CN104312462A - Novel adhesive for wood floor - Google Patents
Novel adhesive for wood floor Download PDFInfo
- Publication number
- CN104312462A CN104312462A CN201410506428.3A CN201410506428A CN104312462A CN 104312462 A CN104312462 A CN 104312462A CN 201410506428 A CN201410506428 A CN 201410506428A CN 104312462 A CN104312462 A CN 104312462A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood floor
- novel adhesive
- wood
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel adhesive for a wood floor. The novel adhesive for the wood floor is characterized by being prepared from the following raw materials in parts by weight: 5-10 parts of water glass, 2-4.7 parts of borax, 1.7-4.5 parts of vinyl versatate, 1.2-2.7 parts of polyurethane, 1.4-2.6 parts of decyl dimethyl ammonium chloride, 0.5-1.2 parts of potassium hydroxide, 2.5-5 parts of milled wood lignin and 0.5-1.6 parts of alkyl polysulfide. Compared with an existing adhesive product, the novel adhesive for the wood floor has the advantages that depositing time is long, and construction efficiency is effectively improved; complete curing time required by the novel adhesive for the wood floor at room temperature is short; meanwhile, raw materials of the novel adhesive for the wood floor are safe and pollution-free and can release negative oxygen ions beneficial to a human body, so that both environmental protection and air purification are realized, and quality of the air is improved.
Description
Technical field
The present invention relates to a kind of wood flooring tackiness agent, belong to building material field.
Background technology
Tackiness agent plays vital effect in laying floor, and the quality of tackiness agent directly has influence on laying quality.On market, existing two-pack timber floor glue still has the following disadvantages; The sizing agent configured can assembly time short, easily solidification is scrapped, and affects operating efficiency; Under room temperature, required complete set time is long; Viscosity is bigger than normal, and mobility is poor, and construction exists certain difficulty, and the feature of environmental protection is not enough.In sum, in existing Bi-component adhesive for wood floor, Problems existing has become existing flooring adhesive field technical barrier urgently to be resolved hurrily.
Summary of the invention
For prior art exist deficiency, technical problem to be solved by this invention is, provides a kind of wood flooring tackiness agent, can assembly time shorter for longer, complete set time, environmental protection.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of wood flooring tackiness agent,
Be made up of the raw material of following parts by weight: water glass 5-10 part, borax 2-4.7 part, tertiary ethylene carbonate 1.7-4.5 part, urethane 1.2-2.7 part, decyl dimethyl ammonium chloride 1.4-2.6 part, potassium hydroxide 0.5-1.2 part, Milled wood lignin 2.5-5 part and alkyl polysulfide 0.5-1.6 part.
Optimize, above-mentioned wood flooring tackiness agent, be made up of the raw material of following parts by weight:
Water glass 8 parts, borax 3.6 parts, tertiary ethylene carbonate 2.8 parts, urethane 2.5 parts, decyl dimethyl ammonium chloride 1.7 parts, potassium hydroxide 0.5-1.20.7 part, Milled wood lignin 3.2 parts and alkyl polysulfide 1.2 parts.
Floor glue of the present invention compared with existing product, the present invention can assembly time long, effectively improve operating efficiency; Under room temperature, invention adhesive is short for required set time completely; The raw materials used equal safety non-pollution of invention adhesive, and can discharge the negative oxygen ion useful to human body, not only environmental protection but also capable of purifying air, improve Air quality.
Embodiment
embodiment 1
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Water glass 5 parts, borax 2 parts, tertiary ethylene carbonate 1.7 parts, urethane 1.2 parts, decyl dimethyl ammonium chloride 1.4 parts, 0.5 part, potassium hydroxide, Milled wood lignin 2.5 parts and alkyl polysulfide 0.5 part.
embodiment 2
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Water glass 5-10 part, borax 2-4.7 part, tertiary ethylene carbonate 1.7-4.5 part, urethane 1.2-2.7 part, decyl dimethyl ammonium chloride 1.4-2.6 part, potassium hydroxide 0.5-1.2 part, Milled wood lignin 2.5-5 part and alkyl polysulfide 0.5-1.6 part.
embodiment 3
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Water glass 8 parts, borax 3.6 parts, tertiary ethylene carbonate 2.8 parts, urethane 2.5 parts, decyl dimethyl ammonium chloride 1.7 parts, potassium hydroxide 0.5-1.20.7 part, Milled wood lignin 3.2 parts and alkyl polysulfide 1.2 parts.
Floor glue of the present invention compared with existing product, the present invention can assembly time long, effectively improve operating efficiency; Under room temperature, invention adhesive is short for required set time completely; The raw materials used equal safety non-pollution of invention adhesive, and can discharge the negative oxygen ion useful to human body, not only environmental protection but also capable of purifying air, improve Air quality.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a wood flooring tackiness agent, is characterized in that: be made up of the raw material of following parts by weight:
Water glass 5-10 part, borax 2-4.7 part, tertiary ethylene carbonate 1.7-4.5 part, urethane 1.2-2.7 part, decyl dimethyl ammonium chloride 1.4-2.6 part, potassium hydroxide 0.5-1.2 part, Milled wood lignin 2.5-5 part and alkyl polysulfide 0.5-1.6 part.
2. wood flooring tackiness agent according to claim 1, is characterized in that:
Be made up of the raw material of following parts by weight: water glass 8 parts, borax 3.6 parts, tertiary ethylene carbonate 2.8 parts, urethane 2.5 parts, decyl dimethyl ammonium chloride 1.7 parts, potassium hydroxide 0.5-1.20.7 part, Milled wood lignin 3.2 parts and alkyl polysulfide 1.2 parts.