CN104327443A - Flame-retardant temperature-resistant glass-fiber-reinforced ABS composite plastic - Google Patents
Flame-retardant temperature-resistant glass-fiber-reinforced ABS composite plastic Download PDFInfo
- Publication number
- CN104327443A CN104327443A CN201410514918.8A CN201410514918A CN104327443A CN 104327443 A CN104327443 A CN 104327443A CN 201410514918 A CN201410514918 A CN 201410514918A CN 104327443 A CN104327443 A CN 104327443A
- Authority
- CN
- China
- Prior art keywords
- composite plastic
- flame
- parts
- fiber
- abs composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant temperature-resistant glass-fiber-reinforced ABS composite plastic and belongs to the technical filed of high polymer materials. The flame-retardant temperature-resistant glass-fiber-reinforced ABS composite plastic comprises following components: ABS, polystyrene, nylon, alkali-free glass fibers, calcium oxide, bromotriazine, bronze powder, an anti-static agent, a coupling agent, a thermal-stabilizing agent, a compatilizer and an anti-oxidant. The composite plastic is good in flame-retardant performance, is excellent in wear-resistant performance, is not liable to deform at a high temperature, is low in cost and is long in service life.
Description
Technical field
The present invention relates to a kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, belong to technical field of polymer materials.
Background technology
Safety helmet, exhaust equipment, the equipment such as electric fan generally need to have good flame-retardance energy, heat resistance, certain physical strength and the indeformable feature of high temperature.Polypropylene-butadiene-styrene (ABS) resin is the conventional starting material making these equipment always.But the multinomial requirement such as conventional ABS plastic generally can not meet flame retardant properties, heat resistance, wear resisting property simultaneously, not yielding.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, the requirement of these plastics solve conventional ABS plastic can not take into account flame retardant properties, heat resistance, wear resisting property simultaneously, not yielding multinomial performance of Denging.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, is characterized in that: the component comprising following weight part, ABS 20-25 part, polystyrene 15-25 part, nylon 15-25 part, alkali free glass fibre 15-45 part, calcium oxide 2-6 part, brominated triazine 5-10 part, bronze powder 5-12 part, static inhibitor 3-5 part, coupling agent 0.5-1.6 part, thermo-stabilizer 0.1-1.2 part, compatilizer 0.5-1.2 part, antioxidant 0.6-2.3 part.
Further, described thermo-stabilizer is sodium stearate.
The fire-retardant heatproof glass fiber reinforced ABS composite plastic adopting technique scheme to produce has following beneficial effect, and fire resistance is good, and wear resisting property is excellent, and not yielding under high temperature, cost is low, long service life.Can be used as safety helmet, exhaust equipment, the temperature tolerances such as electric fan require high equipment.
Embodiment
Below in conjunction with concrete implementation column, the present invention is set forth further, but do not limit the present invention.
Embodiment 1
A kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, is characterized in that: the component comprising following weight part, ABS 20 parts, polystyrene 15 parts, nylon 15 parts, alkali free glass fibre 45 parts, 6 parts, calcium oxide, brominated triazine 5 parts, bronze powder 5 parts, 3 parts, static inhibitor, coupling agent 1.6 parts, thermo-stabilizer 0.1 part, compatilizer 0.5 part, antioxidant 0.6 part.
Embodiment 2
A kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, is characterized in that: the component comprising following weight part, ABS 25 parts, polystyrene 25 parts, nylon 25 parts, alkali free glass fibre 45 parts, 6 parts, calcium oxide, brominated triazine 10 parts, bronze powder 12 parts, 5 parts, static inhibitor, coupling agent 1.6 parts, thermo-stabilizer 0.1 part, compatilizer 1.2 parts, antioxidant 2.3 parts.
Embodiment 3
A kind of fire-retardant heatproof glass fiber reinforced ABS composite plastic, is characterized in that: the component comprising following weight part, ABS 22 parts, polystyrene 20 parts, nylon 20 parts, alkali free glass fibre 30 parts, 4 parts, calcium oxide, brominated triazine 8 parts, bronze powder 10 parts, 4 parts, static inhibitor, coupling agent 1.2 parts, thermo-stabilizer 0.8 part, compatilizer 0.9 part, antioxidant 1.8 parts.
The performance test results of the glass fiber reinforced composite plastics obtained according to embodiment 1 to 3 is as shown in table 1.
| Test event | Testing standard | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Tensile strength (MPa) | ASTMD638-2008 | 140 | 135 | 128 |
| Flexural strength | ASTMD790-2003 | 160 | 168 | 159 |
| Izod non-notch impacts (J/m) | ASTMD256-2006 | 60 | 54 | 57 |
| Flame retardant properties is tested | UL94-2006 | V-0 | V-0 | V-0 |
| Heat resistance 120 DEG C (MPA) | ISO 6721-2 | Pass through | Pass through | Pass through |
Claims (2)
1. a fire-retardant heatproof glass fiber reinforced ABS composite plastic, is characterized in that: the component comprising following weight part, ABS 20-25 part, polystyrene 15-25 part, nylon 15-25 part, alkali free glass fibre 15-45 part, calcium oxide 2-6 part, brominated triazine 5-10 part, bronze powder 5-12 part, static inhibitor 3-5 part, coupling agent 0.5-1.6 part, thermo-stabilizer 0.1-1.2 part, compatilizer 0.5-1.2 part, antioxidant 0.6-2.3 part.
2. ABS composite plastic according to claim 1, is characterized in that: described thermo-stabilizer is sodium stearate.