CN104326663A - Zinc oxide-free microcrystalline - Google Patents
Zinc oxide-free microcrystalline Download PDFInfo
- Publication number
- CN104326663A CN104326663A CN201310309676.4A CN201310309676A CN104326663A CN 104326663 A CN104326663 A CN 104326663A CN 201310309676 A CN201310309676 A CN 201310309676A CN 104326663 A CN104326663 A CN 104326663A
- Authority
- CN
- China
- Prior art keywords
- microlite
- parts
- oxide
- zinc oxide
- microcrystalline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to zinc oxide-free microcrystalline comprising the following components by weight: 60-70 parts of silica; 7-8 parts of aluminum oxide; 16-17 parts of calcium oxide; 0.7-1.2 parts of boron oxide; 4-6 parts of barium oxide; 1-2 parts of potassium oxide; 4-6 parts of sodium oxide; and 0.7-1.2 parts of magnesium oxide. The materials of the zinc oxide-free microcrystalline do not contain zinc oxide, and has no effect on microcrystalline hardness, the enterprise production cost is reduced, and the zinc oxide-free microcrystalline has the advantages of low cost and convenient production, improves the enterprise production efficiency, and greatly satisfies the demand of people for the microcrystalline in living and production.
Description
Technical field
The invention belongs to building materials technology field, relate to microlite, especially a kind of non-oxidation zinc microlite.
Background technology
Along with the develop rapidly of building material industry, all kinds of building material product grows with each passing day, and microlite is also more and more subject to concern and the favor of people with its superior property.
Microlite is a kind of polycrystalline material obtained by the crystallization of control glass.Current microlite has defined a kind of material of special class, and it is various in style, different properties, has purposes very widely.Microlite is the one in the numerous kind of devitrified glass, it is a kind of novel high-grade building and ornament materials, have intensity high, resistance to wear, corrosion-resistant, weather resistance, do not absorb water, physicochemical property and the uniform hue such as cleaning convenience, no radioactivity pollute, gloss is soft sparkling and crystal-clear, and surface compact has no time to wait excellent appearance characteristics.Therefore microlite various aspects of performance is all better than lithotome, has been widely used in now the high-grade finished faced such as building inside and outside wall, ground and corridor post.
At present, need in the raw material of microlite to use zinc oxide, the addition of zinc oxide affects the hardness of microlite, the hardness of the higher then microlite of addition of zinc oxide is better, but, because the price of zinc oxide is higher, the production cost thus causing microlite is higher, improves the production cost of enterprise.
By retrieval, find the following patent publication us relevant to patent application of the present invention:
1, the method (CN101817640A) of microlite is manufactured with tailings of high silicon iron, disclose a kind of method utilizing iron tailings to manufacture microlite, it is characterized in that: iron tailings accounts for 30 ~ 70% of admixtion, all the other compositions are quartz sand, aluminum oxide, zinc oxide, barium carbonate, cupric oxide, chromium sesquioxide etc.The present invention utilizes waste to manufacture microlite, not only reduces the volume of cargo in storage of mine tailing, alleviates environmental pollution, can also enhance product performance, reduces production cost, the Social benefit and economic benefit therefore had.
2, environmental protection type nano composite microlite (CN102021987A), relate to a kind of environmental protection type nano composite microlite, there is a plaque layer, described plaque layer is compounded with microlite ornament layer, enhancing card is set in described plaque layer, uniform multiple combined hole and multiple stud on this enhancing card, described compound crystallite slabstone peripheral region arranges metal edge frame, described plaque layer is cement and pearlstone composite bed, and described microlite ornament layer comprises resin, aluminium hydroxide meal, aluminium hydroxide fine powder, glass granules, pigment, microlith powder; Appearance of the present invention has agate stone effect, waterproof, acid and alkali-resistance, can be used for the decoration of wall, top ceiling, floor, furniture.
3, a kind of microlite and preparation method (CN1247879), disclose a kind of microlite, its composition by unsaturated polyester resin is: 45-55%, light calcium carbonate is: 35-45%, mill base is: 1-10%, promotor is: 1-4%, solidifying agent is: 1-4%, by unsaturated polyester resin, mill base, light calcium carbonate is divided into halves, and mix thoroughly rear add promotor and solidifying agent respectively after mix thoroughly, injection molding is mixed in whole mixing thoroughly again, through the demoulding, polishing, finished product after polishing, it is low that this microlite has raw materials cost, easily shaping, shock-resistant after finished product, sense of touch is good, be applicable to batch production.
By contrast, there are the different of essence in patent application of the present invention and above-mentioned patent publication us.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art part, provide a kind of with low cost, easy to make, reduce the non-oxidation zinc microlite of the production cost of enterprise.
The technical scheme that the present invention realizes object is:
A kind of non-oxidation zinc microlite, its moiety and parts by weight as follows:
And, described non-oxidation zinc microlite, its moiety and parts by weight as follows:
And, the step of the preparation method of described non-oxidation zinc microlite is as follows: after each raw material precise, in the smelting furnace of 1600 ° of C, natural inorganic material is melt into glass metal, shrend, microlite is formed again through 1200 ° of C crystallizations, and then through grinding and polishing, cutting, deep processing, after the assay was approved, obtain non-oxidation zinc microlite finished product.
Advantage of the present invention and beneficial effect are:
Oxygen-freeization zinc in the raw material of microlite of the present invention, but but can not affect the hardness of microlite, reduce the production cost of enterprise, and it is with low cost, easy to make, improve the production efficiency of enterprise, greatly meet people in life and the demand to microlite in producing.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not determinate, can not limit protection scope of the present invention with this.
If no special instructions, the reagent used in the present invention is conventional reagent; If no special instructions, the method used is ordinary method.
Embodiment 1
A kind of non-oxidation zinc microlite, its moiety and parts by weight as follows:
The preparation method of above-mentioned non-oxidation zinc microlite, step is as follows:
After each raw material precise, in the smelting furnace up to 1600 ° of C, natural inorganic material is melt into glass metal (magma), shrend, microlite (stone) is formed again through 1200 ° of C crystallizations, and then through grinding and polishing, cutting, deep processing, after the assay was approved, obtain non-oxidation zinc microlite finished product.
Embodiment 2
A kind of non-oxidation zinc microlite, its moiety and parts by weight as follows:
The preparation method of above-mentioned non-oxidation zinc microlite is with embodiment 1.
Embodiment 3
A kind of non-oxidation zinc microlite, its moiety and parts by weight as follows:
The preparation method of above-mentioned non-oxidation zinc microlite is with embodiment 1.
Claims (3)
1. a non-oxidation zinc microlite, is characterized in that: its moiety and parts by weight as follows:
2. non-oxidation zinc microlite according to claim 1, is characterized in that: its moiety and parts by weight as follows:
3. non-oxidation zinc microlite according to claim 1, it is characterized in that: the step of the preparation method of described non-oxidation zinc microlite is as follows: after each raw material precise, in the smelting furnace of 1600 ° of C, natural inorganic material is melt into glass metal, shrend, microlite is formed again through 1200 ° of C crystallizations, and then through grinding and polishing, cutting, deep processing, after the assay was approved, obtain non-oxidation zinc microlite finished product.