CN102372914A - Polycarbonate composition having light diffusion characteristics and preparation method thereof - Google Patents
Polycarbonate composition having light diffusion characteristics and preparation method thereof Download PDFInfo
- Publication number
- CN102372914A CN102372914A CN2010102527533A CN201010252753A CN102372914A CN 102372914 A CN102372914 A CN 102372914A CN 2010102527533 A CN2010102527533 A CN 2010102527533A CN 201010252753 A CN201010252753 A CN 201010252753A CN 102372914 A CN102372914 A CN 102372914A
- Authority
- CN
- China
- Prior art keywords
- polycarbonate
- gma
- possesses
- light diffusion
- pmma
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a polycarbonate composition having light diffusion characteristics and a preparation method thereof. The composition comprises the following ingredients: 90-99.9 weight portions of polycarbonate and 0.1-10 weight portions of light diffusant, prepared by the following steps: uniformly mixing polycarbonate and light diffusant with stirring through a high speed mixer to obtain a mixture, sending the mixture in a double screw extruder through a primary feeding pipe, carrying out extrusion with controlling the length-diameter ratio to 20-90:1, the screw temperature of 200-350 DEG C and the screw rotating speed of 200-700 rpm and pelletizing. Compared with the prior art, the composition prepared by using the coreshell structure of coating organic silicone resin on PMMA-GMA as the light diffusant has the advantages of high light transmittance, highlight diffusion characteristic, no glare, and easy preparation and the like, and can be used in film, sheet material and injection molding.
Description
Technical field
The present invention relates to a kind of polymeric composition and preparation method thereof, especially relate to a kind of polycarbonate compositions that possesses the light diffusion property and preparation method thereof.
Background technology
The internal characteristics of LED has: 1, volume is little, and LED is that a very little wafer is encapsulated in epoxy resin the inside basically, thus its very little, very light; 2, current consumption is low, and the LED power consumption is quite low, and in general the WV of LED is 2-3.6V; Working current is 0.02-0.03A.In other words: the electric energy that it consumes is no more than 0.1W.3, long service life, under appropriate electric current and voltage, can reach 100,000 hours the work-ing life of LED; 4, high brightness, low in calories, LED use the chemiluminescence technology, and thermal value is more much lower than ordinary luminaire; 5, environmental protection, LED is made by nontoxic material, and containing mercury unlike luminescent lamp can pollute, and simultaneously LED also can recycling; 6, sturdy and durable, LED is encapsulated in the epoxy resin the inside completely, and it is all firmer than bulb and fluorescent tube bulb.Also do not have loosening part in the lamp body, it is non-damageable that these characteristics make that LED can be described as.These advantages have determined that it is that optimal light source goes to replace traditional light source, has purposes widely at light-emitting diode display, illumination etc.
But the tangible inferior position that LED exists is a pointolite for it, on Application Areass such as illumination, exists the pointolite of high brightness can have problems such as dazzling, that illuminated area is limited, needs particular design or material that it is become area source and just can use.Traditional solution is: 1, on original transparent glass or resin, increase the frosted design effect, but this design meeting seriously reduces the light penetration of lampshade, makes the characteristics of LED high brightness to manifest; 2, on the Transparent lamp shade basis, increase prismatical design reaching the effect (US566722) of light diffusion, but should design light diffusion effect limited, still can see dazzling LED lamp pearl, and this design still can reduce light printing opacity flow rate, influence efficiency lf illumination; 3, on original lampshade basis, add color and cover, this method light diffusion effect is not obvious, and has a strong impact on transmittance.The polycarbonate material that possesses the light diffusion property becomes the up-to-date material solution of LED lampshade.
The thermoplastic material that JP378106 discloses two kinds of different refractive index of a kind of use is prepared into the film of sea-island structure, possess high transmission rate and high astigmatic characteristic, but its preparation starting material is complicated, and only is confined to film article.CN1249461C discloses a kind of method of using inorganic particulate as light dispersive medium spray painting transparent film, but repeats this method, and its transmittance descends obviously.JP242862 discloses a kind of material that uses ring-type polyolefin resin as the light diffusing agent preparation, and it possesses high transmission rate and high astigmatic characteristic, but ring-type polyolefin resin preparation process is complicated and prepare strict.JP168904 discloses a kind of method of avoiding material birefringence property, but its transmittance descends obviously.
Summary of the invention
The object of the invention is exactly to provide a kind of in order to overcome the defective that above-mentioned prior art exists and possess high transmission rate, high light diffusion property, do not have outstanding light, be simple and easy to prepare and applicable to polycarbonate compositions of characteristics such as film, sheet material and moulding and preparation method thereof.
The object of the invention can be realized through following technical scheme:
A kind of polycarbonate compositions that possesses the light diffusion property is characterized in that, said composition comprises following component and weight part content:
Polycarbonate 90～99.9;
Light diffusing agent 0.1～10.
The matter average molecular weight of described polycarbonate is that the test melting index is 1～85g/10min under 10000～200000,300 ℃.
The matter average molecular weight of described polycarbonate is tested the preferred 3～70g/10min of melting index down for preferred 15000～80000,300 ℃.
Described light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA); This light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating; The silicone resin grafted functional group can be in the methyl or phenyl one or both; The matter average molecular weight of PMMA-GMA resin is 10000～100000, and the matter average molecular weight of silicone resin is 20000～200000.
The refractive index of described light diffusing agent is 1.40～1.59, and particle diameter is 1～10 μ m, the weight ratio of silicone resin and shell PMMA-GMA resin 30: 70～90: 10, and GMA content is 1～15wt% in the PMMA-GMA resin.
The refractive index of described light diffusing agent is preferred 1.42～1.57, preferred 1～5 μ m of particle diameter, preferred 50: 50～80: 20 of the weight ratio of silicone resin and shell PMMA-GMA resin, the preferred 5～10wt% of GMA content in the PMMA-GMA resin.
A kind of preparation method who possesses the polycarbonate compositions of light diffusion property is characterized in that, this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
Polycarbonate 90～99.9,
Light diffusing agent 0.1～10;
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer; Obtain mixture; Send into twin screw extruder by main feeding, control twin screw extruder length-to-diameter ratio is 20～90: 1, and extruder temperature is 200～350 ℃; Screw speed is that 200～700rpm extrudes pelletizing, promptly obtains product.
Described twin screw extruder length-to-diameter ratio preferred 32～45: 1, preferred 220～320 ℃ of extruder temperature, the preferred 250～550rpm of screw speed.
Can also add additive in the described twin screw extruder, the add-on of additive is 0.1～0.3wt% of mixture.
Described additive comprises UV stablizer, thermo-stabilizer, inhibitor, releasing agent or pigment.
Described additive comprises UV stablizer, thermo-stabilizer, inhibitor, releasing agent or pigment.
Compared with prior art; The present invention coats the compsn that the nucleocapsid structure of silicone resin prepares as light diffusing agent and possesses high transmission rate, high light diffusion property, does not have outstanding light, is simple and easy to preparation and applicable to characteristics such as film, sheet material and mouldings through being used in PMMA-GMA, can be applicable to field of liquid crystal light diffusing sheet, optical lens, light guiding plate, light diffusing sheet optical element, street lamp shade or vehicle with and the instead of glass used of building materials etc.
Embodiment
Below in conjunction with specific embodiment the present invention is elaborated.
Embodiment 1～6
Adopt following raw material:
PC-1：LG-DOW?Calibre?200-10；
PC-2：LG-DOW?Calibre?201-30；
L-1:BaSO
4, (Sachtleben, particle diameter are 4 μ m, and refraction coefficient is 1.64);
L-2:EXL5136, ACR class light diffusing agent, (ROHMHAAS, particle diameter are 5 μ m, and refraction coefficient is 1.54);
L-3: organosilicon-PMMA-GMA the light diffusing agent, (liter of Shanghai day; Particle diameter is 2.5 μ m, and refractive index is 1.54);
Additive: IG-1010: IG-168 is 2: 3 a mixture.
Prescription is formed as shown in table 1:
Table 1
Polycarbonate and light diffusing agent are mixed through high-speed mixer; Obtain mixture, send into twin screw extruder, add additive again by main feeding; Control twin screw extruder length-to-diameter ratio is 32: 1; Extruder temperature is 220 ℃, and screw speed is that 250rpm extrudes pelletizing, promptly obtains product.
Comparative Examples 1～4
Raw materials used identical with embodiment 1～6, it specifically fills a prescription as shown in table 2.
Table 2
Polycarbonate and light diffusing agent are mixed through high-speed mixer; Obtain mixture, send into twin screw extruder, add additive again by main feeding; Control twin screw extruder length-to-diameter ratio is 32: 1; Extruder temperature is 220 ℃, and screw speed is that 250rpm extrudes pelletizing, promptly obtains comparative sample.
Embodiment 1～6 and Comparative Examples 1～4 are prepared product detect as follows, detected result is as shown in table 3.
(1) the material transmittance is estimated
At barrel zone temperature is 300 ℃, and die temperature is 80 ℃ of cold cycling, uses high mirror surface mould injection moulding 10 * 10 * 1mm sheet material of center line average roughness as 1.0nm.According to ASTM D1003 standard, use HR-100 test material transmittance.
(2) the material mist degree is estimated
According to ASTM D1003 standard, use the mist degree of HR-100 test 10 * 10 * 1mm sheet material.
(3) the material light diffusing is estimated
10 * 10 * 1mm is placed on 4.5W LED 1cm place, is observing the light diffusion effect over against the light source place, light is even, and no speck is ◎; Light is even, and it is zero that slight speck is arranged; Light inhomogeneous and have obvious speck for *.
Table 3
Embodiment 7
A kind of preparation method who possesses the polycarbonate compositions of light diffusion property, this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
As raw material, wherein the matter average molecular weight of polycarbonate is that the test melting index is 1g/10min under 10000,300 ℃ with 90kg polycarbonate, 10kg light diffusing agent; Light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA), and this light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating, and the silicone resin grafted functional group is a methyl; The matter average molecular weight of PMMA-GMA resin is 10000; The matter average molecular weight of silicone resin is 20000, and the refractive index of light diffusing agent is 1.4, and particle diameter is 1 μ m; The weight ratio of silicone resin and shell PMMA-GMA resin 30: 70, GMA content are 1wt%.
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer, obtain mixture, send into twin screw extruder by main feeding; Control twin screw extruder length-to-diameter ratio is 20: 1; Extruder temperature is 200 ℃, and screw speed is that 200rpm extrudes pelletizing, promptly obtains product.
Embodiment 8
A kind of preparation method who possesses the polycarbonate compositions of light diffusion property, this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
As raw material, wherein the matter average molecular weight of polycarbonate is that the test melting index is 3g/10min under 15000,300 ℃ with 92kg polycarbonate, 8kg light diffusing agent; Light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA), and this light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating, and the silicone resin grafted functional group is a methyl; The matter average molecular weight of PMMA-GMA resin is 20000; The matter average molecular weight of silicone resin is 40000, and the refractive index of light diffusing agent is 1.42, and particle diameter is 3 μ m; The weight ratio of silicone resin and shell PMMA-GMA resin 50: 50, GMA content are 5wt%.
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer, obtain mixture, send into twin screw extruder by main feeding; Add UV stablizer UVNUL MS-40 again; Add-on is the 0.1wt% of mixture, and control twin screw extruder length-to-diameter ratio is 32: 1, and extruder temperature is 220 ℃; Screw speed is that 250rpm extrudes pelletizing, promptly obtains product.
Embodiment 9
A kind of preparation method who possesses the polycarbonate compositions of light diffusion property, this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
With 95kg polycarbonate, 5kg light diffusing agent as raw material; Wherein the matter average molecular weight of polycarbonate is that the test melting index is 70g/10min under 80000,300 ℃, and light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA); This light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating; The silicone resin grafted functional group is a phenyl, and the matter average molecular weight of PMMA-GMA resin is 50000, and the matter average molecular weight of silicone resin is 80000; The refractive index of light diffusing agent is 1.57; Particle diameter is 5 μ m, the weight ratio of silicone resin and shell PMMA-GMA resin 80: 20, and GMA content is 10wt%.
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer, obtain mixture, send into twin screw extruder by main feeding; Add the thermo-stabilizer dibasic lead stearate again; Add-on is the 0.3wt% of mixture, and control twin screw extruder length-to-diameter ratio is 45: 1, and extruder temperature is 320 ℃; Screw speed is that 550rpm extrudes pelletizing, promptly obtains product.
Embodiment 10
A kind of preparation method who possesses the polycarbonate compositions of light diffusion property, this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
With 99.9kg polycarbonate, 0.1g light diffusing agent as raw material; Wherein the matter average molecular weight of polycarbonate is that the test melting index is 85g/10min under 200000,300 ℃, and light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA); This light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating; The silicone resin grafted functional group is methyl and phenyl, and the matter average molecular weight of PMMA-GMA resin is 100000, and the matter average molecular weight of silicone resin is 200000; The refractive index of light diffusing agent is 1.59; Particle diameter is 10 μ m, the weight ratio of silicone resin and shell PMMA-GMA resin 90: 10, and GMA content is 15wt%.
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer, obtain mixture, send into twin screw extruder by main feeding; Add red iron oxide again; Add-on is the 0.3wt% of mixture, and control twin screw extruder length-to-diameter ratio is 90: 1, and extruder temperature is 350 ℃; Screw speed is that 700rpm extrudes pelletizing, promptly obtains product.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; The present invention is not restricted to the described embodiments; That describes in the foregoing description and the specification sheets just explains principle of the present invention; Under the prerequisite that does not break away from spirit and scope of the invention, the present invention also has various changes and modifications, and these variations and improvement all fall in the scope of the invention that requires protection.The present invention requires protection domain to be defined by appending claims and equivalent thereof.
Claims (10)
1. a polycarbonate compositions that possesses the light diffusion property is characterized in that, said composition comprises following component and weight part content:
Polycarbonate 90～99.9;
Light diffusing agent 0.1～10.
2. a kind of polycarbonate compositions that possesses the light diffusion property according to claim 1 is characterized in that, the matter average molecular weight of described polycarbonate is that the test melting index is 1～85g/10min under 10000～200000,300 ℃.
3. a kind of polycarbonate compositions that possesses the light diffusion property according to claim 1 and 2 is characterized in that, the matter average molecular weight of described polycarbonate is tested the preferred 3～70g/10min of melting index down for preferred 15000～80000,300 ℃.
4. a kind of polycarbonate compositions that possesses the light diffusion property according to claim 1; It is characterized in that; Described light diffusing agent is the multipolymer of silicone resin grafting polymethyl acrylate-glycidyl ester (PMMA-GMA); This light diffusing agent is the nucleocapsid structure of the silicone resin of PMMA-GMA coating; The silicone resin grafted functional group can be in the methyl or phenyl one or both, and the matter average molecular weight of PMMA-GMA resin is 10000～100000, and the matter average molecular weight of silicone resin is 20000～200000.
5. a kind of polycarbonate compositions that possesses the light diffusion property according to claim 4; It is characterized in that; The refractive index of described light diffusing agent is 1.40～1.59; Particle diameter is 1～10 μ m, the weight ratio of silicone resin and shell PMMA-GMA resin 30: 70～90: 10, and GMA content is 1～15wt% in the PMMA-GMA resin.
6. a kind of polycarbonate compositions that possesses the light diffusion property according to claim 5; It is characterized in that; The refractive index of described light diffusing agent preferred 1.42～1.57; Preferred 1～5 μ m of particle diameter, preferred 50: 50～80: 20 of the weight ratio of silicone resin and shell PMMA-GMA resin, the preferred 5～10wt% of GMA content in the PMMA-GMA resin.
7. preparation method who possesses the polycarbonate compositions of light diffusion property as claimed in claim 1 is characterized in that this method may further comprise the steps:
(1) prepare raw material according to following component and weight part content:
Polycarbonate 90～99.9,
Light diffusing agent 0.1～10;
(2) polycarbonate and light diffusing agent are mixed through high-speed mixer; Obtain mixture; Send into twin screw extruder by main feeding, control twin screw extruder length-to-diameter ratio is 20～90: 1, and extruder temperature is 200～350 ℃; Screw speed is that 200～700rpm extrudes pelletizing, promptly obtains product.
8. a kind of preparation method who possesses the polycarbonate compositions of light diffusion property according to claim 7; It is characterized in that; Described twin screw extruder length-to-diameter ratio preferred 32～45: 1, preferred 220～320 ℃ of extruder temperature, the preferred 250～550rpm of screw speed.
9. a kind of preparation method who possesses the polycarbonate compositions of light diffusion property according to claim 7 is characterized in that, can also add additive in the described twin screw extruder, and the add-on of additive is 0.1～0.3wt% of mixture.
10. a kind of preparation method who possesses the polycarbonate compositions of light diffusion property according to claim 7 is characterized in that described additive comprises UV stablizer, thermo-stabilizer, inhibitor, releasing agent or pigment.