium dioxide 0.36Kg, and fluorescence increases
White agent 0.18Kg, mineral oil 0.022Kg mix homogeneously obtains feedstock blend;Then by raw mixture in twin-screw extrusion
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in machine, and each section of temperature of the double screw extruder is:One area's temperature is
170℃;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six area's temperature
Spend for 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly in drying machine with
60 DEG C be dried it is standby after 45min.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound,.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;
Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.Testing standard and instrument test using table 1 is high
The thoroughly transmitance of high shielding diffuser plate, mist degree and diffusance, the transmitance for measuring the diffuser plate of the present embodiment is 60%, mist degree
It is 90%, diffusance is 80%.Titanium dioxide change of size causes the hydraulic performance decline of diffuser plate.
Comparative example 2
By polystyrene 95Kg, organic siliconresin 6Kg, particle diameter is 3 microns of titanium dioxide 0.6Kg, fluorescent whitening agent 0.1Kg
Mix homogeneously, does not use mineral oil, obtains feedstock blend;Then by raw mixture in double screw extruder extruding pelletization
High high shielding diffuser plate masterbatch thoroughly is obtained, each section of temperature of the double screw extruder is:One area's temperature is 170 DEG C;Two area's temperature
Spend for 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;Six area's temperature are 220 DEG C;Seven
Area's temperature is 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is dried 45min in drying machine with 60 DEG C
It is standby afterwards.
Obtain extruding after the dried high high shielding diffuser plate masterbatch thoroughly of 6.1Kg and 100Kg polystyrene melt blendings
Obtain compound,.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;
Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.Testing standard and instrument test using table 1 is high
The thoroughly transmitance of high shielding diffuser plate, mist degree and diffusance, the transmitance for measuring the diffuser plate of the present embodiment is 50%, mist degree
It is 85%, diffusance is 85%.Non- mineral oil is subject to larger to titanium dioxide surface blending and modifying, the transmitance and mist degree of diffuser plate
Impact.
Comparative example 3
By polystyrene 100Kg, organic siliconresin 10.56Kg, particle diameter is 4 microns of modified titanium 0.36Kg, fluorescence
Brightening agent 0.18Kg, mineral oil 0.022Kg (silicone oil) mix homogeneously, obtains feedstock blend;Then by raw mixture double
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in screw extruder, and each section of temperature of the double screw extruder is:One
Area's temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210
℃;Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C.High high shielding diffuser plate masterbatch thoroughly is dry
It is dried with 60 DEG C in dry machine standby after 45min.
Extrusion after the dried high high shielding diffuser plate masterbatch thoroughly of 10Kg and 100Kg polystyrene melt blendings is obtained
Compound.The equipment that blending extrusion is used is double screw extruder, and each section of temperature of extruder is:One area's temperature is 175 DEG C;2nd area
Temperature is 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220 DEG C;
Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C.
By compound imprinting moulding, high high shielding diffuser plate thoroughly is obtained final product.Testing standard and instrument test using table 1 is high
The thoroughly transmitance of high shielding diffuser plate, mist degree and diffusance, the transmitance for measuring the diffuser plate of the present embodiment is 60%, mist degree
It is 92%, diffusance is 83%.Therefore, high high shielding diffuser plate masterbatch thoroughly prepares diffuser plate with polystyrene melt blending
When, the mist degree of the comparison diffuser plate of the consumption of the two has considerable influence.
Although reference be made herein to invention has been described for multiple explanatory embodiments of the invention, however, it is to be understood that
Those skilled in the art can be designed that a lot of other modification and embodiment, and these modifications and embodiment will fall in this Shen
Please be within disclosed spirit and spirit.More specifically, in the range of disclosure and claim, can be to master
The building block and/or layout of topic composite configuration carries out various modifications and improvement.Except what is carried out to building block and/or layout
Modification and improvement are outer, and to those skilled in the art, other purposes also will be apparent.
Claims (3)
1. a kind of high high shielding diffuser plate masterbatch thoroughly, it is characterised in that it includes following components by weight:
100 parts of polystyrene;
10~11 parts of organic siliconresin;
0.3~0.4 part of titanium dioxide;
0.15~0.2 part of fluorescent whitening agent;
0.02~0.025 part of silicone oil or liquid paraffin;
The particle diameter of the titanium dioxide is 2~5 microns;The titanium dioxide is to carry out blending and modifying to its surface by silane coupler
Modified titanium afterwards.
2. high high shielding diffuser plate masterbatch thoroughly according to claim 1, it is characterised in that it include by weight with
Lower component:
100 parts of polystyrene;
10.56 parts of organic siliconresin;
0.36 part of titanium dioxide;
0.18 part of fluorescent whitening agent;
0.022 part of silicone oil or liquid paraffin;
The particle diameter of the titanium dioxide is 3~4 microns.
3. a kind of method for preparing diffuser plate, it is characterised in that it is comprised the following steps:
A, by the component mix homogeneously described in claim 1 or 2, obtain feedstock blend;By the raw mixture in double spiral shells
Extruding pelletization obtains high high shielding diffuser plate masterbatch thoroughly in bar extruder, and each section of temperature of the double screw extruder is:One area
Temperature is 170 DEG C;Two area's temperature are 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 200 DEG C;Five area's temperature are 210 DEG C;
Six area's temperature are 220 DEG C;Seven area's temperature are 210 DEG C;Die head temperature is 210 DEG C;
B, the high high shielding diffuser plate masterbatch thoroughly is dried into 30~60min in drying machine with 60 DEG C of temperature;
C, according to the weight ratio 6.1 of dried high high shielding diffuser plate masterbatch and polystyrene thoroughly:100 melt the two
Compound is obtained with double screw extruder extrusion after blending, each section of temperature of double screw extruder is:One area's temperature is 175 DEG C;Two
Area's temperature is 185 DEG C;Three area's temperature are 195 DEG C;Four area's temperature are 215 DEG C;Five area's temperature are 225 DEG C;Six area's temperature are 220
℃;Seven area's temperature are 215 DEG C;Die head temperature is 210 DEG C;
D, the compound imprinting moulding for obtaining step C, obtain high high shielding diffuser plate thoroughly.