CN104358138A - 一种具有美容功效的棉纤维及其制作方法 - Google Patents
一种具有美容功效的棉纤维及其制作方法 Download PDFInfo
- Publication number
- CN104358138A CN104358138A CN201410542395.8A CN201410542395A CN104358138A CN 104358138 A CN104358138 A CN 104358138A CN 201410542395 A CN201410542395 A CN 201410542395A CN 104358138 A CN104358138 A CN 104358138A
- Authority
- CN
- China
- Prior art keywords
- parts
- cotton fiber
- fiber
- minute
- butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有美容功效的棉纤维，其特征在于，由下列重量份的原料制成：彩棉纤维25-35、亚麻纤维10-13、天丝纤维11-14、木纤维7-9、蓖麻油4-7、硝酸钾1-2、纳米TiO22.1-3.5、柔软剂VS1.1-2.3、脂肪酸甲酯10-15、乙二醇18-21、对苯二甲酸二甲酯16-18、芦荟5-7、黄连2-5、白茅根3-4、1-丁基-3-乙基咪唑磷酸二丁酯100-120、1-丁基-3-甲基咪唑乙酸盐120-130、助剂4-7、适量水；本发明优化了生产工艺和配方，添加多种动植物纤维，不仅改善了天然棉纤维各项性能指标还具有美容养颜、抗菌防螨、手感滑腻等功效，可广泛应用于美容面膜、美容毛巾等领域。
Description
技术领域
本发明涉及纺织材料技术领域，具体涉及一种具有美容功效的棉纤维及其制作方法。
背景技术
棉纤维是锦葵科棉属植物的种籽上被覆的纤维，又称棉花，简称棉，是我国纺织工业的主要原料。棉纤维制品吸湿和透气性好、耐磨耐洗、柔软而保暖，冬季穿着保暖性好，夏季穿着透气凉爽，广泛用于服装面料、装饰织物等领域。
然而在现有技术中棉纤维由于其存在诸多缺陷使其应用受到了限制。比如棉纤维制品易受微生物作用，容易被细菌、霉菌侵蚀，抗菌防霉效果不显著；棉纤维本身抗紫外线能力差，使得其制作夏季服装会导致皮肤产生色素沉淀甚至会引发皮肤癌；棉纤维阻燃效果差，由此引起的火灾隐患呈上升趋势······。为克服现有技术的不足，有必要对天然棉纤维加以改性，从而制得适合现代人对于棉纤维制品的不同需求的具有成本低、功能多元化、阻燃、强度高、杀菌抗紫外线、防辐射等功能的棉纤维。
发明内容
本发明的目的就是提供一种具有美容功效的棉纤维及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种具有美容功效的棉纤维，其特征在于，由下列重量份的原料制成：彩棉纤维25-35、亚麻纤维10-13、天丝纤维11-14、木纤维7-9、蓖麻油4-7、硝酸钾1-2、纳米TiO22.1-3.5、柔软剂VS 1.1-2.3、脂肪酸甲酯10-15、乙二醇18-21、对苯二甲酸二甲酯16-18、芦荟5-7、黄连2-5、白茅根3-4、1-丁基-3-乙基咪唑磷酸二丁酯100-120、1-丁基-3-甲基咪唑乙酸盐120-130、助剂4-7、适量水。
所述的助剂由下列重量份原料制成：二乙烯三胺1-2、环氧氯丙烷3-6、乙二醛7-9、乙二醇12-14、聚六亚甲基胍0.4-0.7、氢化松香1.2-2.5、柠檬酸钠2.1-2.6、烷基磷酸酯5-7、脂肪醇聚氧乙烯醚6-8、纳米二氧化硅2-3，其制备方法是将纳米二氧化硅在蒸馏水中室温溶胀23小时，形成悬浮液，然后把二乙烯三胺、环氧氯丙烷、乙二醛、乙二醇、烷基磷酸酯、脂肪醇聚氧乙烯醚混合搅拌并升温至140-160℃搅拌1-2小时，加入到上述悬浮液中搅拌30-40分钟，再加入其他剩余成分强烈搅拌2-3小时即得。
所述的一种具有美容功效的棉纤维的制备方法，其特征在于包括以下步骤：
（1）取黄连、白茅根加水煎煮4-6小时，过滤，冷却后往滤液中加入芦荟倒入料理机中打成汁，放入彩棉纤维、亚麻纤维、天丝纤维、木纤维浸泡7-10小时，过滤烘干后放入磨粉机中磨成80-100目粉末；
（2）将上述中药滤渣烘干放入炭化炉中炭化30-40分钟，研磨成粉并喷入蓖麻油，加入脂肪酸甲酯、乙二醇、对苯二甲酸二甲酯一起放入反应釜中搅拌混匀，升温至180-210℃，保持温度搅拌2-3小时；
（3）将步骤（1）反应产物置于步骤（2）中浸泡15-20分钟，轧压10-15分钟，水蒸气处理5-10分钟，清洗并烘干；
（4）称取1-丁基-3-乙基咪唑磷酸二丁酯、1-丁基-3-甲基咪唑乙酸盐投入反应釜中搅拌混匀，加入步骤（3）产物搅拌20-40分钟，加热到100-115℃，再加入其它剩余成分搅拌反应40-60分钟，制得纺丝原液，最后将制得的纺丝原液进行纺丝、卷绕、集束、拉伸即得。
本发明有以下有益效果：本发明优化了生产工艺和配方，添加多种动植物纤维，不仅改善了天然棉纤维各项性能指标还具有美容养颜、抗菌防螨、手感滑腻等功效，可广泛应用于美容面膜、美容毛巾等领域。
具体实施方式
所述的一种具有美容功效的棉纤维，其特征在于，由下列重量份的原料制成：彩棉纤维27、亚麻纤维12、天丝纤维13、木纤维8、蓖麻油6、硝酸钾1、纳米TiO22.5、柔软剂VS 1.4、脂肪酸甲酯13、乙二醇19、对苯二甲酸二甲酯17、芦荟7、黄连2、白茅根4、1-丁基-3-乙基咪唑磷酸二丁酯100、1-丁基-3-甲基咪唑乙酸盐126、助剂7、适量水。
所述的助剂由下列重量份原料制成：二乙烯三胺1、环氧氯丙烷5、乙二醛8、乙二醇13、聚六亚甲基胍0.5、氢化松香1.6、柠檬酸钠2.5、烷基磷酸酯6、脂肪醇聚氧乙烯醚8、纳米二氧化硅3，其制备方法是将纳米二氧化硅在蒸馏水中室温溶胀23小时，形成悬浮液，然后把二乙烯三胺、环氧氯丙烷、乙二醛、乙二醇、烷基磷酸酯、脂肪醇聚氧乙烯醚混合搅拌并升温至140-160℃搅拌1-2小时，加入到上述悬浮液中搅拌30-40分钟，再加入其他剩余成分强烈搅拌2-3小时即得。
制作方法包括以下步骤：
（1）取黄连、白茅根加水煎煮4-6小时，过滤，冷却后往滤液中加入芦荟倒入料理机中打成汁，放入彩棉纤维、亚麻纤维、天丝纤维、木纤维浸泡7-10小时，过滤烘干后放入磨粉机中磨成80-100目粉末；
（2）将上述中药滤渣烘干放入炭化炉中炭化30-40分钟，研磨成粉并喷入蓖麻油，加入脂肪酸甲酯、乙二醇、对苯二甲酸二甲酯一起放入反应釜中搅拌混匀，升温至180-210℃，保持温度搅拌2-3小时；
（3）将步骤（1）反应产物置于步骤（2）中浸泡15-20分钟，轧压10-15分钟，水蒸气处理5-10分钟，清洗并烘干；
（4）称取1-丁基-3-乙基咪唑磷酸二丁酯、1-丁基-3-甲基咪唑乙酸盐投入反应釜中搅拌混匀，加入步骤（3）产物搅拌20-40分钟，加热到100-115℃，再加入其它剩余成分搅拌反应40-60分钟，制得纺丝原液，最后将制得的纺丝原液进行纺丝、卷绕、集束、拉伸即得。
使用本发明生产的棉纤维的技术参数指标如下：
（1）柔软度蓬松滑爽有弹性，强度高、阻燃效果优；
（2）成品对大肠杆菌、金黄色葡萄球菌、白色念珠菌的抑菌率均大于97%；
（3）经30次洗涤后，抗菌率仍然达到92%。
Claims (2)
1.一种具有美容功效的棉纤维，其特征在于，由下列重量份的原料制成：彩棉纤维25-35、亚麻纤维10-13、天丝纤维11-14、木纤维7-9、蓖麻油4-7、硝酸钾1-2、纳米TiO22.1-3.5、柔软剂VS 1.1-2.3、脂肪酸甲酯10-15、乙二醇18-21、对苯二甲酸二甲酯16-18、芦荟5-7、黄连2-5、白茅根3-4、1-丁基-3-乙基咪唑磷酸二丁酯100-120、1-丁基-3-甲基咪唑乙酸盐120-130、助剂4-7、适量水；所述的助剂由下列重量份原料制成：二乙烯三胺1-2、环氧氯丙烷3-6、乙二醛7-9、乙二醇12-14、聚六亚甲基胍0.4-0.7、氢化松香1.2-2.5、柠檬酸钠2.1-2.6、烷基磷酸酯5-7、脂肪醇聚氧乙烯醚6-8、纳米二氧化硅2-3，其制备方法是将纳米二氧化硅在蒸馏水中室温溶胀23小时，形成悬浮液，然后把二乙烯三胺、环氧氯丙烷、乙二醛、乙二醇、烷基磷酸酯、脂肪醇聚氧乙烯醚混合搅拌并升温至140-160℃搅拌1-2小时，加入到上述悬浮液中搅拌30-40分钟，再加入其他剩余成分强烈搅拌2-3小时即得。
2.根据权利要求1所述的一种具有美容功效的棉纤维的制作方法，其特征在于包括以下步骤：
（1）取黄连、白茅根加水煎煮4-6小时，过滤，冷却后往滤液中加入芦荟倒入料理机中打成汁，放入彩棉纤维、亚麻纤维、天丝纤维、木纤维浸泡7-10小时，过滤烘干后放入磨粉机中磨成80-100目粉末；
（2）将上述中药滤渣烘干放入炭化炉中炭化30-40分钟，研磨成粉并喷入蓖麻油，加入脂肪酸甲酯、乙二醇、对苯二甲酸二甲酯一起放入反应釜中搅拌混匀，升温至180-210℃，保持温度搅拌2-3小时；
（3）将步骤（1）反应产物置于步骤（2）中浸泡15-20分钟，轧压10-15分钟，水蒸气处理5-10分钟，清洗并烘干；
（4）称取1-丁基-3-乙基咪唑磷酸二丁酯、1-丁基-3-甲基咪唑乙酸盐投入反应釜中搅拌混匀，加入步骤（3）产物搅拌20-40分钟，加热到100-115℃，再加入其它剩余成分搅拌反应40-60分钟，制得纺丝原液，最后将制得的纺丝原液进行纺丝、卷绕、集束、拉伸即得。