CN104341614A - 一种阻燃耐油橡胶 - Google Patents

一种阻燃耐油橡胶 Download PDF

Info

Publication number
CN104341614A
CN104341614A CN201310319134.5A CN201310319134A CN104341614A CN 104341614 A CN104341614 A CN 104341614A CN 201310319134 A CN201310319134 A CN 201310319134A CN 104341614 A CN104341614 A CN 104341614A
Authority
CN
China
Prior art keywords
parts
flame
rubber
carbon black
resistant rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310319134.5A
Other languages
English (en)
Inventor
项宗武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Original Assignee
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd filed Critical ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority to CN201310319134.5A priority Critical patent/CN104341614A/zh
Publication of CN104341614A publication Critical patent/CN104341614A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种阻燃耐油橡胶，含有以下重量份的组分：天然橡胶100份，氢化丁腈橡胶10-20份，氧化锌4-7份，硬脂酸1-3份，炭黑10-20份，白炭黑5-10份，古马隆树脂30-40份，防老剂RD1-3份，防老剂40200.2-0.8份，硫磺0.05-1.2份，三氧化二锑10-20份。本发明阻燃耐油橡胶以天然橡胶为主要原料，加入氢化丁腈橡胶和其他助剂，用于改善天然橡胶的性能。本发明阻燃耐油橡胶具有优良的阻燃性能，耐臭氧性能、耐油性能和抗扯断性。

Description

一种阻燃耐油橡胶
技术领域
本发明涉及橡胶技术领域，具体是一种阻燃耐油橡胶。 
背景技术
天然橡胶是一种以聚异戊二烯为主要成分的天然高分子化合物。天然橡胶在常温下具有较高的弹性，稍带塑性，具有非常好的机械强度，具有优良的耐屈挠性、电绝缘性，具有较好的耐碱性能，但不耐浓强酸。 
氢化丁腈橡胶（HNBR）是由丁腈橡胶进行加氢处理而得到的一种高度饱和的弹性体。氢化丁腈橡胶具有良好的耐油性能，并且由于其高度饱和的结构，使其具有良好的耐热性能，优良的耐化学腐蚀性能，优异的耐臭氧性能，较高的抗压缩永久变形性能，高强度、高撕裂性能、耐磨性能优异等特点。 
发明内容
本发明的目的在于提供一种阻燃耐油橡胶。 
本发明的目的可以通过以下技术方案实现： 
一种阻燃耐油橡胶，其特征在于，含有以下重量份的组分：
天然橡胶                                         100份
氢化丁腈橡胶                                     10-20份
氧化锌                                            4-7份
硬脂酸                                            1-3份 
炭黑                                              10-20份
白炭黑                                             5-10份
古马隆树脂                                         30-40份
防老剂RD                                          1-3份
防老剂4020                                         0.2-0.8份
硫磺                                               0.05-1.2份
三氧化二锑                                         10-20份。
各组分重量份进一步优选为： 
天然橡胶                                          100份
氢化丁腈橡胶                                      15份
氧化锌                                            5.6份
硬脂酸                                            2份 
炭黑                                              15份
白炭黑                                            8份
古马隆树脂                                        35份
防老剂RD                                         2份
防老剂4020                                        0.5份
硫磺                                              0.8份
三氧化二锑                                        15份。
本发明的制备方法与现有技术相同。 
本发明的有益效果：本发明阻燃耐油橡胶以天然橡胶为主要原料，加入氢化丁腈橡胶和其他助剂，用于改善天然橡胶的性能。本发明阻燃耐油橡胶具有优良的阻燃性能，耐臭氧性能、耐油性能和抗扯断性。 
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。 
实施例1
一种阻燃耐油橡胶，包括以下重量份的组分：
天然橡胶                                          100份
氢化丁腈橡胶                                      15份
氧化锌                                            5.6份
硬脂酸                                            2份 
炭黑                                              15份
白炭黑                                            8份
古马隆树脂                                        35份
防老剂RD                                         1-3份
防老剂4020                                        0.5份
硫磺                                              0.8份
三氧化二锑                                        15份。
实施例2
一种阻燃耐油橡胶，包括以下重量份的组分：
天然橡胶                                         100份
氢化丁腈橡胶                                     10份
氧化锌                                            4份
硬脂酸                                            1份 
炭黑                                              10份
白炭黑                                             5份
古马隆树脂                                         30份
防老剂RD                                          1份
防老剂4020                                         0.2份
硫磺                                               0.05份
三氧化二锑                                         10份。
实施例3
一种阻燃耐油橡胶，包括以下重量份的组分：
天然橡胶                                         100份
氢化丁腈橡胶                                     20份
氧化锌                                           7份
硬脂酸                                           3份 
炭黑                                             20份
白炭黑                                           10份
古马隆树脂                                       40份
防老剂RD                                        3份
防老剂4020                                       0.8份
硫磺                                              1.2份
三氧化二锑                                        20份。

Claims (2)

1.一种阻燃耐油橡胶，其特征在于，含有以下重量份的组分：
天然橡胶                                         100份
氢化丁腈橡胶                                     10-20份
氧化锌                                            4-7份
硬脂酸                                            1-3份 
炭黑                                              10-20份
白炭黑                                             5-10份
古马隆树脂                                         30-40份
防老剂RD                                          1-3份
防老剂4020                                         0.2-0.8份
硫磺                                               0.05-1.2份
三氧化二锑                                         10-20份。
2.根据权利要求1所述的阻燃耐油橡胶，其特征在于，各组分重量份进一步优选为：
天然橡胶                                          100份
氢化丁腈橡胶                                      15份
氧化锌                                            5.6份
硬脂酸                                            2份 
炭黑                                               15份
白炭黑                                             8份
古马隆树脂                                         35份
防老剂RD                                          2份
防老剂4020                                         0.5份
硫磺                                               0.8份
三氧化二锑                                         15份。
CN201310319134.5A 2013-07-28 2013-07-28 一种阻燃耐油橡胶 Pending CN104341614A (zh)