CN104356736A - 多彩柔性砖中专用腻子层的制备方法 - Google Patents
多彩柔性砖中专用腻子层的制备方法 Download PDFInfo
- Publication number
- CN104356736A CN104356736A CN201410675193.0A CN201410675193A CN104356736A CN 104356736 A CN104356736 A CN 104356736A CN 201410675193 A CN201410675193 A CN 201410675193A CN 104356736 A CN104356736 A CN 104356736A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- base
- layer
- flexible brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多彩柔性砖中专用腻子层的制备方法,包括A基料的制备,B基料的制备,C基料的制备,B基料和C基料的混合形成专用的腻子,将专用的腻子批刮到保护层和网格布层上形成专用腻子层,再在专用腻子层上制备涂料层,即可制得多彩柔性砖。本发明制备的多彩柔性砖不仅牢固、不易破损,而且柔韧性高、遮盖裂纹能力强,可有效起到美化装饰效果。本发明制备的多彩柔性砖可以作为卷材保存,存储空间缩小,大大节约了储存成本和运输成本。
Description
技术领域
本发明涉及一种腻子层的制备方法,具体是一种多彩柔性砖中专用腻子层的制备方法。
背景技术
目前,市面上的多彩柔性砖一类的产品还较少。由于现有的多彩柔性砖的柔韧性不足,容易出现开裂等问题,尤其现有的多彩柔性砖不能作为卷材进行保存,使得其占地面积较大,增加了存储成本和运输成本。现有多彩柔性砖的这些问题大大降低了消费者的购买欲。
发明内容
本发明的目的在于提供一种多彩柔性砖中专用腻子层的制备方法,通过柔性硅乳液进行配制的高柔韧性的腻子,使得柔性砖不仅牢固,而且可作为卷材进行保存。
为实现上述目的,本发明提供如下技术方案:
一种多彩柔性砖中专用腻子层的制备方法,具体包括以下步骤:
1)A基料的制备:采用20份纤维素加入到970份水中,高速搅拌30min,加入6份多功能助剂AMP-95和4份杀菌剂得到A基料;
2)B基料的制备:将200份A基料、300份柔性硅乳液、6份分散剂、4份润湿剂、2份杀菌剂、175份重钙、300份石英砂、10份成膜助剂和3份消泡剂混合均匀后,高速分散30min得到B基料;
3)C基料的制备:将600份乳液、380份水和20份助剂混合均匀得到C基料;
4)将B基料和C基料按一定的比例混合,搅拌5min后就形成了这种专用的腻子;
5)准备好保护层和网格布层,将制备好的腻子批刮上去,养护干燥形成腻子层;
6)在腻子层上制备涂料层,即可制得多彩柔性砖。
作为本发明进一步的方案:所述步骤(1)中,成膜助剂为乙二醇、丙二醇、丙二醇苯醚、十二碳醇酯中的一种或几种的混合物。
作为本发明进一步的方案:所述步骤(1)中,A基料的制备过程中,至少搅拌30min。
作为本发明进一步的方案:所述步骤(1)中,B基料的制备过程中,至少搅拌30min。
作为本发明进一步的方案:所述步骤(1)中,C基料的制备过程中,低速搅拌5min。
与现有技术相比,本发明的有益效果是:本发明制备的多彩柔性砖不仅牢固、不易破损,而且柔韧性高、遮盖裂纹能力强,可有效起到美化装饰效果。本发明制备的多彩柔性砖可以作为卷材保存,存储空间缩小,大大节约了储存成本和运输成本。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
本发明实施例中,一种多彩柔性砖中专用腻子层的制备方法,具体包括以下步骤:
1)A基料的制备:采用20份纤维素加入到970份水中,高速搅拌30min,加入6份多功能助剂AMP-95和4份杀菌剂得到A基料;
2)B基料的制备:将200份A基料、300份柔性硅乳液、6份分散剂、4份润湿剂、2份杀菌剂、175份重钙、300份石英砂、10份成膜助剂和3份消泡剂混合均匀后,高速分散30min得到B基料;
3)C基料的制备:将600份乳液、380份水和20份助剂混合均匀得到C基料;
4)将B基料和C基料按一定的比例混合,搅拌5min后就形成了这种专用的腻子;
5)准备好保护层和网格布层,将制备好的腻子批刮上去,养护干燥形成腻子层;
6)在腻子层上制备涂料层,即可制得多彩柔性砖。
将制作成的专用腻子按照GB/T23455-2009的标准进行检验,具体检测结果如下表所示:由表中可知,本发明制作成的专用腻子混合后均匀、无结块,刮涂无障碍、无打卷,初期干燥无裂纹;本发明制作成的专用腻子的干燥时间快、磨耗值大,比GB/T23455-2009的标准规定的技术指标高出一倍左右;本发明制作成的专用腻子与柔性砖的拉伸粘接强度,如标准状态、浸水处理、冻融循环处理等指标均高于GB/T23455-2009的标准规定的技术指标;本发明制作成的专用腻子的柔韧性,如标准状态、冷热循环5次的指标均达到GB/T23455-2009的标准。因此,本发明制作成的专用腻子的全部项目都检测合格,特别是按照GB/T 1748的标准进行检测的结果非常好。采用本发明制备的专用腻子制成的多彩柔性砖的柔韧性非常好,做成卷材后储存,没有发现表面开裂的情况,牢固性也比较优异,不易破损。
本发明制备的多彩柔性砖不仅牢固、不易破损,而且柔韧性高、遮盖裂纹能力强,可有效起到美化装饰效果。本发明制备的多彩柔性砖可以作为卷材保存,存储空间缩小,大大节约了储存成本和运输成本。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种多彩柔性砖中专用腻子层的制备方法,其特征在于,具体包括以下步骤:
1)A基料的制备:采用20份纤维素加入到970份水中,高速搅拌30min,加入6份多功能助剂AMP-95和4份杀菌剂得到A基料;
2)B基料的制备:将200份A基料、300份柔性硅乳液、6份分散剂、4份润湿剂、2份杀菌剂、175份重钙、300份石英砂、10份成膜助剂和3份消泡剂混合均匀后,高速分散30min得到B基料;
3)C基料的制备:将600份乳液、380份水和20份助剂混合均匀得到C基料;
4)将B基料和C基料按一定的比例混合,搅拌5min后就形成了这种专用的腻子;
5)准备好保护层和网格布层,将制备好的腻子批刮上去,养护干燥形成腻子层;
6)在腻子层上制备涂料层,即可制得多彩柔性砖。
2.根据权利要求1所述的多彩柔性砖中专用腻子层的制备方法,其特征在于,所述步骤(1)中,成膜助剂为乙二醇、丙二醇、丙二醇苯醚、十二碳醇酯中的一种或几种的混合物。
3.根据权利要求1所述的多彩柔性砖中专用腻子层的制备方法,其特征在于,所述步骤(1)中,A基料的制备过程中,至少搅拌30min。
4.根据权利要求1所述的多彩柔性砖中专用腻子层的制备方法,其特征在于,所述步骤(1)中,B基料的制备过程中,至少搅拌30min。
5.根据权利要求1所述的多彩柔性砖中专用腻子层的制备方法,其特征在于,所述步骤(1)中,C基料的制备过程中,低速搅拌5min。