CN104342254B - High wear-resistant type knitting machine oil composition and application thereof - Google Patents
High wear-resistant type knitting machine oil composition and application thereof Download PDFInfo
- Publication number
- CN104342254B CN104342254B CN201410494831.9A CN201410494831A CN104342254B CN 104342254 B CN104342254 B CN 104342254B CN 201410494831 A CN201410494831 A CN 201410494831A CN 104342254 B CN104342254 B CN 104342254B
- Authority
- CN
- China
- Prior art keywords
- knitting machine
- wear
- machine oil
- ester
- resistant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of high wear-resistant type knitting machine oil composition and application thereof, mainly solves the problem of knitting needle, syringe and three corner wears that prior art has knitting equipment, knitting machine oil wear resistence difference.The present invention is made up of following component by using being counted with parts by weight：A) 0.2~1 part of extreme pressure anti-wear additives；B) 0.2~3 part of emulsifying agent；C) 0.1~1 part of antioxidant；D) 0.05~0.3 part of antirust agent；E) technical scheme of 95~99 parts of base oil preferably solves the problem, the lubrication available for high speed circular cyiinder knitting machine seamless knitting equipment.
Description
Technical field
The present invention relates to a kind of high wear-resistant type knitting machine oil composition and application thereof.
Background technology
With electronics, the continuous progress of industrial technology such as automatically control, knitting is also to automatic, high-speed and high-efficiency direction
Development, but the thing followed is the increased wear of knitting needle and syringe, temperature rise, therefore modern knitting equipment is especially without suture needle
Lubricity and cooling requirement of the loom to knitting machine oil proposes higher requirement.The quality of knitting machine oil quality directly affects
To the service life of knitting needle and the quality of product.But existing market upper inlet knitting machine oil price, and domestic knitting machine oil resists
Poor-performing is ground, corrodes machine parts, easy the shortcomings of polluting fabric.
Therefore, must possess excellent wearability first suitable for the knitting machine oil of high speed knitting equipment now, reduction is knitted
The abrasion of pin and syringe, extend its service life；In addition, knitting machine oil outward appearance is wanted water white transparency and easily washed away from fabric,
Prevent from polluting fabric；Possess certain rust-preventing characteristic, prevent equipment from getting rusty and corroding；With higher cost performance.Patent
CN101235336A《High abrasion-resisting easy-cleaning knitting machine oil composition》Disclose it is a kind of be applied to circular disc knitting machine, footwear machine with
The knitting machine oil of the equipment lubrications such as inner wear machine, including following component and weight percentage：Base oil 70~95%, activating agent 1
~10%, emulsifying agent 1~10%, cleaning agent 1~10%.The knitting machine oil possesses good lubricity, wear resistence, rust-preventing characteristic with
And the features such as cleaning, wear scar diameter minimum 0.43mm.Patent CN1995302A《Emulsifiable oil for knitting》Disclose a kind of for spinning
Knit, weave process as lubrication, the fluid composition of antistatic, antirust and cooling, including 85~92% by a variety of viscous
Degree base oil compounding the mineral type base oil and 8~15% additive that form, the additive include emulsifying agent, antirust agent,
Anti-friction composition, antioxidant, metal deactivator and distilled water, wear scar diameter 0.44mm.Therefore, the wear scar diameter of knitting machine oil is reduced
Its application will further be expanded.
The content of the invention
One of technical problems to be solved by the invention are knitting needle, syringe and the triangle mill that prior art has knitting equipment
A kind of damage, the problem of knitting machine oil wear resistence difference, there is provided new high wear-resistant knitting machine oil composition.Said composition can be used at a high speed
The lubrication of circular cyiinder knitting machine and seamless knitting equipment, has the characteristics of wear resistence is good, while provides cooling down, prevent well for equipment
Rust acts on, and ensures that knitting process is smoothed out.The two of the technical problems to be solved by the invention are to provide a kind of and solution technology
The purposes of the corresponding high wear-resistant type knitting machine oil composition of one of problem.
To solve one of above-mentioned technical problem, the technical solution adopted by the present invention is as follows：A kind of high wear-resistant type knitting machine oil
Composition, counted with parts by weight and be made up of following component：
A) 0.2~1 part of extreme pressure anti-wear additives；
B) 0.2~3 part of emulsifying agent；
C) 0.1~1 part of antioxidant；
D) 0.05~0.3 part of antirust agent；
E) 95~99 parts of base oil；
The extreme pressure anti-wear additives are selected from phosphorous acid two (2- ethylhexyls) ester, phosphorous acid two (octadecylene base) ester, castor oil
Phosphate, fatty alcohol ether phosphate, different tridecyl alcohol phosphate ester, Tryfac 5573, phosphoric acid butoxyethyl, amine neutralising phosphoric acid ester
At least one of；
The emulsifying agent is in AEO, polyoxyethylene carboxylate or APES
At least one；
The antioxidant is selected from 2- (2'- hydroxyl -5'- aminomethyl phenyls) BTA, 2- (2'- hydroxyl -5'- t-octyl benzene
Base) BTA, Irganox L135 phenol, at least one of Vanlube BHC phenol；
The antirust agent is selected from alkaline dinonyl naphthalene sulfonate barium, middle base number calcium mahogany sulfonate or sorbitan fatty acid ester
In one kind；
The base oil is selected from least one of II class hydrogenation mineral oil or III class hydrogenation mineral oil.
In above-mentioned technical proposal, the amine neutralising phosphoric acid ester, its phosphorus content is 3~10 weight %, and nitrogen content is 1.5~4
Weight %.
To solve the two of above-mentioned technical problem, the technical solution adopted by the present invention is as follows：The wear-resistant type knitting machine oil of height
Composition is used for the lubrication of high speed circular cyiinder knitting machine and seamless knitting equipment.
The preparation method of high wear-resistant type knitting machine oil composition of the invention is as follows：Base oil is added into reactor, unlatching is stirred
Mix, then by extreme pressure anti-wear additives, emulsifying agent and antioxidant add reactor, be warming up to 55~65 DEG C continue stir 1-2 hours it is straight
To composition clear, the knitting machine oil composition is produced.
The present invention by preferred extreme pressure anti-wear additives, in the case where extreme pressure anti-wear additives addition is few with emulsifying agent, antioxygen
Agent carries out compatibility, and selects the hydrogenated base oil of colourless high viscosity index (HVI), obtains high wear-resistant type knitting machine oil composition, and mill spot is straight
Footpath reaches 0.28mm, meets high speed circular knitting machine, the lubricating requirement of seamless knitting equipment, while provide well cold for equipment
But, anti-rust action, preferable technique effect is achieved.
Below by embodiment, the invention will be further elaborated.
Embodiment
【Embodiment 1~7】
High wear-resistant type knitting machine oil composition each component and its content are shown in Table 1.
Table 1
Will【Embodiment 1~7】Wear resistence detection is carried out with existing knitting machine oil, such as table 2.
【Comparative example 1】
Wear resistence detection is carried out from domestic knitting machine oil (Bamda cylinder knitting machine oil), as a result such as table 2.
【Comparative example 2】
According to document CN101235336《High abrasion-resisting easy-cleaning knitting machine oil composition》Embodiment 2 (5cst60 parts, 5#
21 parts of white oil, 10 parts of butyl phthalate, RL-33 parts, 4 parts of oleic acid, TX-101 parts, Span801 parts) disclosure preparation
Composition, and wear resistence detection is carried out, as a result such as table 2.
Table 2
| Project | Outward appearance | Wear scar diameter (mm) | Corrosion (steel disc, 100 DEG C, 3h) |
| Test method | Range estimation | SH/T 0189 | SH/T0195 |
| Embodiment 1 | Colourless transparent liquid | 0.32 | It is qualified |
| Embodiment 2 | Colourless transparent liquid | 0.37 | It is qualified |
| Embodiment 3 | Colourless transparent liquid | 0.34 | It is qualified |
| Embodiment 4 | Colourless transparent liquid | 0.33 | It is qualified |
| Embodiment 5 | Colourless transparent liquid | 0.28 | It is qualified |
| Embodiment 6 | Colourless transparent liquid | 0.35 | It is qualified |
| Comparative example 1 | Colourless transparent liquid | 0.42 | It is qualified |
| Comparative example 2 | Colourless transparent liquid | 0.43 | It is qualified |
As shown in Table 2, the abrasion resistance of the high wear-resistant knitting machine oil composition of the present invention is better than common domestic knitting machine oil.
The wear-resistant type knitting machine oil composition of height is applied on certain factory's seamless underwear machine, and production practices show, the present invention
The lubricity of knitting machine oil is good, wear-resistant sexual satisfaction technological requirement, and product water white transparency easy cleaning, will not pollute fabric, obtain
Producer is approved.
Claims (2)
1. a kind of high wear-resistant type knitting machine oil composition is used for the purposes of the lubrication of high speed circular cyiinder knitting machine and seamless knitting equipment,
The wear-resistant type knitting machine oil composition of height, is counted with parts by weight and is made up of following component：
A) 0.2~1 part of extreme pressure anti-wear additives；
B) 0.2~3 part of emulsifying agent；
C) 0.1~1 part of antioxidant；
D) 0.05~0.3 part of antirust agent；
E) 95~99 parts of base oil；
The extreme pressure anti-wear additives are selected from phosphorous acid two (2- ethylhexyls) ester, phosphorous acid two (octadecylene base) ester, castor-oil plant oleophosphoric acid
In ester, fatty alcohol ether phosphate, different tridecyl alcohol phosphate ester, Tryfac 5573, phosphoric acid butoxyethyl, amine neutralising phosphoric acid ester
It is at least one；
The emulsifying agent in AEO, polyoxyethylene carboxylate or APES extremely
Few one kind；
The antioxidant is selected from 2- (2'- hydroxyl -5'- aminomethyl phenyls) BTA, 2- (2'- hydroxyl -5'- t-octyls phenyl) benzene
And at least one of triazole, Irganox L135 phenol, Vanlube BHC phenol；
The antirust agent is in alkaline dinonyl naphthalene sulfonate barium, middle base number calcium mahogany sulfonate or sorbitan fatty acid ester
It is a kind of；
The base oil is selected from least one of II class hydrogenation mineral oil or III class hydrogenation mineral oil.
2. high wear-resistant type knitting machine oil composition is used for high speed circular cyiinder knitting machine and seamless knitting equipment according to claim 1
Lubrication purposes, it is characterised in that the amine neutralising phosphoric acid ester, its phosphorus content are 3~10 weight %, and nitrogen content is 1.5~4
Weight %.