CN104357855A - 一种金属油污表面清洗剂及其制备方法 - Google Patents
一种金属油污表面清洗剂及其制备方法 Download PDFInfo
- Publication number
- CN104357855A CN104357855A CN201410622194.9A CN201410622194A CN104357855A CN 104357855 A CN104357855 A CN 104357855A CN 201410622194 A CN201410622194 A CN 201410622194A CN 104357855 A CN104357855 A CN 104357855A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- greasy dirt
- metal
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金属油污表面清洗剂,其特征是由下述重量份的原料制得:麦饭石粉8-10,月桂醇磺基琥珀酸酯二钠3-5,月桂醇聚醚硫酸酯钠2-4,甲基异噻唑啉酮0.1-0.2,海藻胶1-2,果胶0.3-0.5,魔芋葡甘聚糖1-2,玉米蛋白粉0.3-0.5,磷酸二氢钙0.5-1,碳酸氢钠0.3-0.5,酒石酸钾钠1-2,助剂3-5,水40-50。本发明的金属表面清洗剂具有强力清洗金属表面油污的作用,适用于清洗表面油污较重的金属材料以及工件,去油污效力强,且不造成二次污染,对材料表面性质的影响小。
Description
技术领域
本发明涉及金属处理领域,具体涉及一种金属油污表面清洗剂及其制备方法。
背景技术
金属及其制品在加工过程中常会在表面沾染各种污物和杂质,如不能及时清除,将会影响下一道工序的加工效果,进而影响到产品的整体性能。金属表面清洗剂的主要作用就是清洗金属材料表面油、蜡、锈、胶、漆、粉、积碳、手印、汗渍、切削液及其它污物。传统的金属表面清洗剂常为溶剂型,成本高、毒性大、安全性低且环境污染大。研制并推广应用环保、安全、高效的水基表面活性剂型金属表面清洗剂,已经成为大势所趋。
发明内容
本发明的目的是提供一种金属油污表面清洗剂。
本发明是通过以下技术方案实现的:
一种金属油污表面清洗剂,其特征在于,其是由下述重量份的原料制得:
麦饭石粉8-10,月桂醇磺基琥珀酸酯二钠3-5,月桂醇聚醚硫酸酯钠2-4,甲基异噻唑啉酮0.1-0.2,海藻胶1-2,果胶0.3-0.5,魔芋葡甘聚糖1-2,玉米蛋白粉0.3-0.5,磷酸二氢钙0.5-1,碳酸氢钠0.3-0.5,酒石酸钾钠1-2,助剂3-5,水40-50
其中助剂由下列重量份的原料制成:
葡萄皮渣15-20,草酸2-4,柠檬酸2-4,三聚磷酸钠1-2,丙二醇3-5,壬基酚聚氧乙烯醚1-2,石英粉1-2,水20-30;
助剂的制备方法是:
将葡萄皮渣与1/3-1/2量的水混合后搅拌均匀,超声处理0.5-1h,再加入草酸、柠檬酸、三聚磷酸钠和丙二醇200-400r/min、60-80℃处理12-24h,过滤后将滤渣与余量的水混合,加入壬基酚聚氧乙烯醚和石英粉1000-1200r/min、60-80℃处理6-8h,再次过滤并将两次得到的滤液合并,将pH调至中性,即得。
一种金属油污表面清洗剂的制备方法,其特征在于,包括以下步骤:
(1)将麦饭石粉、魔芋葡甘聚糖和玉米蛋白粉混合后研磨1-2h,再加入1/5-1/4量的水,先超声分散10-15min,再8000-10000r/min高速匀浆15-30min,得A组分;
(2)将月桂醇磺基琥珀酸酯二钠、月桂醇聚醚硫酸酯钠和甲基异噻唑啉酮加入余量的水中800-1000r/min搅拌5-10min,再加入海藻胶和果胶60-80℃、同样转速下搅拌20-30min,得B组分;
(3)将A组分、B组分和其余原料混合后800-1000r/min搅拌15-30min,分装后即得。
本发明的优点是:
1. 通过配方与工艺的改进,增强了产品对金属表面油污的清洗作用,适用于清洗表面油污较重的金属材料以及工件,去油污效力强,且不造成二次污染,对材料表面性质的影响小;
2. 通过添加麦饭石粉能有效吸附附着在金属表面的油污,既缩短了清洗时间,又使清洗更加彻底;且在金属清洁剂废水排放时能通过离心、过滤等方式分离大部分污染物,有利于减轻污水处理负担,更易达到排放标准。
具体实施方式
本发明非限定实施例如下:
一种金属油污表面清洗剂,由下列重量(kg)的组分原料制备而成:
麦饭石粉9,月桂醇磺基琥珀酸酯二钠4,月桂醇聚醚硫酸酯钠3,甲基异噻唑啉酮0.15,海藻胶1.5,果胶0.4,魔芋葡甘聚糖1.5,玉米蛋白粉0.4,磷酸二氢钙0.8,碳酸氢钠0.4,酒石酸钾钠1.5,助剂4,水45;
其中,助剂由下列重量(kg)的原料制成:
葡萄皮渣18,草酸3,柠檬酸3,三聚磷酸钠1.5,丙二醇4,壬基酚聚氧乙烯醚1.5,石英粉1.5,水25;
助剂的制备方法:
将葡萄皮渣与1/2量的水混合后搅拌均匀,超声处理0.5h,再加入草酸、柠檬酸、三聚磷酸钠和丙二醇400r/min、80℃处理24h,过滤后将滤渣与余量的水混合,加入壬基酚聚氧乙烯醚和石英粉1200r/min、60℃处理8h,再次过滤并将两次得到的滤液合并,将pH调至中性,即得。
金属油污表面清洗剂的制备方法包括以下步骤:
(1)将麦饭石粉、魔芋葡甘聚糖和玉米蛋白粉混合后研磨2h,再加入1/5量的水,先超声分散10min,再8000r/min高速匀浆15min,得A组分;
(2)将月桂醇磺基琥珀酸酯二钠、月桂醇聚醚硫酸酯钠和甲基异噻唑啉酮加入余量的水中1000r/min搅拌5min,再加入海藻胶和果胶80℃、同样转速下搅拌20min,得B组分;
(3)将A组分、B组分和其余原料混合后1000r/min搅拌15min,分装后即得。
经检验,本实施例的清洗剂油污清洗率≥98%。
Claims (2)
1.一种金属油污表面清洗剂,其特征在于,其是由下述重量份的原料制得:
麦饭石粉8-10,月桂醇磺基琥珀酸酯二钠3-5,月桂醇聚醚硫酸酯钠2-4,甲基异噻唑啉酮0.1-0.2,海藻胶1-2,果胶0.3-0.5,魔芋葡甘聚糖1-2,玉米蛋白粉0.3-0.5,磷酸二氢钙0.5-1,碳酸氢钠0.3-0.5,酒石酸钾钠1-2,助剂3-5,水40-50;
所述助剂由下列重量份的原料制成:
葡萄皮渣15-20,草酸2-4,柠檬酸2-4,三聚磷酸钠1-2,丙二醇3-5,壬基酚聚氧乙烯醚1-2,石英粉1-2,水20-30;
所述助剂的制备方法是:
将葡萄皮渣与1/3-1/2量的水混合后搅拌均匀,超声处理0.5-1h,再加入草酸、柠檬酸、三聚磷酸钠和丙二醇200-400r/min、60-80℃处理12-24h,过滤后将滤渣与余量的水混合,加入壬基酚聚氧乙烯醚和石英粉1000-1200r/min、60-80℃处理6-8h,再次过滤并将两次得到的滤液合并,将pH调至中性,即得。
2.根据权利要求1所述的一种金属油污表面清洗剂的制备方法,其特征在于,包括以下步骤:
(1)将麦饭石粉、魔芋葡甘聚糖和玉米蛋白粉混合后研磨1-2h,再加入1/5-1/4量的水,先超声分散10-15min,再8000-10000r/min高速匀浆15-30min,得A组分;
(2)将月桂醇磺基琥珀酸酯二钠、月桂醇聚醚硫酸酯钠和甲基异噻唑啉酮加入余量的水中800-1000r/min搅拌5-10min,再加入海藻胶和果胶60-80℃、同样转速下搅拌20-30min,得B组分;
(3)将A组分、B组分和其余原料混合后800-1000r/min搅拌15-30min,分装后即得。