CN103100656A - Method for preparing quick-drying solid-mold casting coating material - Google Patents
Method for preparing quick-drying solid-mold casting coating material Download PDFInfo
- Publication number
- CN103100656A CN103100656A CN2012105310607A CN201210531060A CN103100656A CN 103100656 A CN103100656 A CN 103100656A CN 2012105310607 A CN2012105310607 A CN 2012105310607A CN 201210531060 A CN201210531060 A CN 201210531060A CN 103100656 A CN103100656 A CN 103100656A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- powder
- water
- mold casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preparing a quick-drying solid-mold casting coating material. According to the method, the quick-drying solid-mold casting coating material is prepared from the following ingredients in parts by weight: 65-75 parts of quartz powder, 5-7 parts of plant ash, 10-12 parts of corundum powder, 10-12 parts of sodium bentonite, 4-6 parts of nano attapulgite, 1-2 parts of lignosulfonic acid, 0.8-1.5 parts of polyvinyl alcohol, 5-7 parts of starch paste, 1.4-1.6 parts of silica sol, 1-2 parts of nanoscale ceramic powder, 0.5-0.8 part of red ferric oxide powder and 525-535 parts of water, wherein a binder consists of a normal-temperature binder and a high-temperature binder, and the mass ratio of the normal-temperature binder to the high-temperature binder is 2: 3. The solid-mold casting coating material prepared by the method has excellent gas permeability and quick-drying performance in both high-temperature environments and low-temperature environments, thereby being capable of meeting the production requirements of large-sized cast parts.
Description
Technical field
The present invention relates to casting field, particularly a kind of preparation method of quick-drying full-mold casting coating.
Background technology
The disperse system that full-mold casting coating is comprised of the material of multiple different in kind, its composition mainly comprises the compositions such as refractory material, binding agent, carrier, nano-attapulgite and special additive, needs coating good processing performance, service behaviour, quality stability are arranged and apply reappearance.Full-mold casting coating is coated in the outer surface of foamed polystyrene pattern, could the moulding cast after the coating drying.Foamed plastics is airtight, and heat distortion temperature low (approximately 70 ℃ of left and right) is poor to the affinity of water; Liquid residue after foamed plastics melted by heating, gasification is many, and gas forming amount is large, if these gases and liquid residue can not in time be discharged, foundry goods will produce the carbon defects such as gas, carburetting, Surface Wrinkle in iron.These characteristics have determined that full-mold paint should possess following performance requirement, and namely coating should have good wetability and being coated with property, good high-temperature resistant property and elevated temperature strength and good hot permeability.
The resistance to elevated temperatures of the cast paint of prior art is relatively poor, can only be fit to shorter finding of high-temperature process time (in 200kg) and produce, and can not adapt to for the production of heavy castings (in 20 tons) and small lot handwork.Have the production technology that resistant to elevated temperatures performance can be applicable to heavy castings, but its manufacturing cost is higher, and can not be applicable to manual brushing, this coating is black, easily causes the image of working environment black pollution.
Summary of the invention
For the deficiencies in the prior art, the preparation method who the purpose of this invention is to provide a kind of quick-drying full-mold casting coating, all have quick-drying, quick-drying, good gas permeability and drip-dry full-mold casting coating under high temperature, low temperature environment, can satisfy the heavy castings production requirement.
Technical scheme of the present invention is as follows:
A kind of preparation method of quick-drying full-mold casting coating, formed by following component in weight portion: silica flour 65-75 part, plant ash 5-7 part, schmigel 10-12 part, sodium bentonite 10-12 part, nano-attapulgite 4-6 part, lignin sulfonic acid 1-2 part, polyvinyl alcohol 0.8-1.5 part, starch paste 5-7 part, Ludox 1.4-1.6 part, nanometer scale ceramics powder 1-2 part, ferric oxide red powder 0.5-0.8 part, iron ore tailings 3-5 part, waterglass 2-3 part, water 55-65 part, described preparation method comprises the steps:
1) plant ash was soaked 3-4 hour with 10-15% sulfuric acid, the deionized water washing, soaked 3-4 hour with the 10-12% sodium hydroxide solution again, extremely neutral with the deionized water washing again, then, add the starch paste, the NaOH powder of 5-9%, the suitable quantity of water that are equivalent to its weight 5-8% to mix rear pelletizing and be broken into modification plant ash particle after 2-3 hour in calcining under 500-530 ℃;
2) the modification plant ash particle that above-mentioned steps is obtained mixes with the water of nano-attapulgite, 1/3 weight, and stirring is heated to 150-160 ℃, is incubated 1-2 hour, stove is chilled to 50 ℃, is incubated 2 hours, then is heated to 100-120 ℃, be incubated 1 hour, be cooled to normal temperature with 20 ℃/hour;
3) schmigel, sodium bentonite, nanometer scale ceramics powder, starch paste, the polyvinyl alcohol with above-mentioned weight portion mixes with the water of 1/4 weight, and fully stirs, and then standing 40-60min, then slowly be heated to 75-85 ℃ and fully stirring;
4) with step 2) water of product, step 3) product, silica flour, Ludox, ferric oxide red powder, iron ore tailings, waterglass, residuals weight adds in reactor, open reactor, mixing speed is: 110-120r/min, add other raw material in stirring downhill reaction still, the temperature that heats simultaneously reactor slowly rises to 75-85 ℃, constant temperature stirs 14-18min, grinds, gets final product.
Compared with prior art, the present invention has following beneficial effect:
1) on the basis of great many of experiments, determined composition and separately the content of aggregate, nano-attapulgite, bonding agent and the auxiliary material of coating, make the effect between above-mentioned each component reach collaborative, the combination property of coating is improved.Full-mold casting coating of the present invention had both reached high anti-stick sand ability, rigidity and the resistance to elevated temperatures of raising apperance, minimized cost again.Optimization allotment through aggregate and various additives forms high current sex change fluid, all reaches better state with foamed polystyrene pattern wetability and brushability.Facts have proved, this coating just can reach the above paint thickness of 1.7mm through 2 times brushings, and the anti-stick sand that can satisfy heavy castings requires and carry needs.
2) full-mold casting coating of the present invention has good suspension and thixotropy, also has good gas permeability and higher surface strength, and preparation technology is simple, easy to operate, abundant raw materials, production cost are low.Full mold cast(ing) surface with its production is bright and clean, without carbon defects such as elephant skin; Coating is easy to peel off, and is convenient to cleaning.
The specific embodiment
A kind of preparation method of quick-drying full-mold casting coating is comprised of following component in weight portion (kilogram): 75 parts of silica flours, 7 parts of plant ash, 12 parts of schmigels, 12 parts of sodium bentonites, 4 parts of nano-attapulgites, 2 parts of lignin sulfonic acids, 0.8 part of polyvinyl alcohol, 7 parts of starch pastes, 1.6 parts of Ludox, 1 part, nanometer scale ceramics powder, 0.8 part of ferric oxide red powder, 5 parts of iron ore tailings, 2 parts of waterglass, 65 parts, water, the preparation method comprises the steps:
1) plant ash was soaked 3-4 hour with 15% sulfuric acid, the deionized water washing, soaked 3-4 hour with the 10-12% sodium hydroxide solution again, extremely neutral with the deionized water washing again, then after 2-3 hour, add the starch paste that is equivalent to its weight 5%, 9% NaOH powder, the rear pelletizing of suitable quantity of water mixing to be broken into modification plant ash particle in calcining under 500-530 ℃;
2) the modification plant ash particle that above-mentioned steps is obtained mixes with the water of nano-attapulgite, 1/3 weight, and stirring is heated to 150-160 ℃, is incubated 1-2 hour, stove is chilled to 50 ℃, is incubated 2 hours, then is heated to 100-120 ℃, be incubated 1 hour, be cooled to normal temperature with 20 ℃/hour;
3) schmigel, sodium bentonite, nanometer scale ceramics powder, starch paste, the polyvinyl alcohol with above-mentioned weight portion mixes with the water of 1/4 weight, and fully stirs, and then standing 40-60min, then slowly be heated to 75-85 ℃ and fully stirring;
4) with step 2) water of product, step 3) product, silica flour, Ludox, ferric oxide red powder, iron ore tailings, waterglass, residuals weight adds in reactor, open reactor, mixing speed is: 110-120r/min, add other raw material in stirring downhill reaction still, the temperature that heats simultaneously reactor slowly rises to 75-85 ℃, constant temperature stirs 14-18min, grinds, gets final product.
Utilize the suspensibility of coating placement after 42 hours of method preparation of the present invention greater than 94%; The shear stress of coating is limited to 18-22Pa; Be 42-45s with the apparent viscosity value that is coated with 4 viscometer determining coating, thixotroping rate 15-18%, the brushing index of coating, an amount of dropping down and a time of dropping down are respectively 5.8,0.6g and 9s.The normal temperature strength of coating is higher than 690g/mm.Through the intensity of paint coatings after 1200 ℃ of roastings higher than 490g/mm.The normal temperature gas permeability of coating is higher than 12cm
2(kPamin)
-1, hot permeability is greater than 22cm
2(kPamin)
-1
Claims (1)
1. the preparation method of a quick-drying full-mold casting coating, it is characterized in that, formed by following component in weight portion: silica flour 65-75 part, plant ash 5-7 part, schmigel 10-12 part, sodium bentonite 10-12 part, nano-attapulgite 4-6 part, lignin sulfonic acid 1-2 part, polyvinyl alcohol 0.8-1.5 part, starch paste 5-7 part, Ludox 1.4-1.6 part, nanometer scale ceramics powder 1-2 part, ferric oxide red powder 0.5-0.8 part, iron ore tailings 3-5 part, waterglass 2-3 part, water 55-65 part, described preparation method comprises the steps:
1) plant ash was soaked 3-4 hour with 10-15% sulfuric acid, the deionized water washing, soaked 3-4 hour with the 10-12% sodium hydroxide solution again, extremely neutral with the deionized water washing again, then, add the starch paste, the NaOH powder of 5-9%, the suitable quantity of water that are equivalent to its weight 5-8% to mix rear pelletizing and be broken into modification plant ash particle after 2-3 hour in calcining under 500-530 ℃;
2) the modification plant ash particle that above-mentioned steps is obtained mixes with the water of nano-attapulgite, 1/3 weight, and stirring is heated to 150-160 ℃, is incubated 1-2 hour, stove is chilled to 50 ℃, is incubated 2 hours, then is heated to 100-120 ℃, be incubated 1 hour, be cooled to normal temperature with 20 ℃/hour;
3) schmigel, sodium bentonite, nanometer scale ceramics powder, starch paste, the polyvinyl alcohol with above-mentioned weight portion mixes with the water of 1/4 weight, and fully stirs, and then standing 40-60min, then slowly be heated to 75-85 ℃ and fully stirring;
4) with step 2) water of product, step 3) product, silica flour, Ludox, ferric oxide red powder, iron ore tailings, waterglass, residuals weight adds in reactor, open reactor, mixing speed is: 110-120r/min, add other raw material in stirring downhill reaction still, the temperature that heats simultaneously reactor slowly rises to 75-85 ℃, constant temperature stirs 14-18min, grinds, gets final product.