CN104312537B - 一种建筑工地抑尘剂及其制备方法 - Google Patents
一种建筑工地抑尘剂及其制备方法 Download PDFInfo
- Publication number
- CN104312537B CN104312537B CN201410530760.3A CN201410530760A CN104312537B CN 104312537 B CN104312537 B CN 104312537B CN 201410530760 A CN201410530760 A CN 201410530760A CN 104312537 B CN104312537 B CN 104312537B
- Authority
- CN
- China
- Prior art keywords
- parts
- construction site
- dust suppressant
- hydroxypropylcelliloxe
- lignocellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明建筑工地抑尘剂由如下重量份数的组分制成:高取代羟丙基纤维素66份、木质纤维素50份、聚乳酸20份、二烷基二硫代磷酸锌4份、辛烯基琥珀酸铝淀粉6份、十二烷基磺酸钠1份、硬脂酸锌8份、丙基三甲氧基硅烷6份、去离子水25份制成。制备方法,包括:(1)将高取代羟丙基纤维素、木质纤维素、聚乳酸制成200目以上粉末,搅拌混合均匀;(2)取二烷基二硫代磷酸锌、辛烯基琥珀酸铝淀粉、十二烷基磺酸钠、硬脂酸锌、丙基三甲氧基硅烷加入到去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,既得。
Description
技术领域
本发明属于生态环保技术领域,具体涉及一种建筑工地抑尘剂及其制备方法。
背景技术
随着经济高速发展,旧城改造和市政建设日新月异,建筑物拆除和建筑工地随处可见,相对明显的标志就是烟尘缭绕,大量灰尘随风飘扬。给周边居民的生活和工作带来不便,施工单位也常常招来城管、环保部门的“光临”和罚单。建筑物拆除的常规控制扬尘措施一般为高压喷水(浪费大量市政自来水),其效果并不理想;建筑工地土方裸露堆积,有的采用无纺布或遮阳网遮盖,遇到大风天气扬尘依然存在,而土方运输大部分没有采取抑尘措施,包括装卸环节和运输路段的路面扬尘处理。
抑尘剂是由新型多功能高分子聚合物组合而成。聚合物分子间的交联度会形成网状结构,同时分子间存在各种离子基团,能与离子之间产生较强的亲合力。它的作用机理是通过捕捉、吸附、团聚粉尘微粒,将其紧锁于网状结构之内,起到湿润、粘接、凝结、吸湿、防尘、防浸蚀和抗冲刷的作用。抑尘剂具有良好的成膜特性,可以有效的固定尘埃并在物料表面形成防护膜。
发明内容
本发明的目的是提供一种无腐蚀、无污染、可生物降解建筑工地抑尘剂及其制备方法。
本发明建筑工地抑尘剂;由如下重量份数的组分制成: 高取代羟丙基纤维素60~68份、木质纤维素48~53份、聚乳酸18~25份、二烷基二硫代磷酸锌3~5份、辛烯基琥珀酸铝淀粉4~6份、十二烷基磺酸钠1~2份、硬脂酸锌6~10份、丙基三甲氧基硅烷6~10份、去离子水20~30份。
作为优化,该建筑工地抑尘剂;由如下重量份数的组分制成: 高取代羟丙基纤维素66份、木质纤维素50份、聚乳酸20份、二烷基二硫代磷酸锌4份、辛烯基琥珀酸铝淀粉6份、十二烷基磺酸钠1份、硬脂酸锌8份、丙基三甲氧基硅烷6份、去离子水25份制成。
制备该建筑工地抑尘剂的方法,包括以下步骤:
(1)将所述重量分数的高取代羟丙基纤维素、木质纤维素、聚乳酸制成200目以上粉末,搅拌混合均匀;
(2)取所述重量分数的二烷基二硫代磷酸锌、辛烯基琥珀酸铝淀粉、十二烷基磺酸钠、硬脂酸锌、丙基三甲氧基硅烷加入到去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;
(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,既得。
本发明建筑工地抑尘剂,抑尘效果优异,抑尘周期长(喷洒一次抑尘效果可达六个月以上),用量少,适应风力范围广,性能稳定,使用方便,施工简单,无毒副作用,且对物料和周围环境不会造成二次污染。
抑尘剂的抑尘性能在中国科学院沙漠与沙漠化重点实验室用风洞试验进行表征。具体按照QB/KH SB-BS08-2003 QB/KH《风沙打磨、防沙尘密封、风沙破坏性风洞鉴定方法》和SB-BS03-2003《土壤风蚀强度、分布及其变化的风洞测定方法》进行风洞实验。分别使用实施例1、实施例2、实施例3中抑尘剂,抑尘剂的使用浓度为5%,实验样品制备过程如下:选取(285mm*185mm*30mm )不锈钢托盘并编号,抑尘剂用量均为60克/平方米。用普通花洒喷洒抑尘剂,抑尘剂喷洒后的试样放置一个月,目测外观无变化,进行风洞试验。风损及风损率按下式计算:风损=吹前试样重-吹后试样重;风损率=风损/前试样重。试验结果如表1:
粘度的测定,取5ml制备好的试剂,在25℃下用NDJ-7型旋转粘度计进行测定。成膜时间的测定,按照GBT 13477.5-2002进行测试,并记录成膜时间。表面张力的测定,采用瑞士Krüss公司生产的Krüss-k12程序界面张力仪,用吊片法恒温25℃测试各种溶液的表面张力。有关结果见表2
具体实施方式
下面给出的实施例拟对本发明作进一步说明,但不能理解为是对本发明保护范围的限制,本领域技术人员根据本发明内容对本发明的一些非本质的改进和调整,仍属于本发明的保护范围。
实施例1: (1)将高取代羟丙基纤维素66克、木质纤维素50克、聚乳酸20克制成200目以上粉末,搅拌混合均匀;
(2)取二烷基二硫代磷酸锌4克、辛烯基琥珀酸铝淀粉6克、十二烷基磺酸钠1克、硬脂酸锌8克、丙基三甲氧基硅烷6克加入到25克去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;
(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,既得。
实施例2: (1)将高取代羟丙基纤维素68克、木质纤维素53克、聚乳酸25克制成200目以上粉末,搅拌混合均匀;
(2)取二烷基二硫代磷酸锌5克、辛烯基琥珀酸铝淀粉6克、十二烷基磺酸钠2克、硬脂酸锌10克、丙基三甲氧基硅烷10克加入到30克去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;
(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,既得。
实施例3: (1)将高取代羟丙基纤维素60克、木质纤维素48克、聚乳酸18克制成200目以上粉末,搅拌混合均匀;
(2)取二烷基二硫代磷酸锌3克、辛烯基琥珀酸铝淀粉4克、十二烷基磺酸钠1克、硬脂酸锌6克、丙基三甲氧基硅烷6克加入到20克去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;
(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,既得。
Claims (3)
1.一种建筑工地抑尘剂,其特征在于由如下重量份数的组分制成:高取代羟丙基纤维素60~68份、木质纤维素48~53份、聚乳酸18~25份、二烷基二硫代磷酸锌3~5份、辛烯基琥珀酸铝淀粉4~6份、十二烷基磺酸钠1~2份、硬脂酸锌6~10份、丙基三甲氧基硅烷6~10份、去离子水20~30份。
2.根据权利要求1所述的建筑工地抑尘剂,其特征在于由如下重量份数的组分制成:高取代羟丙基纤维素66份、木质纤维素50份、聚乳酸20份、二烷基二硫代磷酸锌4份、辛烯基琥珀酸铝淀粉6份、十二烷基磺酸钠1份、硬脂酸锌8份、丙基三甲氧基硅烷6份、去离子水25份。
3.一种制备权利要求1、2任一项所述建筑工地抑尘剂的方法,其特征在于包括以下步骤:
(1)将所述重量份数的高取代羟丙基纤维素、木质纤维素、聚乳酸制成200目以上粉末,搅拌混合均匀;
(2)取所述重量份数的二烷基二硫代磷酸锌、辛烯基琥珀酸铝淀粉、十二烷基磺酸钠、硬脂酸锌、丙基三甲氧基硅烷加入到去离子水中;加热到50~58℃,在超声波条件下,搅拌40~50分钟;
(3)将步骤(1)中混合物和步骤(2)中混合物搅拌均匀,在20℃条件下真空干燥后,即得。