CN104327596A - Solid ink - Google Patents
Solid ink Download PDFInfo
- Publication number
- CN104327596A CN104327596A CN201410681685.0A CN201410681685A CN104327596A CN 104327596 A CN104327596 A CN 104327596A CN 201410681685 A CN201410681685 A CN 201410681685A CN 104327596 A CN104327596 A CN 104327596A
- Authority
- CN
- China
- Prior art keywords
- solid ink
- printing
- rosin
- pigment
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses solid ink which is composed of the following ingredients in percentage by mass: 88-92% of EVA hot melt adhesive, 3-7% of rosin and 3-7% of pigment. The solid ink disclosed by the invention has a series of advantages such as excellent printing quality, rapid curing at normal temperature without roasting, no solvent volatilization and accelerated printing speed.
Description
Technical field
The invention belongs to technical field of ink, particularly relate to a kind of solid ink.
Background technology
Ink is the important materials for printing, and it by printing by pattern, literal table now on the substrate.In order to ensure the precision of printing, ink needs the rapid dry solidification of the equipment such as baking oven after printing, and this just causes equipment occupation space large.In addition, the solvent that existing ink contains easily to volatilize generation dusty gas in printing and bake process, and also can make stock dilatational strain.
Summary of the invention
For this reason, the solid ink of solvent evaporates is not had, to overcome the defect that prior art exists without the need to solidification after technical problem to be solved by this invention is to provide a kind of printing.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A kind of solid ink, is characterized in that, be grouped into by the one-tenth of following masses percentages:
EVA hot-melt adhesive 88-92%; Rosin 3-7%; Pigment 3-7%.
In a preferred embodiment of the invention, described EVA hot-melt adhesive 90%, rosin 5%; Pigment 5%.
In addition, present invention also offers the preparation method of above-mentioned solid ink, it is characterized in that: after EVA hot-melt adhesive, rosin, pigment ratio is good, add smelting furnace, stirred with the heating temperatures 3-5 of 145-155 DEG C minute, then naturally cooling; Described proportioning is quality proportioning, is respectively EVA hot-melt adhesive 88-92%, rosin 3-7%, pigment 3-7%.
In a preferred embodiment, Heating temperature asks 150 DEG C, and heat-up time is 4 minutes.
Adopt technique scheme, solid ink tool of the present invention has the following advantages:
1, printing quality is good.Solid ink can produce distinct color and remarkable printing quality on medium materials widely, as carton paper, envelope, transparent film, recycled writing paper;
2, after ink printing transfers to paper, namely normal temperature solidify, long baking oven that must be not traditional, energy-saving and emission-reduction and can save larger production space.
3, after printing, ink solidification speed is fast, is convenient to two-shot chromatography, improves print speed.
4, solvent-free volatilization, pollution-free other produces, more environmental protection.，
5, water need not be printed again or spread thermal fusing powder and can realize hot transfer printing, reduce the cost of manufacture of thermal transfer printing product.
Embodiment
Embodiment 1
The solid ink of the present embodiment, be the EVA hot-melt adhesive 88% of mass percent, rosin 5%, pigment 7% proportioning is good after add smelting furnace, stir with the heating temperatures 3 minutes of 155 DEG C, naturally cooling is formed.
Embodiment 2
The solid ink of the present embodiment, be the EVA hot-melt adhesive 90% of mass percent, rosin 5%, pigment 5% proportioning is good after add smelting furnace, stir with the heating temperatures 4 minutes of 150 DEG C, naturally cooling is formed.
Embodiment 3
The solid ink of the present embodiment, be the EVA hot-melt adhesive 92% of mass percent, rosin 7%, pigment 5% proportioning is good after add smelting furnace, stir with the heating temperatures 5 minutes of 145 DEG C, naturally cooling is formed.
In use, first heat solid ink, prints respectively the solid ink of above-described embodiment after becoming liquid state in ink on carton paper, envelope, transparent film, recycled writing paper, does not need baking oven to toast after printing.After printing, above-mentioned printing is through observing, and is in bright colors and trace is clear, meets printing quality requirement.
Claims (2)
1. a solid ink, is characterized in that, is grouped into by the one-tenth of following masses percentages:
EVA hot-melt adhesive 88-92%; Rosin 3-7%; Pigment 3-7%.
2. solid ink according to claim 1, is characterized in that: described EVA hot-melt adhesive 90%, rosin 5%; Pigment 5%.