CN105273424A - Multifunctional vibration-absorptive material - Google Patents
Multifunctional vibration-absorptive material Download PDFInfo
- Publication number
- CN105273424A CN105273424A CN201510820768.8A CN201510820768A CN105273424A CN 105273424 A CN105273424 A CN 105273424A CN 201510820768 A CN201510820768 A CN 201510820768A CN 105273424 A CN105273424 A CN 105273424A
- Authority
- CN
- China
- Prior art keywords
- parts
- density polyethylene
- graphite
- zinc oxide
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multifunctional vibration-absorptive material. The multifunctional vibration-absorptive material includes calcium carbonate, barium stearate, zinc oxide, a plasticizer, a foaming agent, plant fibers, graphite, high density polyethylene and low density polyethylene. The multifunctional vibration-absorptive material is prepared from, by weight, 3-5 parts of the calcium carbonate, 3-8 parts of the barium stearate, 2-6 parts of the zinc oxide, 1-3 parts of the plasticizer, 0.5-0.8 part of the foaming agent, 5-15 parts of the plant fibers, 0.2-0.6 part of the graphite, 1-10 parts of the high density polyethylene and 1-10 parts of the low density polyethylene according to the mass percent. In this way, the multifunctional vibration-absorptive material is good in vibration-absorptive effect and can have a good effect and function in the home furnishing industry, the automobile industry and the construction industry; besides, due to the fact that the formula is improved, raw materials are greatly saved, and social development can be better promoted.
Description
Technical field
The present invention relates to a kind of novel material, particularly relate to Multifunctional shock-absorbing material.
Background technology
Cushioning material of the prior art also has a lot, and effect is also good, but in formula and manpower, is but with very large deficiency and needs improvements in prior art, and the present invention can head it off.
Summary of the invention
The technical problem that the present invention mainly solves be how to provide a kind of damping effect good, good effect and effect can be had in household, automobile and building trade, and in formula, had improvement because of it, in raw material, there is very large saving, helped lend some impetus to the novel material formula of the development of society.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of Multifunctional shock-absorbing material, comprise: calcium carbonate, barium stearate, zinc oxide, softening agent, whipping agent, vegetable fibre, graphite, high density polyethylene(HDPE) and Low Density Polyethylene, described Multifunctional shock-absorbing material calculates according to mass percent, comprise weight part: calcium carbonate 3-5 part, barium stearate 3-8 part, zinc oxide 2-6 part, softening agent 1-3 part, whipping agent 0.5-0.8 part, vegetable fibre 5-15 part, graphite 0.2-0.6 part, high density polyethylene(HDPE) 1-10 part and Low Density Polyethylene 1-10 part.
In a preferred embodiment, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 4 parts, 3 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.6 part, 10 parts, vegetable fibre, 0.3 part, graphite, high density polyethylene(HDPE) 2 parts and Low Density Polyethylene 3 parts.
In a preferred embodiment, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 6 parts, 5 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.7 part, 12 parts, vegetable fibre, 0.5 part, graphite, high density polyethylene(HDPE) 8 parts and Low Density Polyethylene 8 parts.
The invention has the beneficial effects as follows: damping effect is good, can have good effect and effect in household, automobile and building trade, and in formula, had improvement because of it, had very large saving, help lend some impetus to the development of society in raw material.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
A kind of Multifunctional shock-absorbing material is provided in one particular embodiment of the present invention, described Multifunctional shock-absorbing material comprises: calcium carbonate, barium stearate, zinc oxide, softening agent, whipping agent, vegetable fibre, graphite, high density polyethylene(HDPE) and Low Density Polyethylene, described Multifunctional shock-absorbing material calculates according to mass percent, comprise weight part: calcium carbonate 3-5 part, barium stearate 3-8 part, zinc oxide 2-6 part, softening agent 1-3 part, whipping agent 0.5-0.8 part, vegetable fibre 5-15 part, graphite 0.2-0.6 part, high density polyethylene(HDPE) 1-10 part and Low Density Polyethylene 1-10 part.
Preferably, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 4 parts, 3 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.6 part, 10 parts, vegetable fibre, 0.3 part, graphite, high density polyethylene(HDPE) 2 parts and Low Density Polyethylene 3 parts.
Preferably, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 6 parts, 5 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.7 part, 12 parts, vegetable fibre, 0.5 part, graphite, high density polyethylene(HDPE) 8 parts and Low Density Polyethylene 8 parts.
Therefore, the present invention has the following advantages: damping effect is good, can have good effect and effect in household, automobile and building trade, and in formula, had improvement because of it, had very large saving, help lend some impetus to the development of society in raw material.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a Multifunctional shock-absorbing material, it is characterized in that, comprise: calcium carbonate, barium stearate, zinc oxide, softening agent, whipping agent, vegetable fibre, graphite, high density polyethylene(HDPE) and Low Density Polyethylene, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: calcium carbonate 3-5 part, barium stearate 3-8 part, zinc oxide 2-6 part, softening agent 1-3 part, whipping agent 0.5-0.8 part, vegetable fibre 5-15 part, graphite 0.2-0.6 part, high density polyethylene(HDPE) 1-10 part and Low Density Polyethylene 1-10 part.
2. Multifunctional shock-absorbing material according to claim 1, it is characterized in that, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 4 parts, 3 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.6 part, 10 parts, vegetable fibre, 0.3 part, graphite, high density polyethylene(HDPE) 2 parts and Low Density Polyethylene 3 parts.
3. Multifunctional shock-absorbing material according to claim 1, it is characterized in that, described Multifunctional shock-absorbing material calculates according to mass percent, comprises weight part: 4 parts, calcium carbonate, barium stearate 6 parts, 5 parts, zinc oxide, 2 parts, softening agent, whipping agent 0.7 part, 12 parts, vegetable fibre, 0.5 part, graphite, high density polyethylene(HDPE) 8 parts and Low Density Polyethylene 8 parts.